Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation. Final report, 20 October 1980-20 October 1981
A large three-zone cyrstallizer system was constructed and successfully operated for growing KH/sub 2/PO/sub 4/ single crystals. Under conditions of constant crystallization temperature and supersaturation, growth rates exceeding 5 mm per day were demonstrated for KH/sub 2/PO/sub 4/ crystals of 5 x 5 cm cross section. The optical quality of these crystals was equivalent to that of crystals grown at rates presently considered as state-of-the-art (approx. 1 mm/day). Sample crystals were supplied for comparison testing. The three-zone system appears to be ideally suitable for growth of large-diameter KH/sub 2/PO/sub 4/ crystals for the Laser Fusion Program.
- Research Organization:
- Philips Labs., Briarcliff Manor, NY (USA)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 6086745
- Report Number(s):
- UCRL-15341-81-4; ON: DE83013792
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation. Final report, October 20, 1980-October 20, 1981
Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation. Quarterly progress report, 20 October 1980-31 January 1981
Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation: Final report, 20 August 1982-30 May 1984
Technical Report
·
Mon Feb 01 00:00:00 EST 1982
·
OSTI ID:6086745
Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation. Quarterly progress report, 20 October 1980-31 January 1981
Technical Report
·
Thu Jan 01 00:00:00 EST 1981
·
OSTI ID:6086745
Growth of KH/sub 2/PO/sub 4/ crystals at constant temperature and supersaturation: Final report, 20 August 1982-30 May 1984
Technical Report
·
Thu Aug 01 00:00:00 EDT 1985
·
OSTI ID:6086745
Related Subjects
70 PLASMA PHYSICS AND FUSION TECHNOLOGY
36 MATERIALS SCIENCE
ACID PHOSPHATES
CRYSTAL GROWTH
LASER FUSION REACTORS
OPTICAL SYSTEMS
POTASSIUM COMPOUNDS
MONOCRYSTALS
NEODYMIUM LASERS
SOLUBILITY
ALKALI METAL COMPOUNDS
CRYSTALS
LASERS
OXYGEN COMPOUNDS
PHOSPHATES
PHOSPHORUS COMPOUNDS
SOLID STATE LASERS
THERMONUCLEAR REACTORS
700208* - Fusion Power Plant Technology- Inertial Confinement Technology
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication
36 MATERIALS SCIENCE
ACID PHOSPHATES
CRYSTAL GROWTH
LASER FUSION REACTORS
OPTICAL SYSTEMS
POTASSIUM COMPOUNDS
MONOCRYSTALS
NEODYMIUM LASERS
SOLUBILITY
ALKALI METAL COMPOUNDS
CRYSTALS
LASERS
OXYGEN COMPOUNDS
PHOSPHATES
PHOSPHORUS COMPOUNDS
SOLID STATE LASERS
THERMONUCLEAR REACTORS
700208* - Fusion Power Plant Technology- Inertial Confinement Technology
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication