Abstract
The Co−Se phase diagram was constructed using results of thermal and X-ray investigations. For the thermal analyses a fully automaticDTA-apparatus for constant heating and cooling rates in the range 200 to 1100 °C was built. In addition to the miscibility gap in liquid cobalt-rich alloys previously reported there exists another miscibility gap in melts with more than 70 at %Se above 952 °C. The B8 (NiAs) phase Co1−x Se has a congruent melting point at 54,0 at % Se and 1078 °C and a maximal range of homogeneity between 50,7 at %Se (910 °C) and 59,0 at %Se (952 °C). The eutectic between Co1−x Se and α-Co occurs at 44,5 at %Se and 910 °C. CoSe2 decomposes peritectically at 938 °C into Co1−x Se and a Se-rich melt. X-ray investigations confirmed the existence of the three compounds Co9Se8, Co1−x Se, and CoSe2.
Zusammenfassung
Das Phasendiagramm Co−Se wurde auf Grund der Resultate thermischer und röntgenographischer Untersuchungen aufgestellt. Für die thermischen Analysen wurde eine vollautomatischeDTA-Anlage mit konstanten Heiz- und Kühlgeschwindigkeiten im Bereich von 200 bis 1100 °C konstruiert. Neben der schon früher gefundenen Mischungslücke in kobaltreichen Schmelzen tritt eine weitere Mischungslücke in Schmelzen mit mehr als 70 At %Se oberhalb 952 °C auf. Die B8(NiAs)-Phase Co1−x Se hat einen kongruenten Schmelzpunkt bei 54,0 At %Se und 1078 °C und eine maximale Phasenbreite von 50,7 At %Se (910 °C) bis 59,0 At %Se (952 °C). Das Eutektikum zwischen Co1−x Se und α-Co liegt bei 44,5 At %Se und 910 °C. CoSe2 zerfällt peritektisch bei 938 °C in Co1−x Se und eine Se-reiche Schmelze. Die röntgenographischen Untersuchungen bestätigten die Existenz der drei Verbindungen Co9Se8, Co1−x Se und CoSe2.
Similar content being viewed by others
Literatur
M. Hansen, Constitution of Binary Alloys, S. 502, New York: McGraw-Hill. 1958.
R. P. Elliott, Constitution of Binary Alloys, First Supplement, S. 334. New York: McGraw-Hill. 1965.
F. A. Shunk, Constitution of Binary Alloys, Second Supplement, S. 264. New York: McGraw-Hill. 1969.
U. Haschimoto, Nippon Kinzoku Gakkai-Shi2, 67 (1938).
L. D. Dudkin undV. I. Vaidanich, Soviet Physics-Solid State.2, 1384 (1961); Fiz. Tverd. Tela2, 1526 (1960).
I. Oftedal, Z. physik. Chem.128, 137 (1927).
W. F. de Jong undH. W. V. Willems, Physica7, 74 (1927).
W. F. de Jong undH. W. V. Willems, Z. anorg. allgem. Chem.170, 241 (1928).
S. Tengnér, Z. anorg. allgem. Chem.239, 126 (1938).
B. Lewis undN. Elliott, J. Amer. Chem. Soc.62, 3180 (1940).
F. Bøhm, F. Grønvold, H. Haraldsen undH. Prydz, Acta Chem. Scand.9, 1510 (1955).
N. G. Eror undJ. B. Wagner, Jr., Acta Met.11, 1339 (1963).
J. Körbl undW. Pribil, Chem. Listý51, 1061 (1957).
E. Hayer undG. Stummerer, Veröffentlichung in Arbeit, Universität Wien.
A. Taylor undH. Sinclair, Proc. Phys. Soc. [London]57, 108 (1945).
A. L. N. Stevels, Philips Res. Rep. Suppl. Nr. 9 (1969).
Author information
Authors and Affiliations
Additional information
Herrn Prof. Dr.O. Kratky zum 70. Geburtstag gewidmet.
Mit 4 Abbildungen
Rights and permissions
About this article
Cite this article
Komarek, K.L., Wessely, K. Übergangsmetall-Chalkogensysteme, 1. Mitt.: Das System Kobalt-Selen. Monatshefte für Chemie 103, 896–906 (1972). https://doi.org/10.1007/BF00905452
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00905452