Abstract
Electroplated thin-walled tubes were tested in compression. Most cracks were found at defects, i. e. protrusions on the surface of the tubes. The study focusses on the characterization of these defects. Optical microscopy revealed that the defects were already present in the metallization layer and occurred during the metallization process. When electrodepositing a Nickel coating on top, grains grow perpendicular to the surface of the metallization layer creating local orientation changes. Thus, protrusions occur on the surface of the tube where imperfections are located in the metallization layer.
The results will be valuable for improving the deformation characteristics of the electrodeposited tubes; they can also be used to design new types of electrodeposits by patterning the substrate.
Kurzfassung
Dünnwandige galvanisierte Rohre wurden einer Druckprüfung unterzogen. Die meisten Risse konnten an Defekten bzw. an Protrusionen (Vorwölbungen) auf der Rohroberfläche ausgemacht werden. Die vorliegende Untersuchung konzentriert sich auf die Charakterisierung dieser Defekte. Bei der lichtmikroskopischen Untersuchung wurde ermittelt, dass die Fehler bereits in der Metallisierungsschicht vorhanden waren und während des Metallisierungsvorgangs auftraten. Wird eine Nickeldeckschicht elektrolytisch abgeschieden, wachsen Körner senkrecht zur Oberfläche der Metallisierungsschicht und rufen so lokale Orientierungsveränderungen hervor. Daher treten an Fehlerstellen der Metallisierungsschicht Protrusionen auf der Oberfläche des Rohrs auf.
Die Ergebnisse leisten einen Beitrag zur Verbesserung des Verformungsverhaltens der galvanisch beschichteten Rohre; sie können außerdem zur Entwicklung neuer Arten von galvanischen Überzügen durch Strukturierung des Substrats verwertet werden.
References / Literatur
[1] AshbyM.; ShercliffH.; CebonD.: Materials – engineering, science, processing and design, Butterworth-Heinemann, 2nd edition, 2010.Search in Google Scholar
[2] SuralvoM.; BouwhuisB.; McCreaJ.L.; Palumbo,G.; HibbardG.D.: Scripta Materialia58 (2008) 247–250. 10.1016/j.scriptamat.2007.10.018Search in Google Scholar
[3] GordonL.M.; BouwhuisB.A.; SuralvoM.; McCreaJ.L.; PalumboG.; HibbardG.D.: Acta Materialia57 (2009) 932–939. 10.1016/j.actamat.2008.10.038Search in Google Scholar
[4] BoonyongmaneeratY.; SchuhC.A.; DunandD.C.: Scripta Materialia59 (2008) 336–339. 10.1016/j.scriptamat.2008.03.035Search in Google Scholar
[5] BouwhuisB.; McCreaJ.L.; Palumbo,G.; Hibbard,G.D.: Acta Materialia57 (2009) 4046–4053. 10.1016/j.actamat.2009.04.053Search in Google Scholar
[6] El-SherikA.M.; ErbU.: Journal of Materials Science30 (1995) 5743–574910.1007/BF00356715Search in Google Scholar
[7] LianJ.; JangD.; ValdevitL.; SchaedlerT.A.; JacobsenA.J.; CarterW.B.; GreerJ.R.: Nano Lett. 2011, 11, 4118–4125. 10.1021/nl202475pSearch in Google Scholar
[8] ParkinsonR.: Nickel Development Institute (NiDI) Technical Series N° 10 084, 1998.Search in Google Scholar
[9] AlghamdiA.A.A.: Thin Walled Structures39 (2001) 189–213. 10.1016/S0263-8231(00)00048-3Search in Google Scholar
[10] MortazaviS.N.: MSc thesis, Chalmers University of Technology, 2013.Search in Google Scholar
[11] JungA.; DiebelsS.; Koblischka-VenevaA.; SchmauchJ.; BarnoushA.; KoblischkaM.R.: Advanced Engineering Materials2013, 10.1002/adem.201300187, 1–6.Search in Google Scholar
© 2013, Carl Hanser Verlag, München