Document Type : Original Research Paper

Authors

1 Research Laboratory of Real Samples Analysis, Faculty of Chemistry, Iran University of Science and Technology, Tehran, Iran

2 Electroanalytical Chemistry Research Centre, Iran University of Science and Technology, Tehran, Iran

3 Research Institute of Petroleum Industry, Tehran, Iran

Abstract


The magnetic mesoporous Fe3O4 and Fe3O4/Carbon Nanocomposite (Fe3O4/C) are synthesized by a facile hydrothermal method in one- step and are used for methylene blue dye removal. Nanomaterials are characterized by field-emission scanning electron microscope (FE-SEM), transition electron microscopy (TEM), energy dispersive X-ray spectrometry (EDX), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and Vibrating sample magnetometry (VSM). The specific surface area of the samples and mean pore diameter were measured via Brunauer–Emmett–Teller (BET) surface area measurement technique. To improve the adsorption performance some important parameters affecting dye removal are optimized. Maximum capacity for methylene blue (MB) adsorption on to Fe3O4 and Fe3O4/C Nanocompositeis 169.5 and 208.33 mg. g-1, respectively, which compared to some same recent reports, has a better adsorption capacity. Thermodynamic parameters (ΔGοΔΗο and ΔSο) were calculated and the result showed a spontaneous, endothermic and increase in randomness for dye adsorption. The obtained data has the best fitting with Langmuir isotherm and the kinetic analysis has the best fit by pseudo-second order model.

Keywords

INTRODUCTION

In recent years, the environmental crisis is a great challenge to human life. One of the examples is dyes that are one important and basic pollutants in water pollution. There are over 100,000 dyes as commercially in the world with more than 7×105 tons of dyestuff produced every year worldwide and used extensively in textile dyeing and printing industries. About 15% of the total dyes from various textile and other industries get discharged in wastewater causing extensive pollution [1-4]. The presence of low amounts of dyes in water (less than 1 mg. L-1 for some dyes) is highly visible and undesirable for humans, animals, and plants, that at long run lead to dangerous disease like genetic mutations and cancer in living organisms. One of the dyes is methylene blue, which is a heterocyclic aromatic compound and is used in the textile industry such as textile, paper, and leather [5-7].

The harmful of MB dye for humans can be noted as follows; if it can be leading to shortness of breath, produces a burning sensation, vomiting, and gastritis or a great amount of it causes chest pain, headache, sweating too much, painful micturition. And so, it causes heart rate, shock, cyanosis, and jaundice, in humans [8, 9]. Hence, the presence of MB in water is hazardous and its elimination from wastewaters is necessary.

There are various methods for dye removal from wastewaters, including adsorption, membrane filtration, electrochemical treatment, photocatalytic decomposition, advanced oxidation processes, coagulation, flocculation, treatment with ozone and chemical & biological process [10-12]. Among these methods, adsorption is the most effective technique, which some of its advantages are easy to use, low cost and often recoverable for further use[13, 14].

Magnetite (Fe3O4) and its composites have been widely synthesized and is a suitable case for removal of dye from waste, the advantage of this material are privileged magnetic properties, chemical stability, nontoxic synthesis, biocompatibility, economic, facile separation from the aqueous solution rather than others sorbents also helping to dye adsorption and increasing efficiently is other role of Fe3O4 nanoparticles [15, 16] . There are different methods for the synthesis of magnetic particles (Fe3O4) Such as co-precipitation[17, 18], mechanochemical [19], microwave [20], hydrothermal [21], ball mill [22] and combustion, with using a variety of precursors. For example, Cornelia Pa˘curariu and coworkers synthesized Fe3O4 nanoparticles (NPs )with combustion method and used for MB removal [23]. Also, magnetic separation of carbon nano-adsorbents has been reported recently and have been proven effective. For example, Datta et al used Fe3O4/ activated carbon (AC) for adsorption of nicotinic acid from aqueous [24]. Cazetta and coworkers used magnetic activated carbon (MAC) derived from biomass waste for toxic dye removal [25]. In another study, Kakavandi et al.synthesized Fe3O4/AC magnetic nanoparticles for the removal of aniline from aqueous solution [26]. Du et al. applied the carbon/Fe3O4 nanoparticle as an adsorbent for methyl orange removal [27].In another study Kong et al synthesized Fe3O4/C nanoparticles in two steps with glucose as a carbon source and used for organic dyes removal (MB, Cresol red and Congo red) from aqueous solution [28]. In another work, Luo et al. synthesized B-Fe3O4/C core-shell composites with a particles size of 500 nm, by usingof sodium gluconate as a shell of Fe3O4 for dye removal [29] and so phenol removal by MAC prepared through physicochemical activation [30]. Also, some papers reportadsorptive removal of malachite green and Rhodamine B dyes [31], Acid Yellow dye [32] and As(III) and As(V) [33] as a heterogeneous catalyst for Fenton oxidation of tetracycline [34] and other applications in supercapacitors [35-37].

Cellulose is a cheap material and so is abundant and available in nature. For this reason, in this study, it was used as a carbon source for the synthesis of the Fe3O4/C nanocomposite. In the present work, mesoporous Fe3O4/C and Fe3O4 nanomaterials were synthesized by facile and one-pot hydrothermal method. The proposed sorbent was used for dye removal from water solutions, which its adsorption capacity compared to same sorbents was considerably improved.

EXPERIMENTAL SECTION

Chemicals

Sodium metaperiodate, microcrystal cellulose (MCC) powder, LiCl, (FeCl3.6H2O), (FeCl2.4H2O), KCl, NaCl, Ca (NO3)2, Mg (NO3)2 and MB (Scheme 1) were purchasedfrom Merck. All chemicals were analytical grade and were used without any purifications, and all the aqueous solutions were prepared with deionized (DI) water.

Synthesis of Magnetic Nps

In brief, 1.44 g of FeCl3·6H2O and 0.69 g of FeCl2·4H2O (with 1:1.5 molar ratio) were simultaneously added in a deoxygenated 60 mL alkaline solution (0.2 M NaOH) with vigorous stirring under an Ar gas flow. Mix up the solution for a few minutes and then sealed by autoclave and placed in an oven at 160 °C for 10 h. The product was a black precipitate, then it is separated by a magnet and washed with DI water and ethanol, and was dried at 60 °C for 12 h in a vacuum oven.

Synthesis of 2, 3-Dialdehyde Cellulose

Oxidation of the cellulose (MCC) by a chemical reaction was conducted with the following instruction, 2 g of cellulose powder, 200 mL of deionized water, 1 g LiCl and 2 g sodium metaperiodate were added to a beaker respectively. The pH of the mixture was adjusted to acidic pH, and then placed in a dark (to avoid periodate decomposition) and closed vessel at 55 °C was stirred gently for 2-3 h. During this period cellulose is oxidized to 2,3-dialdehyde cellulose (2,3- DAC) (Fig. 1) and this product was filtered with a funnel and then washed with DI water to remove iodine-containing compounds and at the end dried in vacuum oven at 50 °C for 10 h. 2,3-DAC was used for the preparation of Fe3O/C.

Synthesis of Fe3O4/C Nanocomposite

0.5 g NaOH was dissolved in 60 mL DI water and 2, 3-DAC obtained from the previous step was stirred and dissolved in this solution to obtain a homogeneous solution. After this, for oxygen removal, Ar inert gas was purged in the solution, and then 0.15 g of FeCl2.4H2O and 0.28 g of FeCl3.6H2O were added to this solution and mixed for 1 h. Similar to the preparation of Fe3O4 NPs the mixture was heated in a Teflon-sealed autoclave in the same conditions preparation of Fe3O4.The magnetic materials were collectedby a magnet and washed for several times with DI water and ethanol. The final material was dried in an oven with vacuum conditions at 60 °C.

Apparatus

The synthesized materials were characterized by different techniques. Morphology of adsorbent was studied by the FE-SEM model of Hitachi S-4160 operating at 30 kV and TESCAN, Mira III LMU, Czech Republic at 15 KV and TEM images were taken with a model of Zeiss-EM10C (Germany) at 100 KV. FT-IR spectra were obtained by Shimadzu FTIR 8400S spectrometer (Japan). FE-SEM with energy dispersive X-ray spectroscopy (FESEM/EDX, TESCAN, Mira II LMU, Czech Republic) was used for the elemental analysis. XRD patterns were obtained in 2θ between 10 to 80° with a Philips-PW 1800 diffractometer, which was equipped with Cu-Kα irradiation (λ = 0.1524 nm) source. Specific surface area measurements were performed using a standard Brunauer–Emmett–Teller (BET) apparatus (ASAP 2020, micromeritics, USA). Adsorption was carried out at a liquid N2 temperature at 77 K. Magnetic properties was measured by vibrating sample magnetometry (VSM) analysis (Lakeshore 7410, USA). UV-Vis spectra were obtained with a Shimadzu UV-Visible spectrophotometer model UV-mini 1240 (Japan).

RESULTS AND DISCUSSION

Morphology of Nano Sorbent

The morphology of Fe3Oand Fe3O4/C nanomaterials was studied by FE-SEM. Fig. 2 (a-d) illustrates images of these particles with different magnifications. As this Figure shows the Fe3Oand Fe3O/C Nanocomposite are almost cubic and spherical. The TEM images (Fig. 2 (e, f)) obviously show the Fe3ONPs over carbon structure. With regard to these images, clearly seen that particles size is nanoscale especially in TEM images that size of magnetic nanoparticles is almost 10 nm.

Elemental Analysis

Elemental analysis of the nanomaterials was performed by EDX. Presence of iron, oxygen, and carbon can be observed clearly in the EDX spectrum (Fig. 3). It reveals thatthe iron is from magnetic Fe3O4, the carbon source is from 2,3-DAC and the source of oxygen is related to both samples (Fe3Oand 2, 3-DAC together).

FT-IR Studies

Fig. 4 shows the FT-IR spectra of Fe3O4, microcrystal cellulose (MCC) powder, 2, 3 -DAC and Fe3O4/C nanocomposite. The bands around 1054 cm-1 are related to the C–O stretching vibrations. A small peak near of 2930 cm-1 is observed, which illustrates the existence of C–H bonds. In 2,3-DAC the presence of C=O is indicated by the peak at 1737 cm-1 and so in 1640 cm-1 for Fe3O4/C Nanocomposite, and two small peaks about 2850-2950 cm-1 are attributed to C-H bonds connected to the carbonyl group.Characteristic bands of Fe–O at 590 cm-1 is observed in Fe3O4 and Fe3O4/C spectra (Fig. 4a, b). A broad peak almost in 3400 cm-1 in three samples are assigned to hydroxyl groups [38-40]. A little shift in the position of C=O, C-H and C-O peaks in Fe3O4/C sample compared to 2, 3-DAC sample is seen. This shift may be related to the link between C=O, C-H and C-O groups with a Fe3O4 structure that decreases the frequency and energy of functional groups bonds and according to the E=hcλ-1formula the wave number shifts to lower quantities.

XRD Patterns

Fig. 5 shows the XRD patterns of Fe3O4/C Nanocomposite and Fe3O4 NPs. The position of all diffraction peaks at 2θ = 75.09, 62.62, 57.02, 53.49, 43.12, 35.48, 30.12 and 18.31° corresponding to (6 2 2), (4 4 0), (5 1 1), (4 2 2), (4 0 0), (3 1 1), (2 0 0) and (1 1 1) of the crystal planes that was indexed to Fe3O4 (JCPDS card number 88-0866). The obvious peak between 2θ = 20 to 25° belongs to the carbon structure in Fe3O4/C sample.

Because in this study the magnetic crystallites are smaller than 100 nm, the Scherer equation (Eq. 1) can be used for determining and estimating the crystal size.

 (1)

Where t is the mean size of the ordered (crystalline) domains, which perhaps smaller or equal to the crystal size; is a shape factor and is a dimensionless quantity and its value is almost 0.9; l is the X-ray wavelength (here λ = 0.154056 nm); b is the line broadening at half the maximum intensity (FWHM), after the instrumental line broadening was subtracted, its unit must be in radians, and q is the Bragg angle in degree. The peak with more intensity (2θ = 35.48°) was selected for crystallite size measurements by Scherer equation, and the average particle size of Fe3O4 NPs and Fe3O4/C Nanocomposite were 11.9 and 12.9 nm, respectively.

VSM Study

Magnetic NPs was characterized by VSM for determination of magnetic property at room temperature (Fig. 6). The saturation magnetization for Fe3ONPs is found to be 39.88 emu. g-1 and for Fe3O4/C is about 14.15 emu. g-1. The obtained magnetic NPs has a good magnetic potential and could be separated easily from a water solution by a magnet.

N2 Adsorption/Desorption (BET)

The N2 adsorption-desorption isotherms curves of Fe3O4 NPs and Fe3O4/C Nanocomposite was measured at 77 K (Fig. 7a). It is observed that the decrease in the values of surface area for Fe3O4 NPs than Fe3O4/C Nanocomposite and so loop hysteresis is seen in curves, which indicates samples have mesoporous structure. The measured BET surface areas of the Fe3O4 NPs and Fe3O4/C Nanocomposite were 7.08 and 26.13 m2. g-1, respectively.

The pore size distributions obtained from the Barret–Joyner–Halenda (BJH) analysis (Fig. 7b) shows narrow and intensity peaks in the pore size distribution curve that appear in a range of 1 to 10 nm and so indicative a uniform distribution. The total pore volume of the Fe3O4 and Fe3O4/C are 0.013 and 0.023 cm3. g-1, respectively and the average of the pore size distribution for Fe3ONPs is 7.85 and for the Fe3O4/C Nanocomposite sample is 4.613 nm. The value of the pore diameter indicates that Fe3O4/C and Fe3O4 are mesoporous materials.

MB Dye Removal Studies

In this work, MB was specified by a UV-spectrophotometer at λmax = 664 nm. The removal percent and adsorption capacity qe (mg. g-1) were obtained by the following equations:

 (2)

 (3)

Where, qe is the adsorption capacity (mg. g-1), C(mg. L-1) and C0 (mg. L-1) is the equilibrium and initial concentrations of MB (mg. L-1), respectively, and m (g) is the adsorbent dosage.

For optimization of dye removal conditions, the effect of some important parameters was studied by one at a time method. In all experiments, during the adsorptionprocess, the mixture of adsorbent and dye solutions were shaken by 200 rpm speed.

Effect of adsorbent dosage

For investigating the effect of the required adsorbent amount, different amounts of Fe3O4/C nano-adsorbent in the range of 5 to 20 mg were added to 30 mL of 30 mg. L-1MB solutions. The results of these experiments are illustrated in Fig. 8. As this Figure shows by increasing the amount of adsorbent, the adsorption sites increase and consequently the dye removal percent and qe increase, and in amounts greater than 10 mg of adsorbent these values remain almost constant, which likely the saturation of the adsorbent activated sites. So, for the rest of the experiments, 10 mg of adsorbent was used for dye removal.

Effect of Initial Ph

One of the most influential factors on dye removal is the pH of the solution, which influences on the properties of adsorption and self-adsorption. In this experiment, whileC0 was kept at 30 mg. L-1, the pH was changed (2 - 12 (using 0.1 M NaOH and 0.1 M HCl solutions. Fig. 9. shows the change of qe and dye removal with pH increasing. As the Figure shows the best result is obtained at pH = 10. In alkaline solutions, the adsorbent has a negative charge and MB has a positive charge. Therefore, their attractive interaction is stronger. Very low adsorption capacity at acidic pHs implied that Fe3O4/C nano adsorbent could be renewable at low pH values.

Effect of Ionic Strength

Effect of ionic strength on pollution removal is an important parameter. Because dye wastewater contains various metal ions and salts and presence of this ions cause to increasing of ionic strength. In this study, the influence of four common metal ions (Na+, K+, Ca2+, Mg2+) with a concentration of 0.01 M in 30 mL dye solution with pH = 10 was investigated. Fig. 10. shows that salts and metal ions might be adsorbed on Fe3O4/C magnetic nano-adsorbent as a competitor, leading to decrease of adsorption capacity, which this decrease is more significant for ions with two positive charges (Ca2+ and Mg2+). According to the negative charge of adsorbent, the attraction of more positive charges to it is stronger. The interfering effect of Mg2+ can be eliminated by setting pH at higher amounts (pH > 10) because the magnesium ions precipitate at pH > 10.

Influence of Contact Time

The effect of contact time on the MB adsorption was tested to determine equilibrium time for the adsorption process. For this reason, 10 mg of adsorbent was added in 30 mL solution of 30 mg. L-1 MB and the solution was shacked with 200 rpm for various contact time (up to 300 min). Fig. 11 shows the result of this experiment. It is observed that with increasing contact time, adsorption of MB increases, but after time about 60 min qe and dye removal remain almost constant. So, this time was used as adsorptiontime for the rest of the experiments.

Effect of Temperature

Fig. 12 shows the effect of temperature on dye adsorption by two nano-adsorbents (Fe3O4 and Fe3O4/C). Experiments were carried out at different temperatures (25, 35, 45, 55, and 65 °C), all other parameters in the experiment were kept constant (dosage: 10 mg, dye concentration: 70 mg L-1 and pH=10). Results show that by increasing temperature the adsorption capacity of MB increases may be due to an acceleration in the mobility of the MB molecules and consequently enhancement of its interaction with the active sites of the nano-adsorbent surface.

Effect of Initial Dye Concentration

The effect of initial MB concentration on its removal by Fe3O4 and Fe3O4/C nano-adsorbent was investigated in the concentrations between 20 to 100 mg. L-1 (Fig. 13). The result shows that when the initial concentration of MB increases, dye removal percent decreases, which perhaps be due to the saturation of the adsorption sites on the adsorbent surface. On the other hand, with increasing dye concentration, adsorption capacity increases, because at higher concentrations the adsorption equilibrium (MB + Sorbent « MB-Sorbent) moves to the right. Fig. 14 shows a photograph of the dye adsorption by Fe3O4/C nano sorbent. In this experiment, the nanospheres were dispersed in the dye solution, and after some minutes MB was adsorbed and magnetic NPs were separated easily by an external magnet.

Adsorption Isotherm Study

Equilibrium adsorption in this research was done by 30 mL solutions containing dye with different initial concentrations (20 to 100 mg. L-1) with 10 mg of nano-adsorbentfor a period of 180 min.

Adsorption isotherm is one of the significant parameters in the adsorption process. In the present study, three available and major models (Langmuir, Freundlich, andTemkin) were studied to describe the adsorption equilibrium. Langmuir adsorption isotherm has the most application in adsorbing pollutants from the aqueous solutions. If experimental results fitted with Langmuir isotherm model it reveals that dye adsorption on the adsorbent has been done as a monolayer with uniform distribution on active sites of the outer surface of the adsorbent [41, 42] and there isn’t any interaction between the dye molecules. In this model, a linear relation is between 1/qe and 1/Ce as the following equation:

 (4)

Which Ce is the concentration of dye in equilibrium conditions (mg. L-1), qe is the adsorbed value of dye at equilibrium concentration (mg. g-1), qm is the maximum capacityas monolayer adsorption on adsorbent (mg. g-1), and b is the Langmuir constant that depends on the adsorption energy (L. mg-1).

RL is an important factor, specifies adsorption shape that defined in equation (5) with details (Table 1). In this formula, K(L. mg-1) and C(mg. L-1) are Langmuir isotherm constant and initial dye concentration, respectively.

Calculation of RL values on to Fe3O4/C Nanocomposite and Fe3O4 NPs show that 0 < RL > 1, so adsorption occurs normally and it is a favorable adsorption for two nano-adsorbent (Table 1) [43].

 (5)

Freundlich model is used to describe a heterogeneous adsorption process, and the amount of materials that are adsorbed is not limited to a monolayer adsorption, which describes the reversible adsorption process [44]. In the Freundlich model a linear relation is between ln qe and ln C(equation 6):

 (6)

In this equation, Kf and n are the Freundlich constants which are related to the system’s characteristics.

In Temkin model, it is assumed that the heat of adsorption increases linearly with coverage due to adsorbent–adsorbate interactions [45]. It is expressed linearly as equation (7):

 (7)

Where A is the equilibrium binding constant (L. mg-1) in accordance with the constant B (B = RT/b) and maximum binding energy is the Temkin isotherm energy that is related to the heat of adsorption. R is the gas constant (8.314 J. mol-1. K-1), T is the absolute temperature (K), and b is a constant (adsorption enthalpy). Fig. 15 shows the plots of three isotherms (Langmuir, Freundlich, and Temkin) for the MB adsorption on to nano-adsorbent and the related values of parameters and constants for these isotherms are presented in Table 2. As the results show, the obtained data better fitted to a Langmuir isotherm (for Fe3O4R2 = 0.9902 and Fe3O4/C, R2 = 0.9962) compared to the other isotherms (Freundlich and Temkin).

Thermodynamic and Mechanistic Studies

For the study of the nature and spontaneity of dye adsorption process, the thermodynamic parameters were investigated. they include energy change (ΔG°), enthalpy change (ΔH°), and entropy change (ΔS°) were mentioned in the following equations (8, 9, 10). The values of ΔH° and ΔS° were calculated from the slope and intercept of the plot ln Kdvs. 1/T.

 (8)

 (۹)

 (۱۰)

Where Kd is the equilibrium constant, R (8.314 J mol-1 K-1) is the universal gas constant, T (K) is the absolute temperature, qe (mg g-1) is the amount of adsorbate adsorbed atequilibrium and Ce (mg L-1) is the equilibrium concentration. The value of Gibbs free energy (ΔGο) was calculated by Eq. (10) [46]. The results of these calculations are presented in Table 3.

For two adsorbents negative values of ΔG° shows the dye adsorption is a spontaneous and feasibility processPositive values of ΔS° shows the increase in randomness at the solid–solution interface during the MB adsorption process. The values of enthalpy for dye adsorption (ΔH°) is positive that shows the endothermic nature of the adsorption process. This value for Fe3O4 and Fe3O4/C is 7.05 and 12.65 respectively, which are less than 40 kJ. mol-1 and indicates the adsorption of MB onto magnetic adsorbent is physisorption [47]. With regard to the functional groups in the nano-adsorbent (C-O, OH, C=O), and functional groups in MB (N-R, S-R), an attractive link by hydrogen bonding and Van der Waals interactions is possible, and with the presence of the positive charge on methylene blue there is also the possibility of creating an electrostatic bond.

Kinetic Studies

Adsorption kinetic models are used for determination of the mechanisms controlling the dyes adsorption from an aqueous solution. In this study, two kinetic models were adopted to match the obtained data from experimental. The first adopted method is a Lagergren pseudo-first-order [48]], which is used widely and explained by the following formula:

 (11)

In equation (11) qt is the adsorption capacity (mg. g-1) at time t and k1 is the rate constant for pseudo-first order model (min-1). Integrating this equation generates the equation (12), that k1 and qe are achieved by drawing the ln (qe – qt) vs. t

 (12)

The second model is a pseudo-second-order kinetic, presented as:

 (13)

Where, k2 is the rate constant of pseudo-second-order equation (g. mg-1. min-1) and for the other parameters, they have their usual meanings. In this model, it is assumed that the rate of concentration change moment over time is directly proportional to the difference in saturation concentration and moment saturation concentration [49, 50]. Assuming qt = 0 at t = 0 integration of the equation (14) gives the following equation:

 (14)

Fig. 16 shows the plots of pseudo-first and pseudo-second-order models, which as obvious the removal of MB by adsorbent follows a pseudo-second-order kinetic (R2 = 0.9998), and the related kinetic results are reported in Table 4.

Recycling of Adsorbent and Desorption of Dye

One advantage of the proposed nano-adsorbent is easy separation from soluble waste and reuse it by magnet without centrifugation or filtration. For this purpose, amount of 10 mg Fe3O4/C in 30 mL solution of dye with 30 mg. L-1 concentration was used for dye removal in optimum parameters. After the separation of Fe3O4/C nano-adsorbenteasily recoverable by washing with diluted HCl water solution. The relative adsorption capacity was calculated referring to the Fe3O4/C Nanocomposite without recycling. The result of this study is shown in Fig. 17. As illustrated in this Figure by recycling of Fe3O4/C as a magnetic nano sorbent from solution, adsorption capacity decreases. After the first use, the relative adsorbent capacity was 95.13%, and after 5 cycles this value decreased to 62.58%. Although by recycling the adsorption capacity decreases, but according to low-cost, nontoxic and ease of preparation, Fe3O4/C Nanocomposite could be a good adsorbent for dye removal.

Table 5 compares several recently reported magnetic adsorbents for MB removal, with the proposed adsorbent. As this table shows the proposed adsorbent has the betterqmax than most of these adsorbents.

CONCLUSIONS

In summary, mesoporous Fe3O4 and Fe3O4/C nanomaterials were synthesized by a hydrothermal method and characterized by various methods such as FT-IR, FE-SEM, TEM, VSM, XRD, EDX, and BET. These nanomaterials were used for removal of the MB cationic dye from water and showed a good adsorption capacity in alkaline pH. Thermodynamic parameters (ΔGο, ΔΗο, and ΔSο) were investigated that showed a spontaneous and endothermic adsorption process. The adsorption isotherm had the better fit with Langmuir isotherm, and the kinetic studies indicate that the adsorption of MB on the proposed adsorbent follows a pseudo-second-order kinetic model. Due to its low cost, ease of preparation and high adsorption capacity the proposed magnetic NPs can be considered as an excellent adsorbent for cationic dye removal.

ACKNOWLEDGMENTS

As authors of the article, we gratefully acknowledge the support of this report by the Research Council of Iran University of Science and Technology.

CONFLICTS OF INTEREST

The authors declare that there are no conflicts of interest.

 

4. Shojaei, S., et al., Removal of Reactive Red 198 by Nanoparticle Zero Valent Iron in the Presence of Hydrogen Peroxide. Journal of Water and Environmental Nanotechnology, 2017. 2(2): p. 129-135.
13. Mohammadi, A. and A. Aliakbarzadeh Karimi, Methylene Blue Removal Using Surface-Modified TiO2 Nanoparticles: A Comparative Study on Adsorption and Photocatalytic Degradation. Journal of Water and Environmental Nanotechnology, 2017. 2(2): p. 118-128.
17. Indira T, Lakshmi P. Magnetic nanoparticles–a review. International Journal of Pharmaceutical Sciences and Nanotechnology 2010; 3(3): 1035-42.