Next Article in Journal
Effects of Driving Frequency and Voltage on the Performances of Vibrating Mesh Nebulizers
Previous Article in Journal
Thermodynamic and Quality Performance Studies for Drying Kiwi in Hybrid Hot Air-Infrared Drying with Ultrasound Pretreatment
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Applied Sciences
Volume 11
Issue 3
10.3390/app11031300
applsci-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Microstructure and Corrosion Performance of Aluminium Matrix Composites Reinforced with Refractory High-Entropy Alloy Particulates

by
Elias Ananiadis
1,
Konstantinos T. Argyris
1,
Theodore E. Matikas
1,*,
Athanasios K. Sfikas
2 and
Alexandros E. Karantzalis
1
1
Department of Materials Science and Engineering, University of Ioannina, 45110 Ioannina, Greece
2
Experimental Techniques Centre, Brunel University London, Uxbridge UB8 3PH, UK
*
Author to whom correspondence should be addressed.
Appl. Sci. 2021, 11(3), 1300; https://doi.org/10.3390/app11031300
Submission received: 8 January 2021 / Revised: 26 January 2021 / Accepted: 27 January 2021 / Published: 1 February 2021
(This article belongs to the Section Materials Science and Engineering)
Browse Figures
Versions Notes

Abstract

:
Novel aluminium matrix composites reinforced by MoTaNbVW refractory high-entropy alloy (HEA) particulates have been fabricated by powder metallurgy. The microstructure of the produced composites has been studied and the corrosion behaviour assessed in 3.5% NaCl solution. The composites exhibited low porosity, good homogeneity, few defects, and good distribution of the reinforcing phase in the Al matrix. No secondary intermetallic phases have been formed while the interface between matrix/reinforcement showed good bonding with no signs of reactivity. Increasing the volume of the reinforcing phase leads to increased hardness values. Al-HEA composites exhibited susceptibility to localised forms of corrosion in 3.5% NaCl solution. The microstructure has been analysed and corrosion mechanisms have been formulated.

1. Introduction

Metal matrix composites (MMCs) consist of a metallic matrix with a ceramic or a metallic reinforcement. MMCs exhibit improved properties such as high specific strength, high modulus, high hardness, and improved tribological properties. MMCs have been replacing monolithic alloys in various applications in aerospace, transportation, and other sectors [1,2,3,4,5]. A variety of MMCs has been developed with different matrices such as aluminium, copper, and stainless steel. Aluminium matrix composites (AMCs) reinforced with various particulates including Al2O3 [6,7,8,9], SiC [10,11,12,13], TiC [14,15,16], and B4C [17,18,19,20] have been studied.
Several studies on the electrochemical properties of AMCs reinforced with various ceramic reinforcements, including Al2O3/SiC [21], B4C [17], SiC [10,11], and AlN [22], indicate that the composites exhibit decreased corrosion resistance compared to the monolithic alloy. This is attributed to the breakdown of the continuous passive film on matrix–reinforcement interface [23], the formation of galvanic couples between Al and reinforcement [17,24], the formation of voids at matrix–reinforcements interfaces [25], interfacial layers around the reinforcement that may promote the galvanic effect [26], and increase in the dislocation density around particles clusters [27]. Another possible explanation for the decreased corrosion resistance of Al-based composites compared to the monolithic alloys is the pitting corrosion at the interfaces between the reinforcing particulates, secondary precipitates, and the reduction of oxygen on cathodic particles and precipitates [28]. On the other hand, several studies indicate that the introduction of the reinforcement in the Al matrix leads to improved corrosion performance [12,13,29,30]. Various interpretations may explain the improved corrosion performance, including the formation of reaction products that may act as barriers, interrupting the continuity of the matrix channels within the matrix [12], and matrix/reinforcement decoupling [29]. In other research efforts, AMCs exhibited comparable corrosion resistance with the monolithic alloy [14,15]. The effect of the reinforcement on the corrosion performance of AMCs may vary and depends on the environmental conditions and processing route [31]. Furthermore, other factors that may modify corrosion behaviour include primary interfacial reaction products between matrix/reinforcement [32], secondary precipitates in the as-cast states [33,34] and heat-treated states [34], aging kinetics [35], and electrolyte type [36].
High-entropy alloys (HEAs) have attracted a lot of attention. A high-entropy alloy contains at least five principal elements with concentrations of each element from 5 to 35 at.%, with exceptional physical and anti-corrosive properties deriving from four core effects: (a) high entropy, (b) sluggish diffusion, (c) severe lattice distortion, and (d) cocktail effect [37,38].
Due to their sluggish diffusion behaviour, less reactive nature, and attractive properties, HEAs are an outstanding choice for reinforcement in AMCs [39,40]. Various researchers studied these novel MMCs reinforced with HEA particulates using different types of matrixes, HEA reinforcement, and manufacturing routes [4,40,41,42,43,44,45,46]. Al-5083 matrix composites reinforced with CoCrFeNi and AlCoCrFeNi HEAs, have been fabricated by additive manufacturing and submerged friction stir processing, respectively [39,40]. The produced composites exhibited improved tensile properties, compressive strength, ultimate tensile strength, yield strength compared to the monolithic alloys. AlCoCrFeNi HEA, in equiatomic and non-equiatomic compositions, has been employed as the reinforcement in spark plasma sintered AMCs. The fabricated composites exhibited improved yield strength, high strength, increased fracture surface energy, but low plasticity [41,42]. Composites based on Al-7075 and commercially pure Al have been fabricated with the addition of AlCoCrFeNiTi HEA particulates (equiatomic and non-equiatomic). The produced composites manifested improved strength, plasticity, and extreme improvement in ultimate tensile strength compared to the monolithic alloys [43,44]. Al-based composites reinforced by various HEA particulates exhibited improved hardness, Young modulus, and strength compared to conventional Al alloys [4,45,46].
The aim of the current investigation is to evaluate the feasibility of fabricating novel AMCs reinforced by MoTaNbVW refractory HEA particulates via a powder metallurgy route. Furthermore, to study the microstructure and the corrosion behaviour of the composites in 3.5 wt.% NaCl solution. To the best of the authors’ knowledge, this is the first effort to fabricate and study Al-based composites with the employment of refractory HEA particulates. Furthermore, works on the corrosion behaviour of AMCs reinforced by HEA particulates are extremely limited [47]. It should be mentioned that this is a preliminary study and part of a larger effort to study different AMCs reinforced by various HEA particulates with different reinforcement volumes. The final goal is to develop AMCs with improved mechanical, corrosion, and tribological properties, while at the same time, maintain high ductility and keep production costs low.

2. Materials and Methods

2.1. Fabrication

MoTaNbVW reinforcement has been produced by vacuum arc melting. Details on the fabrication route and attained microstructures can be found elsewhere [48,49,50,51]. Afterwards, HEA samples were crushed into fine particles using a planetary mill (Fritsch Pulverisette 7 Premium Line, Idar-Oberstein, Germany). The samples were ground in a bowl with a capacity of 20 mL and 10 grinding balls with 10 mm diameter, the grinding time was 10 min at 850 rpm. The process took place in intervals of 20 s grinding and 80 s of pausing to prevent the samples from overheating. The achieved fineness of the HEA powder was approximately 40 μm. Commercial aluminium AA-1050 powder (purity 99.5%) was used as the matrix and the equiatomic refractory high entropy alloy MoTaNbVW as the reinforcement in order to produce composites of various compositions (0, 1, 3, and 5 vol% reinforcement). A powder metallurgy route was followed as the fabrication technique. For each configuration, the powder of Al and HEA were weighted and stirred into a beaker with methanol to avoid agglomeration and left to dry into a hot plate stirrer. The final powders for the monolithic alloy and Al-HEA composites were compacted into a cylindrical pellet of 14 mm in diameter using a hydraulic press at 7.6 tons of force. Each specimen had a weight of approximately 5 g. Due to the variation of volume and density of the reinforcement, the height of each pellet ranged from 12 mm for the monolithic alloy to 11.2 mm for the 5 vol% composition. Then, the pellets were carried into a steel die with a diameter of 15.3 mm (slightly bigger from the cold press specimens to avoid a breakdown during the insertion), covered with graphite powder for lubrication, and sintered into a hot press furnace (manufactured by Termolab, Agueda, Portugal). The final height for specimens ranged from 10.2 mm for the monolithic alloy to 9.2 mm for the 5 vol% composition. Sintering was executed in three steps. Initially, the temperature was increasing at a rate of 50 °C/min until it was stabilised at 550 °C under vacuum conditions. Afterwards, after 1 h, the loading process began gradually at a rate of 1000 N/min until the press obtained the desired load of 6500 Ν. The load was applied to the specimens for 30 min. Then, the specimens were left to cool in the furnace.
Afterwards, specimens have been subject to standards metallographic procedures for further analysis. More specifically, each specimen was cleaned after extraction from the die to remove impurities. The surface of the samples was ground with SiC sandpapers with final grit of 1200. Polishing was carried on with the use of a fine polishing cloth and diamond spray of 1 micron. After polishing, each specimen was rinsed with ethanol to remove contamination. The final outcome was a mirror-polished surface.

2.2. X-ray Diffraction and Hardness Testing

The phase identification of the composites was performed by a Bruker D-8 Advance Diffractometer (Bruker, Billerica, MA, USA), Cu K-alpha radiation. An Innovatest IN-700M (Innovatest, Europe BV, Maastricht, Netherlands) tester was employed to perform the hardness testing (average of five measurements per sample, two samples per configuration).

2.3. Scanning Electron Microscopy

The microstructure of the produced materials was studied with a Zeiss Supra 35VP (Carl Zeiss Microscopy, Jena, Germany) field emission gun scanning electron microscope and an LEO 1455VP (Carl Zeiss Microscopy, Jena, Germany) scanning electron microscope. Both were equipped with EDAX EDX detectors (Ametek, Berwyn, PA, USA). After potentiodynamic polarisation, the surface of Al and the composites were studied by scanning electron microscopy.

2.4. Corrosion Testing

Potentiodynamic polarisation testing was performed by a Gamry Reference 600 (Gamry Instruments, Warminster, PA, USA) potentiostat/galvanostat with the employment of a standard three-electrode cell (saturated calomel as the reference electrode (SCE) and a graphite gauge used as the counter electrode). Corrosion behaviour was studied in aerated 3.5% NaCl solution (pH 7). Open-circuit potential (Eocp) was determined after 1 h of immersion in the solution. The scan rate for the polarisation testing was 10 mV/ min. Four measurements were performed for each composition.

3. Results and Discussion

3.1. Microstructural Analysis-Hardness

Figure 1 presents a panoramic view of the HEA particulates after the milling process, through SEM examination. It also presents the mean actual composition of the powder particles in at.% after energy dispersive X-ray spectroscopy (EDS) analysis at various particle areas. It can be observed that most of the particles show an angular morphology. The first estimation of their size shows that it lays within the range of 1 μm to 30 μm.
Figure 2 presents the X-ray diffractograms for the different materials produced in the present effort. It can be seen that in all cases, two different phases can be distinguished- an FCC phase of the higher intensities that dominates, corresponding to Al, and a BCC phase of significantly lower peak intensities that corresponds to the HEA-reinforcing particles. These significantly lower peak intensities of the reinforcing phase particles are expected since their overall content is relatively small (up to 5 vol.%). MoTaNbVW produced in the form of bulk material consists of two BCC solid solutions- one rich in MoTaW and one rich in NbV. This is the result of a low-extend segregation of these two phases during the solidification process. It is well understood that the segregation of phases is inevitable, and it is acceptable as long as these phases are solid solutions rather than brittle intermetallic phases. It should be mentioned that MoTaNbVW was one of the pioneering refractory HEAs that has been developed and it meets the prerequisites of simple solid solutions formation. A thorough evaluation of the microstructure of MoTaNbVW can be found in previous efforts [50,51].
The particle distribution within the Al matrix for all the different composite systems is shown in Figure 3. As a first observation, it can be noticed that the actual particle content is in agreement with the nominal compositions: the higher the nominal composition, the more increased the actual reinforcing particle content. This observation refers to all the different particle sizes—as the particle content increases, the number of both the bulk and the sub-micron particles increases. As far as the particle distribution is concerned, it can be observed from Figure 3 that the distribution appears to be almost homogeneous for all the different particle sizes. Such a homogeneous distribution is expected since powder metallurgy processing route, due to the primary powder mixing process, ensures this type of microstructural homogeneity at the final sintered products. Another important observation that rises from Figure 3 is related to the quality of the actual sintering process. It can be noticed that in all cases there is no significant evidence of pores or other defects (flaws, micro-cracks, micro-voids) which implies that the sintering process was fully developed and concluded, leading to fully dense and rigid composite systems.
Figure 4 illustrates an EDS mapping on a selected region around a bulk reinforcing particle in order to reveal the elemental distribution. It can be observed that the reinforcing particle consists of the elements related to the refractory HEA system adopted in the present effort. Figure 4 also reveals useful information on the nature and integrity of the matrix–reinforcement interfacial area. Indeed, no signs of pores or interfacial detachment can be observed. Additionally, there is no significant evidence- at least at the observed magnification of severe reactivity between the Al matrix and the HEA system elements at the interfacial areas. This observation is very important because it indicates a lack of potential brittle intermetallic phase formation. The presence of intermetallic phases at the interfacial area would cause deteriorating effects on the properties of final composite systems [52]. EDX analysis revealed no significant traces of oxide phases (especially associated with Al). This may be attributed to the use of elemental Al powder that was protected in the supply container and used at the very last moment of the overall process. This handling reduced the exposure time to the atmosphere that could result in potential oxygen absorption. Furthermore, graphite powder was employed as a lubricant during the mechanical processing stage. The presence of graphite creates a reduction atmosphere at the following stage of hot pressing, ensuring intensive oxygen removal from the powders. The hot-pressing stage was performed under vacuum reducing further the potential for oxygen contamination.
Figure 5 presents the hardness measurements for the different systems produced in the present effort. The increase of the HEA particle content results in an increase of the overall composite hardness, indicating the reinforcing action of the hard and strong HEA phase. It should be noticed here that the selected HEA system possesses a hardness of 97 ± 4 HRB (Rockwell B) [50]. Another interesting observation is the consistency of the values and the deviation of hardness measurements. This may be explained by the good microstructural homogeneity and the good particle distribution of the reinforcement in the matrix.

3.2. Corrosion Performance

Figure 6 illustrates the potentiodynamic polarisation curves for monolithic Al and the produced composites in aerated 3.5% NaCl solution (pH 7). Polarisation curves for the composites with the lower HEA particulate content appear to be similar to the polarisation curve of Al. However, Al-5 vol% HEA exhibits somewhat different polarisation behaviour. More specifically, corrosion potential (Ecorr) appear to be slightly increased while the cathodic current densities correspond to higher values compared to Al and lower HEA containing composites. The increased cathodic current density values can be explained by the increased volume of the cathodic HEA particulates [15]. Nonetheless, the curves exhibit typical polarisation behaviour for Al and Al alloys in NaCl solutions; pitting potentials (Epit) are a few decades of mV higher than the corrosion potentials (Ecorr). The anodic part of the polarisation curves is divided into areas with a decreased rate of current density increase and areas with a sustained flat gradient; in the sustained flat gradient current density increases by several orders of magnitude, an indication of susceptibility to localised forms of corrosion [52,53,54]. It is thus concluded that the corrosion behaviour of the composites in 3.5% NaCl solution appears to be mainly controlled by the corrosion of matrix, in agreement with other studies [14,28].
Figure 7 presents the surface of the monolithic alloy and the composites under SEM after potentiodynamic polarisation in 3.5% NaCl solution. The surface appears to be degraded with the formation of pits. A most interesting observation is that Al on the matrix-reinforcement interface (Figure 7b–d) appears to be subject to preferential dissolution. This can be attributed to the high nobility of the reinforcing phase compared to the Al matrix. The galvanic effect between the matrix and the reinforcement can be further postulated by the presence of high amounts of oxygen on areas of the matrix close to the reinforcement (Figure 7e). It should be mentioned that the reinforcement appears to be free of any corrosion signs. The main corrosion mechanism of MoTaNbVW in 3.5% NaCl solution is uniform corrosion and intergranular corrosion of inter-dendrites at the dendritic/inter-dendritic boundaries due to the electrochemical potential difference between the dendrites (rich in Mo, Ta, W) and inter-dendrites (rich in Nb, V). Mo, W, and Nb are beneficial in decreasing the occurrence of pit corrosion in the MoTaNbVW system [55].
Corrosion behaviour of the composites appears to be the sum of counterbalancing mechanisms: HEA particulates may improve corrosion performance of the composites by stabilising the oxide film. Indeed, Wang et al. reported that the introduction of CuZrNiAlTiW HEA particulates in Al led to improved corrosion performance due to the stabilising effect of Ni and W in the transition layer [47]. In addition, the introduction of HEA particulates in Al leads to a decrease of the available Al area that may be subject to degradation. On the other hand, the introduction of HEA particulates might lead to the formation of discontinuities on the Al oxide film; the interface of Al/reinforcement may act as a corrosion initiation site. Increasing the volume of the reinforcement might lead to a more pronounced galvanic effect that may accelerate the dissolution of Al on the Al/ reinforcement interface. Another consideration is the galvanic effect between areas richer in HEA particulates and areas with a lower concentration of particulates. However, the intensity of the galvanic effect might be lessened by the good homogeneity/particle distribution and the lack of formation of secondary intermetallic phases or layers with different compositions. Other studies highlighted the importance of the high sintering quality and relative density on enhancing the corrosion resistance of AMCs reinforced by HEA particulates in a seawater solution [47].

4. Conclusions

  • Novel aluminium matrix composites reinforced by MoTaNbVW refractory high-entropy alloy particulates have been successfully produced by powder metallurgy.
  • The microstructure of the produced AMCs appears to be homogenous, with low porosity, few defects, and good distribution of the reinforcing phase in the Al matrix.
  • No secondary intermetallic phases have been formed while the interface between matrix and reinforcement showed good bonding without any signs of reactivity.
  • Increasing the volume of the reinforcing phase leads to increased hardness values.
  • Al-HEA composites exhibited typical polarization behaviour for Al and Al alloys in NaCl solutions. All examined materials were susceptible to localised forms of corrosion in 3.5% NaCl solution, while aluminium matrix on the reinforcement/matrix interface has been subject to selective dissolution. The corrosion behaviour of the produced composites appears to be mainly controlled by the corrosion of the matrix.

Author Contributions

Conceptualisation, E.A. and T.E.M.; methodology, E.A., T.E.M., A.K.S., and A.E.K.; software, E.A.; validation, E.A., T.E.M., and A.E.K.; formal analysis, E.A., K.T.A., and A.K.S.; investigation, E.A., K.T.A., and A.K.S.; resources, T.E.M.; data curation, E.A.; writing—original draft preparation, E.A., K.T.A., A.K.S., and A.E.K.; writing—review and editing, T.E.M. and A.E.K.; visualisation, E.A. and A.K.S.; supervision, T.E.M.; project administration, T.E.M.; funding acquisition, T.E.M. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this manuscript are available upon request.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Surappa, M.K. Aluminium matrix composites: Challenges and opportunities. Sadhana 2003, 28, 319–334. [Google Scholar] [CrossRef]
  2. Wlodarczyk-Fligier, A.; Dobrzanski, L.A.; Adamiak, M. Influence of heat treatment on properties and corrosion resistance of Al-composite. J. Achiev. Mater. Manuf. Eng. 2007, 21, 55–58. [Google Scholar]
  3. Mattern, A.; Huchler, B.; Staudenecker, D.; Oberacker, R.; Nagel, A.; Hofmann, M.J. Preparation of interpenetrating ceramic-metal composites. J. Eur. Ceram. Soc. 2004, 24, 3399–3408. [Google Scholar] [CrossRef]
  4. Prabakaran, R.K.; Sait, A.N.; Sentilkumar, V. Synthesis and Characteristization of High Entropy Alloy (CrMnFeNiCu) Reinforced AA6061 Aluminium Matrix Composite. J. Mech. Mechan. Eng. 2017, 21, 415–424. [Google Scholar]
  5. Miracle, D.B.; Donaldson, S.L. Handbook ASM; ASM International: Materials Park, OH, USA, 2001; pp. 27–34. [Google Scholar]
  6. El-Aziz, K.A.; Saber, D.; Sallam, H.E.-D.M. Wear and Corrosion Behavior of Al-Si Matrix Composite Reinforced with Alumina. J. Bio. Tribo. Corros. 2015, 1, 5. [Google Scholar] [CrossRef] [Green Version]
  7. Kang, Y.C.; Chan, S.L.I. Tensile properties of nanometric Al2O3 particulate-reinforced aluminum matrix composites. Mater. Chem. Phys. 2004, 85, 438–443. [Google Scholar] [CrossRef]
  8. Mazahery, A.; Ostadshabani, M. Investigation on mechanical properties of nano-Al2O3-reinforced aluminum matrix composites. J. Comp. Mat. 2011, 45, 2579–2586. [Google Scholar] [CrossRef]
  9. Hesabi, Z.R.; Simchi, A.; Reihani, S.M.S. Structural evolution during mechanical milling of nanometric and micrometric Al2O3 reinforced Al matrix composites. Mater. Sci. Eng. A 2006, 428, 159–168. [Google Scholar] [CrossRef]
  10. Gurrappa, I.; Bhanu Prasad, V.V. Corrosion characteristics of aluminium based metal matrix composites. Mater. Sci. Tech. 2006, 22, 115–122. [Google Scholar] [CrossRef]
  11. Cheng, Y.L.; Chen, Z.H.; Wu, H.L.; Wang, H.M. The Corrosion Behaviour of the Aluminum Alloy 7075/SiCp Metal Matrix Composite Prepared by Spray Deposition. Mater. Corros. 2007, 58, 280–284. [Google Scholar] [CrossRef]
  12. Candan, S.; Bilgic, E. Corrosion Behavior of Al-60 vol.% SiCp Composites in NaCl Solution. Mater. Lett. 2004, 58, 2787–2790. [Google Scholar] [CrossRef]
  13. Zakaria, H.M. Microstructural and corrosion behavior of Al/SiC metal matrix composites. Ain Shams Eng. J. 2014, 5, 831–838. [Google Scholar] [CrossRef]
  14. Lekatou, A.G.; Poulia, A.; Mavros, H.; Karantzalis, A.E. Thermal Treatment, Sliding Wear and Saline Corrosion of Al In Situ Reinforced with Mg2Si and Ex Situ Reinforced with TiC Particles. J. Mater. Eng. Perform. 2018, 27, 5030–5039. [Google Scholar] [CrossRef]
  15. Lekatou, A.; Karantzalis, A.E.; Evangelou, A.; Gousia, V.; Kaptay, G.; Gácsi, Z.; Baumli, P.; Simon, A. Aluminium reinforced by WC and TiC nanoparticles (ex-situ) and aluminide particles (in-situ): Microstructure, wear and corrosion behaviour. Mater. Des. 2015, 65, 1121–1135. [Google Scholar] [CrossRef]
  16. Dikici, B.; Bedir, F.; Gavgali, M. The effect of high TiC particle content on the tensile cracking and corrosion behavior of Al–5Cu matrix composites. J. Comp. Mater. 2020, 54, 1681–1690. [Google Scholar] [CrossRef]
  17. Han, Y.M.; Chen, X.G. Electrochemical Behavior of Al-B4C Metal Matrix Composites in NaCl Solution. Materials 2015, 32, 6455–6470. [Google Scholar] [CrossRef] [Green Version]
  18. Kalaiselvan, K.; Murugan, N.; Parameswaran, S. Production and characterization of AA6061–B4C stir cast composite. Mater. Des. 2011, 32, 4004–4009. [Google Scholar] [CrossRef]
  19. Topcu, I.; Gulsoy, H.O.; Kadioglu, N.; Gulluoglu, A.N. Processing and mechanical properties of B4C reinforced Al matrix composites. J. Alloy Compd. 2009, 482, 516–521. [Google Scholar] [CrossRef]
  20. Nie, C.; Gu, J.; Liu, J.; Zhang, D. nvestigation on microstructures and interface character of B4C particles reinforced 2024Al matrix composites fabricated by mechanical alloying. J. Alloy Compd. 2008, 454, 118–122. [Google Scholar] [CrossRef]
  21. Nunes, P.C.R.; Ramanathan, L.V. Corrosion Behavior of Alumina-Aluminum and Silicon Carbide-Aluminum Metal-Matrix Composites. Corrosion 1995, 51, 610–617. [Google Scholar] [CrossRef]
  22. Liu, Z.S.; Wu, B.T.; Gu, M.Y. Effect of AlN Particles on the Corrosion Behavior of Al/AlNp Composites. J. Mater. Sci. 2007, 42, 5736–5741. [Google Scholar] [CrossRef]
  23. Nath, D.; Namboodhiri, T.K.G. Some corrosion characteristics of aluminium-mica particulate composites. Corros. Sci. 1989, 23, 1215–1221, 1223–1229. [Google Scholar] [CrossRef]
  24. Hihara, L.H.; Latanision, R.M. Galvanic Corrosion of Aluminum-Matrix Composites. Corrosion 1992, 48, 546–552. [Google Scholar] [CrossRef]
  25. Trowsdale, A.G.; Noble, B.; Harris, S.J.; Gibbins, I.S.R.; Thompson, G.E.; Wood, G.C. The influence of silicon carbide reinforcement on the pitting behaviour of aluminium. Corros. Sci. 1996, 38, 177–191. [Google Scholar] [CrossRef]
  26. De Salazar, J.M.G.; Urena, A.; Manzanedo, S.; Barrena, M.I. Corrosion behaviour of AA6061 and AA7005 reinforced with Al2O3 particles in aerated 3.5% chloride solutions: Potentiodynamic measurements and microstructure evaluation. Corros. Sci. 1988, 41, 529–545. [Google Scholar] [CrossRef]
  27. Paciej, R.C.; Agarwala, V.S. Influence of Processing Variables on the Corrosion Susceptibility of Metal-Matrix Composites. Corrosion 1988, 44, 680–684. [Google Scholar] [CrossRef]
  28. Lekatou, A.G.; Gkikas, N.; Gousia, V.; Lentzaris, K.; Karantzalis, A.E. Effects of In Situ Intermetallics on the Microstructural Array and Saline Corrosion Performance of Cast Al/WCp Composites. J. Mater. Eng. Perform. 2018, 27, 5164–5176. [Google Scholar] [CrossRef]
  29. Ananda Murthy, H.C.; Bheema Raju, V.; Shivakumara, C. Effect of TiN Particulate Reinforcement on Corrosive Behaviour of Aluminium 6061 Composites in Chloride Medium. Bull. Mater. Sci. 2013, 36, 1057–1066. [Google Scholar] [CrossRef] [Green Version]
  30. Seah, K.H.W.; Krishna, M.; Vijayalakshmi, V.T.; Uchil, J. Corrosion Behaviour of Garnet Particulate Reinforced LM13 Al Alloy MMCs. Corros. Sci. 2002, 44, 917–925. [Google Scholar] [CrossRef]
  31. Griffiths, A.J.; Turnbull, A. An investigation of the electrochemical polarization behaviour of 6061 aluminum metal matrix composites. Corros. Sci. 1994, 34, 23–35. [Google Scholar] [CrossRef]
  32. Hu, J.; Chu, W.Y.; Fei, W.D.; Zhao, L.C. Effect of Interfacial Reaction on Corrosion Behavior of Alumina Borate Whisker Reinforced 6061Al Composite. Mater. Sci. Eng. A 2004, 374, 153–159. [Google Scholar] [CrossRef]
  33. Kiourtsidis, G.E.; Skolianos, S.M. Corrosion Behavior of Squeeze-Cast Silicon Carbide-2024 Composites in Aerated 3.5 wt.% Sodium Chloride. Mater. Sci. Eng. A 1998, 248, 165–172. [Google Scholar] [CrossRef]
  34. Albiter, A.; Contreras, A.; Salazar, M.; Gonzalez-Rodriguez, J.G. Corrosion Behaviour of Aluminium Metal Matrix Composites Reinforced with TiC Processed by Pressureless Melt Infiltration. App. Electr. 2006, 36, 303–308. [Google Scholar] [CrossRef]
  35. Kiourtsidis, G.E.; Skolianos, S.M. Pitting Corrosion of Artificially Aged T6 AA2024/SiCp Composites in 3.5 wt.% NaCl Aqueous Solution. Corros. Sci. 2007, 49, 2711–2725. [Google Scholar] [CrossRef]
  36. Alaneme, K.K.; Bodunrin, M.O. Corrosion Behavior of Alumina Reinforced Aluminum (6063) Metal Matrix Composites. J. Min. Mat. Char. Eng. 2011, 10, 1153–1165. [Google Scholar]
  37. Yeh, J.W.; Chen, S.K.; Lin, S.J.; Gan, T.S.; Chin, T.S.; Shun, T.T. Nanostructured high entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes. Adv. Eng. Mat. 2004, 6, 299–303. [Google Scholar] [CrossRef]
  38. Yeh, J. Recent progress in high-entropy alloys. Ann. Chim. Sci. Mat. 2006, 31, 633–648. [Google Scholar] [CrossRef]
  39. Karthik, G.M.; Panikar, S.; Janaki Ram, G.D.; Kottada, R.S. Additive manufacturing of an aluminum matrix composite reinforced with nanocrystalline high-entropy alloy particles. Mater. Sci. Eng. A 2017, 679, 193–203. [Google Scholar] [CrossRef]
  40. Yang, X.; Dong, P.; Yan, Z.; Cheng, B.; Zhai, X.; Chen, H.; Zhang, H.; Wang, W. AlCoCrFeNi high-entropy alloy particle reinforced 5083Al matrix composites with fine grain structure fabricated by submerged friction stir processing. J. Alloy. Compd. 2020, 836, 155411. [Google Scholar] [CrossRef]
  41. Liu, Y.; Chen, J.; Li, Z.; Wang, X.; Fan, X.; Liu, J. Formation of transition layer and its effect on mechanical properties of AlCoCrFeNi high-entropy alloy/Al composites. J. Alloy. Compd. 2019, 780, 558–564. [Google Scholar] [CrossRef]
  42. Tan, Z.; Wang, L.; Xue, Y.; Zhang, P.; Cao, T.; Cheng, X. High entropy alloy particle reinforced Al-based amorphous alloy composite with ultrahigh strength prepared by spark plasma sintering. Mater. Des. 2016, 109, 219–226. [Google Scholar] [CrossRef]
  43. Lu, T.; Scudino, S.; Chen, W.; Wang, P.; Li, D.; Mao, M.; Kang, L.; Liu, Y.; Fu, Z. The influence of nanocrystalline CoNiFeAl0.4Ti0.6Cr0.5 high-entropy alloy particles addition on microstructure and mechanical properties of SiCp/ 7075Al composites. Mater. Sci. Eng. A 2018, 726, 126–136. [Google Scholar] [CrossRef]
  44. Li, Q.; Bao, X.; Zhao, S.; Zhu, Y.; Lan, Y.; Feng, X.; Zhang, Q. The Influence of AlFeNiCrCoTi High-Entropy Alloy on Microstructure, Mechanical Properties and Tribological Behaviors of Aluminum Matrix Composites. Int. J. Met. 2020, 14, 1–11. [Google Scholar] [CrossRef]
  45. Kumar, K.P.; Krishna, G.M.; Rao, J.B.; Bhargava, N. Fabrication and characterization of 2024 aluminium—High entropy alloy composites. J. Alloy Comp. 2015, 640, 421–427. [Google Scholar] [CrossRef]
  46. Yuan, Z.; Tian, W.; Li, F.; Fu, Q.; Wang, X.; Qian, W.; An, W. Effect of heat treatment on the interface of high-entropy alloy particles reinforced aluminum matrix composites. J. Alloy. Comp. 2020, 822, 153658. [Google Scholar] [CrossRef]
  47. Wang, N.; Wu, B.; Wu, W.; Li, J.; Ge, C.; Dong, Y.; Zhang, L.; Wang, Y. Microstructure and properties of aluminium-high entropy alloy composites fabricated by mechanical alloying and spark plasma sintering. Mater. Today Commun. 2020, 25, 101366. [Google Scholar] [CrossRef]
  48. Senkov, O.N.; Wilks, G.B.; Miracle, D.B.; Chuang, C.P.; Liaw, P.K. Refractory high-entropy alloys. Intermetallics 2010, 18, 1758–1765. [Google Scholar] [CrossRef]
  49. Senkov, O.N.; Wilks, G.B.; Scott, J.M.; Miracle, D.B. Mechanical properties of Nb25Mo25Ta25W25 and V20Nb20Mo20Ta20W20 refractory high entropy alloys. Intermetallics 2011, 19, 698–706. [Google Scholar] [CrossRef]
  50. Poulia, A.; Georgatis, E.; Lekatou, A.; Karantzalis, A.E. Microstructure and wear behavior of a refractory high entropy alloy. Int. J. Refract. Met. Hard Mater. 2016, 57, 50–63. [Google Scholar] [CrossRef]
  51. Poulia, A.; Georgatis, E.; Lekatou, A.; Karantzalis, A.E. Dry sliding wear response of MoTaWNbV high entropy alloy. Adv. Eng. Mater. 2017, 19, 1600535. [Google Scholar] [CrossRef]
  52. Lekatou, A.; Sfikas, A.K.; Karantzalis, A.E.; Sioulas, D. Microstructure and corrosion performance of Al-32% Co alloys. Corros. Sci. 2012, 63, 193–209. [Google Scholar] [CrossRef]
  53. Lekatou, A.; Sfikas, A.K.; Petsa, C.; Karantzalis, A.E. Al-Co Alloys Prepared by Vacuum Arc Melting: Correlating Microstructure Evolution and Aqueous Corrosion Behavior with Co Content. Metals 2016, 6, 46. [Google Scholar] [CrossRef] [Green Version]
  54. Lekatou, A.; Sfikas, A.K.; Karantzalis, A.E. The influence of the fabrication route on the microstructure and surface degradation properties of Al reinforced by Al9Co2. Mater. Chem. Phys. 2017, 200, 33–49. [Google Scholar] [CrossRef]
  55. Poulia, A. Development and Characterization of Refractory High Entropy Alloys-Evaluation of Their Mechanical Properties and Surface Degradation Behavior. Ph.D. Thesis, University of Ioannina, Ioannina, Greece, 2018. [Google Scholar]
Applsci 11 01300 g001 550
Figure 1. Microstructure and composition (average of six different measurements) of MoTaNbVW powder under SEM (Secondary electron mode). (a,b) represent two different areas where point analysis has been performed in 6 points in total.
Figure 1. Microstructure and composition (average of six different measurements) of MoTaNbVW powder under SEM (Secondary electron mode). (a,b) represent two different areas where point analysis has been performed in 6 points in total.
Applsci 11 01300 g001
Applsci 11 01300 g002 550
Figure 2. X-ray diffractograms of Al-HEA composites.
Figure 2. X-ray diffractograms of Al-HEA composites.
Applsci 11 01300 g002
Applsci 11 01300 g003 550
Figure 3. Microstructure of the produced composites (Back scattered electron mode): (a) Al-1 vol% HEA, (b) Al-3 vol% HEA, and (c) Al-5 vol% HEA.
Figure 3. Microstructure of the produced composites (Back scattered electron mode): (a) Al-1 vol% HEA, (b) Al-3 vol% HEA, and (c) Al-5 vol% HEA.
Applsci 11 01300 g003
Applsci 11 01300 g004 550
Figure 4. Microstructure and elemental map of MoTaNbVW particulate in higher magnification (BE mode).
Figure 4. Microstructure and elemental map of MoTaNbVW particulate in higher magnification (BE mode).
Applsci 11 01300 g004
Applsci 11 01300 g005 550
Figure 5. Hardness values for monolithic Al and Al-HEA composites.
Figure 5. Hardness values for monolithic Al and Al-HEA composites.
Applsci 11 01300 g005
Applsci 11 01300 g006 550
Figure 6. Potentiodynamic polarisation curves for Al and Al-HEA composites in aerated 3.5% NaCl solution.
Figure 6. Potentiodynamic polarisation curves for Al and Al-HEA composites in aerated 3.5% NaCl solution.
Applsci 11 01300 g006
Applsci 11 01300 g007 550
Figure 7. Microstructure of the corroded surface (SE mode) after polarisation in aerated 3.5% NaCl solution: (a) Al, (b) Al-1 vol% HEA, (c) Al-3 vol% HEA, and (d,e) Al-5 vol% HEA with elemental map.
Figure 7. Microstructure of the corroded surface (SE mode) after polarisation in aerated 3.5% NaCl solution: (a) Al, (b) Al-1 vol% HEA, (c) Al-3 vol% HEA, and (d,e) Al-5 vol% HEA with elemental map.
Applsci 11 01300 g007
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Ananiadis, E.; Argyris, K.T.; Matikas, T.E.; Sfikas, A.K.; Karantzalis, A.E. Microstructure and Corrosion Performance of Aluminium Matrix Composites Reinforced with Refractory High-Entropy Alloy Particulates. Appl. Sci. 2021, 11, 1300. https://doi.org/10.3390/app11031300

AMA Style

Ananiadis E, Argyris KT, Matikas TE, Sfikas AK, Karantzalis AE. Microstructure and Corrosion Performance of Aluminium Matrix Composites Reinforced with Refractory High-Entropy Alloy Particulates. Applied Sciences. 2021; 11(3):1300. https://doi.org/10.3390/app11031300

Chicago/Turabian Style

Ananiadis, Elias, Konstantinos T. Argyris, Theodore E. Matikas, Athanasios K. Sfikas, and Alexandros E. Karantzalis. 2021. "Microstructure and Corrosion Performance of Aluminium Matrix Composites Reinforced with Refractory High-Entropy Alloy Particulates" Applied Sciences 11, no. 3: 1300. https://doi.org/10.3390/app11031300

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop