Nanomaterials
Volume 10
Issue 1
10.3390/nano10010040
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation of Ionic Liquid-Coated Graphene Nanosheets/PTFE Nanocomposite for Stretchable, Flexible Conductor via a Pre-Stretch Processing

by
Yu Zhang
1,
Kaichang Kou
1,
Tiezheng Ji
1,
Zhengyong Huang
2,*,
Shuangcun Zhang
1,
Shijie Zhang
1 and
Guanglei Wu
3,4,*
1
Ministry of Education and Shaanxi Key Laboratory of Macromolecular Science and Technology, School of Science, Northwestern Polytechnical University, Xi’an 710129, China
2
State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400040, China
3
Institute of Materials for Energy and Environment, State Key Laboratory of Bio-Fibers and Eco-Textiles, College of Materials Science and Engineering, Qingdao University, Qingdao 266071, China
4
Key Laboratory of Engineering Dielectrics and Its Application, Ministry of Education, Harbin University of Science and Technology, Harbin 150080, China
*
Authors to whom correspondence should be addressed.
Nanomaterials 2020, 10(1), 40; https://doi.org/10.3390/nano10010040
Submission received: 8 November 2019 / Revised: 13 December 2019 / Accepted: 14 December 2019 / Published: 23 December 2019
(This article belongs to the Section Nanocomposite Materials)
Browse Figures
Review Reports Versions Notes

Abstract

:
The various volume concentrations of ionic liquid-modified graphene nanosheets filled polytetrafluoroethylene nanocomposites (IL-GNs/PTFE) for flexible conductors were fabricated via a pre-stretch processing method after cold-press sintering. The results indicated that pre-stretching has no significant weakening in the electrical conductivity of the nanocomposites, while the Young’s modulus greatly reduced by 62.5%, which is more suitable for flexible conductors. This may be because the reduced conductivity by the destructive conductive pathway cancels out the enhanced conductivity by the increased interlamellar spacing of IL-GNs via a pre-stretch processing, and the nanocomposite exhibits a phase transition from two to three-phase (with the introduction of an air phase) during pre-stretching. It was also found that the tensile strength of the nanocomposites was enhanced by 42.9% and the elongation at break and thermal conductivity decreased slightly with the same filler content after pre-stretching. The electrical conductivity of the pre-stretched nanocomposites tended to stabilize at 5.5 × 10−2 s·m−1, when the volume content of the packings achieved a percolation threshold (1.49 vol%). Meanwhile, the electrical resistivity of the pre-stretched 3.0 vol% IL-GNs/PTFE nanocomposite was slightly reduced by 0.30%, 0.38%, and 0.87% respectively after 180° twisting, 180° bending, and 10% stretching strain for 1000 cycles.

1. Introduction

Nowadays, the flexible and stretchable conductor, which is a fastest developing material, is one of the most widely used in the electronics industry, such as flexible sensors, stretchable supercapacitors, health monitoring installation, and wearable devices [1,2,3,4,5]. Generally, polymers are regarded as excellent insulating and soft materials in comparison with metal. Hence, if appropriate conductive fillers (such as metal powder [6,7], carbon black [8,9,10], carbon nanotubes [7,11,12]) cooperate with the polymeric matrix and the contents of the filler reach the percolation threshold, which means that the fillers in contact with each other in the matrix form a conductive network, it completes the transition from insulating material to semiconductor or conductor material.
Consequently, with the objective of actually fabricating high-performance flexible conductors, respectable researchers have been devoted to exploiting polymer-based conductors with flexibility and stretchability [13,14,15,16,17]. For instance, Liu and co-workers [18] transferred silver nanowires (AgNWs) into polydimethylsiloxane (PDMS) via an effective method to obtain AgNW/PDMS stretchable electrodes of maintained low sheet resistance after stretching, twisting, and bending for 1000 cycles. Hwang et al. [19] fabricated sandwich structure films of AgNWs hybridized with 0.025 wt% single-walled carbon nanotubes (SWCNTs) between layers of PDMS and transparent polyurethane (TPU), with the observed low sheet resistance value of 30 Ω/sq.
In recent years, graphene nanosheets (GNs) have attracted more attention as a hopeful packing to fill polymeric matrixes for electrically conductive properties, due to their unique electrical conductivity [20,21,22]. Yan et al. [23] designed and prepared flexible conductive bilayer films composed of elastomeric copolymer (N-isopropylacrylamide and 2-methoxyethyl acrylate) and wrinkled graphenes, which exhibited a high electrical conductivity of 126 s·cm−1. Yang et al. [24] fabricated a novel polyimide-based graphene foam via chemical and thermal reduction after dip-coating a polyimide foam to achieve 0.4 s·m−1 in electrical conductivity. However, the most critical challenge in the fabrication is the uniform dispersion of graphene nanosheets in the polymer matrix, which have a poor dispersion in solvent due to agglomeration [25,26,27]. In order to improve the dispersibility of GNs in substrate, significant scholars prepared graphene into reduced graphene oxide (rGO) [28,29] or grafted the hydroxyl group (–OH) [30], epoxy group (–CH(O)CH–) [31], carboxyl group (–COOH) [31,32], and other functional groups at the edge or defect of graphite oxide. Although these methods can prepare covalently bonded graphene with stable dispersion ability, the oxygen-containing functional groups abate the electrical performance of graphene. However, it has been reported that the functionalization of non-covalent bonds can be used to prepare graphene with stable dispersion and a less damaged lattice structure while retaining its excellent properties [33,34]. As a solvent with a small molecular volume, ionic liquid (IL) is often used as a non-covalently functionalized modifier, which can be better inserted or adsorbed into the nanopackings and can effectively prevent the agglomeration of the filler [35,36]. Zhao and co-authors had reported that the graphene sheets were functionalized with a synthetic poly(1-vinylimidazole) type ionic liquid by a quaternarization reaction, which showed improved dispersibility in DMF (Dimethyl Formamide) and ethanol solution [37].
As is known to all, polytetrafluoroethylene (PTFE) has unique properties due to its high fluorine–carbon bond energy, which has attracted extensive attention in the industrial field with its required thermostable performance [38]. Nevertheless, up to now, most of the investigations on PTFE have focused on improving its disadvantages, such as poor creep resistance, while the few references on the electrical conductivity of PTFE composites are available. In addition, due to the very regular molecular chains of PTFE and their high crystallinity after sintering, the PTFE matrix composite has a relatively high hardness that could not be suitable as a flexible material. However, through our previous study, it was found that when the PTFE-based composites were stretched within a specific range for a fast speed at ambient or high temperature, the characteristics of the material would change from rigidity to flexibility [39,40]. Hence, our purpose of this experiment is the preparation of a flexible conductor. First, we need to evenly disperse graphene nanosheets in the acetone; then, we need to prepare the PTFE nanocomposite by using the traditional cold-pressing and sintering process after mixing the ionic liquid-modified graphene nanosheets (IL-GNs) with PTFE powders by the wet-mixing method in the acetone. Finally, we need to soften the nanocomposite by a pre-stretching treatment, which can make it more suitable as a conductor nanocomposite (IL-GNs/PTFE) with flexibility and stretchability. Meanwhile, the influence of pre-stretching on the tensile, thermal, and electrical properties of the IL-GNs/PTFE nanocomposite and the conductivity of flexible conductors after twisting, bending, and stretching were investigated.

2. Experimental Procedure

2.1. Preparation of IL-GNs

Since we prepared the nanocomposite by the wet mixing method, we first needed to prepare GNs that could be dispersed uniformly in acetone solution. The specific preparation methods are as follows. Firstly, the commercial expansible graphite (75 μm, Shanghai Aladdin Biochemical Technology Co., Ltd., Shanghai, China) was transferred into a crucible and heated for 60 s in a preheated furnace at 800 °C. Subsequently, the obtained expanded graphite (EG) was mixed with 1-butyl-3-methylimidazolium hexafluorophosphate (BMIMPF6, 97%, Shanghai Macklin Biochemical Technology Co., Ltd., Shanghai, China) at a mass ratio of 1:1, and then added into ethanol solution (Xi’an Chemical Reagent Corporation, Xi’an, China) for ultrasonic dispersion for 1 h. Finally, the mixed solution was added into the jar mill with mechanical exfoliation for an hour before being dried at 70 °C for 2 h to constant weight. The fabrication of graphene nanosheets modified with ionic liquid (IL-GNs) is described in Scheme 1.

2.2. Fabrication of IL-GNs/PTFE Nanocomposites for Flexible Conductors

Firstly, the IL-GNs/PTFE nanocomposite specimens were prepared by wet mixing in acetone solution and then cold pressing and the sintering method. Secondly, the pre-stretching method was used to fabricate the flexible conductors, which is consistent with the PTFE composite preparation method in our previous literature [40,41]. In these experiments, the IL-GNs/PTFE nanocomposites with IL-GNs volume fractions of 0.5%, 1%, 1.5%, 2%, 2.5%, and 3% (the graphite density 2.2 g·cm−3 can be used to convert a weight fraction into a volume fraction.) for flexible conductors were fabricated via high-temperature (180 °C) unidirectional pre-stretching treatment to 1.5 fold of the original length at a rate of 100 mm·min−1 and remained stretched for 10 min before quenching. The unstretched test bar was 50 mm in length, 10 mm in width, and 2.2 mm in thickness, and it can be transmuted into the strip-shape sample with approximate dimensions of 55 mm length, 10 mm width, and 2 mm thickness after pre-stretching treatment due to the shrinkage of the polymer molecular chains. The fabrication of the IL-GNs/PTFE flexible conductor nanocomposite is also shown in Scheme 1.

2.3. Characterization Methods

Fourier transform infrared (FT-IR) spectra were recorded by a RAYLEIGH WQF-510A Fourier transform infrared spectrometer (Beijing, China) in the range from 4000 cm−1 to 400 cm−1. X-ray diffraction (XRD) was carried out using an X’Pert PRO MPD X-ray diffraction spectrometer (Almelo, The Netherlands) in the interval 2θ between 10° and 60° with Cu Kα radiation. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) images were made using a FEI Talos F200X TEM (Hillsboro, OR, USA) and FEI Verios G4 (Hillsboro, OR, USA), respectively.
The tensile properties of nanocomposites were investigated following ASTM D638-14 in the SANS CMT7204 tensile test machine (Shenzheng, China). A high precision digital scleroscope WHW MC010 (Shanghai, China) was used to test for shore hardness at a dead load of 5 kg and a residence time of 15 s according to ASTM D2240-2005. The density (ρ) of nanocomposites was characterized by the Archimedes method according to ASTM D792-2008. Thermal conductivity was measured using a thermal conductivity testing instrument Netzsch LFA427 (Selb, Germany) by the flash method according to standard test method ASTM E1461-2013. The specimen geometry is a test cube with a length of 10 mm and a thickness of 2 mm. The crystallization behavior of nanocomposites was employed by a TA Q600ADT (New Castle, DE, USA) different scanning calorimetry (DSC) instrument, and the heating rate was 10 °C·min−1. The calculation method of crystallinity adopted the equation recorded in the previous article. Six pieces of data were collected for these tests, and the reliability of the data was ensured by calculating the average.
The electrical resistivity of IL-GNs/PTFE nanocomposites was measured on a four-point conductivity probe with a linearly arranged four-point head. The volume resistance of nanocomposites in various temperatures was recorded by a self-made RT109A high-precision resistivity tester (non-continuous recording equipment).

3. Results and Discussion

3.1. Characterization Analysis of IL-GNs

Figure 1 shows the absorption peaks of BMIMPF6, GNs, and GNs surface-modified by BMIMPF6 (IL-GNs) in the FT-IR spectra, respectively. The characteristic peaks of both BMIMPF6 and IL-GNs curves are observed at 3172, 1385, 1169, 748, and 555 cm−1, corresponding to the vibration of methine (C–H) in cyclic BMIM+. The bands at 842 and 1574 cm−1 are attributed to the stretching vibration of PF6− and the carbon–nitrogen bond (C–N) inside BMIMPF6, respectively [42,43,44,45]. In addition, the FT-IR spectrum of GNs shows the bands at 1649 cm−1 for carbonyl (C=O) [46], which means that GNs were partially oxidized to graphene oxide (GO) during the heat treatment of expandable graphite. These results clearly indicate that ionic liquids have been successfully inserted into GNs.
Figure 2 shows the XRD pattern of expanded graphite (EG), GNs, and GNs surface-modified by ionic liquids (BMIMPF6) (IL-GNs). XRD is used to investigate the effect of surface treatment on the plane of GNs. By comparing the XRD curves of the three, it is found that there is a diffraction peak at 2θ = 26.5°, which correspond to the characteristic plane (003) of graphene [47,48]. However, the diffraction peak strength of EG is significantly smaller than that of the other two, which may be because the excessive layer spacing affects the test results of XRD. Furthermore, the diffraction peak of IL-GNs was slightly leftwards compared with that without ionic liquids. This consequence has further confirmed that ionic liquids facilitate a complete mechanical exfoliation.
The interlamellar spacing (d) between GNs can be calculated by using the Bragg equation [49,50]:
n λ = 2 d sin θ
where n represents the diffraction order (usually, n = 1), λ = wavelength of the X-rays (0.154056 nm), and θ = diffraction angle. The calculation results are represented in Table 1. It can be seen from the calculation results that the d of IL-GNs is smaller than that of expanded graphite and GNs, indicating that mechanical exfoliation and ionic liquid have a good effect on improving the agglomeration of GNs.
Through SEM technology, it can be noted from Figure 3a that the high-temperature expansion converted the expansible graphite into a worm-like expanded graphite consisting of loosely jointed thin GNs. Figure 3(b1,c1) shows that the worm-like structure completely disappeared after mechanical exfoliation, and the graphene nanosheets came to exist in a single or multi-layer crimped morphology. The SEM image of GNs (Figure 3(c1)) with horizontal dimensions over 10 μm interconnected edges by edges via van der Waals forces after mechanical exfoliation is quite different from that of IL-GNs (Figure 3(b1)). The TEM (Figure 3(b2,c2)) photographs also show that the delamination effect of the IL-GNs was better than that of the GNs.
Moreover, the sample photograph in Scheme 1a shows the dispersity of GNs and IL-GNs in acetone solution after 24 h. Apparently, the GNs modified by BMIMPF6 formed a uniformly and stably distributed black suspension in acetone, while the GNs were deposited at the bottom of the suspension due to agglomeration. This may be because BMIMPF6 functionalized GNs via non-covalent π–π interactions between the imidazole ring and basal plane of GNs, which leads to the interlamination of GNs that existed in coulomb forces and repelled each other. Scheme 1b shows that the IL-GNs have a better dispersion in PTFE powders than that of GNs after the wet-mixing method.

3.2. Tensile Properties of PTFE-Based Nanocomposites

The strain–stress curves of the PTFE-based nanocomposites with different packing volume contents are presented in Figure 4, and the corresponding tensile properties are listed in Table 2. It is obvious that the pre-stretch processing has a remarkable influence on the tensile properties. In particular, it is worth noting that the Young’s modulus of unstretched nanocomposites decreased sharply from approximately 48 MPa to about 18 MPa of pre-stretched ones, which has largely reduced by 62.5%. Generally, PTFE with higher modulus and hardness has a larger area of crystallization. However, in our experiment, the crystallinity of the pre-stretched nanocomposites was nothing breathtakingly different from that of the unstretched ones (As shown in Table 3, according to the results of crystallinity calculation, the crystallinity of the pre-stretched nanocomposite basically agreed with that of the unstretched one, so it can be judged that the pre-stretched treatment has not destroyed the crystal region of the material). Therefore, it was speculated that the large crystal region in the PTFE substrate would be split into multiple microcrystalline regions due to the pre-tensile treatment, which may be an important factor in the softening of nanocomposites. In addition, the spiral structure of the PTFE molecular chain in the high crystallinity region can be seen as a “miniature spring” with a locked deformation ability, whose freedom has been provided by the fragmented crystalline regions. Combined with the above two possible reasons, the PTFE-based nanocomposite presents a transition from rigidity to flexibility. Pre-stretching can also transparently enhance the tensile strength of the nanocomposites from approximately 14 MPa to about 20 MPa (increase by 42.9%), which contributes to the orientation of PTFE molecular chains, while the elongation at break declined from approximately 340% to 310% (decreased by 8.8%), which was due to the increased defects (microvoids) resulting from pre-stretching.
In addition, the maximum additive amount of filler only accounts for 3 vol% of the nanocomposite, and the low addition of filler does not affect the continuity of the PTFE matrix molecular chain. Hence, the packings have little effect on the tensile properties of nanocomposites, which is far less than the effect of pre-stretching.
The shore hardness and density of the PTFE-based nanocomposites with different packing volume contents are listed in Table 3. It was detected that the hardness and density of the pre-stretched nanocomposites are lower than those of the unstretched ones, which was consistent with a previous conclusion of Young’s modulus variation. Furthermore, from the SEM of the nanocomposite fracture surface (Figure 5), it can be clearly observed that the microvoids were induced by pre-stretch processing in the polymer matrix, which may be another key factor for the softening of the nanocomposite. These micrographs further explain that the “freedom-space” (microvoids) for the “miniature spring” are formed during the pre-stretch processing.

3.3. Thermal and Electrical Conductivities of PTFE-Based Nanocomposites

Figure 6 presents the thermal conductivities (λ) of the PTFE-based nanocomposites. It can be noted that the thermal conductivity of all the nanocomposites increases significantly with the increase of the packing content. This variation is consistent with the expectation: the packings with higher thermal conductivity can significantly improve the thermal conductivity of the nanocomposites, and the higher the content density of the packings, the higher the thermal conductivity of the composite. However, it was also found that the λ decreased slightly after pre-stretching. For instance, we could see the λ for the 1.5 vol% pre-stretched nanocomposite achieved 0.428 W·m−1·K−1, which was lower than that of the unstretched one (0.440 W·m−1·K−1) with the same packing volume content. This variation can be ascribed to two reasons: On the one hand, as the contact area of the thermal conductive channels formed by the packings decrease or disconnect due to the pre-stretching treatment, the heat is more likely to accumulate in the PTFE substrate with lower thermal conductivity. The variation of thermal pathways could be observed in Figure 7. It is easy to detect from Figure 7a that the packed IL-GNs in the unstretched nanocomposite are tightly bound together, while the contact area of packings is reduced or directly interrupted after pre-stretching, as shown in Figure 7b. On the other side, the two-phase (packings and polymer matrix) nanocomposite is transformed into a three-phase one during the pre-stretching; that is, the air phase (microvoids) with poor thermal conductivity is introduced into the initial two phases.
Generally, a conductive polymer is prepared by adding conductor filler, and the destruction of the conductive path in a polymer matrix would seriously affect the conductive property of the composite. However, the results of this experiment show an interesting phenomenon. As can be seen from Table 4, the electrical conductivities of pre-stretched nanocomposites are almost the same as that of the unstretched one, which means that the pre-stretch treatment did not have a serious impact on the electrical conductivity of the nanocomposite. These experimental results contradict the theory that the reduced conductivity was caused by the specimen irreversibly lengthening during pre-stretch processing.
Combined with XRD analysis (Figure 8 and Table 4), it was found that the interlamellar spacing (d) of IL-GNs in the unstretched matrix was smaller than that after pre-stretching. This may be because ionic liquid intercalated graphene has been pressed tightly by the cold-pressing during sample preparation (The d of IL-GNs in unstretched nanocomposites is less than that of IL-GNs powders, as shown in Table 1). Adding graphene thickness would inevitably increase the probability of the transferred electrons being exposed to the defects, which consists of imperfect graphene nanosheets. Zhang et al. [51] has reported that increasing the interlayer spacing of graphene could enhance the electrical conductivity of composites. Hence, the pre-stretching treatment would have a negative impact on the conductive pathways as a matter of course, but at the same time that the increase in the packing interlamellar spacing would have a positive impact on the enhancement of electrical conductivity, which may cancel each other out. As a result, the pre-stretching would not seriously affect the electrical conductivity of the IL-GNs/PTFE nanocomposites.

3.4. Percolation Threshold of Pre-Stretched Nanocomposites

Figure 9 represents the variation in the electrical conductivity of the pre-stretched IL-GNs/PTFE nanocomposites as a function of the IL-GNs concentration. In order to ensure the reliability of data, the electrical conductivity measured values were performed on at least three specimens and nine test points for each IL-GN content. Similar to the curves of typical carbon packed polymer matrix composites, the electrical conductivity increases sharply with the increase of IL-GNs content at a certain volume fraction due to the conductive filler forming a definite interconnection paths in the insulating substrate, which is the percolation threshold ( ϕ c ). It is evident from Figure 9 that when the addition of graphene is in excess of 1.0 vol%, the electrical conductivity of the composite increases rapidly, and the electrical conductivity increased by nine orders of magnitude as the IL-GNs concentration increased from 1.0 vol% to 1.5 vol%, which means that the formation of the interconnection paths within this scope could be identified. Meanwhile, the minuscule error bar for each specimen also indicates that the IL-GNs have been uniformly distributed in the PTFE matrix. A classical percolation model is used to correlate the percolation threshold ( ϕ c ), as indicated in Equation (2):
σ c = σ f ( ϕ − ϕ c ) t
where σc is the electrical conductivity of the composite, σf is the filler conductivity (graphene, 104.92 ± 0.52 ≈ 105 s·m−1 [52]), ϕ is the filler volume fraction, and t represents the exponential coefficient. The values of t = 1.99 and ϕ c = 1.49 vol% could be obtained by fitting the test data with the above equation.

3.5. Electrical Conductivity under Cyclic Deformation

Deformability is a significant feature of flexible composites. In this work, twisting, bending, and stretching experiments were carried out on four kinds of IL-GNs/PTFE nanocomposites, which had a greater filler volume fraction than the percolation threshold, i.e., 1.5, 2.0, 2.5 and 3.0 vol%, and the electrical conductivity of the nanocomposites after deformation (twisting, bending, or stretching) 1, 100, 500, and 1000 times was measured respectively (The unstretched nanocomposites were not discussed due to the insufficient deformation capacity). Here, R0 represents the original resistance of the nanocomposite, and ΔR/R0 refers to the resistance change as a function of the deformation cyclic number. As shown in Figure 10a,b, the ΔR/R0 increases after twisting or bending several times respectively, and the increase in ΔR/R0 of a low IL-GNs volume content nanocomposite is greater than those of the material with high volume content. This may be due to the poor creep resistance of PTFE. It is all known that the molecular chains of PTFE are prone to slip under long-term pressure, resulting in the disconnection of the conductive path inside the composite material. Commonly, the addition of filler can prevent molecular chains slippage of the substrate to some extent, and the resistance stabilities of nanocomposites with high IL-GNs volume fractions are stronger than those with low volume fractions. Moreover, it should be also noted that the ΔR/R0 remains stable when the deformation increased from 90° to 180°, whether twisting or bending.
However, it is observed that the increase amplitude of ΔR/R0 is inappreciable even after 1000 twisting or bending releasing cycles. For instance, the ΔR/R0 was increased by 0.13% and 0.14% in the first 180° twisting and 180° bending, respectively, and it only further increased to 0.29% and 0.38% after 180° twisting and 180° bending for 1000 cycles, respectively. The explanation factor of this phenomenon could be that the pre-stretching treatment has better released the flexible characteristics of the PTFE molecular chain, and the deformation of the material in the later stage (twisting and bending) is not enough to have a decisive influence on the conductive path of the pre-stretched IL-GNs/PTFE nanocomposite.
So far, as we know, the resistivity of the flexible conductor increases rapidly with the increase of tensile strain, even less than 10% for the tensile ratio [53,54]. Therefore, the fabrication of a flexible conductive polymer with high tensile strain has become a research hotspot. In this study, we also conducted 1, 100, 500, and 1000 stretching–releasing cycles on the electrical conductivity of the IL-GNs/PTFE nanocomposites at the tensile ratios of 5% and 10%, respectively. Similar to the results of twisting and bending, the ΔR/R0 increases with the number of stretching cycles, and the ΔR/R0 for the 10% tensile ratio is significantly higher than that for 5% tensile ratio at the same IL-GNs volume content, as shown in Figure 10c. Interestingly, a significant increase in ΔR/R0 was noted as the number of stretching process cycles increased from 1 to 100. This may be due to the pre-stretching process carried out in the early preparation of nanocomposites, which resulted in the stretched PTFE matrix chains that have a good cushioning effect against the deformation in the direction of stretching in a short time.

3.6. Resistance Change in Stretching at Different Temperatures

Scheme 2 illustrates the custom-made test equipment. The volume resistivity could be calculated according to Equation (3) [55,56,57]:
R = U S I h
where R is the volume resistivity, U is the voltage applied to the sample, I is the current passing through the sample, and S and h respectively represent the area of the sample in contact with the sensor and thickness of the specimen.
Figure 11a–c shows the ΔR/R0 of the three pre-stretched IL-GNs/PTFE nanocomposites with the highest electrical conductivity and materials after 100 stretching cycles at different temperatures as a function of the stretching strain. Apparently, the high volume fraction of IL-GNs has a slight advantage in deformation resistant capability compared to that of the low volume fraction. For example, the ΔR/R0 of the pre-stretched IL-GNs/PTFE nanocomposite decreases from 4.96% for 2.0 vol% IL-GNs to 3.43% for 3.0 vol% IL-GNs with the condition of 10% stretching strain at 25 °C (Similar changes occurred at 75 °C and 125 °C). The decreased ΔR/R0 should directly relate to the more densely conductive pathways, which is also evident from the tests of twisting and bending shown in Figure 10. Meanwhile, the ΔR/R0 of the nanocomposite is slightly increased after 100 stretching cycles under different temperatures (as shown by the solid line in Figure 11a–c). As can be noticed from Figure 11d, the high temperature has a significant effect on the ΔR/R0 of nanocomposites, the ΔR/R0 at low temperature has a lower value than that at high temperature with the same packing content normally due to the positive temperature coefficient (PTC). Compared to metal materials, non-metallic materials usually have a larger thermal expansion coefficient (CTE), resulting in the fracture of conductive paths and an increase of resistivity due to the wide difference in CTE between fillers (−8 × 10−6 K−1 for graphene [58]) and the polymer matrix (approximate 100 × 10−6 K−1 for PTFE [59]). It is interesting to observe that the growth rate of ΔR/R0 with low packing content is slightly higher than that of ΔR/R0 with high packing content, as shown by the dotted line in Figure 11d. While at 10% stretching strain, the ΔR/R0 increased from 4.95% to 8.27% (up 67.07%) at 2.0% filler volume fraction; in comparison, the ΔR/R0 increased from 3.43% to 5.72% (up 65.80%) at 3.0% filler volume fraction. Although the increase of packing content would reduce the ΔR/R0, this may be attributed to the nanocomposite with a higher content of high thermal conductivity fillers (IL-GNs) having better heat dissipation performance, which means that a high packing content nanocomposite with lower CTE can do better at preventing the destruction of conductive pathways in the matrix.

4. Conclusions

The IL-GNs were prepared by micromechanically exfoliating the expanded graphite (EG) in ionic liquid BMIMPF6. Then, PTFE matrix nanocomposites containing the IL-GNs with volume concentrations of 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, and 3%, respectively, were fabricated via the cold-pressing and sintering method. The IL-GNs/PTFE flexible conductor nanocomposites were prepared by pre-stretch processing after sintering, and the tensile, thermal, and electrical properties of pre-stretched and unstretched nanocomposites were investigated. Due to the surface treatment by ionic liquid, GNs can be dispersed stably in acetone suspension for at least 24 h and uniformly distributed easily with PTFE by wet-mixing. Analyzing the results from tensile properties, Young’s modulus decreased from approximately 48 MPa for pre-stretched nanocomposites to about 18 MPa for unstretched ones. The density, shore hardness, DSC, and SEM characterizations can indicate that this variation tendency may be due to the existed microvoids in the polymer matrix and split crystalline regions after pre-stretch processing. In addition, the tensile strength of the pre-stretched nanocomposites strengthened from 14 MPa to 20 MPa in comparison with the unstretched ones, while elongation at break declined slightly from 340% to 310%. The thermal conductivity of the pre-stretched nanocomposite is slightly lower than that of the unstretched ones, which may be attributed to the transition of the nanocomposite from two-phase (polymer, fillers) before stretching to three-phase (polymer, fillers, and air) after stretching. It is also interesting to note that the pre-stretching treatment had little influence on the electrical properties of IL-GNs/PTFE nanocomposites. This may be because the treatment reduced the conductivity via destroying the conductive paths offset by the enhanced conductivity via increasing interlamellar spacing. Through simulation calculation, the pre-stretched IL-GNs/PTFE nanocomposite was shown to have a lower percolation threshold of 1.49 vol%, which achieved an approximate electrical conductivity of 5.5 × 10−2 s·m−1. The pre-stretched nanocomposite exhibits stable electrical conductivity after 180° twisting, 180° bending, and 10% stretching strain for 1000 cycles, even though it is slightly reduced by 0.30%, 0.38%, and 0.87% respectively. The volume resistivity of the nanocomposites under high temperature with stretching strain is analyzed; it is noted that the ΔR/R0 of the nanocomposites increases with the increase of temperature due to the PTC, and which is slightly increased for 100 stretched cycles at high temperatures. It is also observed that the growth rate of ΔR/R0 with low packing content is slightly higher than that with high packing content, which may be because the nanocomposites with high IL-GNs concentration have higher thermal conductivity (0.639 W·m−1·K−1 for 3.0 vol% IL-GNs versus 0.305 W·m−1·K−1 for 0.5 vol% IL-GNs). The results revealed that pre-stretch processing for IL-GNs/PTFE nanocomposite can not only significantly reduce the hardness of the material, but it can also maintain the stable electrical conductivity of the nanocomposites even after repeated deformation at ambient or high temperatures. An IL-GNs/PTFE nanocomposite flexible conductor prepared by a pre-stretching method can provide a good guideline for a wide range of applications in ambient or high-temperature strain sensors.

Author Contributions

Y.Z. collected the related literature and designed the experiment; K.K. and T.J. gave relevant guidance in manuscript writing; S.Z. (Shuangcun Zhang) provided adequate help in the experiment process; S.Z. (Shijie Zhang) also gave some great suggestions in the experiment process. Z.H. and G.W. also gave some great enlightenment and helpful advices during the writing process. All authors have read and agreed to the published version of the manuscript.

Funding

This work was financially supported by the Natural Science Foundation of Shandong Province (No.ZR2019YQ24), the Qingchuang Talents Induction Program of Shandong Higher Education Institution (Research and Innovation Team of Structural-Functional Polymer Composites), the National Natural Science Foundation of China (Nos. 51707016, 51407134), the Key Laboratory of Engineering Dielectrics and Its Application (Harbin University of Science and Technology), and the Ministry of Education (No. KFZ1803) and China Postdoctoral Science Foundation (No. 2016M590619).

Acknowledgments

The authors thank the colleagues in the laboratory for their support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Chen, Q.; Wang, X.Q.; Chen, F.; Zhang, N.; Ma, M.M. Extremely strong and tough polythiophene composite for flexible electronics. Chem. Eng. J. 2019, 368, 933–940. [Google Scholar] [CrossRef]
  2. Dong, D.D.; Ma, J.Z.; Ma, Z.L.; Chen, Y.M.; Zhang, H.M.; Shao, L.; Gao, J.P.; Wei, L.F.; Wei, A.J.; Kang, S.L. Flexible and lightweight microcellular RGO@Pebax composites with synergistic 3D conductive channels and microcracks for piezoresistive sensors. Compos. A Appl. Sci. 2019, 123, 222–231. [Google Scholar] [CrossRef]
  3. Chen, S.Y.; Cheng, Y.H.; Xie, Q.; Xiao, B.; Wang, Z.D.; Liu, J.Y. Enhanced breakdown strength of aligned-sodium-titanate- nanowire/epoxy nanocomposites and their anisotropic dielectric properties. Compos. Part A Appl. Sci. 2019, 120, 84–94. [Google Scholar] [CrossRef]
  4. Benight, S.J.; Wang, C.; Tok, J.B.H.; Bao, Z.N. Stretchable and self-healing polymers and devices for electronic skin. Prog. Polym. Sci. 2013, 38, 1961–1977. [Google Scholar] [CrossRef]
  5. Jia, Z.; Wang, B.; Feng, A.; Liu, J.; Zhang, M.; Huang, Z. Development of spindle-cone shaped of Fe/α-Fe2O3 hybrids and their superior wideband electromagnetic absorption performance. J. Alloys Compd. 2019, 799, 216–223. [Google Scholar] [CrossRef]
  6. Boland, C.S.; Khan, U.; Benameur, H.; Coleman, J.N. Surface coatings of silver nanowires lead to effective, high conductivity, high-strain, ultrathin sensors. Nanoscale 2017, 9, 18507–18515. [Google Scholar] [CrossRef]
  7. Hou, T.Q.; Wang, B.B.; Ma, M.L.; Feng, A.L.; Huang, Z.Y.; Zhang, Y.; Jia, Z.R.; Tan, G.X.; Cao, H.J.; Wu, G.L. Preparation of two-dimensional titanium carbide (Ti3C2Tx and NiCo2O4 composites to achieve excellent microwave absorption properties. Compos. Part B Eng. 2020, 180, 107577. [Google Scholar] [CrossRef]
  8. Huang, T.; Ma, C.G.; Dai, P.B.; Zhang, J. Improvement in dielectric constant of carbon black/epoxy composites with separated structure by surface-modified hollow glass beads with reduced graphene oxide. Compos. Sci. Technol. 2019, 176, 46–53. [Google Scholar] [CrossRef]
  9. Liu, X.H.; Li, C.H.; Pan, Y.M.; Schubert, D.W.; Liu, C.T. Shear-induced rheological and electrical properties of molten poly(methyl methacrylate)/carbon black nanocomposites. Compos. Part B Eng. 2019, 164, 37–44. [Google Scholar] [CrossRef]
  10. Feng, A.; Ma, M.; Jia, Z.; Zhang, M. Fabrication of NiFe2O4@carbon fiber coated with phytic acid-doped polyaniline composite and its application as an electromagnetic wave absorber. RSC Adv. 2019, 9, 25932–25941. [Google Scholar] [CrossRef] [Green Version]
  11. Wang, M.; Zhang, K.; Dai, X.X.; Li, Y.; Guo, J.; Liu, H.; Li, G.H.; Tan, Y.J.; Zeng, J.B.; Guo, Z.H. Enhanced electrical conductivity and piezoresistive sensing in multi-wall carbon nanotubes/polydimethylsiloxane nanocomposites via the construction of a self-segregated structure. Nanoscale 2017, 9, 11017–11026. [Google Scholar] [CrossRef] [PubMed]
  12. Wu, G.L.; Jia, Z.R.; Zhou, X.F.; Nie, G.Z.; Lv, H.L. Interlayer Controllable of Hierarchical MWCNTs@C@FexOy Cross-linked Composite with Wideband Electromagnetic Absorption Performance. Compos. Part A Appl. Sci. 2020, 128, 105687. [Google Scholar] [CrossRef]
  13. Li, J.; Ma, J.; Chen, S.; Huang, Y.; He, J. Adsorption of lysozyme by alginate/graphene oxide composite beads with enhanced stability and mechanical property. Mater. Sci. Eng. C 2018, 89, 25–32. [Google Scholar] [CrossRef]
  14. Jia, Z.; Wang, C.; Feng, A.; Shi, P.; Zhang, C.; Liu, X.; Wang, K.; Wu, G. A low dielectric decoration strategy to achieve absorption dominated electromagnetic shielding material. Compos. B Eng. 2019, 107690. [Google Scholar] [CrossRef]
  15. Pan, C.; Zhang, J.; Kou, K.; Zhang, Y.; Wu, G. Investigation of the through-plane thermal conductivity of polymer composites with in-plane oriented hexagonal boron nitride. Int. J. Heat Mass Transf. 2018, 120, 1–8. [Google Scholar] [CrossRef]
  16. Chen, S.; Meng, G.; Kong, B.; Xiao, B.; Wang, Z.; Jing, Z.; Gao, Y.; Wu, G.; Wang, H.; Cheng, Y. Asymmetric alicyclic amine-polyether amine molecular chain structure for improved energy storage density of high-temperature crosslinked polymer capacitor. Chem. Eng. J. 2019. [Google Scholar] [CrossRef]
  17. Pan, C.; Kou, K.; Jia, Q.; Zhang, Y.; Wu, G.; Ji, T. Improved thermal conductivity and dielectric properties of hBN/PTFE composites via surface treatment by silane coupling agent. Compos. B Eng. 2017, 111, 83–90. [Google Scholar] [CrossRef]
  18. Liu, H.S.; Pan, B.C.; Liou, G.S. Highly transparent AgNW/PDMS stretchable electrodes for elastomeric electrochromic devices. Nanoscale 2017, 9, 2633–2639. [Google Scholar] [CrossRef]
  19. Hwang, B.; Choi, S.; Lee, K.; Kim, J. Highly stretchable and transparent electrode film based on SWCNT/Silver nanowire hybrid nanocomposite. Compos. B Eng. 2018, 151, 1–7. [Google Scholar] [CrossRef]
  20. Wu, G.; Cheng, Y.; Yang, Z.; Jia, Z.; Wu, H.; Yang, L.; Li, H.; Guo, P.; Lv, H. Design of Carbon Sphere/Magnetic Quantum Dots with Tunable Phase Compositions and Boost Dielectric Loss Behavior. Chem. Eng. J. 2018, 333, 519–528. [Google Scholar] [CrossRef]
  21. Yang, G.; Wang, Y.; Xu, H.; Zhou, S.; Jia, S.; Zang, J. Preparation and properties of three dimensional graphene/phenolic resin composites via in-situ polymerization in graphene hydrogels. Appl. Surf. Sci. 2018, 447, 837–844. [Google Scholar] [CrossRef]
  22. Ruiz-Hitzky, E.; Sobral, M.M.C.; Gómez-Avilés, A.; Nunes, C.; Ruiz-García, C.; Ferreira, P.; Aranda, P. Clay-Graphene Nanoplatelets Functional Conducting Composites. Adv. Funct. Mater. 2016, 26, 7394–7405. [Google Scholar] [CrossRef]
  23. Yan, S.; Zhang, G.; Jiang, H.; Li, F.; Zhang, L.; Xia, Y.; Wang, Z.; Wu, Y.; Li, H. Highly Stretchable Room-Temperature Self-Healing Conductors Based on Wrinkled Graphene Films for Flexible Electronics. ACS Appl. Mater. Interfaces 2019, 11, 10736–10744. [Google Scholar] [CrossRef] [PubMed]
  24. Yang, J.; Ye, Y.; Li, X.; Lü, X.; Chen, R. Flexible, conductive, and highly pressure-sensitive graphene-polyimide foam for pressure sensor application. Compos. Sci. Technol. 2018, 164, 187–194. [Google Scholar] [CrossRef]
  25. García-Macías, E.; Rodríguez-Tembleque, L.; Sáez, A. Bending and free vibration analysis of functionally graded graphene vs. carbon nanotube reinforced composite plates. Compos. Struct. 2018, 186, 123–138. [Google Scholar] [CrossRef]
  26. Li, Z.; Chu, J.; Yang, C.; Hao, S.; Bissett, M.A.; Kinloch, I.A.; Young, R.J. Effect of functional groups on the agglomeration of graphene in nanocomposites. Compos. Sci. Technol. 2018, 163, 116–122. [Google Scholar] [CrossRef]
  27. Xie, Y.; Wen, L.; Zhang, J.; Zhou, T. Enhanced local controllable laser patterning of polymers induced by graphene/polystyrene composites. Mater. Des. 2018, 141, 159–169. [Google Scholar] [CrossRef]
  28. Shin, D.G.; Yeo, H.; Ku, B.; Goh, M.; You, N. A facile synthesis method for highly water-dispersible reduced graphene oxide based on covalently linked pyridinium salt. Carbon 2017, 121, 17–24. [Google Scholar] [CrossRef]
  29. Wang, D.; Duan, H.; Lü, J.; Lü, C. Fabrication of thermo-responsive polymer functionalized reduced graphene oxide@Fe3O4@Au magnetic nanocomposites for enhanced catalytic applications. J. Mater. Chem. A 2017, 5, 5088–5097. [Google Scholar] [CrossRef]
  30. Cai, L.; Lin, Z.; Wang, M.; Pan, F.; Chen, J.; Wang, Y.; Shen, X.; Chai, Y. Improved interfacial H2O supply by surface hydroxyl groups for enhanced alkaline hydrogen evolution. J. Mater. Chem. A 2017, 5, 24091–24097. [Google Scholar] [CrossRef]
  31. Vinod, S.; Tiwary, C.S.; Samanta, A.; Ozden, S.; Narayanan, T.N.; Vajtai, R.; Agarwal, V.; Singh, A.K.; John, G.; Ajayan, P.M. Graphene Oxide Epoxy (GO-xy): GO as Epoxy Adhesive by Interfacial Reaction of Functionalities. Adv. Mater. Interfaces 2018, 5, 1700657. [Google Scholar] [CrossRef]
  32. Eng, A.Y.S.; Sofer, Z.; Sedmidubský, D.; Pumera, M. Synthesis of Carboxylated-Graphenes by the Kolbe-Schmitt Process. ACS Nano 2017, 11, 1789–1797. [Google Scholar] [CrossRef] [PubMed]
  33. Wang, X.; Liu, X.; Yuan, H.; Liu, H.; Liu, C.; Li, T.; Yan, C.; Yan, X.; Shen, C.; Guo, Z. Non-covalently functionalized graphene strengthened poly(vinyl alcohol). Mater. Des. 2018, 139, 372–379. [Google Scholar] [CrossRef]
  34. Chen, C.; Qiu, S.; Cui, M.; Qin, S.; Yan, G.; Zhao, H.; Wang, L.; Xue, Q. Achieving high performance corrosion and wear resistant epoxy coatings via incorporation of noncovalent functionalized graphene. Carbon 2017, 114, 356–366. [Google Scholar] [CrossRef]
  35. Chen, X.; Shi, T.; Zhong, K.; Wu, G.; Lu, Y. Capacitive behavior of MoS2 decorated with FeS2@carbon nanospheres. Chem. Eng. J. 2020, 379, 122240. [Google Scholar] [CrossRef]
  36. He, Z.Q.; Alexandridis, P. Ionic liquid and nanoparticle hybrid systems: Emerging applications. Adv. Colloid Interface Sci. 2017, 244, 54–70. [Google Scholar] [CrossRef] [PubMed]
  37. Zhao, W.; Tang, Y.; Xi, J.; Kong, J. Functionalized graphene sheets with poly(ionic liquid)s and high adsorption capacity of anionic dyes. Appl. Surf. Sci. 2015, 326, 276–284. [Google Scholar] [CrossRef]
  38. Puts, G.J.; Crouse, P.; Ameduri, B.M. Polytetrafluoroethylene: Synthesis and Characterization of the Original Extreme Polymer. Chem. Rev. 2019, 119, 1763–1805. [Google Scholar] [CrossRef]
  39. Pan, C.; Kou, K.C.; Zhang, Y.; Li, Z.Y.; Wu, G.L. Enhanced through-plane thermal conductivity of PTFE composites with hybrid fillers of hexagonal boron nitride platelets and aluminum nitride particles. Compos. Part B Eng. 2018, 153, 1–8. [Google Scholar] [CrossRef]
  40. Zhang, Y.; Kou, K.C.; Pan, C.; Li, Z.Y.; Ji, T.Z. Effect of tensile rates on thermal and mechanical properties of porous PTFE composites. J. Appl. Polym. Sci. 2019, 136, 48175. [Google Scholar] [CrossRef]
  41. Pan, C.; Kou, K.C.; Zhang, Y.; Li, Z.Y.; Ji, T.Z.; Wu, G.L. Investigation of the dielectric and thermal conductive properties of core–shell structured HGM@hBN/PTFE composites. J. Mater. Sci. Mater. Electron. 2018, 27, 238–239. [Google Scholar] [CrossRef]
  42. Wang, J.; Cheng, D.; Chen, X.; Du, Z.; Fang, Z. Direct Extraction of Double-Stranded DNA Into Ionic Liquid 1-Butyl-3-methylimidazolium Hexafluorophosphate and Its Quantification. Anal. Chem. 2007, 79, 620–625. [Google Scholar] [CrossRef] [PubMed]
  43. Ramenskaya, L.M.; Grishina, E.P. Intensification phenomenon of weak ionic interactions of 1-butyl-3-methylimidazolium hexafluorophosphate ionic liquid macro-dispersed in poly(methyl methacrylate): FTIR spectroscopic evidence. J. Mol. Liqulds 2016, 218, 133–137. [Google Scholar] [CrossRef]
  44. Srinivasa Rao, V.; Vijaya Krishna, T.; Madhu Mohan, T.; Madhusudana Rao, P. Thermodynamic and volumetric behavior of green solvent 1-butyl-3-methylimidazolium tetrafluoroborate with aniline from T = (293.15 to 323.15) K at atmospheric pressure. J. Chem. Thermodyn. 2016, 100, 165–176. [Google Scholar] [CrossRef]
  45. Sun, W.; Gao, R.; Jiao, K. Electrochemistry and Electrocatalysis of a Nafion/Nano-CaCO3/Hb Film Modified Carbon Ionic Liquid Electrode Using BMIMPF6 as Binder. Electroanalysis 2007, 19, 1368–1374. [Google Scholar] [CrossRef]
  46. Shaikh, M.; Singh, S.K.; Khilari, S.; Sahu, M.; Ranganath, K.V.S. Graphene oxide as a sustainable metal and solvent free catalyst for dehydration of fructose to 5-HMF: A new and green protocol. Catal. Commun. 2018, 106, 64–67. [Google Scholar] [CrossRef]
  47. Bafana, A.P.; Yan, X.; Wei, X.; Patel, M.; Guo, Z.; Wei, S.; Wujcik, E.K. Polypropylene nanocomposites reinforced with low weight percent graphene nanoplatelets. Compos. B Eng. 2017, 109, 101–107. [Google Scholar] [CrossRef]
  48. Kang, S.; Yu, T.; Liu, T.; Guan, S. Eco-friendly preparation of large-sized graphene via short-circuit discharge of lithium primary battery. J. Colloid Interface Sci. 2018, 512, 489–496. [Google Scholar] [CrossRef]
  49. Jia, Z.; Wang, B.; Feng, A.; Liu, J.; Zhang, C.; Zhang, M.; Wu, G. Fabrication of NixCo3-xS4 hollow nanosphere as wideband electromagnetic absorber at thin matched thickness. Ceram. Int. 2019, 45, 15854–15859. [Google Scholar] [CrossRef]
  50. Zhou, X.F.; Zhang, C.H.; Zhang, M.; Feng, A.L.; Qu, S.L.; Zhang, Y.; Liu, X.H.; Jia, Z.R.; Wu, G.L. Synthesis of Fe3O4/carbon foams composites with broadened bandwidth and excellent electromagnetic wave absorption performance. Compos. Part A Appl. Sci. 2019, 127, 105627. [Google Scholar] [CrossRef]
  51. Zhang, Y.H.; Park, S.J. Imidazolium-optimized conductive interfaces in multilayer graphene nanoplatelet/epoxy composites for thermal management applications and electroactive devices. Polymer 2019, 168, 53–60. [Google Scholar] [CrossRef]
  52. Stankovich, S.; Dikin, D.A.; Dommett, G.H.B.; Kohlhaas, K.M.; Zimney, E.J.; Stach, E.A.; Piner, R.D.; Nguyen, S.T.; Ruoff, R.S. Graphene-based composite materials. Nature 2006, 442, 282–286. [Google Scholar] [CrossRef] [PubMed]
  53. Wang, J.; Lee, P.S. Progress and Prospects in Stretchable Electroluminescent Devices. Nanophotonics 2017, 6, 435–451. [Google Scholar] [CrossRef] [Green Version]
  54. Kayser, L.V.; Lipomi, D.J. Stretchable Conductive Polymers and Composites Based on PEDOT and PEDOT:PSS. Adv. Mater. 2019, 31, 1806133. [Google Scholar] [CrossRef] [Green Version]
  55. Wu, W.; Yu, C.D.; Wang, Q.; Zhao, F.Y.; He, H.; Liu, C.Z.; Yang, Q.L. Research advances of DNA aptasensors for foodborne pathogen detection. Crit. Rev. Food Sci. Nutr. 2019. [Google Scholar] [CrossRef]
  56. Wang, Z.; Yang, M.; Cheng, Y.; Liu, J.; Xiao, B.; Chen, S.; Huang, J.; Xie, Q.; Wu, H. Dielectric properties and thermal conductivity of epoxy composites using quantum-sized silver decorated core/shell structured alumina/polydopamine. Compos. A Appl. Sci. 2019, 118, 302–311. [Google Scholar] [CrossRef]
  57. Wu, W.; Yu, C.; Chen, J.; Yang, Q. Fluorometric detection of copper ions using click chemistry and the target-induced conjunction of split DNAzyme fragments. Int. J. Environ. Anal. Chem. 2019. [Google Scholar] [CrossRef]
  58. Yoon, D.; Son, Y.; Cheong, H. Negative Thermal Expansion Coefficient of Graphene Measured by Raman Spectroscopy. Nano Lett. 2011, 11, 3227–3231. [Google Scholar] [CrossRef] [Green Version]
  59. Zhang, Y.; Kou, K.; Zhang, S.; Ji, T. Improving thermal properties of ultrafine-glass-fiber reinforced PTFE hybrid composite via surface modification by (3-aminopropyl)triethoxysilane. J. Polym. Res. 2019, 26, 214. [Google Scholar] [CrossRef]
Nanomaterials 10 00040 sch001 550
Scheme 1. Fabrication of ionic liquid-modified graphene nanosheets filled polytetrafluoroethylene (IL-GNs/PTFE) flexible conductor nanocomposite. (a) Dispersion of GNs and IL-GNs in acetone solution after 24 h. (b) The presence of conspicuous white particles (PTFE) in the GNs/PTFE mixture suggests that GNs without modification by ionic liquid are more difficult to distribute uniformly in PTFE by the wet-mixing method.
Scheme 1. Fabrication of ionic liquid-modified graphene nanosheets filled polytetrafluoroethylene (IL-GNs/PTFE) flexible conductor nanocomposite. (a) Dispersion of GNs and IL-GNs in acetone solution after 24 h. (b) The presence of conspicuous white particles (PTFE) in the GNs/PTFE mixture suggests that GNs without modification by ionic liquid are more difficult to distribute uniformly in PTFE by the wet-mixing method.
Nanomaterials 10 00040 sch001
Nanomaterials 10 00040 g001 550
Figure 1. Fourier transform infrared (FT-IR) spectrum of 1-butyl-3-methylimidazolium hexafluorophosphate (BMIMPF6), GNs and IL-GNs.
Figure 1. Fourier transform infrared (FT-IR) spectrum of 1-butyl-3-methylimidazolium hexafluorophosphate (BMIMPF6), GNs and IL-GNs.
Nanomaterials 10 00040 g001
Nanomaterials 10 00040 g002 550
Figure 2. XRD patterns of expanded graphite (EG), GNs, and IL-GNs.
Figure 2. XRD patterns of expanded graphite (EG), GNs, and IL-GNs.
Nanomaterials 10 00040 g002
Nanomaterials 10 00040 g003 550
Figure 3. SEM of (a) EG, (b1) IL-GNs and (c1) GNs. TEM of (b2) IL-GNs and (c2) GNs.
Figure 3. SEM of (a) EG, (b1) IL-GNs and (c1) GNs. TEM of (b2) IL-GNs and (c2) GNs.
Nanomaterials 10 00040 g003
Nanomaterials 10 00040 g004 550
Figure 4. Stress–strain curves of PTFE-based nanocomposites.
Figure 4. Stress–strain curves of PTFE-based nanocomposites.
Nanomaterials 10 00040 g004
Nanomaterials 10 00040 g005 550
Figure 5. SEM micrographs of the fracture surface for (a) unstretched 1.5 vol% IL-GNs/PTFE and (b) pre-stretched 1.5 vol% IL-GNs/PTFE nanocomposites.
Figure 5. SEM micrographs of the fracture surface for (a) unstretched 1.5 vol% IL-GNs/PTFE and (b) pre-stretched 1.5 vol% IL-GNs/PTFE nanocomposites.
Nanomaterials 10 00040 g005
Nanomaterials 10 00040 g006 550
Figure 6. Thermal conductivity of the PTFE-based nanocomposites.
Figure 6. Thermal conductivity of the PTFE-based nanocomposites.
Nanomaterials 10 00040 g006
Nanomaterials 10 00040 g007 550
Figure 7. SEM morphologies of (a) unstretched and (b) pre-stretched IL-GNs/PTFE nanocomposite (1.5 vol%).
Figure 7. SEM morphologies of (a) unstretched and (b) pre-stretched IL-GNs/PTFE nanocomposite (1.5 vol%).
Nanomaterials 10 00040 g007
Nanomaterials 10 00040 g008 550
Figure 8. XRD curves of PTFE-based nanocomposites. (a) Boxes A, B, and C respectively represent the characteristic diffraction peaks of PTFE, graphene, and PTFE. (b) The graphene characteristic peaks of the pre-stretched nanocomposite are significantly shifted to the left in the enlarged box B. According to Formula (1), it can be calculated that the interlamellar spacing of the IL-GNs increases after pre-stretch processing.
Figure 8. XRD curves of PTFE-based nanocomposites. (a) Boxes A, B, and C respectively represent the characteristic diffraction peaks of PTFE, graphene, and PTFE. (b) The graphene characteristic peaks of the pre-stretched nanocomposite are significantly shifted to the left in the enlarged box B. According to Formula (1), it can be calculated that the interlamellar spacing of the IL-GNs increases after pre-stretch processing.
Nanomaterials 10 00040 g008
Nanomaterials 10 00040 g009 550
Figure 9. Variation in the electrical conductivity as a function of the volume fraction of the IL-GNs content. A percolation model implies the threshold of 1.49 vol% for the nanocomposites.
Figure 9. Variation in the electrical conductivity as a function of the volume fraction of the IL-GNs content. A percolation model implies the threshold of 1.49 vol% for the nanocomposites.
Nanomaterials 10 00040 g009
Nanomaterials 10 00040 g010 550
Figure 10. The (a) twisting, (b) bending, and (c) stretching of the resistance change (ΔR/R0) as a function of the cycle numbers.
Figure 10. The (a) twisting, (b) bending, and (c) stretching of the resistance change (ΔR/R0) as a function of the cycle numbers.
Nanomaterials 10 00040 g010
Nanomaterials 10 00040 sch002 550
Scheme 2. Experimental equipment to test the volume resistivity of nanocomposites.
Scheme 2. Experimental equipment to test the volume resistivity of nanocomposites.
Nanomaterials 10 00040 sch002
Nanomaterials 10 00040 g011 550
Figure 11. The resistance change (ΔR/R0) of the pre-stretched IL-GNs-based flexible conductor nanocomposites and 100 cycles of stretched materials at different temperature as a function of stretching strain, respectively at (a) 25 °C, (b) 75 °C, and (c) 125 °C; (d) ΔR/R0 of nanocomposites with various packing content at 10% stretching strain.
Figure 11. The resistance change (ΔR/R0) of the pre-stretched IL-GNs-based flexible conductor nanocomposites and 100 cycles of stretched materials at different temperature as a function of stretching strain, respectively at (a) 25 °C, (b) 75 °C, and (c) 125 °C; (d) ΔR/R0 of nanocomposites with various packing content at 10% stretching strain.
Nanomaterials 10 00040 g011
Table
Table 1. Structural parameters of expanded graphite (EG), GNs, and IL-GNs.
Table 1. Structural parameters of expanded graphite (EG), GNs, and IL-GNs.
Specimen2 Theta (Degree)d (Å)Miller Index
Expanded Graphite26.6203.3458(003)
54.6401.6783(006)
GNs26.4793.3633(003)
54.5991.6795(006)
IL-GNs26.1613.4035(003)
54.2801.6886(006)
Table
Table 2. Tensile properties of PTFE-based nanocomposites.
Table 2. Tensile properties of PTFE-based nanocomposites.
SpecimenTensile Strength (MPa)Young’s Modulus (MPa)Elongation at Break (%)
0.5 vol%
IL-GNs/PTFE nanocomposite		14.89 ± 1.6648.56 ± 3.86341 ± 10.39
19.23 ± 1.5618.68 ± 2.81318 ± 7.88
1.0 vol%
IL-GNs/PTFE nanocomposite		13.54 ± 2.0549.98 ± 4.23336 ± 7.67
20.03 ± 1.4517.97 ± 2.68305 ± 6.76
1.5 vol%
IL-GNs/PTFE nanocomposite		14.64 ± 2.1146.44 ± 2.77333 ± 9.49
18.86 ± 1.5717.33 ± 1.55311 ± 8.52
2.0 vol%
IL-GNs/PTFE nanocomposite		15.18 ± 1.9947.59 ± 2.71340 ± 8.05
20.02 ± 1.7319.05 ± 2.01320 ± 5.99
2.5 vol%
IL-GNs/PTFE nanocomposite		15.05 ± 2.0049.34 ± 3.46337 ± 10.20
19.97 ± 1.6918.49 ± 1.79310 ± 6.05
3.0 vol%
IL-GNs/PTFE nanocomposite		14.94 ± 2.1648.76 ± 3.12343 ± 9.58
20.14 ± 1.5018.11 ± 1.98307 ± 9.69
The gray background part refers to the properties of pre-stretched nanocomposites.
Table
Table 3. Other parameters of PTFE-based nanocomposites.
Table 3. Other parameters of PTFE-based nanocomposites.
SpecimenShore HardnessDensity (g·cm−3)Crystallinity (%)
0.5 vol%
IL-GNs/PTFE nanocomposite		57.8 ± 0.822.1656 ± 0.04633.7 ± 3.04
47.1 ± 0.932.0989 ± 0.03432.5 ± 2.68
1.0 vol%
IL-GNs/PTFE nanocomposite		57.4 ± 0.582.1712 ± 0.04531.3 ± 2.45
46.2 ± 0.722.1162 ± 0.08333.9 ± 3.12
1.5 vol%
IL-GNs/PTFE nanocomposite		57.6 ± 0.762.1689 ± 0.07232.0 ± 2.02
46.8 ± 1.042.1073 ± 0.05031.7 ± 2.88
2.0 vol%
IL-GNs/PTFE nanocomposite		57.5 ± 1.022.1697 ± 0.03831.8 ± 2.24
47.2 ± 0.862.0911 ± 0.05732.8 ± 2.54
2.5 vol%
IL-GNs/PTFE nanocomposite		57.7 ± 0.922.1765 ± 0.06232.8 ± 3.16
46.5 ± 0.772.1125 ± 0.07433.1 ± 1.99
3.0 vol%
IL-GNs/PTFE nanocomposite		57.9 ± 0.702.1703 ± 0.04832.4 ± 2.75
46.4 ± 0.902.0998 ± 0.06632.7 ± 2.67
The gray background part refers to the parameters of pre-stretched nanocomposites.
Table
Table 4. Electrical properties of PTFE-based nanocomposites and the interlamellar spacing of corresponding packings.
Table 4. Electrical properties of PTFE-based nanocomposites and the interlamellar spacing of corresponding packings.
SpecimenUnstretchedPre-Stretched
Electrical Conductivity (s·m−1)d (Å)Electrical Conductivity (s·m−1)d (Å)
0.5 vol% IL-GNs/PTFE(5.36 ± 0.08) × 10−133.3681(5.43 ± 0.12) × 10−133.3964
1.0 vol% IL-GNs/PTFE(5.49 ± 0.11) × 10−113.3842(5.51 ± 0.09) × 10−113.4061
1.5 vol% IL-GNs/PTFE(5.64 ± 0.09) × 10−33.3567(5.65 ± 0.11) × 10−33.3983
2.0 vol% IL-GNs/PTFE(5.20 ± 0.08) × 10−23.3912(5.22 ± 0.08) × 10−23.4003
2.5 vol% IL-GNs/PTFE(5.52 ± 0.08) × 10−23.3857(5.47 ± 0.10) × 10−23.3910
3.0 vol% IL-GNs/PTFE(5.75 ± 0.10) × 10−23.3771(5.82 ± 0.12) × 10−23.4121

Share and Cite

MDPI and ACS Style

Zhang, Y.; Kou, K.; Ji, T.; Huang, Z.; Zhang, S.; Zhang, S.; Wu, G. Preparation of Ionic Liquid-Coated Graphene Nanosheets/PTFE Nanocomposite for Stretchable, Flexible Conductor via a Pre-Stretch Processing. Nanomaterials 2020, 10, 40. https://doi.org/10.3390/nano10010040

AMA Style

Zhang Y, Kou K, Ji T, Huang Z, Zhang S, Zhang S, Wu G. Preparation of Ionic Liquid-Coated Graphene Nanosheets/PTFE Nanocomposite for Stretchable, Flexible Conductor via a Pre-Stretch Processing. Nanomaterials. 2020; 10(1):40. https://doi.org/10.3390/nano10010040

Chicago/Turabian Style

Zhang, Yu, Kaichang Kou, Tiezheng Ji, Zhengyong Huang, Shuangcun Zhang, Shijie Zhang, and Guanglei Wu. 2020. "Preparation of Ionic Liquid-Coated Graphene Nanosheets/PTFE Nanocomposite for Stretchable, Flexible Conductor via a Pre-Stretch Processing" Nanomaterials 10, no. 1: 40. https://doi.org/10.3390/nano10010040

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.