Abstract
As scaling of conventional silicon-based electronics is reaching its ultimate limit, considerable effort has been devoted to find new materials and new device concepts that could ultimately outperform standard silicon transistors. In this perspective two-dimensional transition metal dichalcogenides, such as MoS2 and WSe2, have recently attracted considerable interest thanks to their electrical properties. Here, we report the first experimental demonstration of a doping-free, polarity-controllable device fabricated on few-layer WSe2. We show how modulation of the Schottky barriers at drain and source by a separate gate, named program gate, can enable the selection of the carriers injected in the channel and achieved controllable polarity behaviour with ON/OFF current ratios >106 for both electrons and holes conduction. Polarity-controlled WSe2 transistors enable the design of compact logic gates, leading to higher computational densities in 2D-flatronics.
Similar content being viewed by others
Introduction
Two-dimensional (2D) materials of the transition metal di-chalcogenides (TMDCs) family1, such as molybdenum disulphide (MoS2) and tungsten diselenide (WSe2), have been shown to exhibit excellent electrical properties2,3,4,5,6,7,8,9,10,11,12,13,14 and are currently drawing considerable attention as viable candidates for beyond-CMOS (complementary metal-oxide semiconductor) flatronics15,16,17,18. The peculiar layered structure of these materials allows for the growth or exfoliation of few- and monolayer films that have shown to provide exceptional electrostatic control when used as channel material of a field-effect transistor (FET), making them robust to short-channel effects19,20 and well suited for beyond-CMOS logic applications17,18,20. In conventional CMOS technology21, the ability of an electronic device to conduct both electrons and holes, without changing the channel doping or the contact material, known as ambipolarity, is usually considered a drawback. In fact the core elements of CMOS logic circuits are doped, n or p, unipolar devices. Transistor scaling to the nanometer dimensions has brought considerable problems to the doping process, as fluctuations on the number of dopants in the channel cause an undesirable shift in the threshold voltage of the devices22. A device concept that does not require any doping would thus be highly desirable for new generation electronic devices and 2D TMDC materials provide an excellent platform for exploring the development of such technology. The most studied amongst TMDCs, MoS22,3,4, suffers from Fermi level pinning to the conduction band at the contact interface23 which makes it challenging to achieve p-type conduction. Reports of p-type behaviour are, to date, limited to peculiar substrate conditions24, thick flakes24,25, ionic-liquid gating26 and use of high work function non-stoichiometric molybdenum oxide (MoOx, x < 3) at the contact interface27. Other 2D-chalcogenides, such as tungsten diselenide (WSe2)5,6,7,8,9,10,11,12,13,14 and molybdenum telluride (MoTe2)28,29, have recently gained considerable interest thanks to their ability to efficiently conduct both electrons and holes. In MoTe2, electrostatically reversible polarity has been shown29 with on-off current ratios of the order of 102 for p-type and 103 for n-type conduction. Holes conduction has been demonstrated and high mobility values have been reported in WSe25,6. Ambipolar behaviour has been achieved by using different metals to contact the n-type and p-type devices8,11,12, by introducing dopants to create separate n and p-type devices with the same channel material7,8,13 and by using ionic-liquid gating to modulate the work-function of graphene contacts14. WSe2 is the only 2D-chalcogenide for which a stable complementary technology has been demonstrated13 and is arguably the most promising candidate for the realization of high-performance polarity-controllable devices and circuits. In this article, we show how we exploited the ambipolar behaviour of WSe2 to realize double-back-gate devices and to experimentally demonstrate, for the first time on WSe2, the control of carrier injection by tuning the contact Schottky barriers with the additional program gate (PG). The device can be turned ON and OFF by gating the central channel region with a second gate, named control gate (CG), while the PG is able to control the device polarity without the need of changing metal contacts and without introducing any physical doping. The transistor polarity can thus be dynamically configured and thanks to the introduction of the additional PG the device abstraction at the logic level is a comparison-driven switch (device changes status only when the signals applied on CG and PG represent the same logic level). The enhanced functionality of a single device, as compared to conventional MOSFETs enables the realization of smaller, faster, less power-hungry circuits with higher computational density30.
Results and Discussion
For our experiments we used WSe2 flakes, prepared by mechanical exfoliation of WSe2 bulk crystal on a 20 nm SiO2/Si substrates, with the standard scotch-tape technique originally developed for graphene31. The optimal surface roughness of the SiO2 substrate (as low as 0.16 nm) allowed exfoliation of high-quality defect-free flakes. Thanks to the different optical contrast given by flakes with different thicknesses, we selected thin flakes (4–8 nm) with optical inspection32 and further characterized them with atomic force microscope (AFM)33 measurements to determine the exact thickness and verify the absence of folds and cracks (Fig. 1a). The thickness of the flake, extracted from the cutline shown in Fig. 1a, is presented in Fig. 1b. In order to realize our double back-gated geometry (see Supporting Information S1) the flake was transferred (see Methods and Supporting Information S2) to a target substrate and aligned with respect to predefined buried features, which will be acting as the program gate (Fig. 1c). The flake was aligned with respect to the buried structures and metal contacts, Ti (2 nm)/Pd (50 nm), were defined by electron-beam lithography and lift-off (see Methods). The metal contacts were evaporated with an electron-gun evaporation tool and the Ti layer was used only to improve the adhesion of Pd to SiO2, while only the thicker Pd film determined the contact properties. The final fabricated device is shown in Fig. 1c and a schematic cross-section respect to the cut-line in Fig. 1c is presented in Fig. 1d. The device has 1.5 μm channel length, of which 1 μm is gated by the bulk-Si (CG) and two ~0.25 μm regions near the contacts are controlled by the buried PG. The channel width is ~5.5 μm. The thickness of the SiO2 layer is 270 nm and the Al2O3 is 20 nm. The peculiar position of the flake with respect to the PG allowed us to control the carrier concentration underneath the contacts by electrostatic doping, but also to gate a region of the channel. The PG could thus modulate the Schottky barrier at drain and source allowing for the selection of the carriers preferably injected in the channel. The bulk silicon wafer was used as CG to create a potential barrier in the central region of the channel for either electrons or holes, according to the applied voltage polarity and allowed us to control the ON/OFF status of the device (see Supporting Information S3).
The flakes exfoliated on the 20 nm SiO2 were used to study contact properties and the effect of thermal annealing. In our experiments, Ti/Pd-contacted WSe2 FETs on SiO2 dielectric substrate showed a considerably higher electron current with respect to the hole current (100× difference), when measured (see Methods) after contact lift-off and without any additional treatment (Fig. 2a). This pronounced difference between the p- and n-type conduction properties is not ideal for the realization of polarity-controllable devices, as it will lead to asymmetric current-voltage (I-V) characteristics. Hence we performed a contact annealing step (see Methods), following what already reported in literature10,34,35,36,37, in order to improve the ON-current levels. The effect of contact annealing was found to be reproducible and consistent, with an asymmetric increase of the ON-current levels and a decrease of the OFF-current. For the particular device presented in Fig. 2a, we obtained a 10× increase of the hole ON-current (Fig. 2a) and a 4× decrease of the OFF-current, while the electron ON-current did not show a significant improvement. This behavior cannot be attributed to a Fermi level shift at the contacts, which results in a change of the Schottky barrier height, since such effect would increase the current for one type of carriers but reduce it for the other one by a similar amount. The increase in both n- and p-type currents suggests an improved physical contacts between the Ti/Pd contacts and the WSe2 flake, possibly coupled with an improvement in the mobility of the charge carriers. This effect can result from removal of impurities (e.g. photoresist) and desorption of surface adsorbates (e.g water molecules) from the channel region34,35,36,37. The asymmetry in the improvement could point-out to an n-type doping of the channel by the impurities, which are then removed by the contact annealing. However, two-terminal measurements, such as those conducted in this study, obscure the intrinsic properties of the material and do not allow decoupling the decrease of contact resistance from an increase in the mobility of the charge carriers. We performed the same contact annealing procedure on devices realized after transferring the flake to the Al2O3 substrate with the buried PG (see Supporting Information S1) and we measured the full back-gate transfer characteristics leaving the PG floating, thus no control of the Schottky barriers was used. Thanks to the annealing procedure we managed to reduce the asymmetry between p- and n-type conduction and we achieved a more pronounced symmetry, with 15× difference in ON-current between the electron and hole branch (Fig. 2b). The symmetric ambipolar behavior achieved is a key step towards the realization of polarity-controllable devices without the addition of any physical doping.
Considering the ambipolar I-V characteristics presented in Fig. 2b, we now show how applying a voltage on the PG allowed us to modulate the Schottky barriers at drain and source and to select the type of carriers (electrons or holes) that are favorably injected in the channel. For negative voltage values of the PG (Fig. 3a), we completely suppressed electron injection in the channel and we introduced local p-type electrostatic doping in the contact regions. Further decreasing the program gate applied voltage induced more positive charges and caused the effective Schottky barrier height to decrease (thinning of tunnelling barrier and thus increased tunnelling probability for holes). For the lowest negative applied voltage (−12 V in Fig. 3a) the on/off-current levels were restored to the previous values extracted from the back-gate measurement with the program gate floating. In a similar fashion, when applying a positive voltage to the PG, electrons are preferably injected in the channel and the hole current is completely suppressed for all negative voltages applied on the CG (Fig. 3b). Again we showed that for the highest program gate applied voltage (10 V in Fig. 3b) the on/off-current levels matched with the ones extracted in Fig. 2a. Schematic band-diagrams relative to the 4 operation modes of the device are reported in Fig. 3c–f. We achieved ION/IOFF ratios of 107 for n-type operation and of 106 for p-type operation indicating an optimal electrostatic control on the channel for both carriers and the potential for low-power applications, thanks to the low leakage floor (off-current) measured in both configurations (see Supporting Information S4 for further device characterization and S5 for measurements on additional device).
As we mentioned, the ON-current levels corresponding to the highest applied PG values are comparable to the ones extracted from Fig. 2(b). There is instead, a marked discrepancy between the ON-current levels reported in Fig. 3(a,b) and the ones in Fig. 2(b) for smaller positive and negative PG voltages. We believe this is a consequence of capacitive coupling between the CG and the contact pad of the PG, that leads to an increased capacitance acting on the channel region. A similar effect has been reported to occur for conventional double-gated structures38, causing an overestimation of mobility values extracted from conventional back-gated characteristics. Thus, in order to extract relevant parameters (such as carrier’s mobility and sub-threshold slopes), we focused on the two curves taken at the highest positive and negative PG voltages (see Supporting Information S4). The maximum extrinsic low-field mobility measured for electrons (e) was 5.5 cm2V−1s−1 and 0.23 cm2V−1s−1 for holes (h). These values are smaller than those reported in literature for WSe25,6 and we attribute this difference to the presence of large Schottky barriers at the contacts, the lack of high-k passivation and the presence of interface charges at the Al2O3/WSe2 interface, that increase the scattering in the channel. The presence of interface charges is also reflected by the values of sub-threshold swing (S factor) extracted from the measurements. We computed an S factor of 0.875 V/dec over 4 decades of current for n-type conduction and of 0.92 V/dec over 3 decades of current for p-type conduction. These values could be greatly improved by reducing the gate-oxide thickness (switching to a top-gated structure) and by increasing the interface quality between the 2-D material and the dielectric substrate. These steps will be essential to further develop 2D-based polarity controllable electronics and should be explored in the future.
We further characterized the switching properties of the device by sweeping the PG while fixing the value of the CG (Fig. 4a). In this configuration the polarity of the transistor was changed during each sweep showing the ability of the device to transit from a p- to n-type behaviour, or vice-versa, in the same measurement, thus demonstrating “on-the-fly” polarity transition. To further understand the impact of this device on circuit design we look more closely at its switching properties. While a standard 3-terminal device acts as a binary switch, our device compares two values (voltages applied on PG and CG) and when loaded implements an exclusive OR function (XOR) (Fig. 4b).
Indeed when the transistor is not conducting, in the ‘01’ and ‘10’ cases, then no current would be flowing in the device leaving the output to ‘1’ (high). When the values of PG and CG have the same logic value, both high or both low, then the transistor is conducting and the output of the logic gate would be ‘0’ (low) (Fig. 4b inset). The comparison-driven switching property of our device can be exploited at a circuit level because it gives the possibility of realizing logic gates (e.g. XOR, majority gates, as well as other circuit primitives) with smaller area, delay and power consumption for next generation digital electronics.
In conclusion, we showed the first polarity controllable device realized with few-layer WSe2, using a double-back-gate geometry. We operated our device with fixed polarity, by setting the program gate voltage to either positive or negative values and we also demonstrated “on-the-fly” polarity control in 2D devices showing a p-to-n or vice-versa transition during the same measurement sweep. We achieved high ON/OFF ratios for both n-type (107) and p-type (106) operation modes. This work represents a major step on the path to exploiting the full potential of this technology for the realization of novel digital circuits with dynamically controllable polarity gates in WSe2 flatronics.
Methods
Exfoliation and transfer
The WSe2 flakes were exfoliated from commercially available synthetic crystal, provided by HQ-graphene, using a standard low-tack dicing tape. The flake characterization was performed with a dimension edge AFM from Bruker in tapping mode. For the dry-transfer process we used thick (~10 μm) spin-coated poly-methyl methacrylate (PMMA) as transferring agent. After selecting the flake for transfer, PMMA was spin-coated on the sample and annealed at 165 °C on a hot-plate. We then diced the PMMA around the flake using a micro-engraver and, upon release of the WSe2/PMMA stack, we picked it up using a microneedle. The WSe2/PMMA stack was then transferred to the target substrate and aligned with respect to the buried program gate by a manual pick-and-drop process. Adhesion of the WSe2/PMMA stack was assured by 2 min hot-plate annealing at 190 °C. Finally PMMA was dissolved using dichloromethane (DCM) and the sample was cleaned with an hot acetone bath (~12 hours) to ensure the absence of PMMA residues.
E-beam lithography and lift-off
We used a single layer PMMA resist (solution with 3% Chlorobenzene). The resist was spinned for 60 seconds at 4500 rpm with a resulting layer thickness of around 180 nm. The resist was then baked on a hot-plate for 3 minutes at 165 ° C. After exposure the resist was developed in a 1:1 solution (at room temperature) of methyl-isobutyl ketone (MIBK) and Isopropyl alcohol (IPA) for 55 seconds. After metal deposition, done with a commercial electron gun evaporator tool, lift-off was carried out in hot acetone (50 °C) for around 2 hours.
Contact annealing
Contact annealing was performed at 200 °C for 12 hours in a Nabetherm open-tube furnace in vacuum with a constant Argon (Ar) flow of 0.5 l/hr.
Device Characterization
All electrical measurements were performed at room temperature in N2 environment using a Keithley 4200 semiconductor characterization system (SCS) with pre amplifiers probe station. The current measurements were performed with auto-range setting allowing for highest accuracy (1% of reading + 10fA) on off-current measurements. The voltage step for both VCG and VPG sweeps was fixed at 200 mV and the gate leakage currents Ipg and Icg were measured during all sweeps.
Additional Information
How to cite this article: Resta, G. V. et al. Polarity control in WSe2 double-gate transistors. Sci. Rep. 6, 29448; doi: 10.1038/srep29448 (2016).
References
Wilson, J. A. & Yoffe, A. D. The transition metal dichalcogenides: discussion and interpretation of the observed optical, electrical and structural properties. Adv. in Phys. 18, 193–335 (1969).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nature Nanotech. 6, 147–150 (2011).
Das, S., Chen, H. Y., Penumatcha, A. V. & Appenzeller, J. High performance multilayer MoS2 transistors with scandium contacts. Nano Lett. 13, 100–105 (2012).
Wang, H. et al. Integrated circuits based on bilayer MoS2 transistors. Nano Lett. 12, 4674–4680 (2012).
Movva, H. C. P. et al. High-Mobility Holes in Dual-Gated WSe2 Field-Effect Transistors. ACS Nano 9, 10402–10410 (2015).
Pradhan, N. R. et al. Hall and field-effect mobilities in few layered p-WSe2 field-effect transistors. Sci. Rep. 5, 8979 (2015).
Fang, H. et al. High-performance single layered WSe2 p-FETs with chemically doped contacts. Nano Lett. 12, 3788–3792 (2012).
Tosun, M. et al. High-gain inverters based on WSe2 complementary field-effect transistors. ACS Nano 8 4948–4953 (2014).
Huang, J.-K. et al. Large-area synthesis of highly crystalline WSe2 monolayers and device applications. ACS Nano 8, 923–930 (2013).
Liu, W. et al. Role of metal contacts in designing high-performance monolayer n-type WSe2 field effect transistors. Nano Lett. 13, 1983–1990 (2013).
Das, S. & Appenzeller, J. WSe2 field effect transistors with enhanced ambipolar characteristics. Appl. Phys. Lett. 103, 103501 (2013).
Das, S., Dubey, M. & Roelofs, A. High gain, low noise, fully complementary logic inverter based on bi-layer WSe2 field effect transistors. Appl. Phys. Lett. 105, 083511 (2014).
Chuang, H.-J. et al. High Mobility WSe2 p-and n-Type Field-Effect Transistors Contacted by Highly Doped Graphene for Low-Resistance Contacts. Nano Lett. 14, 3594–3601 (2014).
Yu, L. et al. High-Performance WSe2 Complementary Metal Oxide Semiconductor Technology and Integrated Circuits. Nano Lett. 15, 4928–4934 (2015).
Fiori, G. et al. Electronics based on two-dimensional materials. Nature Nanotech. 9, 768–779 (2014).
Jariwala, D., Sangwan, V. K., Lauhon, L. J., Marks, T. J. & Hersam, M. C. Emerging device applications for semiconducting two-dimensional transition metal dichalcogenides. ACS Nano 8, 1102–1120 (2014).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nature Nanotech. 7, 699–712 (2012).
Ferrari, A. C. et al. Science and technology roadmap for graphene, related two-dimensional crystals and hybrid systems. Nanoscale 7, 4598–4810 (2015).
Yoon, Y., Ganapathi, K. & Salahuddin, S. How good can monolayer MoS2 transistors be? Nano Lett. 11, 3768–3773 (2011).
Cao, W., Kang, J., Sarkar, D., Liu, W. & Banerjee, K. 2D semiconductor FETs—Projections and design for sub-10 nm VLSI. IEEE Transactions on Electron Devices 62 3459–3469 (2015).
Rabaey, J. M., Chandrakasan, A. & Nikolic, B. Digital integrated circuits a design perspective, 2nd ed. (Prentice Hall: New York, 2003).
Borkar, S. Designing reliable systems from unreliable components: the challenges of transistor variability and degradation. Micro, IEEE 25, 10–16 (2005).
Gong, C., Colombo, L., Wallace, R. M. & Cho, K. The unusual mechanism of partial Fermi level pinning at metal–MoS2 interfaces. Nano Lett. 14, 1714–1720 (2014).
Bao, W., Cai, X., Kim, D., Sridhara, K. & Fuhrer, M. S. High mobility ambipolar MoS2 field-effect transistors: Substrate and dielectric effects. Appl. Phys. Lett. 102, 042104 (2013).
Sutar, Surajit et al. Reconfigurable pn junction diodes and the photovoltaic effect in exfoliated MoS2 films. Appl. Phys. Lett. 104, 122104 (2014).
Zhang, Y., Ye, J., Matsuhashi, Y. & Iwasa, Y. Ambipolar MoS2 thin flake transistors. Nano Lett. 12, 1136–1140 (2012).
Chuang, S. et al. MoS2 p-Type Transistors and Diodes Enabled by High Work Function MoOx Contacts. Nano Lett. 14, 1337–1342 (2014).
Lin, Y. ‐F. et al. “Ambipolar MoTe2 transistors and their applications in logic circuits”. Adv. Mater. 26, 3263–3269 (2014).
Nakaharai, S. et al. Electrostatically Reversible Polarity of Ambipolar α-MoTe2 Transistors. ACS Nano 9, 5976–5983 (2015).
Bernstein, K., Cavin, R. K., Porod, W., Seabaugh, A. & Welser, J. Device and architecture outlook for beyond CMOS switches. Proceedings of the IEEE 98, 2169–2184 (2010).
Novoselov, K. S. A. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Benameur, M. M. et al. Visibility of dichalcogenide nanolayers. Nanotech. 22, 125706.
Binnig, G., Quate, C. F. & Gerber, C. Atomic force microscope. Phys. Rev. Lett. 56, 930 (1986).
Fuhrer, M. S. & Hone, J. Measurement of mobility in dual-gated MoS2 transistors. Nat. Nano 8, 146–147 (2013).
Namgung, S. D. et al. Influence of post-annealing on the off current of MoS2 field-effect transistors. Nanoscale Research Letters 10, 1–6 (2015).
Kim, S. et al. High-mobility and low-power thin-film transistors based on multilayer MoS2 crystals. Nat. Commun. 3, 1011 (2015).
Baugher, B. W., Churchill, H. O., Yang, Y. & Jarillo-Herrero, P. Intrinsic electronic transport properties of high-quality monolayer and bilayer MoS2 Nano Lett., 13 4212–4216 (2013).
Chiu, M.-H. et al. Determination of band alignment in the single-layer MoS2/WSe2 heterojunction. Nat. Commun. 6, 7666 (2015).
Author information
Authors and Affiliations
Contributions
G.V.R. worked on the device fabrication, performed the measurements and analyzed data presented in the paper. Y.B. performed the flakes transfer. S.S., D.L., I.R., P.R., F.C., A.T., P.-E.G. and G.D.M. helped interpreting the experimental results. G.V.R. wrote the manuscript with contributions from all authors.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Resta, G., Sutar, S., Balaji, Y. et al. Polarity control in WSe2 double-gate transistors. Sci Rep 6, 29448 (2016). https://doi.org/10.1038/srep29448
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep29448
This article is cited by
-
Ferroelectric gating of two-dimensional semiconductors for the integration of steep-slope logic and neuromorphic devices
Nature Electronics (2023)
-
Three-to-one analog signal modulation with a single back-bias-controlled reconfigurable transistor
Nature Communications (2022)
-
A mode-balanced reconfigurable logic gate built in a van der Waals strata
npj 2D Materials and Applications (2021)
-
Gate energy efficiency and negative capacitance in ferroelectric 2D/2D TFET from cryogenic to high temperatures
npj 2D Materials and Applications (2021)
-
Logic-in-memory based on an atomically thin semiconductor
Nature (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.