Next Article in Journal
Graded Morphologies and the Performance of PffBT4T-2OD:PC71BM Devices Using Additive Choice
Previous Article in Journal
The Role of Temperature on the Degree of End-Closing and Filling of Single-Walled Carbon Nanotubes
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 12
10.3390/nano11123366
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synergetic Effect of Potassium Oxysalts on Combustion and Ignition of Al/CuO Composites

by
Xiaohang Ma
,
Wanjun Zhao
*,
Wei Le
,
Jianxin Li
,
Pengwan Chen
and
Qingjie Jiao
State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(12), 3366; https://doi.org/10.3390/nano11123366
Submission received: 7 November 2021 / Revised: 10 December 2021 / Accepted: 10 December 2021 / Published: 12 December 2021
Browse Figures
Review Reports Versions Notes

Abstract

:
In this study, we studied the synergetic effect of potassium oxysalts on combustion and ignition of nano aluminum (Al) and nano copper oxide (CuO) composites. Potassium periodate (KIO4) and potassium perchlorate (KClO4) are good oxidizers with high oxygen content and strong oxidizability. Different contents of KIO4 and KClO4 were added to nano Al/CuO and the composites were assembled by sonication. When the peak pressure of nano Al/CuO was increased ~5–13 times, the pressurization rate was improved by ~1–3 orders of magnitude, the ignition delay time was shortened by ~0.08 ms–0.52 ms and the reaction completeness was adjustable when 30–70% KIO4 and KClO4 were added into the composites. The reaction of Al/KIO4 and Al/KClO4 at a lower temperature was helpful to ignite the ternary composite. Meanwhile, CuO significantly reduced the peak temperature of oxygen released from the decomposition of KIO4 and KClO4. The synergetic effect of binary oxidizers made the combustion performance of the ternary composites better than that of the binary composites. The present work indicates that KIO4 and KClO4 are promising additives for nano Al/CuO to tune and promote the combustion performance. The ternary composites have potential application in energy devices and combustion apparatus.

1. Introduction

Metastable intermolecular composites (MIC) are a kind of energetic material composed of nano-sized fuels and oxidizers. With the development and application of nanotechnology, MIC have recently received more and more attention in the field of energetic materials. The ultra-refinement or nanocrystallization of the energetic materials can significantly improve the energy release and increase the reaction rate [1,2,3,4]. Nano aluminum (Al) powder has become the most commonly used metallic fuel in the MIC system due to its high energy release and low cost [5,6]. The performances of binary MIC systems composed of Al and metallic oxides (such as iron oxide (Fe2O3), copper oxide (CuO), tungsten trioxide (WO3), nickel oxide (NiO), molybdenum trioxide (MoO3), cobalt oxide (Co3O4), and bismuth trioxide (Bi2O3)) have been prepared through different methods and studied by many scholars at home and abroad [7,8,9,10,11,12,13,14,15,16,17].
However, due to the low oxygen content in common metallic oxides, MIC with these metallic oxidizers as the single oxidizer possess less gas production and slower reaction rate. In order to solve this problem, suitable double oxidizers are introduced to replace the single oxidizers in the MIC system to form a ternary system, or ammonium perchlorate (NH4ClO4, AP), potassium perchlorate (KClO4), potassium periodate (KIO4), potassium permanganate (KMnO4), etc., with high oxygen content and strong oxidizability, are also used to replace traditional metallic oxidizers, both of which can increase the reaction rate of MIC. Huang found that the binary mixture of Bi2O3 and CuO was more effective than any single oxide in improving the combustion performance of B [18]. The reaction rate of Al/Fe2O3/WO3 ternary MIC system prepared by Zachariah was dramatically higher than that of any single system [19]. Prakash found that the reaction rate of Al/KMnO4 was much higher than that of Al/Fe2O3 due to the high concentration of the free oxygen [20]. The ignition temperature of the Al/KIO4 and Al/sodium periodate (NaIO4) binary system prepared by Jian was lower than that of Al/CuO, and its peak pressure and pressurization rate were much higher than that of Al/CuO [21]. Song added a small amount of KClO4 and found that its activation energy was lower than that of Al/MnO2 and its combustion rate increased [22]. Wang found that the Al/CuO/AP composite with 13% AP had the best combustion performance, and its peak pressure and pressurization rate were three times higher than the traditional Al/CuO nano-thermites [23]. Thus, potassium oxysalts and double oxidizers play a significant role in improving the combustion and ignition performance of the thermites.
Herein, the effects of KIO4 and KClO4 on the combustion behavior of Al/CuO were systematically studied. A scanning electron microscope (SEM) was used to characterize the prepared energetic composite particles. The theoretical adiabatic flame temperature (AFT) of the energetic composite material was calculated by REAL software. The thermal decomposition reaction behavior of CuO/xKIO4 and CuO/xKIO4 was studied by differential scanning calorimetry (DSC) and thermogravimetric analysis (TG). The peak pressure and pressurization rate of the MIC were characterized by the combustion test. A carbon dioxide (CO2) laser igniter and a high-speed camera were used to test and record the ignition delay time of the composite material. The calorimeter was used to measure the heat release of Al/CuO/xKIO4 and Al/CuO/xKClO4 composites. The results show that KIO4 and KClO4 play important roles in enhancing the combustion performance of nano Al-based MIC composites.

2. Experimental Section

2.1. Chemicals and Preparation of Composites

Aluminum nanoparticles (~30–50 nm) and copper oxide nanoparticles (<50 nm) were purchased from Aladdin Industrial Corporation (Shanghai, China), and KIO4 and KClO4 were purchased from Sinopharm Chemical Reagent Corporation (Shanghai, China), they were ground in the agate mortar before being used in the experiment. The formulations of composites are shown in Table 1, which are based on Equations (1)–(3). The active metals were considered as the fuel with the oxide layer thickness of ~2–5 nm for nAl [24]. Al/CuO/30% KClO4 means that the molar percentage of KClO4 and CuO in the oxidizers are 30% and 70%, respectively. The content of Al was stoichiometric assuming the fuel reacted with the oxidizer completely. The samples were prepared via sonication method. The weighted Al and oxidizers were put into a vial with ~10 mL hexane, followed by sonication of ~30 min, and dried in a hood for 24 h. Finally, the dried powders could be obtained for further measurements.
2Al + 3CuO → Al2O3 + 3Cu, ∆H = −4130 J g−1
8Al + 3KIO4 → 4Al2O3 + 3KI, ∆H = −6016 J g−1
8Al + 3KClO4 → 4Al2O3 + 3KCl, ∆H = −10659 J g−1

2.2. Characterization

Scanning electron microscope (SEM, Hitachi S-4800, Tokyo, Japan) was used to analyze the morphologies of the raw materials and composites. Thermogravimetric analysis and differential scanning calorimetry (TG-DSC, Netzsch STA 449 F3, Selb, Germany) were used to characterize the thermodynamic behavior of CuO/xKIO4 and CuO/xKClO4 binary systems and potassium oxysalts. The sample was heated from room temperature to 700 °C in an argon atmosphere (50 mL min−1) at a heating rate of 10 °C min−1.

2.3. Pressure Cell Tests

The peak pressure was evaluated by combustion cell. Around 25 mg-samples were weighted and loaded into a combustion cell with a constant volume of ~20 cm3. The samples were ignited via joule heating through a nichrome wire above the samples, which was connected to a voltage supply. When ignited, the changes of pressure in time were recorded electrically. The pressurization rate was obtained by calculating the initial slope of the pressure rise, which has been used to present the reactivity of energetic materials. A detailed description about pressure cell could be found in the reference [25].

2.4. Characterization of Ignition and Combustion

Typically, ~15 mg samples were weighted and placed in the center of the specimen stage and the ignition performance of the samples was evaluated by a CO2 laser of 60 W in air. Ignition delay was defined as the time length from the start of the laser to the initial visible spark spot captured by a high-speed camera (i-SPEED 726, Rochford, UK) at 50,000 fps.

2.5. Heat Release Measurement

The released heat by energetic materials has been evaluated via a calorimeter [26].
The diagrammatic sketch of the calorimeter is shown in Figure S1. Around 200 mg of thermites with a nichrome wire above were placed into the steel crucible inside the calorimeter. The calorimeter was sealed, then thermites were ignited by the nichrome wire via joule heating in air. The heat released by energetic composites dispersed into the water bath within the calorimeter and caused a raise of temperature. Thus, the combustion heat of thermites could be measured. Every measurement was conducted in triplicate, and the average values were shown accompanied with the standard deviation.

3. Results and Discussion

3.1. REAL Calculation Results

Based on the formulations of composites, assuming the reaction between the fuel and oxidizers occurs in a constant volume, the REAL code was used based on the principle of minimum free energy to calculate the influence of the addition of KIO4 and KClO4 on the adiabatic flame temperature (AFT) of the Al/CuO system. As demonstrated in Figure 1, the addition of KIO4 and KClO4 can enhance the AFT of Al/CuO significantly. The calculated AFT increase monotonously with the increasing molar percentages of potassium oxysalts. Figure 1 demonstrates that the addition of 50% KIO4 and 50% KClO4 can raise the AFT by ~900 °C and ~1100 °C, respectively. Consequently, the addition of potassium oxysalts could improve the AFT of Al/CuO theoretically. In the reaction process, the addition of potassium salts can significantly increase the adiabatic flame temperature of the system, thus promoting the decomposition of the oxidizers, and enabling the Al and oxidizers to react more completely [19].

3.2. Morphology Characterization

The morphologies of the raw materials, Al/CuO/xKIO4 and Al/CuO/xKClO4 composites were characterized via SEM. As shown in Figure 2, the CuO and Al nanoparticles adhere to micron-sized KIO4 and KClO4 evenly, indicating that the fuels and oxidizers could be mixed up well via sonication.

3.3. Reactivity Characterization

As shown in Figure 3, with the incorporation of KIO4 and KClO4, the combustion performance of Al/CuO was improved significantly. Among the Al/CuO/potassium oxysalts ternary systems, the highest combustion performance, including the highest peak pressure and pressurization rate, was achieved by Al/CuO/30% potassium oxysalts.
As shown in Figure 3a, the peak pressure of all the ternary systems is higher than that of the binary composites. The peak pressure of Al/CuO/30% KClO4 is 10 times and 4 times higher than that of Al/CuO and Al/KClO4, respectively. With the increase of the content of KClO4, the peak pressure reduced slightly compared with Al/CuO/30% KClO4. The peak pressures of Al/CuO/50% KClO4 and Al/CuO/70% KClO4 are still higher than that of Al/CuO and Al/KClO4, which are 8 times and 5 times higher than that of Al/CuO, respectively. Similarly, the peak pressure of Al/CuO/30% KIO4 is 13 times and 8 times higher than Al/CuO and Al/KIO4, respectively. Therefore, the peak pressure of Al/CuO/30% KIO4 (49600 KPa/g) is the highest among all the ternary systems.
For the pressurization rate, which refers to the reactivity of energetic materials [5], the trend is the same as that of peak pressure (Figure 3b). The reactivity of the ternary composites of Al/CuO/xKIO4 and Al/CuO/xKClO4 is higher than that of conventional Al/KIO4, Al/KClO4, and Al/CuO binary composites. In the meanwhile, the reactivity of Al/CuO/30% potassium oxysalts is the highest. With the addition of 30% KIO4, the pressurization rate is tremendously raised, which is three orders of magnitude higher than Al/CuO and Al/KIO4, which is the highest pressurization rate in this study. With the increasing content of KIO4, the pressurization rate reduced slightly. The pressurization rates of Al/CuO/50% KIO4 and Al/CuO/70% KIO4 are 107 times and 152 times higher than that of Al/CuO, respectively. Similarly, the pressurization rate of Al/CuO/30% KClO4 is three and two orders of magnitude higher than that of Al/CuO and Al/KClO4. Thus, the reactivity of Al/CuO can be significantly improved and tailored by the addition of different contents of potassium oxysalts.
The reason why the combustion performance of Al/CuO is significantly enhanced by the addition of KIO4 and KClO4 can be speculated that the reaction between Al/KIO4 and Al/KClO4 starting at a low temperature is helpful to ignite the ternary composite materials. Meanwhile, it is speculated that CuO can accelerate the decomposition of KIO4 and KClO4 to release O2, leading to the reaction of Al with a large amount of gas. The higher flame temperature of Al/KIO4 or Al/KClO4 improves the pressure of the combustion cell and promotes the decomposition of the oxidizers further, thus more oxygen is produced, the oxidation of Al is further accelerated and the reaction rate is accelerated [19,27,28]. All these factors occur at the same time and have synergistic effects on enhancing the combustion performance of Al/CuO. In order to verify and quantify the effect of CuO on the thermal decomposition of KIO4 and KClO4, the TG analysis and DSC analysis of CuO/xKIO4 and CuO/xKClO4 were carried out in the later section.

3.4. Thermal Analysis

TGA/DSC were used to study the thermal decomposition reaction process of CuO/xKIO4 and CuO/xKClO4 at a low heating rate. Figure 4a demonstrates that KIO4 decomposes and releases O2 in two stages, which is consistent with the reported studies [21]. In the first stage, KIO4 decomposes exothermically into KIO3 and O2 with a peak temperature of the O2 release at ~343 °C. In the second stage, KIO3 starts the decomposition at ~535 °C with an endothermic peak at ~552 °C. Figure 4a reveals that the addition of CuO almost has no effect on the decomposition of KIO4 during the first stage with exothermic peak temperatures ranging from ~336 °C to ~339 °C. However, with the addition of CuO, the initiation and the endothermic peak of the second-stage decomposition of KIO4 advance by ~100 °C and ~90 °C compared with pure KIO4, respectively.
The thermal decomposition of KClO4 is shown in Figure 4b, KClO4 decomposes exothermically into KCl and O2 at ~595 °C with an exothermic peak at ~631 °C [29]. The endothermic peak at ~303 °C observed in DSC curves is the crystal transformation of KClO4, and the endothermic peak at ~609 °C is caused by the melting of KClO4. The addition of CuO has basically no influence on the crystal transformation of KClO4, which is ~300 °C. However, the addition of CuO advanced the melting and thermal decomposition of KClO4 significantly, resulting in the disappearance of endothermic peak of the melting and thermal decomposition at a lower temperature. The peak temperature of the thermal decomposition reaction of CuO/xKClO4 is ~500 °C, which is ~130 °C lower than that of pure KClO4. Moreover, the initial decomposition temperatures of KClO4 with different contents of CuO are between ~340 °C to ~390 °C, which are ~200 °C to ~250 °C lower than that of pure KClO4. This can be attributed to the fact that CuO, as a p-type transition metal oxide, promotes the electron transfer process during the decomposition of the oxidant [30,31,32].
Therefore, the addition of CuO has a significant effect on the thermal decomposition reaction process of KIO4 and KClO4, which makes the thermal decomposition reaction process earlier significantly. Meanwhile, the initial temperature and peak temperature of the oxygen releasing are greatly reduced, leading to the rapid reaction of Al with a large amount of gas through the pathways of the oxide shell, which may cause the internal molten Al to continuously absorb heat and expand, accelerating the rupture of the oxide layer, and further promoting the diffusion of Al core and oxidation of Al, thus enhancing the combustion performance of the composites [19,28,33,34].

3.5. Ignition Characterization

The combustion process of Al/CuO/xKIO4 and Al/CuO/xKClO4 composites has been recorded via high-speed camera. As shown in Figure 5, with the existence of KIO4 and KClO4 in the ternary systems, the initiation time of the reaction is earlier than that of Al/CuO.
Figure 5a demonstrates that the ignition delay time of the Al/CuO/xKIO4 ternary composites is shorter than that of the binary composites. Compared with Al/CuO (~1.28 ms), the ignition delay time of the composite with 50% KIO4 is shortened by ~0.38 ms. The ignition delay time of Al/CuO/70% KIO4 (~0.88 ms) is shorter than that of Al/KIO4 by ~0.32 ms. Among the Al/CuO/KIO4 composites, the ignition delay time of Al/CuO/30% KIO4 is the shortest, ~0.76 ms, which is ~0.52 ms and ~0.44 ms shorter than Al/CuO and Al/KIO4, respectively. As for the Al/CuO/xKClO4 systems, it is shown in Figure 5b that the ignition of composites with 30% KClO4 and 50% KClO4 occurs ~0.08 ms and ~0.14 ms earlier compared to Al/CuO. The ignition delay time of Al/CuO/70% KClO4 is the shortest, ~1.08 ms, which is ~0.20 ms and ~0.16 ms earlier than that of Al/CuO and Al/KClO4, respectively.
Herein, the ignition delay time of Al/CuO/xKIO4 and Al/CuO/xKClO4 ternary composites is shorter than that of that of both Al/CuO and Al/potassium oxysalts binary systems. It is reported that in the ternary thermites systems [35], the initiation of the whole system is triggered by the reaction between fuel and oxidizer that can be ignited at a lower temperature. Since the initiation temperature of Al/KIO4 and Al/KClO4 reaction is lower than that of Al/CuO [27,28], the ignition delay time of thermites composing of Al and potassium oxysalts is shorter than Al/CuO. We propose that the ignition of the ternary systems is initiated by the reaction of Al and potassium oxysalts. Combining the fact that the addition of CuO can advance the oxygen release of KIO4 and KClO4, the reaction between Al and potassium oxysalts in ternary systems can initiate earlier than Al/KIO4 and Al/KClO4. Therefore, the application of CuO/potassium oxysalts binary oxidizer system results in a synergetic effect including a lower ignition temperature and earlier oxygen release of oxidizers, thus significantly shortening the ignition delay of ternary thermites.

3.6. Heat Release Results

Assuming that the oxidant reacts completely with the fuel, the theoretical heat release of the composites is calculated based on the theoretical enthalpy of Al/CuO, Al/KIO4 and Al/KClO4 as shown in Equations (1)–(3), and their molar percentage in the ternary composites according to Hess’s law [26]. Figure 6 shows that with the increase of the content of KIO4 and KClO4, the heat release of the composites increases monotonously, which can be attributed to the reason that the theoretical enthalpy of Al/KIO4 and Al/KClO4 is higher than that of Al/CuO according to the Equations (1)–(3). The heat release of Al/CuO/30% KIO4 is 4958 ± 111 J g−1 (Figure 6a), which is ~1200 J g−1 higher than that of Al/CuO. Figure 6b demonstrates that the heat release of Al/CuO/50% KClO4 (6926 ± 150 J g−1) is ~3200 J g−1 higher than that of Al/CuO, which has been increased significantly. In addition, the experimental heat release of the composites is less than the theoretical heat release because the composites cannot react completely during the experiment, which can be confirmed by the XRD characterization of the combustion products (Figure S2). A more detailed description can be seen in the Supplementary Information.
The reaction completeness of composite system is obtained by calculating the ratio of the experimental calorific values to the theoretical ones. For the systems of Al/CuO/xKIO4, the reaction completeness of the ternary composite is higher than that of the binary systems. The highest reaction completeness of 96.1% for Al/CuO/xKIO4 ternary systems is achieved by Al/CuO/50% KIO4, which is 4.8% higher than that of Al/CuO. The reaction completeness of Al/CuO/xKClO4 is higher than that of Al/KClO4, and the reaction completeness of Al/CuO/30% KClO4 is 82.1%, which is 6.8% higher than that of Al/KClO4. It is presumed that as a transition metal oxidizer, CuO can promote the combustion of Al/KIO4 and Al/KClO4 as a catalyst. The relatively lower reaction completeness of Al/CuO/70% KClO4 might be caused by the lower ratio of CuO and the weakening catalysis of CuO.
It is reported that when there is more released gas during the combustion process of MIC, higher combustion efficiency could be achieved due to less aggregation of nAl [36]. Consistent with the results from this work, the higher peak pressure obtained from Al/CuO/KIO4 and Al/CuO/KClO4 composites (Figure 3a) means the amount of gas products is larger, which is corresponding to the higher reaction completeness of the ternary composites in Figure 6.

4. Conclusions

In this study, the binary oxidizers composed of potassium oxysalts and CuO were applied in nano Al-based MIC, and their energetic performance has been tested. The pressure cell tests show that the pressure peak and pressurization rate of Al/CuO/xKIO4 and Al/CuO/xKClO4 ternary composites are significantly higher than that of Al/CuO, Al/KIO4 and Al/KClO4 binary composites. It is speculated that the synergistic effect of CuO/KIO4 and CuO/KClO4 binary oxidizers make the combustion performance of the ternary composites better than that of the binary composites. In other words, the reaction of Al/KIO4 and Al/KClO4 at a lower temperature is helpful to ignite the ternary composite. Meanwhile, CuO promotes the decomposition of KIO4 and KClO4 to release oxygen, which makes Al react quickly with a large amount of gas, accelerates the rupture of the oxide layer, and further promotes the diffusion of Al core and oxidation of Al, thus enhancing the combustion performance of the composites. The results of TG-DSC show that CuO significantly advances the initial temperature and peak temperature of KIO4 oxygen release in the second-step decomposition by ~100 °C and ~90 °C, respectively, and decreases the initial temperature and peak temperature of KClO4 oxygen release by ~200 °C and ~130 °C, respectively. Moreover, the results of ignition tests and heat release measurement show that the ignition delay time of the ternary composites is shorter than that of Al/CuO. The addition of KIO4 and KClO4 can tailor the reaction completeness and heat release of the composites due to more released gas by the reaction between Al and potassium oxysalts. Therefore, KIO4 and KClO4 are promising additives for Al/CuO to tune and promote the combustion performance.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/nano11123366/s1, Figure S1: Diagrammatic sketch of the calorimeter test device, Figure S2: XRD characterization of the combustion products.

Author Contributions

Conceptualization, W.Z. and Q.J.; data curation, X.M. and W.Z.; formal analysis, X.M. and W.Z.; methodology, X.M.; supervision, W.L., J.L. and P.C.; writing—original draft, X.M.; writing—review and editing, X.M. and W.Z. All authors have read and agreed to the published version of the manuscript.

Funding

This work is supported by the National Natural Science Foundation of China (Grant number 22105025) and the China Postdoctoral Science Foundation (Grant number 2021M690376).

Institutional Review Board Statement

The study was conducted according to the guidelines of the Declaration of Helsinki, and approved by the Institutional Review Board of Beijing Institute of Technology.

Informed Consent Statement

Informed consent was obtained from all subjects involved in the study.

Data Availability Statement

Data is contained within the article or supplementary material.

Acknowledgments

We appreciate the support from the State Key Laboratory of Explosive Science.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Asay, B.W.; Son, S.F.; Busse, J.R.; Oschwald, D.M. Ignition Characteristics of Metastable Intermolecular Composites. Propellants Explos. Pyrotech. 2004, 29, 216–219. [Google Scholar] [CrossRef]
  2. Bockmon, B.S.; Pantoya, M.L.; Son, S.F.; Asay, B.W.; Mang, J.T. Combustion velocities and propagation mechanisms of metstable interstitial composites. J. Appl. Phys. 2005, 98, 064903–064910. [Google Scholar] [CrossRef]
  3. Tasker, D.G.; Asay, B.W.; King, J.C.; Sanders, V.E.; Son, S.F. Dynamic measurements of electrical conductivity in metastable intermolecular composites. J. Appl. Phys. 2006, 99, 023705–023712. [Google Scholar] [CrossRef]
  4. Dreizin, E.L. Metal-based reactive nanomaterials. Prog. Energy Combust. Sci. 2009, 35, 141–167. [Google Scholar] [CrossRef]
  5. Sullivan, K.; Young, G.; Zachariah, M.R. Enhanced reactivity of nano-B/Al/CuO MIC’s. Combust. Flame 2009, 156, 302–309. [Google Scholar] [CrossRef]
  6. Firestein, K.L.; Corthay, S.; Steinman, A.E.; Matveev, A.T.; Kovalskii, A.M.; Sukhorukova, I.V.; Golberg, D.; Shtansky, D.V. High-strength aluminum-based composites reinforced with BN, AlB2 and AlN particles fabricated via reactive spark plasma sintering of Al-BN powder mixtures. Mater. Sci. Eng. A 2017, 681, 1–9. [Google Scholar] [CrossRef] [Green Version]
  7. Plantier, K.B.; Pantoya, M.L.; Gash, A.E. Combustion wave speeds of nanocomposite Al/Fe2O3: The effects of Fe2O3 particle syn thesis technique. Combust. Flame 2005, 140, 299–309. [Google Scholar] [CrossRef]
  8. Shende, R.; Subramanian, S.; Hasan, S.; Apperson, S.; Thiruvengadathan, S.; Thiruvengadathan, R.; Gangopadhyay, K.; Gangopadhyay, S. Nanoenergetic Composites of CuO Nanorods, Nanowires, and Al-Nanoparticles. Propellants. Explos. Pyrotech. 2008, 33, 122–130. [Google Scholar] [CrossRef]
  9. Apperson, S.; Shende, R.V.; Subramanian, S.; Tappmeyer, D.; Gangopadhyay, S.; Chen, Z.; Gangopadhyay, K.; Redner, P.; Nicholich, S.; Kapoor, D. Generation of fast propagating combustion and shock waves with copper oxide/aluminum nanothermite composites. Appl. Phys. Lett. 2007, 91, 243109–243111. [Google Scholar] [CrossRef] [Green Version]
  10. Perry, W.L.; Smith, B.L.; Bulian, C.J.; Busse, J.R.; Macomber, C.S.; Dye, R.C.; Son, S.F. Nano-Scale Tungsten Oxides for Metasta- ble Intermolecular Composites. Propellants. Explos. Pyrotech. 2004, 29, 99–105. [Google Scholar] [CrossRef]
  11. Zhang, K.L.; Rossi, C.; Alphonse, P.; Tenailleau, C.; Cayez, S.; Chane-Ching, J.Y. Integrating Al with NiO nano honeycomb to realize an energetic material on silicon substrate. Appl. Phys. A 2008, 94, 957–962. [Google Scholar] [CrossRef] [Green Version]
  12. Son, S.F.; Asay, B.W.; Foley, T.J.; Yetter, R.A.; Wu, M.H.; Risha, G.A. Combustion of Nanoscale Al/MoO3 Thermite in Microchan nels. J. Propul. Power 2007, 23, 715–721. [Google Scholar] [CrossRef] [Green Version]
  13. Sun, J.; Pantoya, M.L.; Simon, S.L. Dependence of size and size distribution on reactivity of aluminum nanoparticles in reactions with oxygen and MoO3. Thermochim. Acta 2006, 444, 117–127. [Google Scholar] [CrossRef]
  14. Wang, J.; Qiao, Z.Q.; Shen, J.P.; Li, R.; Yang, Y.T.; Yang, G.C. Large-Scale Synthesis of a Porous Co3O4 Nanostructure and Its Application in Metastable Intermolecular Composites. Propellants. Explos. Pyrotech. 2015, 40, 514–517. [Google Scholar] [CrossRef]
  15. Wang, L.; Luss, D.; Martirosyan, K.S. The behavior of nanothermite reaction based on Bi2O3/Al. J. Appl. Phys. 2011, 110, 074311–074318. [Google Scholar] [CrossRef] [Green Version]
  16. Sanders, V.E.; Asay, B.W.; Foley, T.J.; Tappan, B.C.; Pacheco, A.N.; Son, S.F. Reaction Propagation of Four Nanoscale Energetic Composites (Al/MoO3, Al/WO3, Al/CuO, and Bi2O3). J. Propul. Power 2007, 23, 707–714. [Google Scholar] [CrossRef]
  17. Zhou, L.; Piekiel, N.; Chowdhury, S.; Zachariah, M.R. Time-Resolved Mass Spectrometry of the Exothermic Reaction between Nanoaluminum and Metal Oxides: The Role of Oxygen Release. J. Phys. Chem. C 2010, 114, 14269–14275. [Google Scholar] [CrossRef]
  18. Huang, S.D.; Deng, S.L.; Jiang, Y.; Zheng, X.L. Experimental effective metal oxides to enhance boron combustion. Combust. Flame 2019, 205, 278–285. [Google Scholar] [CrossRef] [Green Version]
  19. Sullivan, K.; Zachariah, M.R. Simultaneous Pressure and Optical Measurements of Nanoaluminum Thermites: Investigating the Reaction Mechanism. J. Propul. Power 2010, 26, 467–472. [Google Scholar] [CrossRef] [Green Version]
  20. Prakash, A.; McCormick, A.V.; Zachariah, M.R. Tuning the reactivity of energetic nanoparticles by creation of a core-shell nanostructure. Nano Lett. 2005, 5, 1357–1360. [Google Scholar] [CrossRef] [PubMed]
  21. Jian, G.Q.; Feng, J.Y.; Jacob, R.J.; Egan, G.C.; Zachariah, M.R. Super-reactive nanoenergetic gas generators based on periodate salts. Angew. Chem. Int. Ed. 2013, 52, 9925–9928. [Google Scholar] [CrossRef]
  22. Song, J.X.; Guo, T.; Yao, M.; Ding, W.; Zhang, X.N.; Bei, F.L.; Tang, J.; Huang, J.Y.; Yu, Z.S. Thermal behavior and combustion of Al nanoparticles/ MnO2-nanorods nanothermites with addition of potassium perchlorate. RSC Adv. 2019, 9, 41319–41325. [Google Scholar] [CrossRef] [Green Version]
  23. Wang, H.Y.; Zachariah, M.R.; Xie, L.F.; Rao, G.N. Ignition and Combustion Characterization of Nano-Al-AP and Nano-Al-CuO-AP Micro-sized Composites Produced by Electrospray Technique. Energy Procedia 2015, 66, 109–112. [Google Scholar] [CrossRef] [Green Version]
  24. Puri, P.; Yang, V. Thermo-mechanical behavior of nano aluminum particles with oxide layers during melting. J. Nanopart. Res. 2010, 12, 2989–3002. [Google Scholar] [CrossRef]
  25. Liu, J.; Yan, T.; Li, Y.R.; Ren, H.; Wang, Q.; Guan, F.Y.; Jiao, Q.J. Dual-mode response behavior of a graphene oxide implanted energetic system under different thermal stimuli. RSC Adv. 2020, 10, 10789–10798. [Google Scholar] [CrossRef]
  26. Sun, Y.L.; Ren, H.; Du, F.Z.; Yan, S.; Jiao, Q.J. Preparation and characterization of sintered B/MgB2 as heat release material. J. Alloys Compd. 2018, 759, 100–107. [Google Scholar] [CrossRef]
  27. Sullivan, K.T.; Piekiel, N.W.; Wu, C.; Chowdhury, S.; Kelly, S.T.; Hufnagel, T.C.; Fezzaa, K.; Zachariah, M.R. Reactive sintering: An important component in the combustion of nanocomposite thermites. Combust. Flame 2012, 159, 2–15. [Google Scholar] [CrossRef]
  28. Zhou, W.B.; DeLisio, J.B.; Wang, X.Z.; Zachariah, M.R. Reaction mechanisms of potassium oxysalts based energetic composites. Combust. Flame 2017, 177, 1–9. [Google Scholar] [CrossRef] [Green Version]
  29. Lee, J.S.; Hsu, C.K.; Jaw, K.S. The thermal properties of KClO4 with different particle size. Thermochim. Acta 2001, 367, 381–385. [Google Scholar] [CrossRef]
  30. Kishore, K.; Sunitha, M.R. Effect of Transition Metal Oxides on Decomposition and Deflagration of Composite Solid Propellant Systems: A Survey. AIAA J. 1979, 10, 1118–1125. [Google Scholar] [CrossRef]
  31. Haralambous, K.J.; Loizos, Z.; Spyrellis, N. Catalytic properties of some mixed transition-metal oxides. Mater. Lett. 1991, 11, 133–141. [Google Scholar] [CrossRef]
  32. Rudloff, W.K.; Freeman, E.S. The Catalytic Effect of Metal Oxides on Thermal Decomposition Reactions. J. Phys. Chem. 1969, 74, 3317–3324. [Google Scholar] [CrossRef]
  33. Rai, A.; Park, K.; Zhou, L.; Zachariah, M.R. Understanding the mechanism of aluminium nanoparticle oxidation. Combust. Thero. Model. 2006, 10, 843–859. [Google Scholar] [CrossRef]
  34. Henz, B.J.; Hawa, T.; Zachariah, M.R. On the role of built-in electric fields on the ignition of oxide coated nanoaluminum: Ion mobility versus Fickian diffusion. J. Appl. Phys. 2010, 107, 024901–024909. [Google Scholar] [CrossRef] [Green Version]
  35. Zhao, W.J.; Wang, X.Z.; Wang, H.Y.; Wu, T.; Kline, D.J.; Rehwoldt, M.; Ren, H.; Zachariah, M.R. Titanium enhanced ignition and combustion of Al/I2O5 mesoparticle composites. Combust. Flame 2020, 212, 245–251. [Google Scholar] [CrossRef]
  36. Jacob, R.J.; Ortiz-Montalvo, D.L.; Overdeep, K.R.; Weihs, T.P.; Zachariah, M.R. Incomplete reactions in nanothermite composites. J. Appl. Phys. 2017, 121, 054307–054317. [Google Scholar] [CrossRef] [Green Version]
Nanomaterials 11 03366 g001 550
Figure 1. The calculated AFT of Al/CuO/potassium oxysalts systems by REAL.
Figure 1. The calculated AFT of Al/CuO/potassium oxysalts systems by REAL.
Nanomaterials 11 03366 g001
Nanomaterials 11 03366 g002 550
Figure 2. SEM images of samples: (a) Al, (b) CuO, (c) KIO4, (d) KClO4, (e) Al/CuO/30%KIO4, (f) Al/CuO/50%KIO4, (g) Al/KIO4, (h) Al/CuO/50%KClO4, (i) Al/KClO4.
Figure 2. SEM images of samples: (a) Al, (b) CuO, (c) KIO4, (d) KClO4, (e) Al/CuO/30%KIO4, (f) Al/CuO/50%KIO4, (g) Al/KIO4, (h) Al/CuO/50%KClO4, (i) Al/KClO4.
Nanomaterials 11 03366 g002
Nanomaterials 11 03366 g003 550
Figure 3. The measured peak pressure (a) and pressurization rate (b) of Al/CuO/potassium oxysalts systems. Note: “70%” means “Al/CuO/70% potassium oxysalts”.
Figure 3. The measured peak pressure (a) and pressurization rate (b) of Al/CuO/potassium oxysalts systems. Note: “70%” means “Al/CuO/70% potassium oxysalts”.
Nanomaterials 11 03366 g003
Nanomaterials 11 03366 g004 550
Figure 4. DSC and TG curves of (a) CuO/xKIO4 and (b) CuO/xKClO4.
Figure 4. DSC and TG curves of (a) CuO/xKIO4 and (b) CuO/xKClO4.
Nanomaterials 11 03366 g004
Nanomaterials 11 03366 g005 550
Figure 5. The combustion snapshots of (a) Al/CuO/xKIO4 and (b) Al/CuO/xKClO4 systems-based composites.
Figure 5. The combustion snapshots of (a) Al/CuO/xKIO4 and (b) Al/CuO/xKClO4 systems-based composites.
Nanomaterials 11 03366 g005
Nanomaterials 11 03366 g006 550
Figure 6. The experimental, theoretical enthalpy, and corresponding combustion efficiency of (a) Al/CuO/xKIO4 and (b) Al/CuO/xKClO4 composites. Note: ‘‘30% KIO4” in Al/CuO/xKIO4 system means Al/CuO/30%KIO4.
Figure 6. The experimental, theoretical enthalpy, and corresponding combustion efficiency of (a) Al/CuO/xKIO4 and (b) Al/CuO/xKClO4 composites. Note: ‘‘30% KIO4” in Al/CuO/xKIO4 system means Al/CuO/30%KIO4.
Nanomaterials 11 03366 g006
Table
Table 1. Stoichiometric thermites formulation (Al/CuO/x potassium oxysalts).
Table 1. Stoichiometric thermites formulation (Al/CuO/x potassium oxysalts).
ThermitesAl (wt%)CuO (wt%)Potassium Oxysalts (wt%)
Al/CuO27.872.20.0
Al/CuO/30% KIO431.730.537.9
Al/CuO/50% KIO432.917.249.8
Al/CuO/70% KIO433.98.557.6
Al/KIO434.60.065.4
Al/CuO/30% KClO437.435.926.7
Al/CuO/50% KClO441.021.537.4
Al/CuO/70% KClO443.811.145.1
Al/KClO446.80.053.2
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Ma, X.; Zhao, W.; Le, W.; Li, J.; Chen, P.; Jiao, Q. Synergetic Effect of Potassium Oxysalts on Combustion and Ignition of Al/CuO Composites. Nanomaterials 2021, 11, 3366. https://doi.org/10.3390/nano11123366

AMA Style

Ma X, Zhao W, Le W, Li J, Chen P, Jiao Q. Synergetic Effect of Potassium Oxysalts on Combustion and Ignition of Al/CuO Composites. Nanomaterials. 2021; 11(12):3366. https://doi.org/10.3390/nano11123366

Chicago/Turabian Style

Ma, Xiaohang, Wanjun Zhao, Wei Le, Jianxin Li, Pengwan Chen, and Qingjie Jiao. 2021. "Synergetic Effect of Potassium Oxysalts on Combustion and Ignition of Al/CuO Composites" Nanomaterials 11, no. 12: 3366. https://doi.org/10.3390/nano11123366

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop