Fabricating a pearl/PLGA composite scaffold by the low-temperature deposition manufacturing technique for bone tissue engineering

Here we developed a composite scaffold of pearl/poly(lactic-co-glycolic acid) (pearl/PLGA) utilizing the low-temperature deposition manufacturing (LDM). LDM makes it possible to fabricate scaffolds with designed microstructure and macrostructure, while keeping the bioactivity of biomaterials by working at a low temperature. Process optimization was carried out to fabricate a mixture of pearl powder, PLGA and 1,4-dioxane with the designed hierarchical structures, and freeze-dried at a temperature of −40 °C. Scaffolds with square and designated bone shape were fabricated by following the 3D model. Marrow stem cells (MSCs) were seeded on the pearl/PLGA scaffold and then cultured in a rotating cell culture system. The adhesion, proliferation and differentiation of MSCs into osteoblasts were determined using scanning electronic microscopy, WST-1 assay, alkaline phosphatase activity assay, immunofluorescence staining and real-time reverse transcription polymerase chain reaction. The results showed that the composite scaffold had high porosity (81.98 ± 3.75%), proper pore size (micropores: <10 µm; macropore: 495 ± 54 µm) and mechanical property (compressive strength: 0.81 ± 0.04 MPa; elastic modulus: 23.14 ± 0.75 MPa). The pearl/PLGA scaffolds exhibited better biocompatibility and osteoconductivity compared with the tricalcium phosphate/PLGA scaffold. All these results indicate that the pearl/PLGA scaffolds fulfill the basic requirements of bone tissue engineering scaffold.