Electrochemical Properties of Highly Ordered TiO2 Nanotube Arrays as an Anode Material for Lithium-Ion Batteries

Li Li Wang; Shi Chao Zhang; Xiao Meng Wu

doi:10.4028/www.scientific.net/AMM.130-134.1281

Paper Titles

Experimental Research on Buckling of Nano-Thin Film under Impact Load
p.1262

Preparation of AlNPs/CMCN Composite Nanofibers by Electrospinning
p.1266

One-Step Synthesis of Fe₃S₄ Micro-Crystals and its Facile Transformation to Fe₇S₈ Micro-Crystals
p.1270

Influence of MoS₂ on the Microstructures and Properties of Ni-Based Alloying Coating
p.1276

Electrochemical Properties of Highly Ordered TiO₂ Nanotube Arrays as an Anode Material for Lithium-Ion Batteries
p.1281

Analysis on Efficiency of Power Generation for Various Sun Tracking and Fixed Solar Cells under Different Sunshine Environment
p.1286

Wind Energy Resource Assessment for Wind Farm
p.1295

Study on the Design Process Based on Green Design
p.1298

The Effect of the Ratio of H/W on the Performance of the Hybrid Wall Powered by Solar Energy
p.1302

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 130-134Electrochemical Properties of Highly Ordered TiO2...

Electrochemical Properties of Highly Ordered TiO₂ Nanotube Arrays as an Anode Material for Lithium-Ion Batteries

Abstract:

Well-aligned TiO₂ nanotube arrays were fabricated from anodization by a subsequent heat treatment. Rate performance and electrochemical properties of TiO₂ nanotube arrays were studied intensively. The electrode exhibits excellent rate capabilities at various rates with an average coulombic efficiency reaching 95.6%. It is obvious that TiO₂ nanotube array possesses high rate capability and excellent cycling stability.

You might also be interested in these eBooks

Mechanical and Electronics Engineering III

View Preview

Info:

Periodical:

Applied Mechanics and Materials (Volumes 130-134)

Pages:

1281-1285

DOI:

https://doi.org/10.4028/www.scientific.net/AMM.130-134.1281

Citation:

Cite this paper

Online since:

October 2011

Authors:

Li Li Wang, Shi Chao Zhang, Xiao Meng Wu

Keywords:

Charge Transfer, Cycling Performance, Lithium-Ion Battery, Rate Capability, TiO₂ Nanotube

Export:

RIS, BibTeX

Price:

Permissions:

Request Permissions

References

[1] M. Winter, J. O. Besenhard, M. E. Spahr, and P. Novák: Adv. Mater. 10 (1998), No. 10.

Google Scholar

[2] K. H. Reiman, K. M. Brace, T. J. Gordon-Smith, I. Nandhakumar, G. S. Attard, and J. R. Owen: Electrochem. Commun. 8 (2006), p.517.

Google Scholar

[3] H.G. Jung, C.S. Yoon, J. Prakash, and Y.K. Sun: J. Phys. Chem. C 113 (2009), p.21258.

Google Scholar

[4] S.W. Kim, T.H. Han, J. Kim, H. Gwon, H. S . Moon, S.W. Kang, S.O. Kim, and K. Kang: Acs Nano 3 (2009), p.1085.

Google Scholar

[5] B. Erjavec, R. Dominko, P. Umek, S. Sturm, A. Pintar and M. Gaberscek: J. Power Sources 189 (2009), p.869.

DOI: 10.1016/j.jpowsour.2008.07.030

Google Scholar

[6] Y.S. Hu, X. Liu, J.O. Müller, R. Schlögl, J. Maier, and D.S. Su: Angew. Chem. Int. Ed. 48 (2009), p.210.

Google Scholar

[7] G. F. Ortiz, I. Hanzu, P. Lavela, J. L. Tirado, P. Knauth and T. Djenizian: J. Mater. Chem., 20 (2010), p.4041.

DOI: 10.1039/b927122h

Google Scholar

[8] Y. Ren, L. J. Hardwick, and P. G. Bruce: Angew. Chem. Int. Ed. 49 (2010), p.2570.

Google Scholar

[9] G. F. Ortiz, I. Hanzu, T. Djenizian, P. Lavela, J. L. Tirado, and P. Knauth: Chem. Mater. 21 (2009), p.63.

DOI: 10.1021/cm801670u

Google Scholar

[10] J. Wang, J. Polleux, J. Lim, and B. Dunn: J. Phys. Chem. C 111 (2007), p.14925.

Google Scholar

[11] H. Pelouchova, P. Janda, J. Weber, L. Kavan: J. Electroanal. Chemistry 566 (2004), p.73.

Google Scholar

[12] F. F. Santiago, E. M. Barea, J. Bisquert, G. K. Mor, K. Shankar, and C. A. Grimes: J. Am. Chem. Soc. 130 (2008), p.11312.

Google Scholar