Bitte benutzen Sie diese Referenz, um auf diese Ressource zu verweisen: doi:10.22028/D291-24533
Titel: Colored coatings on eye glass lenses by noble metal colloids
VerfasserIn: Mennig, Martin
Endres, Klaus
Schmitt, Mike
Schmidt, Helmut K.
Sprache: Englisch
Erscheinungsjahr: 1997
Quelle: Journal of non-crystalline solids. - 218. 1997, S. 373-379
Kontrollierte Schlagwörter: Kolloides Metall
Glas
Absorption
Dielektrische Eigenschaft
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumenttyp: Journalartikel / Zeitschriftenartikel
Abstract: Metal colloids in glass coatings are suitable for preparation of colored transparent coatings with thicknesses of about 0.2 to 1 µm due to their high molar coefficient of absorbance (approximate to 10(6) 1/(mol cm)). The absorbance of these metallic particles in a dielectric environment is caused by a surface plasmon resonance effect of the conductive electrons of the colloids. Therefore, it is characteristic for the metal, but can be affected by the dielectric properties of the surrounding matrix. Glass sol-gel coatings have been developed for the preparation of 0.2 to 0.4 µm thick, transparent colored coatings on silicate eye glass lenses by incorporation of Au-, Ag- and Pd-colloids into an 87 mol% SiO2-13 mol% PbO glass. A functionalized silane has been used as a complex forming agent for the appropriate noble metal ions to control the nucleation and growth processes of the colloids during the thermal densification of the coatings. By mixing different noble metal salts and addition of Co2+ ions, pink, brown, green and grey colors with optical densities less than or equal to 6 have been obtained. By variation of the glass composition the refractive index of the coating can be adapted to that of different types of substrate glasses (n(D) from 1.52 to 1.6) to obtain coatings with desirable optical performance. In a similar manner the transformation temperature (T-g) of the coatings can be less than the substrate, allowing a complete thermal densification of the coatings at about 500 degrees C. The coatings show glass like chemical durability and mechanical stability. Due to the optical and thermomechanical properties of the colored coatings and due to the thermal and UV-stability of the colloids these coatings were applied to eye glass lenses.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-28430
hdl:20.500.11880/24589
http://dx.doi.org/10.22028/D291-24533
Datum des Eintrags: 30-Apr-2010
Fakultät: SE - Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Sammlung:INM
SciDok - Der Wissenschaftsserver der Universität des Saarlandes

Dateien zu diesem Datensatz:
Datei Beschreibung GrößeFormat 
sm199714.pdf1,46 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.