Abstract
N,N′-bis-(4-carboxyphenyl)bicyclo[2,2,2]oct-7-ene-2,3,5,6-tetracarboxylic diimide was prepared by reaction of bicyclo[2,2,2]oct-7-ene-2,3,5,6-tetra carboxylic dianhydride with p-aminobenzoic acid in a mixture of acetic acid and pyridine (3: 2). Polycondensation of N,N′-bis-(4-carboxyphenyl)bicyclo[2,2,2]oct-7-ene-2,3,5,6-tetracarboxylic diimide with six different aromatic diamines produced a series of new poly(amide-imide)s (PAIs) in high yields with inherent viscosities between 0.49–0.95 dl/g. All PAIs were characterized by means of elemental analysis, viscosity measurement, solubility test, FTIR spectroscopy and 1H-NMR spectroscopy. Dynamic TGA of PAIs shows 10% weight loss temperatures from 410 to 435°C under nitrogen.
Similar content being viewed by others
References
Polyimides, Ed. by D. Wilson, H. D. Stenzenberger, and P. M. Hergenrother (Chapman and Hall, New York, 1990).
M. K. Ghosh and K. Mittal, Polyimides: Fundamentals and Applications (Marcel Dekker, New York, 1996).
S. H. Hsiao, C. P. Yang, C. W. Chen, and G. S. Liou, Eur. Polym. J. 41, 511 (2005).
C. P. Yang, R. S. Chen, and C. S. Wei, Eur. Polym. J. 38, 1721 (2002).
B. W. Chun, Polymer 35, 4203 (1994).
D. J. Liaw, F. C. Chang, J. H. Liu, et al., Polym. Degrad. Stab. 92, 323 (2007).
S. Mallakpour and E. Kowsari, Polym. Bull. (Berlin) 57, 169 (2006).
D. J. Liaw, C. C. Huang, and W. H. Chen, Polymer 47, 2337 (2006).
C. P. Yang, R. S. Chen, and C. S. Wei, Eur. Polym. J. 38, 1721 (2002).
D. J. Liaw, F. C. Chang, J. H. Liu, et al., J. Appl. Polym. Sci. 104, 3096 (2007).
Y. Oishi, M. Ishida, M. A. Kakimoto, et al., J. Polym. Sci., Part A: Polym. Chem. 30, 1027 (1992).
I. Sumio, Y. Masao, and T. Shinji, Macromolecules 26, 3490 (1993).
B. W. Chun, Polymer 35, 4203 (1994).
M. A. Kakimoto, R. Akiyama, Y. S. Negi, and Y. Imai, J. Polym. Sci., Part A: Polym. Chem. 26, 99 (1988).
Y. Imai, N. N. Maldar, and M. A. Kakimoto, J. Polym. Sci., Part A: Polym. Chem. 23, 2077 (1985).
J. F. Dezern, J. Polym. Sci., Part A: Polym. Chem. 26, 2157 (1988).
G. M. Bower and W. Frost, J. Polym. Sci., Part A-1 1, 3135 (1963).
C. P. Yang, R. S. Chen, and C. C. Chang, Colloid Polym. Sci. 278, 1043 (2000).
C. P. Yang, R. S. Chen, and J. A. Chen, J. Polym. Sci., Part A: Polym. Chem. 38, 1 (2000).
C. P. Yang and C. S. Wei, Polymer 42, 1837 (2001).
M. Ghosh, Angew. Makromol. Chem. 172, 165 (1989).
D. Campa and D. J. Abajo, Eur. Polym. J. 19, 667 (1983).
Kh. Faghihi and Kh. Zamani, J. Appl. Polym. Sci. 101, 4263 (2006).
Kh. Faghihi and M. Hajibeygi, J. Appl. Polym. Sci. 92, 3447 (2004).
Kh. Faghihi, M. Shabanian, and M. Hajibeygi, Macromol. Res. 17, 912 (2009).
Kh. Faghihi and M. Hagibeygi, Macromol. Res. 13, 14 (2005).
Kh. Faghihi, M. Hajibeygi, and M. Shabanian, Macromol. Res. 17, 739 (2009).
Kh. Faghihi, M. Hajibeygi, and M. Shabanian, J. Chin. Chem. Soc. 56, 609 (2009).
S. Maiti and A. Ray, J. Appl. Polym. Sci. 28, 225 (1983).
S. Maiti and A. Ray, J. Polym. Sci., Part A: Polym. Chem. 21, 999 (1983).
S. H. Hsiao and C. P. Yang, J. Polym. Sci., Part A: Polym. Chem. 28, 1149 (1990).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Faghihi, K., Hajibeygi, M. Synthesis and characterization of new thermally stable poly(amide-imide)s based on bicyclo[2,2,2]oct-7-ene-2,3,5,6-tetracarboxylic diimide and aromatic diamines. Polym. Sci. Ser. B 53, 137–143 (2011). https://doi.org/10.1134/S156009041103002X
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S156009041103002X