Abstract
Decomposition mechanism of methylene blue (MB) caused by a mixture of metallic iron-maghemite (Fe0-γFe2O3) was investigated by means of 57Fe-Mössbauer spectroscopy, X-ray diffractometry (XRD), Ultraviolet-Visible Absorption Spectroscopy (UV-vis) and electrospray-ionization mass spectroscopy (ESI-MS). Ten day-leaching test of 10 μmol L − 1 MB aqueous solution and Fe0-γFe2O3 mixture (mass ratio 3:7) showed a decrease in the concentration from 10.5 to 4.45 μmol L − 1 with first-order rate constant (k) of \(1.5_{7} \times 10^{-1}\) day − 1. An ESI-MS study of Fe0-γFe2O3 mixture (3:7) after the leaching test revealed new peaks at m/z of 100, 110 and 137 due to fragmentation of MB, in addition to those observed at m/z of 284, 270 and 256 which were ascribed to MB, Azure B and Azure A, respectively. 57Fe-Mössbauer spectra of Fe0-γFe2O3 mixture (3:7) resulted in a decrease in absorption area (A) for Fe0 (δ = 0.00±0.01 mm s − 1, H int = 33.0±0.1 T) from 37.5 to 21.3, 9.7, 7.9, 7.0 and 4.5±0.5 %, together with an increase in A from 0.0 to 5.0, 13.8, 17.2, 21.0 and 22.4±0.5 % for octahedral (O h) iron (FeII + FeIII) of Fe3O4. XRD study of these samples indicated that the peak intensity at 2Θ of 44.7° being ascribed to Fe0 was decreased, while that of 35.6° due to Fe3O4 was almost constant; relative peak ratio of Fe\(^{0}/\mathrm{Fe}_{3}\)O4 was decreased from 26.3 to 2.76 after the leaching, indicating that Fe0 in the Fe0-γFe2O3 mixture was oxidized to Fe3O4. These experimental results suggest that Fe0-γFe2O3 mixture could be utilized for the cleaning or decomposition of toxic organic compounds like trichloroethylene.
Similar content being viewed by others
References
Liu, C.-C., Tseng, D.-H., Wang, C.-Y.: Effects of ferrous ions on the reductive dechlorination of trichloroethylene by zero-valent iron. J. Hazardous Mater. B136, 706–713 (2006)
Kubuki, S., Shibano, K., Akiyama, K., Homonnay, Z., Kuzmann, E., Ristić, M., Nishida, T.: Effect of the structural change of an iron-iron oxide mixture on the decomposition of trichloroethylene. J. Radioanal. Nucl. Chem. (2012). doi:10.1007/s10967-012-1933-5
Wakasa, M.: Magnetic field effects on the photocatalytic reaction. In: Research Report of Comprehensive Research Organization, vol. 4. http://sucra.saitama-u.ac.jp/modules/xoonips/download.php/KP17A05–76.pdf?file_id=1427 (in Japanese) (2006)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kubuki, S., Shibano, K., Akiyama, K. et al. Decomposition mechanism of methylene blue caused by metallic iron-maghemite mixture. Hyperfine Interact 218, 47–52 (2013). https://doi.org/10.1007/s10751-012-0672-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10751-012-0672-x