Abstract
The temperature dependence of the Gibbs free energy difference (ΔG) between the undercooled liquid and the corresponding equilibrium solid has been analysed for metallic glass forming systems in the frame of the expression obtained by expanding free energies of the undercooled liquid and solid phases in the form of Taylor's series expansion. The enthalpy difference (ΔH) and the entropy difference (ΔH) between the undercooled liquid and solid phases have also been analysed. The study is made for five different metallic glass forming materials, Au77Ge13.6Si9.4, Au53.2Pb27.5Sb19.3, Au81.4Si18.6, Mg85.5Cu14.5 and Mg81.6Ga18.4 and a very good agreement is found between calculated and experimental values of ΔG. The ideal glass transition temperature (T k) and the residual entropy (ΔS R) of these materials have also been studied due to their important role in assigning the glass formation ability of materials.
Similar content being viewed by others
References
H. S. Chen and D. Turnbull, J. Appl. Phys., 38 (1967) 3636.
H. S. Chen and D. Turnbull, J. Chem. Phys., 48 (1968) 2560.
D. Turnbull, J. Appl. Phys., 21 (1950) 1022.
J. D. Hoffman, J. Chem. Phys., 29 (1958) 1192.
C. V. Thompson and F. Spaepen, Acta Metall., 27 (1979) 1855.
D. R. H. Jones and G. A. Chadwick, Phil. Mag., 24 (1971) 995.
S. Lele, K. S. Dubey and P. Ramachandrarao, Curr. Sci., 54 (1985) 994.
W. Kauzmann, Chem. Rev., 42 (1948) 219.
K. S. Dubey and P. Ramachandrarao, Bull. Mater. Sci., 15 (1992) 111.
K. S. Dubey, P. Ramachandrarao and S. Lele, Polymer, 28 (1987) 1341.
G. Adam and J. H. Gibbs, J. Chem. Phys., 43 (1965) 139.
K. S. Dubey and P. Ramachandrarao, Int. J. Rapid Solidification, 1 (1984–85) 1.
H. J. Fecht, J. H. Perepezko, M. C. Lee and W. L. Johnson, J. Appl. Phys., 68 (1990) 4494.
F. Sommer, G. Bucher and B. Predel, J. Phys. Colloq., 41 (1980) 563.
B. Predel and K. Hulse, J. Less Common Metals, 63 (1979) 245.
J. H. Perepezko, Rapid Solidification Processing, Principles and Technology II, edited by R. Mehrabian, B. H. Kear and M. Cohen (Baton Rouge, Lousisiana) 1980, p. 56.
J. H. Gibbs and E. A. DiMarzio, J. Phys., 28 (1958) 373.
B. Wunderlich, J. Phys. Chem., 64 (1960) 1052.
Author information
Authors and Affiliations
Additional information
The authors are grateful to Prof. P. Ramachandrarao, N. M. L. Jamshedpur and Prof. S. Lele, Department of Metallurgical Engineering, B. H. U. for their interest in the present work. The part of work was done under C. S. I. R. project and we are also thankful to C. S. I. R., New Delhi for financial support.
Rights and permissions
About this article
Cite this article
Mishra, R.K., Dubey, K.S. Analysis of thermodynamic parameters of glass forming metallic melts. Journal of Thermal Analysis 50, 843–856 (1997). https://doi.org/10.1007/BF01979214
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01979214