Summary
The thermal properties of an epoxy resin (diglycidyl ether Bisphenol A, DGEBA) cured with a primary amine (ethylenediamine, ETDA) and filled with 10, 20 and 30 wt. % of ultra fine copper particles were analyzed. The thermal results were evaluated by means of the Romero-Garcia method, which allowed to obtain the resin degradation kinetic parameters, as well as the possible decomposition mechanism. From the obtained results is possible to infer that higger copper content strongly affects the degradation process of the epoxy resin, which causes a drop off on the composites thermal stability. This behavior could be attributed to water presence, being this effect less pronounced for the resin with 10 wt. % copper and unfilled resin. Regarding to decomposition mechanism, three way transport showed the best correlation for all samples.
Similar content being viewed by others
References
Brito Z, Sánchez G (2000) Composite Structures 48:79
Love BJ, Packme PF (1998) J. Materials Science 33:1559
Nakamura Y, Yamaguchi M, Okubo M, Matsumoto M (1992) J Appl Polym Sci 44:151
Hong SG, Wang TC (1994) J Appl Polym Sci 52:1339
Sánchez MC (2002) Postgraduate Thesis Venezuela
Romero S, García E (1984) Thermochimica Acta 73:101
Orfao JJM, Martins FG (2002) Thermochimica Acta 390:195
Patel RD, Patel RG, Patel VS (1987) Berit. Polym J 19:37
Jenkins R, Karre LR (1966) J Appl Polym Sci 10:303
Schmidt RG, Bell JP (1986) “Epoxy adhesion to metals”, in Advances in Polymer Science, 75, Springer Verlag, Berlin
Andrews EH, King NE (1976) J Materials Sci 11:2004
Bolger JC (1972) “The chemical composition of metal and oxide surfaces and how theses interact with polymeric materials”, 30th An. Tech. Conf. PE, Chicago
Kerr C, MacDonald NC, Orman S (1967) J Appl Chem 17:62
Delollis NJ, Montaya O (1967) J Appl Polym Sci 11:983
Gledhill RA, Kinloch AJ (1979) Polymer Eng Sci 19:82
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Albano, C., Brito, Z., Paredes, H. et al. Application of Romero García method to the degradation process of DGEBA/ETDA filled with ultra fine metallic copper. Polym. Bull. 54, 399–407 (2005). https://doi.org/10.1007/s00289-005-0394-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-005-0394-1