Interface Analysis of Embedded Chip Resistor Device Package and Its Effect on Drop Shock Reliability
In this study, the drop reliability of an embedded passive package is investigated under JESD22-B111 condition. Chip resistors were buried in a PCB board, and it was electrically interconnected by electroless and electrolytic copper plating on a tin pad of a chip resistor without intermetallic
phase. However tin, nickel, and copper formed a complex intermetallic phase, such as (Cu, Ni)6Sn5, (Cu, Ni)3Sn, and (Ni, Cu)3Sn2, at the via interface and via wall after reflow and aging. Since the amount of the tin layer was small compared
with the solder joint, excessive intermetallic layer growth was not observed during thermal aging. Drop failures are always initiated at the IMC interface, and as aging time increases Cu–Sn–Ni IMC phases are transformed continuously due to Cu diffusion. We studied the intermetallic
formation of the Cu via interface and simulated the stress distribution of drop shock by using material properties and board structure of embedded passive boards. The drop simulation was conducted according to the JEDEC standard. It was revealed that the crack starting point related to failure
fracture changed due to intermetallic phase transformation along the via interface, and the position where failure occurs experimentally agrees well with our simulation results.
Document Type: Research Article
Publication date: 01 April 2012
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content