Effects of drawing on molecular motions in polycarbonate

Summary

The effect of drawing on the molecular motions in amorphous polycarbonate is studied by the dielectric relaxation with following conclusions.

• (1) A structural model for the drawn polycarbonate is obtained from the data of the density, the birefringence and the height of the endothermic peak atT _g . The molecular chains of polycarbonate are supposed to be oriented to the draw direction and packed closely by drawing. No process similar to that in polyethylene terephthalate occurs in polycarbonate.

• (2) The rate of the torsional oscillation of the frozen chains in the glassy polycarbonate varies with the draw ratio. It decreases at first and then increases near the severance. This behavior can be explained by the local mode relaxation theory and the structural model proposed here.

• (3) The behavior of polycarbonate by drawing was compared with that of polyethylene terephtalate and discussed.

Zusammenfassung

Der Effekt der Verstreckung auf die molekularen Bewegungen im amorphen Polycarbonat wurde mit dielektrischen Messungen studiert. Folgende Schlüsse lassen sich ziehen:

• 1. Ein Strukturmodell für das verstreckte Polycarbonat läßt sich aus den Daten für die Dichte, die Doppelbrechung und die Höhe des endothermen Piks naheT _g erzwielen. Die molekuraren Ketten des Polycarbonate werden durch die Streckung dicht gepakt. Kein Prozeß ählich demjenigen in Polyänthylenterephthalat tritt in Polycarbonat auf.

• 2. Die Maximallage für ihre Absorption Polycarbonat verändert sich mit dem Streckenverhältnis. Sie sinkt zuerst und steigt dann in der Nähe der Streckgrenze an. Dieses Verhalten kann mittrels der Relaxations-theorie der lokalen Moden und des hier vorgeschlagenen Strukturmodells erkäkt werden.

• 3. Das Verhalten des Polycarbonats beim Verstrecken wird mit demjenigen des Polyänthylenterephthalats verglichen und diskutiert.