On zeophyllite from Radejčín, České středohoří Mts.: X-ray and IR-investigations

Summary

A redetermination of the crystal structure of zeophyllite, idealized Ca₁₃Si₁₀O₂₈F₁₀.6H₂O [a=9.377(2), c=36.57(2) Å; Z=3], space group R3 (No. 148) yielded R = 0.033 for 2238 observed single crystal X-ray data (Fo > 3σ_Fo). The atomic coordinates in combination with the anisotropic thermal displacement parameters as well as the internal R-value from merging equivalent intensities gave no evidence for a violation of trigonal symmetry. The structure is characterized by SiO₄ tetrahedra combined to open branched vierer single layers in an arrangement normal to the threefold axes. These layers are connected via the Ca(O,F)_x polyhedra and hydrogen bridges to a framework with a pronounced cleavage parallel to (00.1). The statistic . occurrence of Si-OH groups in parts of the structure was confirmed by IR-investigations.

Zusammenfassung

Eine Neubestimmung der Kristallstruktur an Zeophyllit, idealisiert Ca₁₃Si{ion10}O₂₈F₁₀· .6H20 [a=9.377(2), c=36.57(2) Å; Z=3], Raumgruppe R3 (No. 148), ergab R = 0.033 für 2238 beobachtete Röntgeneinkristalldaten (Fo > 3σ_Fo). Die Koordinaten der Atome in Verbindung mit den Parametern der anisotropen thermischen Schwingung sowie der interne R-Wert nach Mittelung äquivalenter Intensitäten ergaben keinen Anhaltspunkt für eine Verletzung der trigonalen Symmetrie. Die Struktur ist charakterisiert durch SiO₄-Tetraeder, verknüpft zu “open branched vierer single layers”, die normal zur dreizähligen Achse angeordnet sind. Diese Schichten werden über die Ca(O,F)_x Polyeder und Wasserstoffbrücken zu einem Gerüst mit ausgeprägter Spaltbarkeit parallel (00.1) verbunden. In der Struktur statistisch auftretende Si-OH-Gruppen konnten durch IR-Untersuchungen belegt werden.