Abstract
Colored latexes with polyurea shell were prepared by applying interfacial polycondensation reaction to the miniemulsion polymerization process. These colored latexes were composed of polystyrene core and polyurea shell, and their particle size was adjusted to <100 nm. Diisocyanate was used as a hydrophobic monomer, and the equivalent mole of diamine was used as a hydrophilic monomer for interfacial polymerization. It was important to control the rate of interfacial polycondensation reaction in order to prepare small particles. Dye preservation property of colored latex loaded with oil-soluble dye was investigated. Polyurea shell formed at the surface of latex particles could restrain the migration of dyes from the latex particles and improve the dye preservation property. The ability to prevent dye migration depended on the composition of the polyurea shell.
Similar content being viewed by others
References
Antonietti M, Landfester K (2002) Prog Polym Sci 27:689–757
F Tiarks, K Landfester, and M Antonietti (2001) J Polym Sci Polym Chem 39:2520–2524
Takasu M, Shiroya T, Takeshita K, Sakamoto M, and Kawaguchi H (2003) Colloid Polym Sci 282:119–126
Takasu M, Shiroya T, Takeshita K, Sakamoto M, and Kawaguchi H (2004) Colloid Polym Sci 282:740–746
Kubo M, Harada Y, Kawakatsu T, and Yonemoto T (2001) J Chem Eng Japan 34(12):1506–1515
Mahabadi HK, Ng TH, Tan HS (1996) J Microencapsulation 13(5):559–573
Yadav SK, Ron N, Chandrasekharam D, Khilar KC, Suresh AK (1996) J Macromol Sci Phys B35(5):807–827
Ramarao C, Ley SV, Smith SC, Shirley IM, DeAlmeida N (2002) Chem Commun 10:1132–1133
Chern CS, Chen TJ, Liou YC (1998) Polymer 39(16):3767–3777
Chern CS, Lin CH (1998) Polymer 40:139–147
KuoYM, Wu CT, Wu WH, and Chao DY (1994) J Appl Polym Sci 52: 1165–1173
Hong K, Park S (2000) J Appl Polym Sci 78:894–898
Chao DY (1993) J Appl Polym Sci 47:645–651
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Takasu, M., Kawaguchi, H. Preparation of colored latex with polyurea shell by miniemulsion polymerization. Colloid Polym Sci 283, 805–811 (2005). https://doi.org/10.1007/s00396-004-1248-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00396-004-1248-3