Next Article in Journal
Targeted Gold Nanoparticle–Oligonucleotide Contrast Agents in Combination with a New Local Voxel-Wise MRI Analysis Algorithm for In Vitro Imaging of Triple-Negative Breast Cancer
Next Article in Special Issue
Evolution of Hair Treatment and Care: Prospects of Nanotube-Based Formulations
Previous Article in Journal
Aggregation-Induced Emission (AIE)-Labeled Cellulose Nanocrystals for the Detection of Nitrophenolic Explosives in Aqueous Solutions
Previous Article in Special Issue
Directly Grown Multiwall Carbon Nanotube and Hydrothermal MnO2 Composite for High-Performance Supercapacitor Electrodes
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 9
Issue 5
10.3390/nano9050708
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Antimicrobial Applications of Clay Nanotube-Based Composites

by
Anna Stavitskaya
1,†,
Svetlana Batasheva
2,†,
Vladimir Vinokurov
1,
Gölnur Fakhrullina
1,2,
Vadim Sangarov
1,
Yuri Lvov
3 and
Rawil Fakhrullin
2,*
1
Functional Aluminosilicate Nanomaterials Lab, Gubkin University, 119991 Moscow, Russian Federation
2
Bionanotechnology Lab, Institute of Fundamental Medicine and Biology, Kazan Federal University, 420008 Kazan, Republic of Tatarstan, Russian Federation
3
Institute for Micromanufacturing, Louisiana Tech University, Ruston, LA 71270, USA
*
Author to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Nanomaterials 2019, 9(5), 708; https://doi.org/10.3390/nano9050708
Submission received: 16 April 2019 / Revised: 28 April 2019 / Accepted: 30 April 2019 / Published: 7 May 2019
(This article belongs to the Special Issue Nanotubes for Health, Environment and Cultural Heritages)
Browse Figures
Versions Notes

Abstract

:
Halloysite nanotubes with different outer surface/inner lumen chemistry (SiO2/Al2O3) are natural objects with a 50 nm diameter hollow cylindrical structure, which are able to carry functional compounds both inside and outside. They are promising for biological applications where their drug loading capacity combined with a low toxicity ensures the safe interaction of these nanomaterials with living cells. In this paper, the antimicrobial properties of the clay nanotube-based composites are reviewed, including applications in microbe-resistant biocidal textile, paints, filters, and medical formulations (wound dressings, drug delivery systems, antiseptic sprays, and tissue engineering scaffolds). Though halloysite-based antimicrobial materials have been widely investigated, their application in medicine needs clinical studies. This review suggests the scalable antimicrobial nano/micro composites based on natural tubule clays and outlines research and development perspectives in the field.

1. Introduction

Antimicrobial agents have abundant formulations, found in various applications in food packaging, medical equipment, fabrics, polymers, paints, cosmetics, and even food. The production of materials with antibacterial properties is growing year by year. Industries need antimicrobials to ensure the safety of products and to prevent infections [1]. Together with the use of antibiotics for agricultural productions, the food industry demands new packaging materials with microbe-resistant properties, to guarantee the quality of products for a longer time. The fabrication of sustainable antimicrobial materials for medicine is crucially important, because of a growing number of hospital-acquired infections worldwide [2,3,4,5]. Removing microbes from the surfaces of medical equipment is challenging because of the microbial biofilm formation and complex multi- microbial systems allowing for the survival of persistent bacteria, even in the presence of antibiotics [6]. Infectious diseases associated with the formation of microbial biofilms on implantable medical devices seriously threaten patients and require recurrent operations in order to replace the infected device [7], making prevention of biofilm formation a high priority task.
The development of novel and long-lasting antibacterial materials should be performed in a careful and intelligent way. Currently, uncontrolled overuse of antibiotics has led to their accumulation in the environment and the appearance of new species resistant to antibiotic treatment [8,9,10,11,12,13]. Pharmaceuticals such as amoxicillin, erythromycin, triclosan, trimethoprim, and sulfamethoxazole are commonly detected in surface waters and soil [14]. The big challenge is the efficient disinfection of wastewater from farms and chicken plants, where a high organic content catalyzes bacterial growth and biofilm formations.
Therefore, the development of efficient and eco-friendly antimicrobial materials, which allow a decrease in uncontrolled antibiotic application while working for a longer time, is urgently needed. Clay minerals have been used in healing since early history. Aluminosilicates such as kaolinite, montmorillonite, and sepiolite are widely applied in industries, their properties and antibacterial composites based on this are reviewed in [15]. Iron-rich forms of clays (smectite, illite, etc.) are known to be active against human bacterial pathogens, and even drug resistant [16,17]. Chemical structures of clays such as imogolite (Al/Si-nanotube) make it antibacterial, due to the sorption of metals such as Fe, Co, Cu, and Zn, and its inner Al-rich surface [18]. Here, we cover the development and applications of antimicrobial materials using naturally-occurring tubular nanoclays. Halloysite clay nanotubes serve as a delivery vehicle for loaded bioactive compounds, helping to reduce the amount of antibiotics used by their controlled time-extended release.
Nanosized tubular halloysite (also termed halloysite nanotubes (HNTs)) is a dioctahedral 1:1 clay mineral of the kaolin group [19]. Its tubular structure was confirmed with transmission electron microscopy (TEM) and scanning electron microscopy (SEM). This multilayer tubular structure results in the rolling of aluminosilicate sheets under favourable geological conditions [19]. Transmission and scanning electron microscopy and atomic force microscopy images of halloysite are shown in Figure 1. Large halloysite deposits, allowing for the supply of hundreds of tons of the pure product, are found in Australia, the United States, China, New Zealand, and Turkey, although small amounts of halloysite nanotubes may be found at any kaolin deposit [20,21]. Halloysite tubes vary in length from 0.4 to 2 µm, in external diameter from 40 to 100 nm, and in internal diameter from 10 to 40 nm, but commercially available are 40–60 nm diameter and 0.5–1 µm length nanotubes [21,22,23].
The long history of human exposure to kaolin-type clay materials suggests the low cytotoxicity and high biocompatibility of these natural nanotubes, which was later proven in numerous experiments. Halloysite was found to be nontoxic for mammalian cells [24,25], nematodes [26], protozoa [27], bacterial [28], and yeast [29] cells, and was also tested as a food additive for mice, chicken, and piglets [17]. The nanosafety of halloysite favours its applications in materials intended to be in contact with humans and other organisms.
The chemical structure of halloysite, with a negative external surface composed of Si–O–Si and Si–OH and a positive internal surface of Al2O3 and Al–OH (at pH up to 8.5), makes it an appropriate template for the adsorption of both positively and negatively charged molecules and nanoparticles.
Halloysite is a potent candidate for the development of antibacterial coatings and paints, due to its hollow structure which is capable of encasing antiseptics and tuneable surface properties. One of the most convenient features of the clay nanotubes is that they do not need expensive and high energy consuming processes of exfoliation. Halloysites do not stack one to another like plates of kaolin, bentonite, or montmorillonite, and may be used as a powder, or an aqueous or paint dispersion. A number of reports are focused on producing polymer films and membranes with antibacterial compounds loaded inside halloysites [17].
Apparently, the idea of antibiotics encapsulation into clay nanotubes was proposed by Price, and Lvov, et al., [30,31,32], and these pioneering publications were followed by many others. The nanotube loading required mixing clay with a drug solution in water, alcohol, or acetone, taken at the highest concentrations, followed by the application of vacuum/air cycles and water washing at the end to remove the externally adsorbed molecules. In some cases, loading was performed from the drug melt. This process allowed for loading the nanotube lumen with 10–15 wt % of antibiotics or other drugs. Such formulations could be stored in dry state for years, and allowed for slow drug release within 10–20 h when placed in water. Additional coating of the loaded halloysites with polymers (e.g., dextran) or their embedding in polymers allowed the extension of the release to weeks and months.
One of the most promising applications of clay nanotubes is drug delivery. It is now generally accepted that rod-shaped nanoparticles are internalized in cells more efficiently than spherical ones [33,34,35]. The encapsulation of antibiotics into nanotubes allows for localized drug delivery, and limits undesirable side effects while ensuring the protection of sensitive drugs against oxidative or strongly acidic in vivo environments [36]. Functionalised nanotubes might be able to target specific cells, become ingested, and then release their contents in response to a chemical trigger [36,37]. This makes them promising for the creation of composite materials for bone [38,39] and tissue engineering [40,41], drug immobilization, and target delivery [42,43,44,45]. Several drugs were used in halloysite encapsulation: antibiotics—khellin, oxytetracycline, gentamicin, ciprofloxacin, vancomycin, atorvastatin, and metronidazole; and antiseptics—povidone iodine, amoxicillin, Brilliant green, chlorhexidine, salicylic acid, as well as dexamethasone, doxorubicin, furosemide, nifedipine, curcumin, resveratrol, and others. Novel drug delivery systems based on halloysite or its composite materials were reported, with an emphasis on topical formulations [21,46,47,48]. The only limitation for halloysite antibacterial composite applications in medicine is the restriction on intravenous injections due to slow nanoclay biodegradation and a lack of data on the halloysite injection influence on organisms.

2. Clay Nanotubes Loading with Antimicrobial Agents

2.1. Loading of Organic Compouds Inside Clay Nanotubes

Two approaches are generally accepted to impart antibacterial properties to halloysite nanotubes: (a) loading of organic molecules inside halloysite lumen and adsorption on the external surface (Figure 2), and (b) outside grafting (Figure 2).
Adsorption on halloysite and loading functional agents inside the nanotubes may be achieved by their stirring in drug solutions, assisted with sonication and vacuuming. The loading efficiency depends on the procedure and the charge and size of the molecule. Widely utilized chemicals such as chlorhexidine, povidone iodine, brilliant green, iodine, doxycyclin, amoxicillin, vancomicin, potassium calvulanate, gentamicin sulfate, and tetracyclin were loaded inside halloysite using sonication and vacuum [38,49,50,51,52,53]. Drug loaded halloysite was applied to produce antibacterial composites for bone regeneration, alginate-based wound dressing, electrospun membrane, and nanofibers [54,55,56,57]. Drug release kinetics is the most important parameter for long lasting antibacterial properties. The most practical and common anti-bacterial drugs are cationic chlorhexidine, anionic povidone iodine, and amoxicillin, the chemical structures of which are shown in Figure 3.
An investigation of chlorhexidine gluconate loading inside halloysite was performed in [58]. Though chlorhexidine gluconate has a positive charge, it was successfully loaded inside the nanotubes. The obtained composite showed a sustained drug release with a dialysis bag method; only 25% of chlorhexidine gluconate was released from the nanotubes within the first hour. By contrast, within the first hour, 75% of the unloaded drug was released from its untreated micropowder. Chlorhexidine gluconate loaded inside nanotubes was introduced into cotton fabric coating, to improve its antibacterial properties without the use of silver particles [59]. After coating, the fabric exhibited over 98% bacterial reduction for Staphylococcus aureus, Escherichia coli, and Pseudomonas aeruginosa. Even after 20 washes it showed 90% antibacterial activity, presumably due to a slow release of chlorhexidine gluconate from the nanotubes.
Povidone-iodine and amoxicillin have also been investigated for slower drug release [49]. In our study, we used saturated solutions of povidone iodine (80 mg/mL in water) and amoxicillin (50 mg/mL in ammonium hydroxide). Halloysite was added to the drug solutions and stirred to obtain homogeneous suspensions. The suspensions were placed in a vacuum for three cycles, 1 h each, to ensure maximum loading. Then the halloysite was washed twice to remove any excess/external drug, dried in a vacuum desiccator overnight, and powdered. Such powder formulations may be stored for a long time and dispersed in water with mechanical stirring before usage. Drug loading efficiency was determined by thermogravimetric analysis (TGA), as shown in Figure 4a,b. The drug release was analysed with a UV-Vis spectrophotometer at 224 nm (povidone iodine), and 227 nm (amoxicillin). The TGA curves showed 7.6 and 8.3 wt % of povidone-iodine and amoxicillin loading in halloysite. The loading could be increased with lumen enlarging by inner alumina etching in sulfuric acid. The release kinetics (Figure 4c,d) show the antiseptic extended release during 6–20 h. The formulations were efficient for the inhibition of S. aureus and E. coli for over one week.
Such formulations are also perspective for sprays, when clay nanotubes loaded with antiseptics are used in 3–5 wt % aqueous suspension and after being sprayed form thin coatings with prolonged antimicrobial activity.
The halloysite/salicylic acid system resulted in stable water suspension with a slow release of salicylic acid (over 50 h) [60]. The salicylic acid released from clay tubes showed an antibacterial activity at lower concentrations than free salicylic acid, likely due to the close contact or penetration of halloysite nanotubes in bacteria.
The efficiency reached 15 wt % when vancomycin was loaded in halloysite from a saturated solution [52]. The released drug exhibited high antibacterial activity to S. aureus and B. streptococcus, even after the long period of 33 days. The obtained system is proposed for bone and soft tissue infections treatment, where local antibiotic effect is needed.
Halloysite could be employed as a protecting carrier for chemically sensitive drugs and molecules. Ciprofloxacin attached to an APTES-functionalized halloysite helped to prevent complex formation with iron and other metal ions which are in contact with ciprofloxacin during drug delivery. The complexation studies between ciprofloxacin and iron revealed a 71 ± 1% decrease in undesirable drug absorbance [61]. Clay nanotubes were also investigated for the loading of volatile compounds, like essential oils, to prevent them from evaporation and losing antibacterial activity [62,63,64,65,66].
To reduce the release rate of drug molecules from clay nanotubes, the end-stoppers or polymer surface coating could be synthesized. Dextrin caps were formed on the nanotubes end to prevent early drug release (Figure 5) [67]. Benzotriazole–copper coating on halloysite nanotubes provided a more sustained release of brilliant green, extending it from 50 to 200 h [50]. In [65], thyme oil was encapsulated inside clay nanotubes and then caged inside using end-stoppers or surface coating. Both ends of the nanocapsules were capped with a sodium alginate-calcium chloride complex. Coating the negatively charged surface of untreated clay nanotubes was performed using the layer-by-layer method with positively charged polyethyleneimine. The surface coating of halloysite significantly extended the release behaviour of essential oils at room temperature over that of untreated and end-capped nanotubes.
A standard zone of inhibition assay was developed to compare the antibacterial action of the ciprofloxacin in solution and encapsulated in halloysite; in all cases, 5 µg of the antibiotic was loaded [21]. The size of the zone of inhibition indicates the effectiveness of the antibiotic and is often used as a quick test for the resistance of a strain. After each 24 h, the ciprofloxacin loaded discs were moved and added to a new spread plate to get a new zone of inhibition. Ciprofloxacin not loaded in the nanotubes worked only within 12 h. The nanotube formulations were effective over four days (Figure 6). This indicates a prolonged release that remains effective against multidrug resistant P. aeruginosa over an extended time. Even longer efficiency was observed when ciprofloxacin loaded halloysite was composited with bone implant cement polymethmetacrylate.
The exponential increase in bacterial resistance to chemical antibiotics and losing their effectiveness in the treatment of infections initiated the interest of researchers and pharmaceutical industries to the application of peptides as therapeutic antimicrobial agents [68]. Nicin and pediocin were successfully loaded inside halloysite [69]. The antimicrobial activity was better when halloysite nanotubes were used as a support agent rather than octadecylamine-modified montmorillonite or bentonite clays.

2.2. Grafting of Antimicrobial Nanoparticles on Clay Nanotubes Surfaces

The loading of organic antiseptics inside halloysite, with its further slow release, may have a limitation. It should be taken into consideration that the exposure of pathogens to progressively lower drug concentrations could become a risk factor for the selection of drug resistant strains. This is why other strategies should be developed. A possible issue lies in producing antibacterial composites with metals. Nanostructures containing silver, copper, zinc, iron oxides, and their combinations are well known for killing even antibiotic resistant bacteria, which is why they are widely applied for making materials with antibacterial properties [70,71,72,73,74,75]. The use of templates helps to overcome the aggregation of particles and their release to the environment. Halloysite has great potential as a carrier for metal particles grafting and metal complexes formation [76,77]. Possible metal/halloysite structures are shown in Figure 7, together with various mechanisms of killing pathogenic species.
Silver is a well-known antimicrobial metal. The vacuum loading and grafting of silver on/in modified clay nanotubes are common procedures, starting from [74].
Ag-nanorods were also synthesized inside the lumen of halloysite by thermal decomposition of silver acetate loaded from an aqueous solution [78]. Encasing silver inside the nanotubes allowed the prevention of colour changes in Ag-halloysite doped white paint, while the direct addition of silver nanoparticles converted the coating to a yellow-grey color. In [79], the dispersion of halloysite in a silver salt solution was kept in a vacuum for five cycles, followed by reduction with curcumin. Curcumin is not only a reducing agent, but it also possesses antibacterial activity against gram-positive and gram-negative bacteria. To enhance loading efficiency, an acid treatment of halloysite was used, creating new sites for metal cluster formation inside the tube’s lumen [80].
Modification of clay outer surfaces is another efficient way to decorate them with nanoparticles. In order to get the modified halloysite nanotubes loaded with silver nanoparticles, a series of reactions—including in situ polymerization—were suggested [81]. First, [3-(2-aminoethyl)aminopropyl trimethoxysilane (KH-792 silane) was bound to halloysite, followed by double-bond grafting using acryloyl chloride. Then poly(4-vinylpyridine) was formed on the surface using in-situ polymerization, with a final Ag attachment. A similar approach was proposed for Ag nanoparticles, where KH-792 silane was used as a complexation agent for ions [82]. The average diameter of particles formed after reduction was 5 nm. These materials showed good antibacterial activity against gram-negative bacteria (E. coli) and gram-positive bacteria (S. aureus).
In [83], chitosan was used to immobilize silver nanoparticles on halloysite because it is a good complexation agent that contains nitrogen atoms for binding silver ions through electron pair sharing. Chitosan helps to prevent the leaching of silver ions into the media. To graft chitosan, the surface of the halloysite was modified with 1,6-hexamethylene diisocyanate. Silver nitrate was used, and after the reduction of the silver–chitozan complex, silver nanoparticles of about 5 nm were observed on the tube’s surface. It is also possible to produce silver particles by wet impregnation on aminosilane-modified halloysite [84]; though the particle size distribution is broad and not many particles are attached, this procedure is one of the simplest.
In [72], ZnO nanoparticles were deposited on the outer and inner surfaces of halloysite nanotubes using a solvo-thermal method, and then incorporated into a polylactic acid matrix to give an antimicrobial membrane. Zinc oxide particle formation on clay tubular templates was also investigated in [85]. ZnO-Ag/halloysite composites for antibacterial applications were synthesized using thermal decomposition of zinc salt, followed by the reduction of the silver ions with NaBH4 [86]. CuO, TiO2, and Au nanoparticles were synthesised, exploiting halloysite surfaces as templates for the formation of metal nanoparticles and nanoclusters with tuneable properties [73].

3. Surfaces and Liquids Disinfection and Protection Using Clay Nanotubes-Based Antimicrobial Nanocomposites

One of the biggest problems in medical facilities is the growing number of hospital acquired infections. The World Health Organization reported that one of the most common routes for transmission of infectious diseases is by indirect contact with surfaces contaminated with infectious droplets produced by patients’ coughing, sneezing, and talking. Many microbes and viruses can survive for days on surfaces. Hand contact with contaminated surfaces (i.e., fomites) and subsequent transfer of microbes to the mucosal membranes of the mouth, nose, and eyes is the cause of many reported gastroenteritis outbreaks and other infections [87]. The efficacy of antimicrobial agents is seriously threatened by an alarming increase in microbial resistance. In 2016, the United Nations General Assembly adopted a political declaration giving full attention to antimicrobial resistance, following a call for global action by the World Health Organization. It has been recognized that rates of antibiotic resistance among bacteria are higher in developed nations, particularly in the US and Europe, which hinders long-time disinfection with standard methods, like wiping surfaces with disinfection solutions [88,89]. Formulations with sustained antiseptic delivery could be more efficient than today’s simple sprays like aqueous chlorine dioxide. In this regard, a number of long-lasting antimicrobial systems have been reported, including biocidal nanomaterials such as silver nanoparticles, light-activated photocatalysts based on TiO2, surface-tethered bactericides quaternary ammonium compounds, and phosphonium salts. These materials are effective against a wide spectrum of microorganisms. Halloysite loaded with drugs, or decorated with nanoparticles and compounded with paints, or incorporated into hydrophobic surface coating could become a good alternative to traditional disinfection procedures. Halloysite’s zeta-potential is ca. −30 mV, which does not allow for long stable aqueous dispersions, however, in many cases, internal nanotube loading with anionic drugs drastically increases the halloysite zeta-potential to −50–60 mV, making such formation of stable water-based dispersions applicable for convenient antibacterial sprays that are easily applied to surfaces.
Photo-induced degradation of bacteria using photocatalysts has been widely investigated for water purification. Halloysite nanotubes were applied as a support for photocatalytic nanoparticles, where they act as a stabilizer to prevent the aggregation of nanoparticles [90,91,92,93,94]. One of the most commonly used photocatalysts is TiO2 and its nanocomposites [95,96,97,98]. TiO2 only absorbs wavelengths in the near-UV region (λ < 400 nm), which is about 3% of the solar spectrum, and it cannot efficiently utilize visible light, which is about 43% of the solar spectrum, for photocatalytic disinfection [95]. Its modification may change the band gap and make it more efficient in visible light [98,99,100]. Photocatalytic systems based on halloysite and TiO2 were tested mainly for the degradation of pollutants and as a photocatalyst, but it could be used for antimicrobial applications too [93]. Antibacterial ZnO nanoparticles also act as photocatalysts in UV-light. In [85], ZnO nanoparticles adsorbed on halloysite were developed as a UV barrier for bacteria formation on membranes.
In [84], a role of the plasmonic excitation of silver nanoparticles decorating halloysite nanotubes in their bioactive properties is discussed. The optical absorption measurement revealed a broad plasmonic resonance in the region of 400–600 nm for halloysite with silver nanoparticles. The later samples exhibited a bactericidal effect, which is more pronounced under illumination. Therefore, Ag-functionalized clay seems to be promising for antibacterial treatments of liquids and surfaces stimulated by visible light exposure. Gold-nanoparticles could be applied in the same manner due to plasmonic effects. Halloysite-based core-shell structures with gold coating showed that the morphology, interconnectivity, and thickness of the Au shell define the optical response and photothermal capacity of plasmonic materials [101,102].

4. Application of Clay Nanotube-Based Antibacterial Composites

4.1. Bone and Tissue Engineering

Various functional materials containing halloysite loaded with antibacterial particles or drugs for medical application, coatings, and polymeric films have been developed recently. Nanofibers made with an electrospinning technique have been extensively studied for tissue engineering and other applications. Drug loaded fibers are not only biocompatible due to the polymers used, but also have antibacterial properties with slow drug release due to polymer degradation. Various halloysite-polymer composite fibers made using polylactic acid [54,103], polycaprolactone [49], poly(caprolactone)/gelatin [104] (Figure 8), and poly(lactic-co-glycolic acid) [57] were studied for antimicrobial protection.
In [57], electrospun poly(lactic-co-glycolic acid) nanofiber was modified with halloysite to make a drug delivery system with slow release of tetracycline hydrochloride. The drug loading efficiency was 42.65%. Halloysite loading leads to lower fiber diameter caused by the incorporation of positively charged tetracycline hydrochloride into the electrospinning solution. The tetracycline hydrochloride/halloysite/poly(lactic-co-glycolic acid) nanofibrous mats showed good cytocompatibility, and displayed effective antibacterial activity and ability to inhibit bacterial growth both in liquid and on solid mediums. The release percentages for nanofibrous mats with drug loaded halloysite during the 42 days were much lower than those of the nanofibers with pure drug and tetracycline hydrochloride/halloysite powder within the first day.
Guided tissue/bone regeneration membranes with sustained drug delivery were developed by electrospinning drug-loaded halloysite clay nanotubes doped into poly(caprolactone)/gelatin microfibers [104]. The use of 20 wt % nanotubes in fiber membranes allowed for 25 wt% metronidazole drug loading in the membrane.
Halloysite nanocontainers were used to obtain new dental materials with bioactive and antimicrobial properties, in order to improve clinical outcome in daily practice [105,106,107]. In [108], halloysite plays the role of a drug delivery system for dental implant coatings. The vancomycin loaded HNTs/chitosan composite coatings were electrophoretically deposited (EPD) from different alcoholic suspensions. Ethanol suspensions were selected as the optimum because of their high EPD rate, as well as the formation of coatings with relatively high roughness and high contents of adsorbed and non-adsorbed chitosan. The coating was characterized by burst release during the initial hours (3 h) after immersion in phosphate-buffered saline PBS and then long term slow release. Drug loaded coating showed higher antibacterial activity (about 27%) against S. aureus compared to the similar coating without loaded drugs.

4.2. Wound Dressing

Halloysite can be applied for making flexible multi-layer wound dressings that possess tuneable functionalities, including fluid absorption, antibacterial/fungal protection, and tissue regeneration. The dressing could be used for both prophylactic and therapeutic interventions, as a wound packing material, or as a topical gauze or pad. The addition of doped clay nanotubes provides enhanced dressing properties, the potential to load multiple drug sets, and increased control over the drug release kinetics (50+ hours, all these are favorable properties for the treatment of chronic unhealing wounds, multiple microbial infections, and for multi-vector treatments [49].
A dual drug co-delivery with elastic antibacterial nanocomposite was developed by combining ciprofloxacin and polymyxin B sulfate-loaded halloysite nanotubes into a gelatin elastomer. Ciprofloxacin nanoparticles which act against both gram-positive and gram-negative bacteria were dispersed directly in the matrix, and polymyxin B sulfate was loaded into halloysite and then distributed into the matrix. The effect of ciprofloxacin and polymyxin-loaded halloysite formulations on physical properties, cytotoxicity, fibroblast adhesion and proliferation, in vitro drug release, and antibacterial properties were investigated. Drug loaded halloysite not only enhanced the matrix tensile strength but also slowed down the release rate of the high dissoluble polymyxin B sulfate [109].

4.3. Filtration Membranes with Enhanced Antibacterial Activity

Filtration membranes doped with halloysite have been reported (Figure 9a). Membranes working in water, especially with high organic content, are hindered by biofouling, which decreases the membrane lifetime and increases energy consumption [110]. The inclusion of nanotubes functionalized with antibacterial agents helps to inhibit the development of biofilms. Halloysite was used for membrane preparation, allowing for sustained antimicrobial properties and preventing bio-contamination [72].
N-halamine@halloysite nanocomposites were synthesized and added at 1–3 wt% to a polyethersulfone filter membrane (Figure 9b) [107]. The hybrid membrane was thermos-mechanically stable, had lower surface roughness than the pure polyethersulfone membrane, and the water flux had been increased. The hydrophilicity of the membrane was also enhanced by the addition of halloysite. Immobilization of enzymes serving as natural antibacterial agents on clay nanotubes is another way to face the biofilm problem. Lysozyme was covalently grafted to halloysite functionalized with carboxylic groups, and was then added to polyethersulfone to prepare hybrid antibacterial ultrafiltration membranes [111]. The antibacterial tests revealed that hybrid halloysite membranes demonstrated a good antibacterial performance and were applicable for wastewater treatment.
Polyethersulfone ultrafiltration membranes bearing modified halloysite loaded with A- nanoparticles [81] and copper ions [112] were prepared via phase inversion. The Ag-nanoparticles were grafted as described earlier and the Cu2+-halloysite was synthesized by chemical modification of halloysite with silane, and then mixed with copper dichloride for complexing the Cu- ions. Tests showed that the hybrid membranes had a good antibacterial property, and the protective rates against E. coli and S. aureus were more than 99%.

4.4. Food Contact Materials

Food package materials like polymeric films are susceptible to bacteria colonization and biofilm formation. Meat, fish, cheese, bread, fruits, and vegetables are especially sensitive to bacteria and fungi. The development of polymer composites with antibacterial fillers preventing food from decay, and microorganism growth is very important. During recent years, various types of antimicrobial agents such as essential oils, plant extracts, and natural polymers have been tested in food packaging because of their minimal environmental impact and biodegradability [65,114,115]. Essential oils derived from plants are widely known for their activity, but they are difficult to incorporate into polymers due to their volatility.
Recent studies demonstrated that halloysite nanotubes can be used as active carriers, retaining essential oils during the high-temperature compounding of polymers and preserving high antimicrobial properties for a required time. Low-density polyethylene films containing carvacrol/halloysite showed sustained anti-microbial properties against E. coli and L. innocua, as well as fungicidal activity against A. alternata [64]. Carvacrol and thymol mixtures adsorbed on halloysite showed synergetic antibacterial effects after incorporation into an low-density polyethylene film intended for food package [63]. Carvacrol loaded inside nanotubes was incorporated into low-density polyethylene and ethylene vinyl alcohol copolymer films [62]. Multi-layered low-density polyethylene/ethylene vinyl alcohol copolymer films with loaded halloysite produced by a forced co-extrusion process exhibited a high carvacrol content despite the harsh conditions (200 °C and a long treatment time). Nanocomposites based on pectin-halloysite hybrids with rosemary oil also showed good potential for packaging [66]. Packaging paper containing thyme oil loaded halloysite exhibited strong antibacterial activity against E. coli for 10 days [65].
Table 1 shows a summary of antibacterial organic molecules loaded inside halloysite nanotubes using different procedures. The release kinetics of various agents from the organic–inorganic hybrids and composites based on loaded clay nanotubes are presented.

5. Conclusions

The loading of antibacterial chemicals inside natural halloysite clay nanotubes and capping them with end-stoppers or coatings allow for materials with slow release kinetics (days and weeks) and long-lasting effects. Due to high dispersibility and SiO2-surface chemistry, these nanotubes are a promising filler for composite materials with polymeric films and fibers, allowing for bacterial protection due to antiseptic release. Such nanocomposite formulations could be used for the preparation of wound dressings, fabric coatings, fibers for tissue engineering, and dental and suture materials. A very interesting and simple solution could be antibacterial sprays with water dispersions of halloysite loaded with antiseptics. These clay nanotubes are good candidates for drug delivery systems, especially when a topical effect is needed. Antibacterial halloysite formulations are currently tested, mostly in laboratories and their medical applications need more intensive clinical studies. One of the more significant deterrents limiting the use of such clay-based antimicrobial composites in clinical studies is the lack of cooperation between scientists working in the area of materials and composites preparation and in medical fields. To tackle this challenging issue, the communication between material science, medical science, and medical practices should be facilitated.

Author Contributions

Conceptualization: R.F., Y.L.; investigation: S.B., V.S.; writing—original draft preparation, A.S., G.F.; writing—review and editing: V.V., A.S., S.B., Y.L. and R.F.

Funding

The work of A. Stavitskaya and G. Fakhrullina is supported by the Russian Science Foundation under grant № 18-73-00342 and performed in Gubkin University. The work of S. Batasheva and R. Fakhrullin is supported by RFBR #18-53-80067 BRICS_t grant, the work is performed according to the Russian Government Program of Competitive Growth of Kazan Federal University.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Morais, D.S.; Guedes, R.M.; Lopes, M.A. Antimicrobial approaches for textiles: From research to market. Materials 2016, 9, 498. [Google Scholar] [CrossRef]
  2. Fridkin, S.K. Increasing prevalence of antimicrobial resistance in intensive care units. Crit. Care Med. 2001, 29, 64–68. [Google Scholar] [CrossRef]
  3. Revelas, A. Healthcare—Associated infections: A public health problem. Niger. Med. J. 2012, 53, 59–64. [Google Scholar] [CrossRef] [PubMed]
  4. Haque, M.; Sartelli, M.; McKimm, J.; Abu Bakar, M. Health care-associated infections—An overview. Infect. Drug Resist. 2018, 11, 2321–2333. [Google Scholar] [CrossRef] [PubMed]
  5. Mehta, Y.; Gupta, A.; Todi, S.; Myatra, S.; Samaddar, D.P.; Patil, V.; Bhattacharya, P.K.; Ramasubban, S. Guidelines for prevention of hospital acquired infections. Indian J. Crit. Care Med. 2014, 18, 149–163. [Google Scholar] [PubMed]
  6. Borges, A.; Saavedra, M.J.; Simoes, M. Insights on antimicrobial resistance, biofilms and the use of phytochemicals as new antimicrobial agents. Curr. Med. Chem. 2015, 22, 2590–2614. [Google Scholar] [CrossRef] [PubMed]
  7. Vasilev, K.; Cook, J.; Griesser, H.J. Antibacterial surfaces for biomedical devices. Expert Rev. Med. Devices 2009, 6, 553–567. [Google Scholar] [CrossRef]
  8. Bevan, E.R.; Jones, A.M.; Hawkey, P.M. Global epidemiology of CTX-M beta-lactamases: Temporal and geographical shifts in genotype. J. Antimicrob. Chemother. 2017, 72, 2145–2155. [Google Scholar] [CrossRef]
  9. Flandroy, L.; Poutahidis, T.; Berg, G.; Clarke, G.; Dao, M.C.; Decaestecker, E.; Furman, E.; Haahtela, T.; Massart, S.; Plovier, H.; et al. The impact of human activities and lifestyles on the interlinked microbiota and health of humans and of ecosystems. Sci. Total Environ. 2018, 627, 1018–1038. [Google Scholar] [CrossRef]
  10. Biel-Maeso, M.; Baena-Nogueras, R.M.; Corada-Fernandez, C.; Lara-Martin, P.A. Occurrence, distribution and environmental risk of pharmaceutically active compounds (phacs) in coastal and ocean waters from the gulf of cadiz (Sw Spain). Sci. Total Environ. 2018, 612, 649–659. [Google Scholar] [CrossRef] [PubMed]
  11. Bengtsson-Palme, J.; Kristiansson, E.; Larsson, D.G.J. Environmental factors influencing the development and spread of antibiotic resistance. FEMS Microbiol. Rev. 2018, 42. [Google Scholar] [CrossRef] [PubMed]
  12. Qiao, M.; Ying, G.G.; Singer, A.C.; Zhu, Y.G. Review of antibiotic resistance in china and its environment. Environ. Int. 2018, 110, 160–172. [Google Scholar] [CrossRef]
  13. Grenni, P.; Ancona, V.; Barra Caracciolo, A. Ecological effects of antibiotics on natural ecosystems: A review. Microchem. J. 2018, 136, 25–39. [Google Scholar] [CrossRef]
  14. Wilkinson, J.; Hooda, P.S.; Barker, J.; Barton, S.; Swinden, J. Occurrence, fate and transformation of emerging contaminants in water: An overarching review of the field. Environ. Pollut. 2017, 231, 954–970. [Google Scholar] [CrossRef] [PubMed]
  15. Maisanaba, S.; Pichardo, S.; Puerto, M.; Gutiérrez-Praena, D.; Cameán, A.M.; Jos, A. Toxicological evaluation of clay minerals and derived nanocomposites: A review. Environ. Res. 2015, 138, 233–254. [Google Scholar] [CrossRef]
  16. Haydel, S.E.; Remenih, C.M.; Williams, L.B. Broad-spectrum in vitro antibacterial activities of clay minerals against antibiotic-susceptible and antibiotic-resistant bacterial pathogens. J. Antimicrob. Chemother. 2007, 61, 353–361. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  17. Morrison, K.D.; Misra, R.; Williams, L.B. Unearthing the antibacterial mechanism of medicinal clay: A geochemical approach to combating antibiotic resistance. Sci. Rep. 2016, 6, 19043. [Google Scholar] [CrossRef]
  18. Williams, L.B.; Metge, D.W.; Eberl, D.D.; Harvey, R.W.; Turner, A.G.; Prapaipong, P.; Poret-Peterson, A.T. What makes a natural clay antibacterial? Environ. Sci. Technol. 2011, 45, 3768–3773. [Google Scholar] [CrossRef]
  19. Keeling, J. The Mineralogy, Geology and Occurrences of Halloysite; Apple Academic Press: Oakville, ON, Canada, 2015; pp. 96–115. [Google Scholar]
  20. Joussein, E.; Petit, S.; Churchman, J.; Theng, B.; Righi, D.; Delvaux, B. Halloysite Clay Minerals—A review. Clay Miner. 2005, 40, 383–426. [Google Scholar] [CrossRef]
  21. Lvov, Y.; Wang, W.C.; Zhang, L.Q.; Fakhrullin, R. Halloysite clay nanotubes for loading and sustained release of functional compounds. Adv. Mater. 2016, 28, 1227–1250. [Google Scholar] [CrossRef]
  22. Yuan, P.; Southon, P.D.; Liu, Z.; Green, M.E.; Hook, J.M.; Antill, S.J.; Kepert, C.J. Functionalization of halloysite clay nanotubes by grafting with γ-aminopropyltriethoxysilane. J. Phys. Chem. C 2008, 112, 15742–15751. [Google Scholar] [CrossRef]
  23. Yuan, P.; Tan, D.; Annabi-Bergaya, F.; Yan, W.; Liu, D.; Liu, Z. From platy kaolinite to aluminosilicate nanoroll via one-step delamination of kaolinite: Effect of the temperature of intercalation. Appl. Clay Sci. 2013, 83–84, 68–76. [Google Scholar] [CrossRef]
  24. Micó-Vicent, B.; Martínez-Verdú, F.M.; Novikov, A.; Stavitskaya, A.; Vinokurov, V.; Rozhina, E.; Fakhrullin, R.; Yendluri, R.; Lvov, Y. Stabilized dye–pigment formulations with platy and tubular nanoclays. Adv. Funct. Mater. 2018, 28, 1703553. [Google Scholar] [CrossRef]
  25. Kamalieva, R.F.; Ishmukhametov, I.R.; Batasheva, S.N.; Rozhina, E.V.; Fakhrullin, R.F. Uptake of halloysite clay nanotubes by human cells: Colourimetric viability tests and microscopy study. Nano-Struct. Nano-Obj. 2018, 15, 54–60. [Google Scholar] [CrossRef]
  26. Fakhrullina, G.I.; Akhatova, F.S.; Lvov, Y.M.; Fakhrullin, R.F. Toxicity of halloysite clay nanotubes in vivo: A caenorhabditis elegans study. Environ. Sci. Nano 2015, 2, 54–59. [Google Scholar] [CrossRef]
  27. Kryuchkova, M.; Danilushkina, A.; Lvov, Y.; Fakhrullin, R. Evaluation of toxicity of nanoclays and graphene oxide in vivo: A paramecium caudatum study. Environ. Sci. Nano 2016, 3, 442–452. [Google Scholar] [CrossRef]
  28. Von Klitzing, R.; Stehl, D.; Pogrzeba, T.; Schomäcker, R.; Minullina, R.; Panchal, A.; Konnova, S.; Fakhrullin, R.; Koetz, J.; Möhwald, H.; et al. Halloysites stabilized emulsions for hydroformylation of long chain olefins. Adv. Mater. Interfaces 2017, 4, 1600435. [Google Scholar] [CrossRef]
  29. Konnova, S.A.; Sharipova, I.R.; Demina, T.A.; Osin, Y.N.; Yarullina, D.R.; Ilinskaya, O.N.; Lvov, Y.M.; Fakhrullin, R.F. Biomimetic cell-mediated three-dimensional assembly of halloysite nanotubes. Chem. Commun. 2013, 49, 4208–4210. [Google Scholar] [CrossRef]
  30. Price, R.R.; Gaber, B.P.; Lvov, Y. In-vitro release characteristics of tetracycline hcl, khellin and nicotinamide adenine dineculeotide from halloysite; a cylindrical mineral. J. Microencapsul. 2001, 18, 713–722. [Google Scholar]
  31. Lvov, Y.; Price, R.; Gaber, B.; Ichinose, I. Thin film nanofabrication via layer-by-layer adsorption of tubule halloysite, spherical silica, proteins and polycations. Colloids Surf. A 2002, 198–200, 375–382. [Google Scholar] [CrossRef]
  32. Veerabadran, N.G.; Prise, R.R.; Lvov, Y.M. Clay nanotubes for encapsulation and sustained release of drugs. Nano 2007, 02, 115–120. [Google Scholar] [CrossRef]
  33. Sharma, G.; Valenta, D.T.; Altman, Y.; Harvey, S.; Xie, H.; Mitragotri, S.; Smith, J.W. Polymer particle shape independently influences binding and internalization by macrophages. J. Control. Release 2010, 147, 408–412. [Google Scholar] [CrossRef]
  34. Karaman, D.S.; Desai, D.; Senthilkumar, R.; Johansson, E.M.; Ratts, N.; Oden, M.; Eriksson, J.E.; Sahlgren, C.; Toivola, D.M.; Rosenholm, J.M. Shape engineering vs organic modification of inorganic nanoparticles as a tool for enhancing cellular internalization. Nanoscale Res. Lett. 2012, 7, 358. [Google Scholar] [CrossRef]
  35. Niskanen, J.; Zhang, I.; Xue, Y.; Golberg, D.; Maysinger, D.; Winnik, F.M. Boron nitride nanotubes as vehicles for intracellular delivery of fluorescent drugs and probes. Nanomedicine 2016, 11, 447–463. [Google Scholar] [CrossRef]
  36. Hilder, T.A.; Hill, J.M. Modeling the loading and unloading of drugs into nanotubes. Small 2009, 5, 300–308. [Google Scholar] [CrossRef]
  37. Aschberger, K.; Johnston, H.J.; Stone, V.; Aitken, R.J.; Hankin, S.M.; Peters, S.A.; Tran, C.L.; Christensen, F.M. Review of carbon nanotubes toxicity and exposure-appraisal of human health risk assessment based on open literature. Crit. Rev. Toxicol. 2010, 40, 759–790. [Google Scholar] [CrossRef]
  38. Wei, W.; Abdullayev, E.; Hollister, A.; Mills, D.; Lvov, Y.M. Clay nanotube/poly(methyl methacrylate) bone cement composites with sustained antibiotic release. Macromol. Mater. Eng. 2012, 297, 645–653. [Google Scholar] [CrossRef]
  39. Nair, B.P.; Sindhu, M.; Nair, P.D. Polycaprolactone-laponite composite scaffold releasing strontium ranelate for bone tissue engineering applications. Colloids Surf. B 2016, 143, 423–430. [Google Scholar] [CrossRef]
  40. Naumenko, E.A.; Guryanov, I.D.; Yendluri, R.; Lvov, Y.M.; Fakhrullin, R.F. Clay nanotube–biopolymer composite scaffolds for tissue engineering. Nanoscale 2016, 8, 7257–7271. [Google Scholar] [CrossRef]
  41. Liu, M.; He, R.; Yang, J.; Long, Z.; Huang, B.; Liu, Y.; Zhou, C. Polysaccharide-halloysite nanotube composites for biomedical applications: A review. Clay Miner. 2016, 51, 457–467. [Google Scholar] [CrossRef]
  42. Lvov, Y.M.; DeVilliers, M.M.; Fakhrullin, R.F. The application of halloysite tubule nanoclay in drug delivery. Expert Opin. Drug Deliv. 2016, 13, 977–986. [Google Scholar] [CrossRef]
  43. Sun, L.; Boyer, C.; Grimes, R.; Mills, D. Drug coated clay nanoparticles for delivery of chemotherapeutics. Curr. Nanosci. 2016, 12, 207–214. [Google Scholar] [CrossRef]
  44. Fizir, M.; Dramou, P.; Zhang, K.; Sun, C.; Pham-Huy, C.; He, H. Polymer grafted-magnetic halloysite nanotube for controlled and sustained release of cationic drug. J. Colloid Interface Sci. 2017, 505, 476–488. [Google Scholar] [CrossRef] [PubMed]
  45. Carazo, E.; Borrego-Sanchez, A.; Garcia-Villen, F.; Sanchez-Espejo, R.; Aguzzi, C.; Viseras, C.; Sainz-Diaz, C.I.; Cerezo, P. Assessment of halloysite nanotubes as vehicles of isoniazid. Colloids Surf. B 2017, 160, 337–344. [Google Scholar] [CrossRef] [PubMed]
  46. Li, X.; QianYang; Ouyang, J.; Yang, H.; Chang, S. Chitosan modified halloysite nanotubes as emerging porous microspheres for drug carrier. Appl. Clay Sci. 2016, 126, 306–312. [Google Scholar] [CrossRef]
  47. Yendluri, R.; Lvov, Y.; de Villiers, M.M.; Vinokurov, V.; Naumenko, E.; Tarasova, E.; Fakhrullin, R. Paclitaxel encapsulated in halloysite clay nanotubes for intestinal and intracellular delivery. J. Pharm. Sci. 2017, 106, 3131–3139. [Google Scholar] [CrossRef]
  48. De Kruif, J.K.; Ledergerber, G.; Garofalo, C.; Fasler-Kan, E.; Kuentz, M. On prilled nanotubes-in-microgel oral systems for protein delivery. Eur. J. Pharm. Biopharm. 2016, 101, 90–102. [Google Scholar] [CrossRef]
  49. Patel, S.; Jammalamadaka, U.; Sun, L.; Tappa, K.; Mills, D.K. Sustained release of antibacterial agents from doped halloysite nanotubes. J. Biosci. Bioeng. 2015, 3, 1. [Google Scholar] [CrossRef]
  50. Wei, W.; Minullina, R.; Abdullayev, E.; Fakhrullin, R.; Mills, D.; Lvov, Y. Enhanced efficiency of antiseptics with sustained release from clay nanotubes. RSC Adv. 2014, 4, 488–494. [Google Scholar] [CrossRef]
  51. Karnik, S.; Jammalamadaka, U.M.; Tappa, K.K.; Giorno, R.; Mills, D.K. Performance evaluation of nanoclay enriched anti-microbial hydrogels for biomedical applications. Heliyon 2016, 2, e00072. [Google Scholar] [CrossRef] [Green Version]
  52. Pan, Q.; Li, N.; Hong, Y.; Tang, H.; Zheng, Z.; Weng, S.; Zheng, Y.; Huang, L. Halloysite clay nanotubes as effective nanocarriers for the adsorption and loading of vancomycin for sustained release. RSC Adv. 2017, 7, 21352–21359. [Google Scholar] [CrossRef] [Green Version]
  53. Kelly, H.M.; Deasy, P.B.; Ziaka, E.; Claffey, N. Formulation and preliminary in vivo dog studies of a novel drug delivery system for the treatment of periodontitis. Int. J. Pharm. 2004, 274, 167–183. [Google Scholar] [CrossRef] [PubMed]
  54. Karolina Pierchala, M.; Makaremi, M.; Tan, H.L.; Janarthanan, P.; Muniyandy, S.; Solouk, A.; Mae Lee, S.; Pasbakhsh, P. Nanotubes in nanofibers: Antibacterial multilayered polylactic acid/halloysite/gentamicin membranes for bone regeneration application. Appl. Clay Sci. 2018, 160, 95–105. [Google Scholar] [CrossRef]
  55. Kurczewska, J.; Pecyna, P.; Ratajczak, M.; Gajecka, M.; Schroeder, G. Halloysite nanotubes as carriers of vancomycin in alginate-based wound dressing. Saudi Pharm. J. 2017, 25, 911–920. [Google Scholar] [CrossRef] [PubMed]
  56. Tohidi, S.; Ghaee, A.; Barzin, J. Preparation and characterization of poly(lactic-co-glycolic acid)/chitosan electrospun membrane containing amoxicillin-loaded halloysite nanoclay. Polym. Adv. Technol. 2016, 27, 1020–1028. [Google Scholar] [CrossRef]
  57. Qi, R.; Guo, R.; Zheng, F.; Liu, H.; Yu, J.; Shi, X. Controlled release and antibacterial activity of antibiotic-loaded electrospun halloysite/poly(lactic-co-glycolic acid) composite nanofibers. Colloids Surf. B 2013, 110, 148–155. [Google Scholar] [CrossRef]
  58. Wu, Y.; Yang, Y.; Liu, H.; Yao, X.; Leng, F.; Chen, Y.; Tian, W. Long-term antibacterial protected cotton fabric coating by controlled release of chlorhexidine gluconate from halloysite nanotubes. RSC Adv. 2017, 7, 18917–18925. [Google Scholar] [CrossRef] [Green Version]
  59. Benn, T.M.; Westerhoff, P. Nanoparticle silver released into water from commercially available sock fabrics. Environ. Sci. Technol. 2008, 42, 4133–4139. [Google Scholar] [CrossRef]
  60. Ghezzi, L.; Spepi, A.; Agnolucci, M.; Cristani, C.; Giovannetti, M.; Tiné, M.R.; Duce, C. Kinetics of release and antibacterial activity of salicylic acid loaded into halloysite nanotubes. Appl. Clay Sci. 2018, 160, 88–94. [Google Scholar] [CrossRef]
  61. Rawtani, D.; Pandey, G.; Tharmavaram, M.; Pathak, P.; Akkireddy, S.; Agrawal, Y.K. Development of a novel ‘nanocarrier’ system based on halloysite nanotubes to overcome the complexation of ciprofloxacin with iron: An in vitro approach. Appl. Clay Sci. 2017, 150, 293–302. [Google Scholar] [CrossRef]
  62. Krepker, M.; Zhang, C.; Nitzan, N.; Prinz-Setter, O.; Massad-Ivanir, N.; Olah, A.; Baer, E.; Segal, E. Antimicrobial ldpe/evoh layered films containing carvacrol fabricated by multiplication extrusion. Polymers 2018, 10, 864. [Google Scholar] [CrossRef] [PubMed]
  63. Krepker, M.; Shemesh, R.; Danin Poleg, Y.; Kashi, Y.; Vaxman, A.; Segal, E. Active food packaging films with synergistic antimicrobial activity. Food Control 2017, 76, 117–126. [Google Scholar] [CrossRef]
  64. Shemesh, R.; Krepker, M.; Natan, M.; Danin-Poleg, Y.; Banin, E.; Kashi, Y.; Nitzan, N.; Vaxman, A.; Segal, E. Novel ldpe/halloysite nanotube films with sustained carvacrol release for broad-spectrum antimicrobial activity. RSC Adv. 2015, 5, 87108–87117. [Google Scholar] [CrossRef]
  65. Jang, S.H.; Jang, S.R.; Lee, G.M.; Ryu, J.H.; Park, S.I.; Park, N.H. Halloysite nanocapsules containing thyme essential oil: Preparation, characterization, and application in packaging materials. J. Food Sci. 2017, 82, 2113–2120. [Google Scholar] [CrossRef]
  66. Gorrasi, G. Dispersion of halloysite loaded with natural antimicrobials into pectins: Characterization and controlled release analysis. Carbohydr. Polym. 2015, 127, 47–53. [Google Scholar] [CrossRef]
  67. Dzamukova, M.; Naumenko, E.; Lvov, Y.; Fakhrullin, R. Enzyme-activated intracellular drug delivery with tubule clay nanoformulation. Sci. Rep. 2015, 5, 10560. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  68. Rios, A.C.; Moutinho, C.G.; Pinto, F.C.; Del Fiol, F.S.; Jozala, A.; Chaud, M.V.; Vila, M.M.; Teixeira, J.A.; Balcao, V.M. Alternatives to overcoming bacterial resistances: State-of-the-art. Microbiol. Res. 2016, 191, 51–80. [Google Scholar] [CrossRef]
  69. Meira, S.M.; Jardim, A.I.; Brandelli, A. Adsorption of nisin and pediocin on nanoclays. Food Chem. 2015, 188, 161–169. [Google Scholar] [CrossRef] [Green Version]
  70. Moritz, M.; Geszke-Moritz, M. The newest achievements in synthesis, immobilization and practical applications of antibacterial nanoparticles. Chem. Eng. J. 2013, 228, 596–613. [Google Scholar] [CrossRef]
  71. Tolaymat, T.M.; El Badawy, A.M.; Genaidy, A.; Scheckel, K.G.; Luxton, T.P.; Suidan, M. An evidence-based environmental perspective of manufactured silver nanoparticle in syntheses and applications: A systematic review and critical appraisal of peer-reviewed scientific papers. Sci. Total Environ. 2010, 408, 999–1006. [Google Scholar] [CrossRef] [PubMed]
  72. De Silva, R.T.; Pasbakhsh, P.; Lee, S.M.; Kit, A.Y. Zno deposited/encapsulated halloysite–poly (lactic acid) (PLA) nanocomposites for high performance packaging films with improved mechanical and antimicrobial properties. Appl. Clay Sci. 2015, 111, 10–20. [Google Scholar] [CrossRef]
  73. Shu, Z.; Zhang, Y.; Ouyang, J.; Yang, H. Characterization and synergetic antibacterial properties of ZnO and CeO2 supported by halloysite. Appl. Surf. Sci. 2017, 420, 833–838. [Google Scholar] [CrossRef]
  74. Cervini-Silva, J.; Camacho, A.N.; Palacios, E.; del Angel, P.; Pentrak, M.; Pentrakova, L.; Kaufhold, S.; Ufer, K.; Ramírez-Apan, M.T.; Gómez-Vidales, V.; et al. Anti-inflammatory, antibacterial, and cytotoxic activity by natural matrices of nano-iron(hydr)oxide/halloysite. Appl. Clay Sci. 2016, 120, 101–110. [Google Scholar] [CrossRef]
  75. Karthikeyan, P.; Mitu, L.; Pandian, K.; Anbarasu, G.; Rajavel, R. Electrochemical deposition of a Zn-HNT/p(EDOT-co-EDOP) nanocomposite on LN SS for anti-bacterial and anti-corrosive applications. New J. Chem. 2017, 41, 4758–4762. [Google Scholar] [CrossRef]
  76. Vinokurov, V.A.; Stavitskaya, A.V.; Chudakov, Y.A.; Ivanov, E.V.; Shrestha, L.K.; Ariga, K.; Darrat, Y.A.; Lvov, Y.M. Formation of metal clusters in halloysite clay nanotubes. Sci. Technol. Adv. Mater. 2017, 18, 147–151. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  77. Lazzara, G.; Cavallaro, G.; Panchal, A.; Fakhrullin, R.; Stavitskaya, A.; Vinokurov, V.; Lvov, Y. An assembly of organic-inorganic composites using halloysite clay nanotubes. Curr. Opin. Colloid Interface Sci. 2018, 35, 42–50. [Google Scholar] [CrossRef]
  78. Abdullayev, E.; Sakakibara, K.; Okamoto, K.; Wei, W.; Ariga, K.; Lvov, Y. Natural tubule clay template synthesis of silver nanorods for antibacterial composite coating. ACS Appl. Mater. Interfaces 2011, 3, 4040–4046. [Google Scholar] [CrossRef]
  79. Sudhakar, K.; Moloi, S.J.; Madhusudhana Rao, K. Green synthesis and characterization of halloysite nanoclay/curcumin/Ag hybrid nano materials for antibacterial applications. J. Inorg. Organomet. Polym. Mater. 2017, 27, 1450–1456. [Google Scholar] [CrossRef]
  80. Ouyang, J.; Guo, B.; Fu, L.; Yang, H.; Hu, Y.; Tang, A.; Long, H.; Jin, Y.; Chen, J.; Jiang, J. Radical guided selective loading of silver nanoparticles at interior lumen and out surface of halloysite nanotubes. Mater. Des. 2016, 110, 169–178. [Google Scholar] [CrossRef]
  81. Zhang, J.; Zhang, Y.; Chen, Y.; Du, L.; Zhang, B.; Zhang, H.; Liu, J.; Wang, K. Preparation and characterization of novel polyethersulfone hybrid ultrafiltration membranes bending with modified halloysite nanotubes loaded with silver nanoparticles. Ind. Eng. Chem. Res. 2012, 51, 3081–3090. [Google Scholar] [CrossRef]
  82. Zhang, Y.; Chen, Y.; Zhang, H.; Zhang, B.; Liu, J. Potent antibacterial activity of a novel silver nanoparticle-halloysite nanotube nanocomposite powder. J. Inorg. Biochem. 2013, 118, 59–64. [Google Scholar] [CrossRef] [PubMed]
  83. Chen, Y.; Zhang, Y.; Zhang, H.; Liu, J.; Song, C. Biofouling control of halloysite nanotubes-decorated polyethersulfone ultrafiltration membrane modified with chitosan-silver nanoparticles. Chem. Eng. J. 2013, 228, 12–20. [Google Scholar] [CrossRef]
  84. Jana, S.; Kondakova, A.V.; Shevchenko, S.N.; Sheval, E.V.; Gonchar, K.A.; Timoshenko, V.Y.; Vasiliev, A.N. Halloysite nanotubes with immobilized silver nanoparticles for anti-bacterial application. Colloids Surf. B 2017, 151, 249–254. [Google Scholar] [CrossRef] [PubMed]
  85. Shankar, S.; Kasapis, S.; Rhim, J.W. Alginate-based nanocomposite films reinforced with halloysite nanotubes functionalized by alkali treatment and zinc oxide nanoparticles. Int. J. Biol. Macromol. 2018, 118, 1824–1832. [Google Scholar] [CrossRef] [PubMed]
  86. Shu, Z.; Zhang, Y.; Yang, Q.; Yang, H. Halloysite nanotubes supported ag and zno nanoparticles with synergistically enhanced antibacterial activity. Nanoscale Res. Lett. 2017, 12, 135. [Google Scholar] [CrossRef]
  87. Dancer, S.J.; White, L.F.; Lamb, J.; Girvan, E.K.; Robertson, C. Measuring the effect of enhanced cleaning in a uk hospital: A prospective cross-over study. BMC Med. 2009, 7, 28. [Google Scholar] [CrossRef]
  88. Li, Y.; Kin Leung, W.; Yeung, K.; Lau, A.; K C Kwan, J. A multilevel antimicrobial coating based on polymer-encapsulated ClO2. Langmuir 2009, 25, 13472–13480. [Google Scholar] [CrossRef]
  89. Leung, H.H.; Lai, C.K.; Yeung, K.L.; Kwan, J.K.; Tsang, D.N. Multilevel antimicrobial disinfectant coating in reducing the viability of multidrug-resistant organisms in hospital environment. Hong Kong Med. J. 2018, 24 (Suppl. 6), 37–39. [Google Scholar] [PubMed]
  90. Li, C.; Wang, J.; Feng, S.; Yang, Z.; Ding, S. Low-temperature synthesis of heterogeneous crystalline TiO2–halloysite nanotubes and their visible light photocatalytic activity. J. Mater. Chem. A 2013, 1, 8045–8054. [Google Scholar] [CrossRef]
  91. Papoulis, D.; Komarneni, S.; Nikolopoulou, A.; Tsolis-Katagas, P.; Panagiotaras, D.; Kacandes, H.G.; Zhang, P.; Yin, S.; Sato, T.; Katsuki, H. Palygorskite- and halloysite-TiO2 nanocomposites: Synthesis and photocatalytic activity. Appl. Clay Sci. 2010, 50, 118–124. [Google Scholar] [CrossRef]
  92. Mishra, G.; Mukhopadhyay, M. Flux improvement, rejection, surface energy and antibacterial properties of synthesized TiO2-Mo.HNTs/PVC nanocomposite ultrafiltration membranes. New J. Chem. 2017, 41, 15049–15057. [Google Scholar] [CrossRef]
  93. Pal, A.; Jana, T.K.; Roy, T.; Pradhan, A.; Maiti, R.; Choudhury, S.M.; Chatterjee, K. MoS2-TiO2 nanocomposite with excellent adsorption performance and high antibacterial activity. ChemistrySelect 2018, 3, 81–90. [Google Scholar] [CrossRef]
  94. Vinokurov, V.A.; Stavitskaya, A.V.; Ivanov, E.V.; Gushchin, P.A.; Kozlov, D.V.; Kurenkova, A.Y.; Kolinko, P.A.; Kozlova, E.A.; Lvov, Y.M. Halloysite nanoclay based cds formulations with high catalytic activity in hydrogen evolution reaction under visible light irradiation. ACS Sustain. Chem. Eng. 2017, 5, 11316–11323. [Google Scholar] [CrossRef]
  95. Hu, C.; Guo, J.; Qu, J.; Hu, X. Photocatalytic degradation of pathogenic bacteria with AgI/TiO2 under visible light irradiation. Langmuir 2007, 23, 4982–4987. [Google Scholar] [CrossRef]
  96. Tahir, K.; Ahmad, A.; Li, B.; Nazir, S.; Khan, A.U.; Nasir, T.; Khan, Z.U.H.; Naz, R.; Raza, M. Visible light photo catalytic inactivation of bacteria and photo degradation of methylene blue with Ag/TiO2 nanocomposite prepared by a novel method. J. Photochem. Photobiol. B 2016, 162, 189–198. [Google Scholar] [CrossRef] [PubMed]
  97. Eswar, N.K.; Ramamurthy, P.C.; Madras, G. Novel synergistic photocatalytic degradation of antibiotics and bacteria using V–N doped TiO2 under visible light: The state of nitrogen in V-doped TiO2. New J. Chem. 2016, 40, 3464–3475. [Google Scholar] [CrossRef]
  98. Fagan, R.; McCormack, D.E.; Dionysiou, D.D.; Pillai, S.C. A review of solar and visible light active TiO2 photocatalysis for treating bacteria, cyanotoxins and contaminants of emerging concern. Mater. Sci. Semicond. Process. 2016, 42, 2–14. [Google Scholar] [CrossRef]
  99. Elahifard, M.R.; Rahimnejad, S.; Haghighi, S.; Gholami, M.R. Apatite-coated Ag/AgBr/TiO2 visible-light photocatalyst for destruction of bacteria. J. Am. Chem. Soc. 2007, 129, 9552–9553. [Google Scholar] [CrossRef] [PubMed]
  100. Yang, X.; Qin, J.; Jiang, Y.; Chen, K.; Yan, X.; Zhang, D.; Li, R.; Tang, H. Fabrication of P25/Ag3PO4/graphene oxide heterostructures for enhanced solar photocatalytic degradation of organic pollutants and bacteria. Appl. Catal. B 2015, 166–167, 231–240. [Google Scholar] [CrossRef]
  101. Zieba, M.; Hueso, J.L.; Arruebo, M.; Martinez, G.; Santamaria, J. Gold-coated halloysite nanotubes as tunable plasmonic platforms. New J. Chem. 2014, 38, 2037–2042. [Google Scholar] [CrossRef]
  102. Rostamzadeh, T.; Islam Khan, M.S.; Riche’, K.; Lvov, Y.M.; Stavitskaya, A.V.; Wiley, J.B. Rapid and controlled in situ growth of noble metal nanostructures within halloysite clay nanotubes. Langmuir 2017, 33, 13051–13059. [Google Scholar] [CrossRef] [PubMed]
  103. Dong, Y.; Marshall, J.; Haroosh, H.J.; Mohammadzadehmoghadam, S.; Liu, D.; Qi, X.; Lau, K.-T. Polylactic acid (PLA)/halloysite nanotube (HNT) composite mats: Influence of hnt content and modification. Compos. Part A 2015, 76, 28–36. [Google Scholar] [CrossRef]
  104. Xue, J.; Niu, Y.; Gong, M.; Shi, R.; Chen, D.; Zhang, L.; Lvov, Y. Electrospun microfiber membranes embedded with drug-loaded clay nanotubes for sustained antimicrobial protection. ACS Nano 2015, 9, 1600–1612. [Google Scholar] [CrossRef]
  105. Cunha, D.A.; Rodrigues, N.S.; Souza, L.C.; Lomonaco, D.; Rodrigues, F.P.; Degrazia, F.W.; Collares, F.M.; Sauro, S.; Saboia, V.P.A. Physicochemical and microbiological assessment of an experimental composite doped with triclosan-loaded halloysite nanotubes. Materials 2018, 11, 1080. [Google Scholar] [CrossRef] [PubMed]
  106. Degrazia, F.W.; Genari, B.; Leitune, V.C.B.; Arthur, R.A.; Luxan, S.A.; Samuel, S.M.W.; Collares, F.M.; Sauro, S. Polymerisation, antibacterial and bioactivity properties of experimental orthodontic adhesives containing triclosan-loaded halloysite nanotubes. J. Dent. 2018, 69, 77–82. [Google Scholar] [CrossRef]
  107. Feitosa, S.A.; Munchow, E.A.; Al-Zain, A.O.; Kamocki, K.; Platt, J.A.; Bottino, M.C. Synthesis and characterization of novel halloysite-incorporated adhesive resins. J. Dent. 2015, 43, 1316–1322. [Google Scholar] [CrossRef] [PubMed]
  108. Farrokhi-Rad, M.; Fateh, A.; Shahrabi, T. Electrophoretic deposition of vancomycin loaded halloysite nanotubes-chitosan nanocomposite coatings. Surf. Coat. Technol. 2018, 349, 144–156. [Google Scholar] [CrossRef]
  109. Shi, R.; Niu, Y.; Gong, M.; Ye, J.; Tian, W.; Zhang, L. Antimicrobial gelatin-based elastomer nanocomposite membrane loaded with ciprofloxacin and polymyxin b sulfate in halloysite nanotubes for wound dressing. Mater. Sci. Eng. C 2018, 87, 128–138. [Google Scholar] [CrossRef]
  110. Zodrow, K.; Brunet, L.; Mahendra, S.; Li, D.; Zhang, A.; Li, Q.; Alvarez, P.J.J. Polysulfone ultrafiltration membranes impregnated with silver nanoparticles show improved biofouling resistance and virus removal. Water Res. 2009, 43, 715–723. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  111. Zhao, Q.; Liu, C.; Liu, J.; Zhang, Y. Development of a novel polyethersulfone ultrafiltration membrane with antibacterial activity and high flux containing halloysite nanotubes loaded with lysozyme. RSC Adv. 2015, 5, 38646–38653. [Google Scholar] [CrossRef]
  112. Chen, Y.; Zhang, Y.; Liu, J.; Zhang, H.; Wang, K. Preparation and antibacterial property of polyethersulfone ultrafiltration hybrid membrane containing halloysite nanotubes loaded with copper ions. Chem. Eng. J. 2012, 210, 298–308. [Google Scholar] [CrossRef]
  113. Duan, L.; Huang, W.; Zhang, Y. High-flux, antibacterial ultrafiltration membranes by facile blending with N-halamine grafted halloysite nanotubes. RSC Adv. 2015, 5, 6666–6674. [Google Scholar] [CrossRef]
  114. Huang, Y.; Mei, L.; Chen, X.; Wang, Q. Recent developments in food packaging based on nanomaterials. Nanomaterials 2018, 8, 830. [Google Scholar] [CrossRef]
  115. Gyawali, R.; Ibrahim, S.A. Natural products as antimicrobial agents. Food Control 2014, 46, 412–429. [Google Scholar] [CrossRef]
Nanomaterials 09 00708 g001 550
Figure 1. (a) Scanning electron microscopy (TEM), (b) atomic force microscopy (AFM), (c) transmission electron microscopy (TEM) images of halloysite. Reproduced with permission from [21], Copyright John Wiley and Sons, 2016.
Figure 1. (a) Scanning electron microscopy (TEM), (b) atomic force microscopy (AFM), (c) transmission electron microscopy (TEM) images of halloysite. Reproduced with permission from [21], Copyright John Wiley and Sons, 2016.
Nanomaterials 09 00708 g001
Nanomaterials 09 00708 g002 550
Figure 2. A scheme of antibacterial compound loading into halloysite lumens.
Figure 2. A scheme of antibacterial compound loading into halloysite lumens.
Nanomaterials 09 00708 g002
Nanomaterials 09 00708 g003 550
Figure 3. Chemical structure and zeta potential at pH 7 of commonly used antibacterial compounds.
Figure 3. Chemical structure and zeta potential at pH 7 of commonly used antibacterial compounds.
Nanomaterials 09 00708 g003
Nanomaterials 09 00708 g004 550
Figure 4. Thermogravimetric analysis (TGA) profiles of (a) povidone-iodine and (b) amoxicillin in halloysite, showing 7.6 and 8.3 wt % loading. Sustained release profiles of (c) povidone iodine and (d) amoxicillin from halloysite clay.
Figure 4. Thermogravimetric analysis (TGA) profiles of (a) povidone-iodine and (b) amoxicillin in halloysite, showing 7.6 and 8.3 wt % loading. Sustained release profiles of (c) povidone iodine and (d) amoxicillin from halloysite clay.
Nanomaterials 09 00708 g004
Nanomaterials 09 00708 g005 550
Figure 5. SEM images of (a) an open halloysite lumen, (b) a dextrin capped halloysite lumen. Reproduced from [67] under Creative Commons Attribution 4.0 International License.
Figure 5. SEM images of (a) an open halloysite lumen, (b) a dextrin capped halloysite lumen. Reproduced from [67] under Creative Commons Attribution 4.0 International License.
Nanomaterials 09 00708 g005
Nanomaterials 09 00708 g006 550
Figure 6. Ciprofloxacin sustained release (a) from halloysite tubes and P. aeruginosa inhibition; (b) from 8% halloysite composite with polymethmetacrylate bone cement and P. aeruginosa 48 h inhibition. Reproduced with permission from [21], Copyright John Wiley and Sons, 2016.
Figure 6. Ciprofloxacin sustained release (a) from halloysite tubes and P. aeruginosa inhibition; (b) from 8% halloysite composite with polymethmetacrylate bone cement and P. aeruginosa 48 h inhibition. Reproduced with permission from [21], Copyright John Wiley and Sons, 2016.
Nanomaterials 09 00708 g006
Nanomaterials 09 00708 g007 550
Figure 7. Scheme of antibacterial metal structures deposition onto/into the nanotubes, with their antibacterial applications and image of silver particles coated onto halloysite.
Figure 7. Scheme of antibacterial metal structures deposition onto/into the nanotubes, with their antibacterial applications and image of silver particles coated onto halloysite.
Nanomaterials 09 00708 g007
Nanomaterials 09 00708 g008 550
Figure 8. Electrospinning drug-loaded halloysite clay nanotubes doped into poly(caprolactone)/gelatin microfibers. Reproduced with permission from [104], Copyright American Chemical Society, 2015.
Figure 8. Electrospinning drug-loaded halloysite clay nanotubes doped into poly(caprolactone)/gelatin microfibers. Reproduced with permission from [104], Copyright American Chemical Society, 2015.
Nanomaterials 09 00708 g008
Nanomaterials 09 00708 g009 550
Figure 9. (a) General scheme of a filtration membrane with antibacterial halloysite based fillers. (b) SEM images of the cross-section morphology of membranes: (a) pure polyethersulfone membrane, (b) polyethersulfone membrane containing 1% N-halamine@halloysite, and (c) polyethersulfone membrane containing 3% N-halamine@ halloysite; (d) TEM image of the presence of N-halamine@halloysite in the polyethersulfone hybrid membrane. Reproduced with permission from [113], Royal Society of Chemistry, 2015.
Figure 9. (a) General scheme of a filtration membrane with antibacterial halloysite based fillers. (b) SEM images of the cross-section morphology of membranes: (a) pure polyethersulfone membrane, (b) polyethersulfone membrane containing 1% N-halamine@halloysite, and (c) polyethersulfone membrane containing 3% N-halamine@ halloysite; (d) TEM image of the presence of N-halamine@halloysite in the polyethersulfone hybrid membrane. Reproduced with permission from [113], Royal Society of Chemistry, 2015.
Nanomaterials 09 00708 g009
Table
Table 1. Loading efficiency and release kinetics of organic antibacterial agents loaded inside halloysite nanotubes.
Table 1. Loading efficiency and release kinetics of organic antibacterial agents loaded inside halloysite nanotubes.
№AnticepticChemical Formula, Molecular Mass (g/mol.)Loading ProcedureLoading Efficiency, wt %Release KineticsApplicationReference
1GentamicinC21H43N5O7, 477.6Vacuum cycling, washing1194% after 48 h (halloysite_gentamicin); 60% in 10.4 days (PMMA_ halloysite_gentamicin composite)Bone cement [38]
2Brilliant GreenC27H33N2HO4S, 482.64Vacuum cycling, washing15–2096% after 5 h, 99.9% after 1.1 day (Halloysite-PCL Scaffold); Cu-BTA coated BG/halloysite 99% after 8.3 dayspoly-e-caprolactone scaffolds[49,50]
3MetronidazoleC6H9N3O3, 171.2mixing25Metronidazole/halloysite 70% after 10 h; Polycaprolactone/gelatin polymer/Metronidazole/halloysite 90% after 15 daysanti-infective GTR/GBR implant membrane[104]
4ChlorhexidineC22H30Cl2N10, 505.45Vacuum cycling, washing15–2085% after 4 hScaffolds, wound repair, patient recovery.[49]
Chlorhexidine gluconateC34H54Cl2N10O14, 897.76Vacuum cycling, washing 25% after 1 hCotton fabric coating[58]
5Povidone iodineC6H9I2NO, 364.95Vacuum cycling, washing15–2076% after 6.5 hScaffolds, wound repair, patient recovery.[49]
6DoxycyclinC22H24N2O8, 444,43Vacuum cycling, washing15–2099% after 4 hScaffolds, wound repair, patient recovery.[49]
7IodineI2, 253,8 15–2093% after 5 hScaffolds, wound repair, patient recovery.[49]
8VancomycinC66H75Cl2N9O24, 1449.3Vacuum cycling + sonication, washing1550% at pH 7 after 1 day 74% at pH 7 after 5 weekslocal antibiotic delivery systems[52]
9Tetracycline base C22H24N2O8, 444.4vacuum cycling, two step loading39Hall coated with chitosan 80% after 16 daysPeriodontitis treatment[53]
Tetracycline hydrochlorideC22H25ClN2O8, 480.9vacuum cycling, two step loading42,6TCH/HNTs/89.4% after 24 h; TCH/HNTs/PLGA composite nanofibers 16–18% after 24 h; 68–76% after 42 days drug-loaded electrospun nanofibers[57]
10AmoxicillinC16H19N3O5S, 365,4Vacuum cycling, washing halloysite nanotubes/AMX 43% after 24 h; poly(lactic-co-glycolic acid)/halloysite g/mol,nanotubes/AMX/chitosan nanofibers 36% after 24 hWound healing[56]
11Salicylic acidC7H6O3, 138,12Vacuum cycling, washing10.560% after 10 h; 100% after 50 hActive packaging for food industry[60]
12Polymyxin B sulfateC56H100N16O17S, 1301.57Vacuum cycling, washing13gelatin-based nanocomposites 50% after 70 h
13CarvacrolC10H14O, 150,22Sonication33LDPE/(HNTs/carvacrol hybrid diffusion coefficient of 4.22 * 10−11 m2 s−1Active packaging for food industry[62,63,64]
14Thyme oil (TO)Variable mol. mass, Mixture of compoundssonication5–7TO/HTNs on air 69% after 9 day; TO/capped HNTs 33% after 9 days; TO/polymer coated HNTs 28% after 9 daysPaining for food packaging[65]
15Rosemary essential oilVariable mol. mass, Mixture of compoundsVacuum cycling~50Nano-hybrid/pectin 25% after 4 h; 90% after 28 daysbiodegradable materials for packaging[66]

Share and Cite

MDPI and ACS Style

Stavitskaya, A.; Batasheva, S.; Vinokurov, V.; Fakhrullina, G.; Sangarov, V.; Lvov, Y.; Fakhrullin, R. Antimicrobial Applications of Clay Nanotube-Based Composites. Nanomaterials 2019, 9, 708. https://doi.org/10.3390/nano9050708

AMA Style

Stavitskaya A, Batasheva S, Vinokurov V, Fakhrullina G, Sangarov V, Lvov Y, Fakhrullin R. Antimicrobial Applications of Clay Nanotube-Based Composites. Nanomaterials. 2019; 9(5):708. https://doi.org/10.3390/nano9050708

Chicago/Turabian Style

Stavitskaya, Anna, Svetlana Batasheva, Vladimir Vinokurov, Gölnur Fakhrullina, Vadim Sangarov, Yuri Lvov, and Rawil Fakhrullin. 2019. "Antimicrobial Applications of Clay Nanotube-Based Composites" Nanomaterials 9, no. 5: 708. https://doi.org/10.3390/nano9050708

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop