Development of a thin steel strip casting process. Final report
This is a comprehensive effort to develop direct strip casting to the point where a pilot scale program for casting carbon steel strip could be initiated. All important aspects of the technology were being investigated, however the program was terminated early due to a change in the business strategy of the primary contractor, Armco Inc. (focus to be directed at specialty steels, not low carbon steel). At termination, the project was on target on all milestones and under budget. Major part was casting of strip at the experiment casting facility. A new caster, capable of producing direct cast strip of up to 12 in. wide in heats of 1000 and 3000 lb, was used. A total of 81 1000-1200 lb heats were cast as well as one test heat of 3000 lb. Most produced strip of from 0.016 to 0.085 in. thick. Process reliability was excellent for short casting times; quality was generally poor from modern hot strip mill standards, but the practices necessary for good surface quality were identified.
- Research Organization:
- Armco, Inc., Middletown, OH (United States). Research and Technology Div.
- Sponsoring Organization:
- USDOE Assistant Secretary for Energy Efficiency and Renewable Energy, Washington, DC (United States)
- DOE Contract Number:
- FC07-92ID13086
- OSTI ID:
- 467131
- Report Number(s):
- DOE/ID/13086-1; ON: DE97051973
- Resource Relation:
- Other Information: PBD: Apr 1994
- Country of Publication:
- United States
- Language:
- English
Similar Records
Strip casting with fluxing agent applied to casting roll
Strip casting with fluxing agent applied to casting roll