Growth and luminescence properties of self-organized ZnSe quantum dots

Self-organized ZnSe quantum dots (QDs) were grown on (100) $ZnS/GaAs$ surfaces to study the relation of the size dispersion and luminescence. The exact dot sizes were obtained by measurements of atomic force microscope with its tip calibration and transmission electron microscope. The average dot size was 2.0 nm high and 11 nm in its diameter and the density was $1×1010 cm−2.$ Transition energies of ZnSe QDs were calculated using these measured dot sizes. These calculated peaks were in reasonable agreement with measured photoluminescence (PL) peaks. It was also revealed that the broadening of the PL spectra from ZnSe QDs were consistently explained by the dot size distribution.