Abstract
Dexamethasone is a widely used drug in medical and biological applications. Since the systematic and controllable release of this drug is of significant importance, encapsulation of this anti-inflammatory drug in poly(lactic-co-glycolic acid) (PLGA) nanoparticles can minimize uncontrolled issues. As dexamethasone-encapsulated PLGA nanoparticles are synthesized in the presence of organic solvents, poly(dimethylsiloxane) (PDMS)-based microchannels collapse due to the swelling problem. In present study, PTFE nanoparticles were used for the surface modification of the microchannels to prevent absorption and adhesion of solvents into the microchannels’ wall. The contact angle analysis of microchips after coating showed that the surface of microchannels bear the superhydrophobicity feature (140.30°) and SEM images revealed that PTFE covered the surface of PDMS, favorably. Then, the prepared microchip was tested for the synthesis of dexamethasone-loaded nanoparticles. SEM and atomic force microscopy (AFM) images of the synthesized nanoparticles represented that there was not any evidence of adhesion or absorption of nanoparticles. Furthermore, the monodispersity of nanoparticles was discernible. As AFM results revealed, the average diameters of 47, 63, and 82 nm were achieved for flow ratios of 0.01, 0.05, and 0.1, respectively. To evaluate the drug efficiency, cumulative release and encapsulation efficiency were analyzed which showed much more efficiency than the synthesized nanoparticles in the bulk mode. In addition, MTT test revealed that nanoparticles could be considered as a non-toxic material. Since the synthesis of drug-loaded nanoparticles is ubiquitous in laboratory experiments, the approach presented in this study can render more versatility in this regard.
Similar content being viewed by others
References
Soiberman U, Kambhampati SP, Wu T, Mishra MK, Oh Y, Sharma R, et al. Subconjunctival injectable dendrimer-dexamethasone gel for the treatment of corneal inflammation. Biomaterials. 2017;125:38–53.
Canalis, E., Effect of growth factors on bone cell replication and differentiation. Clin Orthop Relat Res, 1985(193): p. 246–63.
Chen Y, Li J, Kawazoe N, Chen G. Preparation of dexamethasone-loaded calcium phosphate nanoparticles for the osteogenic differentiation of human mesenchymal stem cells. J Mater Chem B. 2017;5(33):6801–10.
Schäcke H, Döcke W-D, Asadullah K. Mechanisms involved in the side effects of glucocorticoids. Pharmacol Ther. 2002;96(1):23–43.
Larrañeta, E., Domínguez-Robles J., Coogan M., Heaney E., Stewart S.A., Singh Thakur R.R., Donnelly R.F., Poly(methyl vinyl ether-co-maleic acid) hydrogels containing cyclodextrins and Tween 85 for potential application as hydrophobic drug delivery systems. Macromol Res, 2019.
Zhang R, Lei L, Song Q, Li X. Calcium ion cross-linking alginate/dexamethasone sodium phosphate hybrid hydrogel for extended drug release. Colloids Surf B: Biointerfaces. 2019;175:569–75.
Gref R, Minamitake Y, Peracchia M, Trubetskoy V, Torchilin V, Langer R. Biodegradable long-circulating polymeric nanospheres. Science. 1994;263(5153):1600–3.
Mittal G, Sahana DK, Bhardwaj V, Ravi Kumar MNV. Estradiol loaded PLGA nanoparticles for oral administration: effect of polymer molecular weight and copolymer composition on release behavior in vitro and in vivo. J Control Release. 2007;119(1):77–85.
Farokhzad OC, Langer R. Impact of nanotechnology on drug delivery. ACS Nano. 2009;3(1):16–20.
Govender T, et al. PLGA nanoparticles prepared by nanoprecipitation: drug loading and release studies of a water soluble drug. J Control Release. 1999;57(2):171–85.
Karnik R, Gu F, Basto P, Cannizzaro C, Dean L, Kyei-Manu W, et al. Microfluidic platform for controlled synthesis of polymeric nanoparticles. Nano Lett. 2008;8(9):2906–12.
Valencia PM, Farokhzad OC, Karnik R, Langer R. Microfluidic technologies for accelerating the clinical translation of nanoparticles. Nat Nanotechnol. 2012;7:623–9.
Mukhopadhyay R. When PDMS isn’t the best. Anal Chem. 2007;79(9):3248–53.
Abate AR, Lee D, Do T, Holtze C, Weitz DA. Glass coating for PDMS microfluidic channels by sol-gel methods. Lab Chip. 2008;8(4):516–8.
Ebert D, Bhushan B. Transparent, superhydrophobic, and wear-resistant surfaces using deep reactive ion etching on PDMS substrates. J Colloid Interface Sci. 2016;481:82–90.
Montazeri L, Bonakdar S, Taghipour M, Renaud P, Baharvand H. Modification of PDMS to fabricate PLGA microparticles by a double emulsion method in a single microfluidic device. Lab Chip. 2016;16(14):2596–600.
Kim B-Y, Hong LY, Chung YM, Kim DP, Lee CS. Solvent-resistant PDMS microfluidic devices with hybrid inorganic/organic polymer coatings. Adv Funct Mater. 2009;19(23):3796–803.
Rolland JP, van Dam RM, Schorzman DA, Quake SR, DeSimone JM. Solvent-resistant photocurable liquid fluoropolymers for microfluidic device fabrication [corrected]. J Am Chem Soc. 2004;126(8):2322–3.
Tropmann A, Tanguy L, Koltay P, Zengerle R, Riegger L. Completely superhydrophobic PDMS surfaces for microfluidics. Langmuir. 2012;28(22):8292–5.
Shi X, Chen S, Zhou J, Yu H, Li L, Wu H. Directing osteogenesis of stem cells with drug-laden, polymer-microsphere-based micropatterns generated by Teflon microfluidic chips. Adv Funct Mater. 2012;22(18):3799–807.
Ren K, Dai W, Zhou J, Su J, Wu H. Whole-Teflon microfluidic chips. Proc Natl Acad Sci. 2011;108(20):8162–6.
Cho SH, Godin J, Lo Y-H. Optofluidic waveguides in Teflon AF-coated PDMS microfluidic channels. IEEE Photon Technol Lett : a publication of the IEEE Laser and Electro-optics Society. 2009;21(15):1057–9.
Ruan M, Zhan Y, Wu Y, Wang X, Li W, Chen Y, et al. Preparation of PTFE/PDMS superhydrophobic coating and its anti-icing performance. RSC Adv. 2017;7(66):41339–44.
Hasani-Sadrabadi MM, Pour Hajrezaei S, Hojjati Emami S, Bahlakeh G, Daneshmandi L, Dashtimoghadam E, et al. Enhanced osteogenic differentiation of stem cells via microfluidics synthesized nanoparticles. Nanomedicine. 2015;11(7):1809–19.
Chronopoulou L, Sparago C, Palocci C. A modular microfluidic platform for the synthesis of biopolymeric nanoparticles entrapping organic actives. J Nanopart Res. 2014;16(11):2703.
Mollajan M, Bazaz SR, Mehrizi AA. A thoroughgoing design of a rapid-cycle microfluidic droplet-based PCR device to amplify rare DNA strands. J Appl Fluid Mech. 2018;11(1):21–9.
Bazaz SR, Mehrizi AA, Ghorbani S, Vasilescu S, Asadnia M, Warkiani ME. A hybrid micromixer with planar mixing units. RSC Adv. 2018;8(58):33103–20.
Rasouli M, Abouei Mehrizi A, Goharimanesh M, Lashkaripour A, Razavi Bazaz S. Multi-criteria optimization of curved and baffle-embedded micromixers for bio-applications. Chem Eng Proc-Process Intensification. 2018;132:175–86.
McDonald JC, Duffy DC, Anderson JR, Chiu DT, Wu H, Schueller OJA, et al. Fabrication of microfluidic systems in poly(dimethylsiloxane). Electrophoresis. 2000;21(1):27–40.
Mata A, Fleischman AJ, Roy S. Characterization of polydimethylsiloxane (PDMS) properties for biomedical micro/nanosystems. Biomed Microdevices. 2005;7(4):281–93.
Lee JN, Park C, Whitesides GM. Solvent compatibility of poly(dimethylsiloxane)-based microfluidic devices. Anal Chem. 2003;75(23):6544–54.
Min KI, Lee TH, Park CP, Wu ZY, Girault HH, Ryu I, et al. Monolithic and flexible polyimide film microreactors for organic microchemical applications fabricated by laser ablation. Angew Chem Int Ed. 2010;49(39):7063–7.
Martin S, Bhushan B. Transparent, wear-resistant, superhydrophobic and superoleophobic poly(dimethylsiloxane) (PDMS) surfaces. J Colloid Interface Sci. 2017;488:118–26.
Wu CW, Gong GC. Fabrication of PDMS-based nitrite sensors using Teflon AF coating microchannels. IEEE Sensors J. 2008;8(5):465–9.
Lu X-C, Wen SZ, Tong J, Chen YT, Ren LQ. Wettability, soil adhesion, abrasion and friction wear of PTFE (+ PPS) + Al2O3 composites. Wear. 1996;193(1):48–55.
Yonghao X, et al. Superhydrophobicity and UV stability of polydimethylsiloxane/polytetrafluoroethylene (PDMS/PTFE) coatings. in 2006 11th International Symposium on Advanced Packaging Materials: Processes, Properties and Interface. 2006.
Amrani S, Tabrizian M. Characterization of nanoscale loaded liposomes produced by 2D hydrodynamic flow focusing. ACS Biomater Sci Eng. 2018;4(2):502–13.
Trantidou T, Elani Y, Parsons E, Ces O. Hydrophilic surface modification of PDMS for droplet microfluidics using a simple, quick, and robust method via PVA deposition. Microsystems: Nanoengineering. 2017;3:16091.
Morita I, Ando Y, Heo YJ. Microsphere formation using SIFEL microfluidic devices with organic-solvent resistance. J Adv Mech Des Syst Manuf. 2017;11(2):JAMDSM0031–1.
Bauer W-AC, Fischlechner M, Abell C, Huck WTS. Hydrophilic PDMS microchannels for high-throughput formation of oil-in-water microdroplets and water-in-oil-in-water double emulsions. Lab Chip. 2010;10(14):1814–9.
Lim H, Moon S. Stable nonpolar solvent droplet generation using a poly(dimethylsiloxane) microfluidic channel coated with poly-p-xylylene for a nanoparticle growth. Biomed Microdevices. 2015;17(4):70.
Lashkaripour A, Mehrizi AA, Goharimanesh M, Rasouli M, Bazaz SR. Size-controlled droplet generation in a microfluidic device for rare dna amplification by optimizing its effective parameters. J Mech Med Biol. 2018;18:1850002.
Ding S, Anton N, Vandamme TF, Serra CA. Microfluidic nanoprecipitation systems for preparing pure drug or polymeric drug loaded nanoparticles: an overview. Expert Opin Drug Deliv. 2016;13(10):1447–60.
Mahmoodi L, et al. Size-tunable alginate nanoparticles synthesis using T-junction microfluidic chip. in Biomedical Engineering and 2016 1st International Iranian Conference on Biomedical Engineering (ICBME), 2016 23rd Iranian Conference on. 2016. IEEE.
Lim J-M, Bertrand N, Valencia PM, Rhee M, Langer R, Jon S, et al. Parallel microfluidic synthesis of size-tunable polymeric nanoparticles using 3D flow focusing towards in vivo study. Nanomedicine. 2014;10(2):401–9.
Min K-I, Im DJ, Lee HJ, Kim DP. Three-dimensional flash flow microreactor for scale-up production of monodisperse PEG-PLGA nanoparticles. Lab Chip. 2014;14(20):3987–92.
Hasani-Sadrabadi MM, Majedi FS, VanDersarl JJ, Dashtimoghadam E, Ghaffarian SR, Bertsch A, et al. Morphological tuning of polymeric nanoparticles via microfluidic platform for fuel cell applications. J Am Chem Soc. 2012;134(46):18904–7.
Bazban-Shotorbani S, Dashtimoghadam E, Karkhaneh A, Hasani-Sadrabadi MM, Jacob KI. Microfluidic directed synthesis of alginate nanogels with tunable pore size for efficient protein delivery. Langmuir. 2016;32(19):4996–5003.
Quintanar-Guerrero D, Allémann E, Fessi H, Doelker E. Preparation techniques and mechanisms of formation of biodegradable nanoparticles from preformed polymers. Drug Dev Ind Pharm. 1998;24(12):1113–28.
Valencia PM, Pridgen EM, Rhee M, Langer R, Farokhzad OC, Karnik R. Microfluidic platform for combinatorial synthesis and optimization of targeted nanoparticles for cancer therapy. ACS Nano. 2013;7(12):10671–80.
Hasani-Sadrabadi MM, Dashtimoghadam E, Bahlakeh G, Majedi FS, Keshvari H, van Dersarl JJ, et al. On-chip synthesis of fine-tuned bone-seeking hybrid nanoparticles. Nanomedicine (London). 2015;10(23):3431–49.
Hung LH, Teh SY, Jester J, Lee AP. PLGA micro/nanosphere synthesis by droplet microfluidic solvent evaporation and extraction approaches. Lab Chip. 2010;10(14):1820–5.
Lu M, Yang S, Ho YP, Grigsby CL, Leong KW, Huang TJ. Shape-controlled synthesis of hybrid nanomaterials via three-dimensional hydrodynamic focusing. ACS Nano. 2014;8(10):10026–34.
Dashtimoghadam E, Mirzadeh H, Taromi FA, Nyström B. Microfluidic self-assembly of polymeric nanoparticles with tunable compactness for controlled drug delivery. Polymer. 2013;54(18):4972–9.
Hickey T, Kreutzer D, Burgess DJ, Moussy F. Dexamethasone/PLGA microspheres for continuous delivery of an anti-inflammatory drug for implantable medical devices. Biomaterials. 2002;23(7):1649–56.
Mo Z, Ban J, Zhang Y, du Y, Wen Y, Huang X, et al. Nanostructured lipid carriers-based thermosensitive eye drops for enhanced, sustained delivery of dexamethasone. Nanomedicine. 2018;13(11):1239–53.
Su Y, Su Q, Liu W, Lim M, Venugopal JR, Mo X, et al. Controlled release of bone morphogenetic protein 2 and dexamethasone loaded in core–shell PLLACL–collagen fibers for use in bone tissue engineering. Acta Biomater. 2012;8(2):763–71.
Ishida Y, Heersche JNM. Glucocorticoid-induced osteoporosis: both in vivo and in vitro concentrations of glucocorticoids higher than physiological levels attenuate osteoblast differentiation. J Bone Miner Res. 1998;13(12):1822–6.
Soleimani S, Hasani-Sadrabadi MM, Majedi FS, Dashtimoghadam E, Tondar M, Jacob KI. Understanding biophysical behaviours of microfluidic-synthesized nanoparticles at nano-biointerface. Colloids Surf B: Biointerfaces. 2016;145:802–11.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
ESM 1
(DOCX 310 kb)
Rights and permissions
About this article
Cite this article
Mahmoodi, Z., Mohammadnejad, J., Razavi Bazaz, S. et al. A simple coating method of PDMS microchip with PTFE for synthesis of dexamethasone-encapsulated PLGA nanoparticles. Drug Deliv. and Transl. Res. 9, 707–720 (2019). https://doi.org/10.1007/s13346-019-00636-z
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13346-019-00636-z