Formation of Structurally Complex U-Phase in Al72Pd12.8Co15.2 Alloy
Abstract:
The U-phase in the Al72Pd12.8Co15.2 alloy was studied under non-equilibrium (casting, differential thermal analysis) and near-equilibrium (long-term annealing) conditions to consider its compositional homogeneity. In the investigation, scanning electron microscopy including energy dispersive X-ray spectroscopy, X-ray diffraction, transmission electron microscopy, and differential thermal analysis were used. Contrary to the finding reported for the Al69.8Pd13.8Co16.4 alloy, the results obtained for the investigated Al72Pd12.8Co15.2 alloy did not confirm the compositional heterogeneity of the near-equilibrium U-phase after annealing at 700°C for 2000 h and at 850°C for 500 h.