Abstract
The thermal and crystallization behaviour of polyphenylene sulfide (PPS) in its blends with high density polyethylene (HDPE) is reported. Three grades of HDPE ranging in MFI from 0.4 to 52 were used in the investigation. The effect of composition and molecular weight of HDPE on the crystallization process and morphology of PPS in the blends has been investigated by the technique of Differential Scanning Calorimetry (DSC).
In the blends, PPS crystallizes in presence of molten HDPE. It is observed that the morphology of PPS in terms of crystallite size and crystallite size distribution in the blends is significantly affected by blending with HDPE. The temperature onset of melting was found to increase with increasing HDPE content and the melting peak width was found to decrease with increasing HDPE content. This indicates a larger crystallite size and a narrower crystallite size distribution of PPS in blends. The effect is more pronounced in HDPE-rich compositions. The extent of the variation in the temperature onset of melting and peak width were comparable for all the grades of HDPE. The degree of crystallinity of PPS in the blends is reduced significantly (55–70%) in HDPE-rich blends. Therefore, it is concluded that the crystallization of PPS is affected by the presence of HDPE melt.
The crystallization scans of PPS in the blends, obtained in the cooling mode, did not show any evidence of accelerated nucleation. On the other hand, a marginal reduction in the temperature onset of crystallization was observed. The temperature range of crystallization of PPS in the blends was found to be less for all compositions except for 90/10 (PPS/HDPE). In summary it is concluded that blending of HDPE with PPS influences the crystal growth of PPS significantly although the effect on its homogeneous nucleation is also considerable. As a result, the morphology of PPS crystallized in blends is different from that of the homopolymer. The changes in the morphology of PPS are not sensitive to the molecular weight of HDPE probably because of the high temperature of PPS crystallization relative to the melting point of HDPE.
References
1 Utracki, L.A.: Poly. Eng. Sci. 22, p. 1166 (1982)10.1002/pen.760221717Search in Google Scholar
2 Escala, A., Stein, R.S., in: Advances in Chemistry. Cooper, S.L., Estes, G.M., (Eds.) Series No. 176, ACS Washington (1979)Search in Google Scholar
3 Siegmann, A.: J. App. Poly.Sci. 27, p. 1053 (1982)10.1002/app.1982.070270324Search in Google Scholar
4 Lovinger, A., Williams, M. L.:J. App. Poly. Sei. 25, p. 1703 (1980)10.1002/app.1980.070250817Search in Google Scholar
5 Bartczak, Z., Galeski, A., Pracella, M.: Polymer 27, p. 537 (1986)10.1016/0032-3861(86)90239-9Search in Google Scholar
6 Kojima, M., Satake, H.:J. Poly. Sei. (Phys.) 22, p. 285 (1984)10.1002/pol.1984.180220213Search in Google Scholar
7 Galeski, A., Pracella, M., Martuscelli, E.: J. Poly. Sci. (Phys.) 22, p. 739 (1984)10.1002/pol.1984.180220415Search in Google Scholar
8 Gupta, A.K., Gupta, V.B., Petters, R.H., Harland, W.G., Berri, J. P.: J. App. Poly. Sei. 27, p. 4669 (1982)10.1002/app.1982.070271214Search in Google Scholar
9 Norton, D. R., Keller, A.: J. Material Sci. 19, p. 447 (1984)10.1007/BF02403231Search in Google Scholar
10 Bartczak, Z., Galeski, A.: Polymer 27, p. 544 (1986)10.1016/0032-3861(86)90240-5Search in Google Scholar
11 Ghijsels, A., Groesbeek, N, Yip, C. W.: Polymer 23, p. 1913 (1982)10.1016/0032-3861(82)90217-8Search in Google Scholar
12 Aref-Azar, A., Hay, J.N., Marsden, B.J., Walker, N.: J. Poly. Sci. (Phys.) 18, p. 637 (1980)10.1002/pol.1980.180180321Search in Google Scholar
13 Barnum, R.S., Barlow, J. W., Paul, D.R.: J. App. Poly. Sci. 27, p. 4065 (1982)10.1002/app.1982.070271035Search in Google Scholar
14 Kocsis, Karger, J., Kallo, A., Szafner, A., Bodor, G., Senyei, Z.S.: Polymer, 20, p. 37 (1979)10.1016/0032-3861(79)90039-9Search in Google Scholar
15 Wang, T. T., Nishi, T ; Macromolecules, 10, p. 421 (1977)10.1021/ma60056a034Search in Google Scholar
16 Kalfoglou, N. K.: J. Poly. Sci. (Phys.), 20, p. 1259 (1982)10.1002/pol.1982.180200712Search in Google Scholar
17 Martuscelli, E., Pracella, M., Yue, W. P.: Polymer 25, p. 1097 (1984)10.1016/0032-3861(84)90346-XSearch in Google Scholar
18 Ong, C.J., Price, F.P:Y Poly. Sci. Poly. Sum. 63, p. 59 (1978)10.1002/polc.5070630109Search in Google Scholar
19 Jog, J. P, Nadkarni, V. M.:Y App. Poly. Sci. 30, p. 997 (1985)10.1002/app.1985.070300310Search in Google Scholar
20 Nadkarni, V.M., Jog, J.P.: J App. Poly. Sci. 32, p. 5817 (1986)10.1002/app.1986.070320714Search in Google Scholar
21 Shenoy, A. V., Chattopadhyay, S., Nadkarni, V.M.: Rheologica Acta, 22, p. 90 (1983)10.1007/BF01679833Search in Google Scholar
22 Nadkarni, V. M., Jog, J. P: Polymer Eng. Sei. 27, p. 457Search in Google Scholar
© 1987 Walter de Gruyter GmbH, Berlin/Boston, Germany