Title:Decoration of growth sector boundaries with single nitrogen vacancy centres in as-grown single crystal HPHT synthetic diamond
View PDFAbstract:Large (> 100 mm$^3$), relatively pure (type II) and low birefringence single crystal diamond can be produced by high pressure high temperature (HPHT) synthesis. In this study we examine a HPHT sample of good crystalline perfection, containing less than 1 ppb (part per billion carbon atoms) of boron impurity atoms in the {001} growth sector and only tens of ppb of nitrogen impurity atoms. It is shown that the boundaries between {111} and {113} growth sectors are decorated by negatively charged nitrogen vacancy centres (NV$^-$): no decoration is observed at any other type of growth sector interface. This decoration can be used to calculated the relative {111} and {113} growth rates. The bulk (001) sector contains concentrations of luminescent point defects (excited with 488 and 532 nm wavelengths) below 10$^{11}$ cm$^{-3}$ (10$^{-3}$ ppb). We observe the negatively charged silicon-vacancy (SiV$^-$) defect in the bulk {111} sectors along with a zero phonon line emission associated with a nickel defect at 884 nm (1.40 eV). No preferential orientation is seen for either NV$^-$ or SiV$^-$ defects, but the nickel related defect is oriented with its trigonal axis along the <111> sector growth direction. Since the NV$^-$ defect is expected to readily re-orientate at HPHT diamond growth temperatures, no preferential orientation is expected for this defect but the lack of preferential orientation of SiV$^-$ in {111} sectors is not explained.
Submission history
From: Mark Newton Prof [view email][v1] Tue, 18 Feb 2020 21:10:56 UTC (1,284 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.