Summary
The bulk tensile behaviour of poly(ether ether ketone) and poly(ether imide) homopolymers and their blends has been investigated, and the temperature and strain rate dependence of the yield stress discussed in terms of simple Eyring rate theory. In fracture mechanics tests, the KIC of PEEK was found to decrease significantly with increasing test speed, whereas the KIC of PEI showed little rate sensitivity. Therefore, although a gradual increase in KIC with increasing PEEK content was observed in the blends at low loading rates, this effect was anticipated to be less pronounced at higher loading rates.
Similar content being viewed by others
References
Crevecoeur, G, Groenickx, G (1991) Macromolecules 24: 1190
Hsiao, BS, Sauer, BB (1993) J. Polym. Sci.-Polym. Phys. 31: 901
Chen, HL, Porter, RS (1992) Polym. Eng. Sci. 32: 1870
Lustig, SR, Van Alsten, JG, Hsiao, B (1993) Macromolecules 26: 3885
Harris, JE, Robeson, LM (1988) J. Appl. Polym. Sci. 35: 1877
Gensler, R, Plummer, CJG, Kausch, H-H, Münstedt, H, submitted to J. Mat. Sci.
Béguelin, Ph, Barbezat, M, Kausch, H-H (1991) J. Phys. III France 1: 1867
Ward, IM (1983) Mechanical Properties of Solid Polymers, John Wiley & Sons Ltd. Chichester, U.K.
Bauwens-Crowet, C, Bauwens, JC, Homes, G (1969) J. Polym. Sci. A-2 7: 735
Han, J, Yang, Y, Li, B, Feng, ZJ (1994) Appl. Polym. Sci. 54: 2045
Furukawa, J (1994) J. Appl. Polym. Sci. 51: 187
Chivers, RA, Moore, DR (1994) Polymer 35: 110
Cebe, P, Hong, S-D, Chung, S, Gupta, A (1987) In: Johnston, NJ (ed) ASTM STP 937, ASTM, Philadelphia (p342)
Kemmish, DJ, Hay, JN (1985) Polymer 26: 905
Lu, X, Weiss, RA (1992) Macromolecules 25: 3242
Chen, H-L, Porter, RS (1993) J. Polym. Sci.-Polym. Phys. 31: 1845
Gensler, R (1994) unpublished results
Béguelin, Ph, Kausch, H-H (1994) J. Mater. Sci. 29: 91
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gensler, R., Béguelin, P., Plummer, C.J.G. et al. Tensile behaviour and fracture toughness of poly(ether ether ketone)/poly(ether imide) blends. Polymer Bulletin 37, 111–118 (1996). https://doi.org/10.1007/BF00313826
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00313826