Strengthening Mechanisms in Low Carbon Lath Martensite as Influenced by Austenite Conditioning

Article Preview

Abstract:

Low carbon lath martensitic microstructures are used in various steel products requiring high strength and toughness. These microstructures are conventionally produced through re-austenitizing and quenching followed by low or high temperature tempering. It is also possible to produce lath martensite through direct quenching immediately following thermomechanical processing. In this study, deformation below the austenite recrystallization temperature before quenching to form martensite was simulated through laboratory scale Gleeble processing of a 0.2 weight percent carbon ASTM A514 steel microalloyed with up to 0.21 weight percent niobium. Thermomechanical processing generally increases the dislocation density of the as-quenched martensite, which is sensitive to the austenite grain size before thermomechanical processing. The hardness of the thermomechanically-processed steels is generally greater than steels austenitized at comparable temperatures without deformation; this hardness difference is attributed to the increase in dislocation density and increased lath misorientation in the thermomechanically-processed conditions. The hardness is generally independent of prior austenite grain size for the thermomechanically processed conditions in contrast to conventionally austenitized and quenched conditions, which have a Hall-Petch correlation with austenite grain size. The strength increase of the thermomechanically processed conditions compared to the conventionally austenitized and quenched conditions is maintained after tempering. However, there is a larger drop in strength for small prior austenite grain sizes for both conventionally austenitized and quenched and thermomechanically processed steels. Overall, the strength of these lath martensitic steels can be directly related to dislocation density through a Taylor hardening model.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

574-582

Citation:

Online since:

December 2018

Export:

Price:

* - Corresponding Author

[1] T. Maki, K. Tsuzaki, and I. Tamura, The morphology of microstructure composed of lath martensites in steels,, Transactions of the Iron and Steel Insitute of Japan, vol. 20, 1980, p.207–214.

DOI: 10.2355/isijinternational1966.20.207

Google Scholar

[2] G. Krauss, Tempering of Lath Martensite in Low and Medium Carbons Steels: Assessment and Challenges, Steel Research International, Vol. 88, No. 10, 2017.

DOI: 10.1002/srin.201700038

Google Scholar

[3] Proceedings of Physical Metallurgy of Direct-Quenched Steels, K. Taylor, S. Thompson, and F. Fletcher, editors, TMS, Warrendale, PA, (1993).

Google Scholar

[4] I. Tamura, C. Ouchi, T. Tanaka, and H. Sekine, Thermomechanical Processing of High Strength Low Alloy Steels. London: Butterworth, (1988).

DOI: 10.1016/b978-0-408-11034-1.50016-7

Google Scholar

[5] M. C. Somani, J. M. Pyykkönen, D. A. Porter, L. P. Karjalainen, J. I. Kömi, Influence of composition and prior deformation on phase transformation temperatures and hardness in direct quenching using physical simulation,, Materials Performance and Characterization, Vol. 4, 2015, pp.341-364.

DOI: 10.1520/mpc20150001

Google Scholar

[6] S. C. Kennett, G. Krauss, K. O. Findley, Prior austensite grain size and tempering effects on the dislocation density of low-C Nb-Ti microalloyed lath martensite,, Scripta Materialia, Vol. 107, 2015, pp.123-126.

DOI: 10.1016/j.scriptamat.2015.05.036

Google Scholar

[7] K. Taylor and S. Hansen, Structure and properties of some directly quenched martensitic steels, in Proceedings of the International Symposium on Accelerated Cooling of Rolled Plates, G. Ruddle and A. Crawley, editors, Pergamon Press. Elmsford, NY, 1988, pp.85-101.

DOI: 10.1016/b978-0-08-035770-6.50011-8

Google Scholar

[8] K. Taylor and S. Hansen, Effects of vanadium and processing parameters on the structures and properties of a direct-quenched low-carbon Mo-B steel,, Metallurgical Transactions, vol. 22A, 1991, pp.2359-2374.

DOI: 10.1007/bf02665002

Google Scholar

[9] K. Taylor and S. Hansen, Microstructure and mechanical properties of experimental low-carbon 0.5 Mo-Ti-B steels, in ref 3. pp.185-204.

Google Scholar

[10] K. Taylor, W. Furdanowicz, and S. Hansen, Precipitation of titanium-rich carbides in experimental low-carbon 0.5 Mo-Ti-B steels,, in ref 3. pp.17-38.

Google Scholar

[11] R. L. Bodnar, R. O. Adebanjo, and S. S. Hansen, Determination of the Tr and the Ar3 temperatures from roll force measurements,, in MWSP Conference Proceedings, 1996, p.743–757.

Google Scholar

[12] F. Boratto, R. Barbosa, S. Yue, and J. J. Jonas, Effect of chemical composition on the critical temperatures of microalloyed steels,, in International Conference on Physical Metallurgy of Thermomechanical Processing of Steels and Other Metals, 1988, p.383.

Google Scholar

[13] T. Revesz, T. Ungar, A. Borbely, and J. Lendvai, Dislocations and grain size in ball-milled iron powder,, Nanostructured Materials, vol. 7, no. 1, 1996, p.779–788.

DOI: 10.1016/s0965-9773(96)00048-7

Google Scholar

[14] S.C. Kennett, Ph.D. thesis, Colorado School of Mines, Golden, CO, (2014).

Google Scholar

[15] A. Baddeley, H. Gundersen, and L. Cruz-Orive, Estimation of surface area from vertical sections,, Journal of Microscopy, vol. 142, 1986, p.259–276.

DOI: 10.1111/j.1365-2818.1986.tb04282.x

Google Scholar

[16] T. Hanamura, S. Torizuka, S. Tamura, S. Enokida, and H. Takechi, effect of austenite grain size on transformation behavior," Microstructure and Mechanical Properties of 0 . 1C – 5Mn Martensitic Steel,, ISIJ International, vol. 53, no. 12, 2013, p.2218.

DOI: 10.2355/isijinternational.53.2218

Google Scholar

[17] S. Lee and Y. Lee, Effect of austenite grain size on martensitic transformation of a low alloy steel,, Materials Science Forum, vol. 475–479, 2005, p.3169–3172.

DOI: 10.4028/www.scientific.net/msf.475-479.3169

Google Scholar

[18] F. R. N. Nabarro, Z. S. Basinski, and D. B. Holt, The plasticity of pure single crystals,, Advances in Physics, vol. 13, no. 50, 1964, p.193–323.

DOI: 10.1080/00018736400101031

Google Scholar

[19] J. W. Hutchinson, Plastic deformation of bcc polycrystals,, Journal of the Mechanics and Physics of Solids, vol. 12, 1964, p.25–33.

Google Scholar

[20] G. Speich, A. Schwoeble, and W. Leslie, Elastic constants of binary iron-base alloys,, Metallurgical Transactions, vol. 3, no. August, p.2031–2037, (1972).

DOI: 10.1007/bf02643211

Google Scholar

[21] R. N. Caron and G. Krauss, The tempering of Fe-C lath martensite,, Metallurgical Transactions, vol. 3, 1972, p.2381–2389.

DOI: 10.1007/bf02647041

Google Scholar

[22] C. A. Apple, R. N. Caron, and G. Krauss, Packet microstructure in Fe-0.2 pct C martensite,, Metallurgical Transactions, vol. 5, 1974, p.593–599.

DOI: 10.1007/bf02644654

Google Scholar

[23] X. Huang, S. Morito, N. Hansen, and T. Maki, Ultrafine structure and high strength in cold-rolled martensite,, Metallurgical and Materials Transactions A, vol. 43, no. 10, 2012, p.3517–3531.

DOI: 10.1007/s11661-012-1275-5

Google Scholar