Abstract
Thin films of the biodegradable polymer poly(DL-lactide-co-glycolide) (PLGA) were deposited using resonant infrared pulsed laser deposition (RIR-PLD). The output of a free-electron laser was focused onto a solid target of the polymer, and the films were deposited using 2.90 (resonant with O-H stretch) and 3.40 (C-H) μm light at macropulse fluences of 7.8 and 6.7 J/cm2, respectively. Under these conditions, a 0.5-μm thick film can be grown in less than 5 min. Film structure was determined from infrared absorbance measurements and gel permeation chromatography (GPC). While the infrared absorbance spectrum of the films is nearly identical with that of the native polymer, the average molecular weight of the films is a little less than half that of the starting material. Potential strategies for defeating this mass change are discussed.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 22 August 2001 / Accepted: 23 August 2001 / Published online: 17 October 2001
Rights and permissions
About this article
Cite this article
Bubb, D., Toftmann, B., Haglund, Jr., R. et al. Resonant infrared pulsed laser deposition of thin biodegradable polymer films. Appl Phys A 74, 123–125 (2002). https://doi.org/10.1007/s003390101010
Published:
Issue Date:
DOI: https://doi.org/10.1007/s003390101010