Abstract
Lead-Free ceramics 0.95(Na0.5K0.5)NbO3-0.05CaTiO3-x mol. % Ag2O have been fabricated as a function of the amount of Ag2O content. NKN-CT ceramics showed the highest piezoelectric properties and ferroelectric properties at the 0.5 mol. %Ag2O content. The NKN-CT-Ag2O0.5 mol. % ceramics show a good performance with piezoelectric constant d 33 = 221 ρC/N, k p = 0.38%, respectively. The corresponding Curie temperature and remnant polarization reached 370°C and 22.5 µC/cm2, respectively. These results appear that NKN-CTAg2O ceramics are promising candidate materials for lead-free piezoelectric application.
Similar content being viewed by others
References
P. Hansen, D. Hennings, and H. Schreinemacher, J. Am. Ceram. Soc. 81, 1369 (1998).
H. Kishi, N. Kohzu, and J. Sugino, J. Eur. Ceram. Soc. 20, 1997 (2000).
S. P. Nam, S. G. Lee, S. G. Bae, and Y. H. Lee, J. Elect. Engin. Tech. 2, 98 (2007).
S. Anwar, P. R. Sagdeo, and N. P. Lalla, Solid State Commun. 138, 331 (2006).
B. J. Sung, E. W. Lee, and J. G. Lee, J. Elect. Engin. Tech. 3, 293 (2008).
I. J. Cho, K. S. Yun, and H. J. Nam, J. Elect. Engin. Tech. 6, 119 (2011).
M. Matsubara, T. Yamaguchi, K. Kikuta, and S. Hirano, Jpn. J. Appl. Phys. 43, 7159 (2004).
W. K. Jeung, S. M. Choi, and Y. J. Kim, J. Elect. Engin. Tech. 1, 263 (2006).
S. J. Zhang, R. Xia, T. R. Shrout, G. Z. Zang, and J. F. Wang, J. Appl. Phys. 100, 104108 (2006).
H. J. Bae, J. Koo, and J. P. Hong, J. Elect. Engin. Tech. 1, 120 (2006).
Y. Saito, H. Takao, T. Tani, T. Nonoyama, K. Takatori, T. homma, and T. Nagayamura, Nature 432, 7013 (2004).
Y. Wang, D. Damjanovic, N. Klein, and N. Setter, J. Am. Ceram Soc. 91, 1962 (2008).
E. Hollenstein, M. Davis, D. Damjanovic, and N. Setter, Appl. Phys. Lett. 87, 182905 (2005).
G. L. Yuan and S. W. Or, Appl. Phys. Lett. 88, 062905 (2006).
M. S. Kim, Y. M. Jeon, Y. M. Im, Y. H. Lee, and T. H. Nam, Trans. Electr. Electron. Mater. 12, 20 (2011).
S. H. Lee, J. Elect. Engin. Tech. 2, 102 (2007).
H.-J. Noh, S. G. Lee, and S. P. Nam, J. Elect. Engin. Tech. 4, 527 (2009).
E.-S. Na, Y.-H. Kim, and S.-C. Choi, J. Kor. Cryst. Growth Cryst. Technol. 10, 245 (2000).
R. D. Shannon, Acta. Cryst. A32, 751 (1976).
V. V. Thang, I. S. Kim, S. J. Jeong, M. S. Kim, and J. S. Song, J. Elect. Engin. Tech. 6, 671 (2011).
K. S. Chang, S. M. Kang, K. G. Park, S. H. Shin, H. S. Kim, and H. S. Kim, J. Elect. Engin. Tech. 7, 75 (2012).
K. A. Fonteyn, A. Belahcen, P. Rasilo, R. Kouhia, and A. Arkkio, J. Elect. Engin. Tech. 7, 336 (2012).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, SH., Baek, SD., Kim, HJ. et al. Dielectric and piezoelectric properties of 0.95(Na0.5K0.5)NbO3-0.05CaTiO3 ceramics with Ag2O contents. Electron. Mater. Lett. 8, 577–580 (2012). https://doi.org/10.1007/s13391-012-2072-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13391-012-2072-4