Abstract
Germanium-silicon alloys of the composition Ge30Si70 have been prepared by hot pressing powder compacts at temperatures between 1300 and 1493 K (the solidus temperature) at pressures up to 40 MPa. The densification of the compacts was observed as a function of time. For each temperature and pressure an end-point density less than the full density was found. The time-dependence of the densification and the pressuredependence of the end-point density can be described empirically in terms of a plastic flow mechanism.
Similar content being viewed by others
References
J. P. Dismukes, L. Ekstrom, E. F. Steigmeier, I. Kudman and D. S. Beers, J. Appl. Phys. 35 (1964) 2899.
F. D. Rosi, Solid State Electronics 11 (1968) 833.
C. E. Kelly, Proceedings of the 10th Intersociety Energy Conversion Engineering Conference (Newark DE, IEEE, New York, 1975) p. 880.
D. M. Rowe, Proc. IEE. 125 (1978) 1113. IEE Reviews.
D. Abeles, D. S. Beers, G. D. Cody and J. P. Dismukes, Phys. Rev. 125 (1962) 44.
R. S. Erofeev, E. K. Iordanishvili and A. V. Petrov, Sov. Phys. Sol. Stat. 7 (1966) 2470.
O. A. Golikova, E. K. Iordanishvili and A. V. Petrov, ibid 8 (1966) 397.
B. Abeles, Phys. Rev. 131 (1963) 1906.
J. E. Parrott, Proc. Phys. Soc. 81 (1963) 726.
E. F. Steigmeier and B. Abeles, Phys. Rev. 136 (1964) A1149.
W. G. Pfann, “Liquid Metals and Solidification”, (American Society for Metals, Cleveland, Ohio, 1958) p. 233.
J. P. Dismukes and L. Ekstrom, Trans. Met. Soc. AIME 233 (1965) 672.
H. J. Goldsmid and A. W. Penn, Phys. Letters 27A (1968) 523.
J. E. Parrott, J. Phys. C: Sol. Stat. Phys. 2 (1969) 147.
N. Savvides and H. J. Goldsmid, Phys. Letters 41A (1972) 193.
C. M. Bhandari and D. M. Rowe, J. Phys. C: Sol. Stat. Phys. 11 (1978) 1787.
J. B. Huffadine, private communication.
D. M. Rowe and R. W. Bunce, J. Phys. D: Appl. Phys. 2 (1969) 1497.
Idem, J. Phys. E: Sci. Iustrum. 4 (1971) 902.
D. M. Rowe, J. Phys. D: Appl. Phys. 8 (1975) 1092.
R. A. Lefever, G. L. Mcvay and R. J. Baughman, Mat. Res. Bull. 9 (1974) 863.
P. R. Sahm and L. H. Gnau, Z. Metalk. 59 (1968) 137.
N. Savvides, Ph.D. Thesis, University of New South Wales, Australia (1978).
H. Stöhr and W. Klemm, Z. Anorg. Chem. 241 (1939) 313.
R. J. Baughman, G. L. Mcvay and R. A. Lefever, Mat. Res. Bull. 9 (1974) 685.
B. Chalmers, “Principles of Solidification” (Wiley, New York, 1964).
A. Smakula and V. Sils, Phys. Rev. 99 (1955) 1744.
J. P. Dismukes, L. Ekstrom and R. J. Paff, J. Phys. Chem. 68 (1964) 3021.
L. E. Cowles and L. A. Dauncey, J. Sci. Iustrum. 39 (1962) 16.
W. Gee and M. Green, J. Phys. E: Sci. Iustrum. 3 (1970) 135.
P. F. Kane and G. B. Larrabee, “Characterisation of Solid Surfaces” (Plenum Press, New York, London, 1974).
G. L. Mcvay, R. A. Lefever and R. J. Bauchman, Mat. Res. Bull. 9 (1974) 35.
J. C. Mcclelland, “Powder Metallurgy”, edited by W. Leszynski (Interscience, New York, 1961) p. 157.
J. K. Mackenzie and R. Shuttleworth, Proc. Phys. Soc. B. 62 (1949) 833.
P. Murray, E. P. Rodgers and A. E. Williams, “Practical and Theoretical Aspects of Hot Pressing of Refractory Oxides” AERE Rept. M/R 893.
J. R. Patel and A. R. Chaudhuri, J. Appl. Phys. 34 (1963) 2788.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Savvides, N., Goldsmid, H.J. Hot-press sintering of Ge-Si alloys. J Mater Sci 15, 594–600 (1980). https://doi.org/10.1007/BF00551721
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00551721