Abstract

LUFFACHITIN obtained from the residue of the sponge-like dried fruit of Luffa aegyptiaca was developed as a weavable skin substitute in this study. A chemical analysis revealed that LUFFACHITIN was composed of a copolymer containing N-acetyl-glucosamine (~40%) as a major monomer with a filamentary structure as demonstrated by both optical and scanning electron microscopy. The pulp-like white residue of the sponge-like dried fruit of Luffa aegyptiaca after treatment was then woven into a thin, porous membrane by filtration and lyophilization as a skin substitute for conducting wound-healing study on rats. The results indicated that the LUFFACHITIN membrane showed significant wound-healing enhancement (25 days to complete healing) compared to cotton gauze (>30 days), but not inferior to that of SACCHACHITIN. Furthermore, the LUFFACHITIN membrane had advantages of having a high yield, better physical properties for fabrication, and a more attractive appearance.

1. Introduction

In an endeavor to develop ideal skin substitutes, the performance of SACCHACHITIN membranes, prepared from the residue of the fruiting body of the medicinal fungus, Ganoderma tsugae, as an effective skin prosthesis was examined [1]. The effectiveness of the SACCHACHITIN membrane in managing excised wounds in guinea pigs was demonstrated to be better than that of gauze and comparable to that of Beschitin, which is mainly composed of chitin from crabs. The SACCHACHITIN membrane is able to promote wound healing by inducing cell proliferation. A mildly acute inflammatory reaction attracted a large number of polymorphonuclear leukocytes and some macrophages to clean away debris and blood clots [2]. Also the secretion of cell cytokines and growth factors by these cells provided an excellent environment for wound healing [3, 4]. The migration of fibroblast cells, which was promoted by SACCHACHITIN, also plays another important role in accelerating wound healing [1]. Furthermore, the fibrous structure of SACCHACHITIN made it convenient to produce a skin substitute with desirable pore characteristics.

Luffa is a genus of tropical and subtropical vines classified in the cucumber (Cucurbitaceae) family. In everyday nontechnical usage, the name, also spelled loofah, usually refers to the fruit of the two species, L. aegyptiaca/cylindrical (Smooth Luffa, its fruit somewhat resembles a cucumber) and L. acutangula (Angled Luffa, its fruit slightly resembles a cucumber or zucchini with ridges). The fruits of these species are cultivated and eaten as a vegetable. When the fruit is fully ripened, it is very fibrous. The fully developed fruit is the source of the loofah scrubbing sponge which is used in bathrooms and kitchens as a sponge tool. Luffa has fruits possessing a net-like fibrous vascular system (Luffa sponges) consisting of cellulose and lignin (1.4% and 2.9%, respectively, of the sponge dry weight) [5]. The struts of this natural sponge are characterized by a microcellular architecture with continuous hollow microchannels (with diameters of 10~20 μm) which form vascular bundles and yield a multimodal hierarchical pore structure. To the present, Luffa sponges have been applied to immobilize biocatalysts such as enzymes, microorganisms, organelles, and plant and animal cells in bioreactors [615], scaffolds for tissue engineering [16, 17], and dye absorbents from aqueous solutions [1820] and for developing biofiber-reinforced bionanocomposites [2123].

The sponge vegetable from L. aegyptiaca is the dried fruit fiber of the sponge cucumber or sponge gourd, which is a commonly eaten vegetable in Taiwan. Similarly, the sponge-like structure of dried fruit fibers makes it suitable for cleaning the body and dishes. These dried fibers are tenacious and can be cooked for a long time with no sign of dissolution, which is similar to the characteristics of SACCHACHITIN. It was suspected that the main component in these fibers was chitin just as in SACCHACHITIN. The potential of this fibrous material for applications as a skin substitute encouraged us to conduct this study.

2. Materials and Methods

2.1. Materials

Dried fruit fibers of L. aegyptiaca were purchased from a local market in Taipei, Taiwan. N-acetylglucosamine, glucosamine, and ketamine were supplied by Sigma (St. Louis, MO, USA). Glucose and galactose were obtained from Nihon Shiyaku Industrial (Taipei, Taiwan). Trifluoroacetic acid and pyridine were provided by Riedel-de Haën (Seelze, Germany). n-Butanol was from Hayashi Pure Chemical (Osaka, Japan). Thin-layer chromatography (TLC) plates (Kieselgel 5554) and the solvents for high-performance liquid chromatography (HPLC) and analytical-grade reagents were obtained from Merck (Hohenbrunn, Germany). Pentobarbital was supplied by Siegfried AG (Zofingen, Switzerland).

2.2. Preparation of Luffa Membranes

The dried fruit fibers were pulverized and autoclaved for 20 min to soften the fibrous structure and then were blended to make a paste. The paste was then digested with 1 N NaOH at 85°C for 4 h. The residue was collected and washed with deionized water to remove any residual NaOH. Hypochlorite at 0.1% was then used to depigment the fibers. After removal of any residual hypochlorite by repeated washing with deionized water, the fibers of lengths ranging 10~50 μm were collected and dispersed in deionized water to form a suspension. The suspension was filtered using filter paper under aseptic conditions. The membrane formed on the filter paper was then freeze-dried (EYELA, model FD-5N, Japan) to obtain the final product for further analysis and animal tests. The membrane so obtained was called “LUFFACHITIN.”

2.3. Chemical Analysis of Membrane Components
2.3.1. Sugar Components [24]

Two grams of the LUFFACHITIN membrane was first pulverized, and then 5 mg of this powder, selected randomly, was digested with 0.25 mL of either 2 N HCl (HC-) or CF3COOH (HF-) at 100°C for 5 (HC-5; HF-5), 10 (HC-10; HF-10), and 15 h (HC-15; HF-15) in a sealed ampoule. After hydrolysis, each 250 μL of distilled water and pyridine was added to each ampoule and mixed thoroughly. The hydrolyte residue of this mixture was divided into two portions and separately analyzed by TLC for aldose/ketose and amino sugar using glucose (galactose) and N-acetylglucosamine (glucosamine), respectively, as reference standards. The developing agent used in the TLC analysis was pyridine : n-butanol : 0.1 N HCl at 30 : 50 : 20, and the respective visualizing agents were naphthoresorcinol for aldose (purple)/ketose (red or pink) and the Elson-Morgan solution for amino sugar.

HPLC was also used to determine the kind of monosaccharides (glucose, galactose, mannose, glucosamine, and N-acetylglucosamine) in the hydrolyte of the LUFFACHITIN membrane. The HPLC system consisted of a pump (Shimadzu LC-10AT, Tokyo, Japan), a manual injector (Rheodyne, Tokyo, Japan), and a column (CHO-620,  mm, 5 μm, Merck) operated at 63°C. The mobile phase consisted of only deionized water at a flow rate of 0.5 mL/min. The eluent was detected with an RI detector (Shimadzu, RID-10A, Tokyo, Japan).

2.4. Sugar Skeleton Analysis

The sugar skeleton of LUFFACHITIN was determined by a gas chromatography/mass spectroscopic (GC/MS) method (Hewlett Packard 5890 plus series II and Hewlett Packard, mass spectrometer 5989B). After methylation, hydrolysis, reduction, and acetylation, the pattern of fragmentation of the mass spectrum of the final product was compared to reference standards for elucidation of the sugar skeleton. GC was equipped with a capillary column (with a length of 50 m and an inner diameter of 0.25 mm) packed with dimethyl siloxane. The temperature of the injector port was 250°C, and heating was programmed from 150 to 240°C at a rate of 2°C/min. Helium was the carrier gas delivered at 1.8 mL/min with a split ratio giving a flow rate of 1.53 mL/min and maintaining a constant pressure of 1.8 kg/cm2. Glucose, galactose, mannose, glucosamine, and N-acetylglucosamine were used as reference standards in both the TLC and GC analyses.

2.5. Scanning Electronic Microscopic (SEM) Examinations

Dried samples were loaded onto aluminum studs and coated with gold for 3 min at 8 mA under a pressure of 0.1 torr. Samples were scanned and examined using a Hitachi model S-2400 SEM.

2.6. Wound-Healing Studies

This animal experiment was approved by the Institutional Animal Care and Use Committee of Taipei Medical University (approval number LAC-100-0101). Prior to the study, rats were anesthetized with separate intraperitoneal (i.p.) injections of ketamine (35 mg/kg) and pentobarbital (12 mg/kg). The dorsal hair of the rats was removed with an electric razor. Equal areas of two parts in a mirror image were marked along the spinal cord, 4.5 cm behind the ear of the rats and 1 cm away from the spinal cord, and two pieces of full-thickness skin, each with a surface area of about 4.0 cm2, were excised. The lesion on the left-hand side was covered with an equal size of SACCHACHITIN or cotton gauze for comparison. The right-hand side was covered with the LUFFACHITIN membrane prepared above. Treated rats were placed in individual cages with an air-filtering device at 30°C and 55±% humidity, where they had free access to food and water. After surgery, changes in the area of the wounds were measured on days 4, 7, 11, 14, 18, 21, and 25, after which fresh dressings were applied. A digital camera was used to document the lesion, and Image-Pro Plus was used to calculate the wound area on the image of the lesion so obtained. Five male rats for each group were included in two comparative studies, and results are reported as the mean with the standard deviation (SD). Student’s -test was performed using the SPSS statistic software (PASW Statistics 18.0). Difference was considered significant when the value was less than 0.05.

3. Results

Figure 1 shows the appearance of LUFFACHITIN (Figure 1(a1), from L. aegyptiaca) developed in different stages of treatment compared to that of SACCHACHITIN (Figure 1(b1), from the fruiting body of Ganoderma). Dried fruit fibers of L. aegyptiaca appeared fiber-like with a light-yellow color as shown in Figures 1(a2) and 1(a3), whereas the fruiting body of Ganoderma was a reddish-brown color with a less-fibrous form and a more-tendon-like structure demonstrated by Figures 1(b2) and 1(b3). Microscopic examination of the LUFFACHITIN membrane (Figure 1(a4)) clearly showed that the light-yellow fibers of L. aegyptiaca were transformed into soft, transparent fibers that formed a porous structure, while SACCHACHITIN fibers appeared to be opaque that formed a porous structure as well (Figure 1(b4)).

The TLC analysis of the acid-treated hydrolyte of LUFFACHITIN membrane is shown in Figure 2. With hydrolysis at the same concentration and time interval, a spot visualized by naphthoresorcinol to be purple appeared in all hydrolytes except that reacting with HCl for only 5 h (HCl-5, Figure 2(a)) as shown in Figure 2(a). Since a purple spot was visualized after treatment with naphthoresorcinol and appeared at similar retention time with glucose/galactose standard in TLC plate, it was concluded that aldose of glucose/galactose is one of the major sugar components of LUFFACHITIN. Figure 2(b) reveals the presence of N-acetylglucosamine in all acid-treated hydrolytes of the LUFFACHITIN membrane, which was confirmed by referring to the N-acetylglucosamine standard with visualization of a purple-violet color. Another purple spot corresponding to the glucosamine standard only appeared in hydrolytes treated with a stronger acid for the longest time interval (CF-15, lane 8, Figure 2(b)). It was concluded that amino sugar of N-acetylglucosamine is another major sugar component of LUFFACHITIN.

Figures 3(a)3(e) illustrated the results of HPLC analysis for monosaccharide standards of glucose, galactose, mannose, glucosamine, and N-acetylglucosamine, respectively, and Figure 3(f) revealed that for acidic hydrolytes of LUFFACHITIN as exemplified by HF-15, which was hydrolyzed in CF3COOH for 15 h. In comparison with aldose standards, it is obvious that the major broad peak in HPLC graph of HF-15 at a retention time around 5.5 min corresponds with the mixture of aldoses, including glucose (5.697 min), galactose (5.287 min), and mannose (5.653 min). This result conforms to that of TLC as deduced above. Another major peak in HPLC graph of HF-15 appears at a retention time similar to that of N-acetylglucosamine standard (Figure 3(e)) but not glucosamine (Figure 3(d)). This result is also consistent with that revealed by TLC analysis. Since a complete acidic hydrolysis of LUFFACHITIN in CF3COOH for 15 h was expectable, the area under the peak corresponding to N-acetylglucosamine would be the highest amount of N-acetylglucosamine released by acidic treatment of LUFFACHITIN. The area under this peak was calculated to be ~40% of total peak area in HPLC graph, which means that LUFFACHITIN is composed of ~40% N-acetylglucosamine and the rest of 60% is glucose (or a mixture of aldoses).

Figure 4 shows a GC graph (Figure 4(a)) of the final products of LUFFACHITIN after methylation, hydrolysis, reduction, and acetylation treatments with corresponding mass spectra for elution peaks at 4.64 (Figure 4(c)), 5.95 (Figure 4(d)), 6.66 (Figure 4(e)), and 6.95 (Figure 4(f)) min. Figure 4(b) reveals that the characteristic fragments for N-acetylglucosamine in the structure of poly[-1,4-N-acetyl-D-glucosamine] included 45, 71, 73, and 189 m/z. The mass spectrum of the elution peak at 6.66 min demonstrated those characteristic fragments, further confirming poly[-1,4-N-acetyl-D-glucosamine] to be part of the structural unit of LUFFACHITIN. Following the same principle as elucidated by the fragmentation of poly[-1,4-N-acetyl-D-glucosamine], characteristic fragments for poly--1,4-glucose and poly--1,3-glucose (-1,3-glucan) were 45, 117, 161, and 205 m/z and 45, 117, 161, and 233 m/z, respectively. All those characteristic fragments except 205 m/z for poly--1,4-glucose and 233 m/z for poly--1,3-glucose appeared in the mass spectra for elution peaks at 4.64, 5.95, and 6.95 min. It seems to indicate that besides the most abundant structural units of poly--1,4-glucose in nature being a part of structural unit of LUFFACHITIN, poly--1,3-glucose backbone could not be excluded.

The wound-healing process for the wound covered by the LUFFACHITIN membrane was compared to both cotton gauze and SACCHACHITIN. Photographic results are shown in the upper panel of Figures 5 and 6. The wound area contraction plotted versus time was shown in the bottom panels of Figures 5 and 6, respectively, to compare the progress of wound healing using these different skin substitutes or wound dressings. In comparison to the control covered with cotton gauze, quite significant improvement in the wound-healing process with the LUFFACHITIN membrane was observed by the change in the wound area. The difference between the LUFFACHITIN and SACCHACHITIN membranes was observed to be minimal. The wound lesion of 4.0-cm2 had completely healed after covering with either substance for 25 days. Skin tissue with normal function recovered, and dorsal hairs also regrew in the healed wound area.

4. Discussion

During treatment, it was found that a longer time in harsher conditions was taken to soften and depigment the SACCHACHITIN preparation than the LUFFACHITIN preparation. Because of that, the total recovery for LUFFACHITIN was about 70%, whereas it was only about 20% for SACCHACHITIN. To be effective as a skin substitute or dressing to treat wounds like with SACCHACHITIN, the porous structures that appeared in the LUFFACHITIN membrane were recognized as an important characteristic. Microscopic examination clearly showed that the LUFFACHITIN membrane is composed of soft and transparent fibers that formed a porous structure. The pore size of these membranes could be optimally controllable by adjusting the fiber concentration of the filtrate during preparation of the membrane. Furthermore, the LUFFACHITIN membrane was softer like facial tissues with better water-absorption ability than the SACCHACHITIN membrane (personal observation). The softness allowed the membrane to easily attach to the skin contour, and the better ability to absorb water led to the efficient expulsion of exudates. It would be expectable to have a minimal injury to skin surface where it attached to and enhance the skin recovery.

It was confirmed that the main constituents of LUFFACHITIN are aldose of glucose/galactose and amino sugar of N-acetylglucosamine by TLC and HPLC. The acetylation products of the hydrolyte determined by GC analysis (data not shown) were also demonstrated to be these two ingredients (glucose and N-acetylglucosamine). In comparison with a calibration standard curve, the ratio of these two components was found to be 60.15 to 39.85. The TLC diagram was also used to validate that the sugar components are released by digestion with various enzymes (data not shown). It demonstrates that only -glucosidase and chitinase are able to hydrolyze LUFFACHITIN and the resulting sugar components were determined to be glucose and N-acetylglucosamine. Measurement of the protein content of LUFFACHITIN produced no color reaction implying that LUFFACHITIN contains virtually no protein. The total nitrogen content was determined to be 3.46%, which was equivalent to the total nitrogen content of N-acetylglucosamine, further confirming that sponge gourd from Luffa aegyptiaca is composed mainly of the -form of glucan and poly-N-acetylglucosamine.

Regarding the wound-healing improvement, quite significant improvement with the LUFFACHITIN membrane was observed in comparison to the control covered with cotton gauze. The difference between the LUFFACHITIN and SACCHACHITIN membranes was observed to be minimal. Overall, the LUFFACHITIN membrane could be utilized as a wound dressing or skin substitute with an efficacy comparable to that of SACCHACHITIN but better than gauge. As reposted, the chitin (polymeric N-acetyl-glucosamine) was demonstrated to play an important role for chitin-containing materials in the wound-healing process [2527]. Previously, the proliferation of human F1000 fibroblasts was also found to correlate with the chitin content of various fungal cultures [28]. As revealed above, N-acetylglucosamine is one of the two main components of the LUFFACHITIN membrane. Therefore, the comparable efficacy of the LUFFACHITIN membrane with respect to SACCHACHITIN in the wound-healing process can partly be attributed to N-acetylglucosamine, a major monomer in the structure of chitin. In addition, the immunological effects and influence of -1,3-glucan on wound healing are elucidated in greater detail elsewhere [2931]. The potential possibility of a 1,3-linkage for polysaccharides obtained from L. aegyptiaca is illustrated although the linkage of the glucose unit has not been confirmed. Since being another main component in the LUFFACHITIN membrane, the potential role of -1,3-glucan in the promotion of wound healing and in the retardation of scar formation cannot be ignored. Biochemical evaluations of the wound-healing process treated with the LUFFACHITIN membrane are under progress.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Authors’ Contribution

Ping-Lun Jiang and Mei-Yin Chien contributed equally to this work.

Acknowledgments

Both financial support from the Center of Excellence for Clinical Trials and Research in Neuroscience (DOH 100-TD-B-111-003) and partial support from the National Science Council (NSC-97-2320-B-038-005-MY3) are highly appreciated.