Zemannite-type Selenites: Crystal structures of K₂[CO₂(SeO₃)₃] · 2H₂O and K₂[Ni₂(SeO₃)₃] · 2H₂O

Summary

Crystals of K₂[Co₂(SeO₃)₃]-2H₂O and K₂[Ni₂(SeO₃)₃]-2H₂O were synthesized under low-hydrothermal conditions. Their structures were determined using single crystal X-ray data up to sin Θ/λ = 0.7Å^-1. [Space group P6₃/m; a = 9.091(3),9.016(2)Å; c = 7.562(2), 7.476(2)Å; Z = 2; R_W = 1.6, 2.5%]. The investigations confirmed that K₂[Co₂(SeO₃)₃].2H₂O and K₂[Ni₂(SeO₃)₃]-2H₂O represent the first selenites belonging to the zemannite structure type, a framework structure with wide channels running parallel [0001]. In both compounds four maxima were clearly located in the channel by Fourier summations and attributed to two K atoms and two H₂O molecules, each with an occupancy factor of 1/6; a possible ordering scheme (full occupancy) with local symmetry 1 and [6]-coordinated K atoms could be derived for the channel atoms.

Zusammenfassung

Kristalle von K₂[Co₂(SeO₃)₃]-2H₂O und K₂[Ni₂(SeO₃)₃]-2H₂O wurden unter niedrig-hydrothermalen Bedingungen synthetisiert. Die Strukturen wurden unter Verwendung von Einkristallröntgendaten bis sin Θ/λ= 0.7Å^-1 bestimmt. [Raumgruppe P6₃/m; a = 9.091(3), 9.016(2)Å; c = 7.562(2), 7.476(2)Å; Z = 2; R_W = 1.6, 2.5%] Die Untersuchungen bestätigten, daß K2[Co₂(SeO₃)₃] - 2H₂O und K₂ [Ni₂(SeO₃)₃] - 2H₂O als erste Selenite dem Strukturtyp des Zemannits angehören, einer Gerüststruktur mit weiten, parallel [0001] verlaufenden Kanälen. In beiden Verbindungen wurden im Kanal vier Maxima durch Fourier-Summationen eindeutig lokalisiert und zwei Kalium-atomen sowie zwei H₂O Molekülen, jeweils mit einem Besetzungsfaktor von 1/6, zugeschrieben. Für die Kanalatome konnte ein möglicher Ordnungszustand (volle Besetzung) mit lokaler Symmetrie 1 und [6]-koordinierten Kaliumatomen abgeleitet werden.