Sodium Hydroxide Activated Nanoporous Carbons Based on Lapsi Seed Stone
Nanoporous activated carbons (ACs) were prepared from Lapsi (Choerospondias axillaris) seed powder by chemical activation with sodium hydroxide (NaOH) at different NaOH impregnation ratios. The prepared ACs were characterized by Fourier transform-infrared (FTIR) spectroscopy,
Raman scattering, X-ray diffraction (XRD), and scanning electron microscopy (SEM). Semi-quantitative information on the surface properties was obtained by estimating iodine number. FTIR spectra showed the presence of oxygenated functional groups such as hydroxyl, carbonyl, and carboxyl in
the prepared ACs. Raman scattering showed clear D and G bands in the spectra. The intensity ratio of G and D band peak intensity was ca. 1.39 at lowest NaOH and Lapsi seed powder ratio 0.25:1 showing high graphitic degree. This ratio decreased with increase in the
NaOH impregnation ratio and reached minimum ca. 0.94 (comparable with commercial AC) at NaOH and Lapsi seed powder ratio 1:1 demonstrating that higher NaOH impregnation reduces the graphitic structure of the carbon. XRD patterns showed two broad peaks at diffraction angles of approximately
25 and 43 degrees indicating the amorphous structure. Surface properties of the ACs (BET surface area, pore volume, and pore size distributions) were evaluated by nitrogen adsorption–desorption isotherm. Our ACs showed strong methylene blue adsorption property (maximum methylene blue
is ca. 200 mg/g). Judging from the iodine number and methylene blue values, structure, and surface areas, it can be concluded that NaOH impregnation ratio is one of the key parameters to tune the surface properties of Lapsi seed stone-based activated carbons.
Document Type: Research Article
Publication date: 01 February 2015
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content