Abstract
Undoped In2O3 and 0.25–1.00 wt% M (M=Pt, Nb, and Ru)-doped/loaded In2O3 nanoparticles were successfully synthesized in a single-step flame spray pyrolysis technique using indium nitrate, platinum (II) acetylacetonate, niobium ethoxide, and ruthenium (III) acetylacetonate precursors. The undoped In2O3 and M-doped In2O3 nanoparticles were characterized by Brunauer–Emmett–Teller (BET) analysis, X-ray diffraction (XRD), and scanning and transmission electron microscopy (SEM & TEM). The BET average diameter of spherical nanoparticles was found to be in the range of 10.2–15.2 nm under 5/5 (precursor/oxygen) flame conditions. All XRD peaks were confirmed to correspond to the cubic structure of In2O3. TEM images showed that there is no Pt nanoparticle loaded on In2O3 surface, suggesting that Pt should form solid solution with the In2O3 lattice. Gas sensing studies showed that 0.5 wt% Pt doping in In2O3 nanoparticles gave a significant enhancement of NO2 sensing performances in terms of sensor response and selectivity. 0.5 wt% Pt/In2O3 exhibited a high NO2 response of ~1904 to 5 ppm NO2 at 250 °C and good NO2 selectivity against NO, H2S, H2, and C2H5OH. In contrast, Nb and Ru loading resulted in deteriorated NO2 response. Therefore, Pt is demonstrated to be an effective additive to enhance NO2 sensing performances of In2O3-based sensors.
Graphical Abstract
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Ali M, Wang CY, Röhlig CC, Cimalla V, Stauden T, Ambacher O (2008) NOx sensing properties of In2O3 thin films grown by MOCVD. Sens Actuators, B 129:467–472. doi:10.1016/j.snb.2007.08.011
Cai P, Bai W, Zhang L, Song H, Su Y, Lv Y (2012) Hierarchical hollow microspheres and flower-like indium oxide: controllable synthesis and application as H2S cataluminescence sensing materials. Mater Res Bull 47:2212–2218. doi:10.1016/j.materresbull.2012.06.002
Chen C, Wei Y, Chen D, Jiao X (2011) Indium oxide nanocrystals: capping-agent-free synthesis, size-control mechanism, and high-gas sensing performance. Mater Chem Phys 125:299–304. doi:10.1016/j.matchemphys.2010.09.042
Chen N, Li X, Wang X, Yu J, Wang J, Tang Z, Akbar SA (2013) Enhanced room temperature sensing of Co3O4-intercalated reduced graphene oxide based gas sensors. Sens Actuators, B 188:902–908. doi:10.1016/j.snb.2013.08.004
Choi Y, Hwang I, Park J, Choi K, Park J, Lee J (2008) Novel fabrication of an SnO2 nanowire gas sensor with high sensitivity. Nanotechnology 19:095508. doi:10.1088/0957-4484/19/9/095508
Dong H, Liu Y, Li G, Wang X, Xu D, Chen Z, Zhang T, Wang J, Zhang L (2013) Hierarchically rosette-like In2O3 microspheres for volatile organic compounds gas sensors. Sens Actuators B Chem 178:302–309. doi:10.1016/j.snb.2012.12.103
Guo P, Pan H (2006) Selectivity of Ti-loaded In2O3 ceramics as an ammonia sensor. Sens Actuators, B 114:762–767. doi:10.1016/j.snb.2005.07.040
Huang BR, Lin JC (2012) Core-shell structure of zinc oxide/indium oxide nanorod based hydrogen sensors. Sens Actuators, B 174:389–393. doi:10.1016/j.snb.2012.08.065
Huang SZ, Lin W, Chen WZ (2009) Gas sensitivity of indium oxide. Trans NonferrMet Soc China 19:s80–s82. doi:10.1016/S1003-6326(10)60249-X
Kannan S, Rieth L, Solzbacher F (2010) NOx sensitivity of In2O3 thin film layers with and without promoter layers at high temperatures. Sens Actuators, B 149:8–19. doi:10.1016/j.snb.2010.06.042
Kemmler JA, Pokhrel S, Birkenstock J, Schowalter M, Rosenauer A, Barsan N, Weimar U, Madler L (2012) Quenched, nanocrystalline In4Sn3O12 high temperature phase for gas sensing applications. Sens Actuators, B 161:740–747. doi:10.1016/j.snb.2011.11.026
Kruefu V, Peterson E, Chantha C, Siriwong C, Phanichphant S, Carroll DL (2010) Flame –made niobium doped zinc oxide nanoparticles in bulk heterojunction solar cells. Appl Phys Lett 97:053302. doi:10.1063/1.3465866
Kruefu V, Liewhiran C, Wisitsoraat A, Phanichphant S (2011) Selectivity of flame-spray-made Nb/ZnO thick films towards NO2 gas. Sensors and Actuators B Chem 156:360–367. doi:10.1016/j.snb.2011.04.046
Kruefu V, Wisitsoraat A, Phanichphant S (2014) Effects of niobium-loading on sulfur dioxide gas-sensing characteristics of hydrothermally prepared tungsten oxide thick film. J Nanomater 51:7318. doi:10.1016/j.snb.2011.04.046
Liewhiran C, Tamaekong N, Wisitsoraat A, Phanichphant S (2009) H2 sensing response of flame-spray-made Ru/SnO2 thick films fabricated from spin-coated nanoparticles. Sensors 9:8996–9010. doi:10.3390/s91108996
Liewhiran C, Tamaekong N, Tuantranont A, Wisitsoraat A, Phanichphant S (2014) The effect of Pt nanoparticles loading on H2 sensing properties of flame-spray-made SnO2 sensing films. Mater Chem Phys 147:661–672. doi:10.1016/j.matchemphys.2014.06.005
Lim SK, Hwang SH, Chang D, Kim S (2010) Preparation of mesoporous In2O3 nanofibers by electrospinning and their application as a CO gas sensor. Sens Actuators, B 149:28–33. doi:10.1016/j.snb.2010.06.039
Liu L, Zhang T, Li S, Wang L, Tian Y (2009) Preparation, characterization, and gas-sensing properties of Pd-loaded In2O3 nanofibers. Mater Lett 63:1975–1977. doi:10.1016/j.matlet.2009.05.060
Liu X, Wang R, Zhang T, He Y, Tu J, Li X (2010) Synthesis and characterization of mesoporous indium oxide for humidity-sensing applications. Sens Actuators, B 150:441–448. doi:10.1016/j.snb.2010.05.033
Liu S, Yu B, Zhang H, Fei T, Zhang T (2014) Enhancing NO2 gas sensing performances at room temperature based on reduced graphene oxide-ZnO nanoparticles hybrids. Sens Actuators, B 202:272–278. doi:10.1016/j.snb.2014.05.086
Liu S, Wang Z, Zhang Y, Zhang C, Zhang T (2015) High performance room temperature NO2 sensors based on reduced graphene oxide-multiwalled carbon nanotubes-tin oxide nanoparticles hybrids. Sens Actuators, B 211:318–324. doi:10.1016/j.snb.2015.01.127
Lu X, Yin L (2011) Porous indium oxide nanorods: synthesis, characterization and gas sensing properties. J Mater Sci Technol 27(8):680–684. doi:10.1016/S1005-0302(11)60125-4
Luyo C, Ionescu R, Reyes LF, Topalian Z, Estrada W, Llober E, Graqvist CG, Heszler P (2009) Gas sensing response of NiO nanoparticle films made by reactive gas deposition. Sens Actuators B Chem 138:14–20. doi:10.1016/j.snb.2008.11.057
M’adler L, Kammler HK, Mueller R, Pratsinis SE (2002) Controlled synthesis of nanostructured particles by flame spray pyrolysis. Aerosol Sci 33:369–389. doi:10.1016/S0021-8502(01),00159-8
Min Y, Tuller HL, Palzer S, llenstein JW, Bo H (2003) Gas response of reactively sputtered ZnO films on Si-based micro-array. Sens Actuators B Chem 93:435–441. doi:10.1016/S0925-4005(03)00170-9
Neri G, Bonavita A, Micali G, Rizzo G, Pinna N, Niederberger M (2007) In2O3 and Pt-In2O3 nanopowders for low temperature oxygen sensors. Sens Actuators, B 127:455–462. doi:10.1016/j.snb.2007.04.046
Neri G, Leonardi SG, Latino M, Donato N, Baek S, Conte DE, Russo PA, Pinna N (2013) Sensing behavior of SnO2/reduced graphene oxide nanocomposites toward NO2. Sens Actuators, B 179:61–68. doi:10.1016/j.snb.2012.10.031
Niu X, Zhong H, Wang X, Jiang K (2006) Sensing properties of rare earth oxide loaded In2O3 by a sol–gel method. Sens Actuators, B 115:434–438. doi:10.1016/j.snb.2005.10.004
Penza M, Martucci C, Cassano G (1998) NOx gas sensing characteristics of WO3 thin films activated by noble metals (Pd, Pt, Au) layers. Sens Actuators, B 50:52–59. doi:10.1016/S0925-4005(98),00156-7
Qurashi A, Maghraby EME, Yamazaki T, Kikuta T (2010) Catalyst supported growth of In2O3 nanostructures and their hydrogen gas sensing properties. Sens Actuators, B 147:48–54. doi:10.1016/j.snb.2010.03.024
Samerjai T, Liewhiran C, Wisitsora-at A, Tamaekong N, Phanichphant S (2014) NO2 Gas sensing of flame-made Pt-loaded WO3 thick films. J Solid State Chem 214:47–52. doi:10.1016/j.jssc.2013.10.041
Seetha M, Meena P, Mangalaraj D, Masuda Y, Senthil K (2012) Synthesis of indium oxide cubic crystals by modified hydrothermal route for application in room temperature flexible ethanol sensors. Mater Chem Phys 133:47–54. doi:10.1016/j.matchemphys.2011.12.034
Singh N, Ponzoni A, Comini E, Lee PS (2012) Chemical sensing investigations on Zn-In2O3 nanowires. Sens Actuators, B 171–172:244–248. doi:10.1016/j.snb.2012.03.054
Srivastava V, Jain K (2008) Highly sensitive NH3 sensor using Pt catalyzed silica coating over WO3 thick films. Sens Actuators, B 133:46–52. doi:10.1016/j.snb.2008.01.066
Stankova M, Vilanova X, Calderer J, Llobet E, Brezmes J, Gràcia I, Cané C, Correig X (2006) Sensitivity and selectivity improvement of rf-sputtered WO3 micro hotplate gas sensors. Sens Actuators, B 113:241–248. doi:10.1016/j.snb.2005.02.056
Su PG, Peng SL (2015) Fabrication and NO2 gas-sensing properties of reduced graphene oxide/WO3 nanocomposite films. Talanta 132:398–405. doi:10.1016/j.talanta.2014.09.034
Suchea M, Katsarakis N, Christoulakis S, Nikolopoulou S, Kiriakidis G (2006) Low temperature indium oxide gas sensors. Sens Actuators, B 118:135–141. doi:10.1016/j.snb.2006.04.020
Tamaekong N, Liewhiran C, Wisitsoraat A, Tuantranont A, Phanichphant S (2009) Sensing characteristics of flame-spray-made Pt/ZnO thick films as H2 gas sensor. Sensors 9:6652–6669. doi:10.3390/s90906652
Tamaekong N, Liewhiran C, Wisitsoraat A, Tuantranont A, Phanichphant S (2014) NO2 sensing properties of flame-made MnOx-loaded ZnO-nanoparticle thick film. Sens Actuators B Chem 204:239–249. doi:10.1016/j.snb.2014.07.089
Tu J, Li N, Lai X, Chi Y, Zhang Y, Wang W, Xi X (2010) H2S-sensing properties of Pt-loaded mesoporous indium oxide. Appl Surf Sci 256:5051–5055. doi:10.1016/j.apsusc.2010.03.055
Wagner T, Sauerwald T, Kohl CD, Waitz T, Weidmann C, Tiemann M (2009) Gas sensor based on ordered mesoporous In2O3. Thin Solid Films 517:6170–6175. doi:10.1016/j.tsf.2009.04.013
Xu J, Chen Y, Shen J (2008) Ethanol sensor based on hexagonal indium oxide nanorods prepared by solvothermal methods. Mater Lett 62:1363–1365. doi:10.1016/j.matlet.2007.08.054
Xu L, Dong B, Wang Y, Bai X, Liu Q, Song H (2010) Electrospinning preparation and room temperature gas sensing properties of porous In2O3 nanotubes and nanowires. Sens Actuators, B 147:531–538. doi:10.1016/j.snb.2010.04.003
Xu X, Wang D, Liu J, Sun P, Guan Y, Zhang H, Sun Y, Liu F, Liang X, Gao Y, Lu G (2012) Template-free synthesis of novel In2O3 nanostructures and their application to gas sensors. Sens Actuators, B 185:32–38. doi:10.1016/j.snb.2013.04.078
Yang H, Tang A, Zhang X, Yang W, Qiu G (2004) In2O3 nanoparticles synthesized by mechanochemical processing. Scr Mater 50:413–415. doi:10.1016/j.scriptamat.2003.11.011
Zhang H, Feng J, Fei T, Liu S, Zhang T (2014) SnO2 nanoparticles-reduced graphene oxide nanocomposites for NO2 sensing at low operating temperature. Sens Actuators, B 190:472–478. doi:10.1016/j.snb.2013.08.067
Zheng W, Lu X, Wang W, Li Z, Zhang H, Wang Y, Wang Z, Wang C (2009) A highly sensitive and fast-responding sensor based on electrospun In2O3 nanofibers. Sens Actuators, B 142:61–65. doi:10.1016/j.snb.2009.07.031
Acknowledgments
The authors would like to gratefully acknowledge the financial support from the National Research University Project under the Office of the Higher Education Commission, Ministry of Education, Thailand. The Graduate School, Chiang Mai University, Thailand and Graduate Institute of Science and Technology (TGIST–01–56–026), National Science and Technology Development Agency, Thailand are also greatly appreciated for their support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Inyawilert, K., Channei, D., Tamaekong, N. et al. Pt-doped In2O3 nanoparticles prepared by flame spray pyrolysis for NO2 sensing. J Nanopart Res 18, 40 (2016). https://doi.org/10.1007/s11051-016-3341-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11051-016-3341-1