Looking at the Bigger Picture—Considering the Hurdles in the Struggle against Nanoplastic Pollution
Next Article in Special Issue
Nucleic Acid-Based Nanobiosensor (NAB) Used for Salmonella Detection in Foods: A Systematic Review
Previous Article in Journal
Grand Canonical Monte Carlo Simulations to Determine the Optimal Interlayer Distance of a Graphene Slit-Shaped Pore for Adsorption of Methane, Hydrogen and their Equimolar Mixture
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 10
10.3390/nano11102533
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

SBA-Pr-Is-TAP Functionalized Nanostructured Silica as a Highly Selective Fluorescent Chemosensor for Fe3+ and Cr2O72− Ions in Aqueous Media

by
Ghodsi Mohammadi Ziarani
1,*,
Maryam Akhgar
1,
Fatemeh Mohajer
1,
Alireza Badiei
2 and
Rafael Luque
3,*
1
Department of Chemistry, Faculty of Physics and Chemistry, Alzahra University, Tehran 1993893979, Iran
2
School of Chemistry, College of Science, University of Tehran, Tehran 1417614411, Iran
3
Departamento de Quimica Organica, Grupo FQM-383, Campus de Rabanales, Universidad de Cordoba, Edificio Marie Curie, Ctra Nnal IV-A, Km 396, E14014 Córdoba, Spain
*
Authors to whom correspondence should be addressed.
Nanomaterials 2021, 11(10), 2533; https://doi.org/10.3390/nano11102533
Submission received: 4 June 2021 / Revised: 13 September 2021 / Accepted: 14 September 2021 / Published: 28 September 2021
(This article belongs to the Special Issue Current Trends in Nanostructured Biosensors)
Browse Figures
Versions Notes

Abstract

:
SBA-Pr-Is-TAP was synthesized via functionalization of SBA-15. The synthesized hybrid nanomaterial was characterized by various techniques including FT-IR, TGA, XRD, SEM, and BET. SBA-Pr-Is-TAP could precisely bind Fe3+ and Cr2O72− ions among a range of different species in aqueous media, consequently acting as a nanoporous chemosensor of Fe3+ and Cr2O72− ions. An excellent linear relation was observed between the nanoporous chemosensor and ion concentrations, with acceptable detection limits of 2.43 × 10−6 M and 3.96 × 10−7 M for Fe3+ and Cr2O72− ions respectively.

1. Introduction

Ordered mesoporous silica was discovered for the first time in 1992 [1]. Several mesoporous scaffolds have been classified into three types based on their pore forms: round cage, cylindrical, and continuous channel [2]. Properties including morphology, pore size, and applications have been changed and improved by functionalization reactions [3,4,5]. The most popular form of mesoporous nanosilicas is SBA-15, which has attracted significant consideration due to its benefits [6,7,8,9,10,11,12,13]. SBA-15 nanoporous silica has excellent properties including adjustable cavities, large surface area, thick framework walls, complementary porosity, and thermal stability [14,15,16].
Functionalized SBA-15 by different organic compounds can provide access to different chemosensors to detect different ions. For example, a highly ordered mesoporous silica material (SBA-15) functionalized with 5-(4-carboxy-phenylazo)-8-hydroxyquinoline (CPA-8-HQL) acts as a fluorescence chemosensor for sensing Pb2+ ions [17]. Furthermore, another fluorescence nano-chemosensor for Cr2O72− anion was synthesized by the assembly of a fluorescent aluminum complex of 8-hydroxyquinoline (AlQx) within the channels of modified SBA-15 [18].
Since isatin and its derivatives have excellent properties including biological and pharmacological activities, these have been used in various organic syntheses [19,20,21]. Functionalized nanoporous materials by Fe3+ ion can play a vital role in important processes including the transformation of an electron in DNA and RNA as well as biological metabolism [22]. The lack or excess of iron has been reported to lead to a number of diseases such as skin problems, iron shortage anemia (IDA), low immunity, Alzheimer’s, Huntington’s, and Parkinson’s [23]. The increase of iron could disturb biological systems and cause water contamination [24]. On the other hand, Cr2O72− has also been made by industrial companies as one of the heavy-metal water pollutants. Consequently, low-cost, sensitive, selective, and fast detection of Fe3+ and Cr2O72− will be highly valuable [25]. In continuation with recent research from our groups [26,27,28,29,30,31,32,33,34,35], the design of a nanostructured chemosensor based on modified SBA-15 (SBA-Pr-Is-TAP) was attempted in this work, with its chemosensor activities studied in the detection of Fe3+ and Cr2O72− in the presence of other ions.

2. Results and Discussion

The overall process for the preparation of the SBA-Pr-Is-TAP is illustrated in Scheme 1. Firstly, SBA-15 was functionalized with (3-chlorpropyl) triethoxysilane to provide SBA-Pr-Cl, which was modified by isatin to give SBA-Pr-Is. In the final step, SBA-Pr-Is were reacted with 2,4,6-triaminopyrimidine to provide SBA-Pr-Is-TAP, fully characterized by different analysis methods including IR, TGA, XRD, etc. Full information on characterization equipment and experiments is provided in the experimental section.
Three amine groups on 2,4,6-triaminopyrimidine can potentially react with carbonyl groups for the formation of a Schiff Base. NH2 groups in positions of 4 and 6 are chemically equivalent, therefore two types of amine groups present for Schiff base reaction (two amine groups at positions of 4 and 6, and the other at position 2). On the other hand, the basicity of the amino group at position 2 is lower than the others, suggesting that the surface adduct should be formed via reaction at the 4 or 6 positions.
FT-IR spectroscopy shows the organic moieties covalently bonded on the SBA-15 surface. FT-IR spectra for SBA-15, SBA-Pr-Cl, SBA-Pr-Is, and SBA-Pr-Is-TAP are depicted in Figure 1. The bands at 800 and 1100 cm−1, respectively, are related to Si-O-Si bonds, while the band at 960 is related to Si-OH. Then, the band around 3456 cm−1 could be attributed to O–H stretching of Si-OH functional groups. The peak around 1650 cm−1 is associated with C=O stretching vibration and the bending vibrations of water molecules (in spectrum c). The presence of a new band in spectra b and c in at 2881–2990 cm−1 range is due to the stretching vibrations of methylene in propyl groups. In c, the new band at 1479 and 1754 cm−1 corresponded to C=C and C=O stretching vibrations. The new band at 1706 is related to C=N groups. In spectra d, the new band at 3400 cm−1 is related to NH2 groups of triaminopyrimidine. These new bands proved that aliphatic compounds, isatin, and triaminopyrimidine were successfully immobilized on the surface of SBA-15.
X-ray powder diffraction (XRD) of SBA-15 and SBA-Pr-Is-TAP is shown in Figure 2. According to the obtained results, a strong reflection was observed at around 2θ = 1° corresponding to (100) plane, while the other two intense reflections at ca. 2θ = 1.8° and 2.0° could be assigned to (110) and (200) planes. These reflections demonstrate that the functionalized products maintained highly ordered mesoporous hexagonal structures. Comparing the XRD of SBA-15 with SBA-Pr-Is and SBA-Pr-Is-TAP, the same diffraction lines could be visualized in all three materials (with different intensities). These results confirmed the successful incorporation of the organic moieties onto SBA-15.
SEM and TEM images also proved the nano-ordered arrays of SBA-15 and SBA-Pr-Is-TAP hexagonal nanoporous channels, as shown in Figure 3 and Figure 4. The prepared materials’ physical properties and porosity were investigated by nitrogen adsorption-desorption isotherms (Figure 5). These compounds display type IV isotherms with H1-type hysteresis loops, which proved the pore walls of SBA-Pr-Is and SBA-Pr-Is-TAP are still open. After the attachment of organic compounds on SBA-15, certain changes in physical properties became evident including a reduction in surface area (SBET), average pore diameter (dp), and pore volume (Vp) as shown in Table 1. The reasons for the reduced surface area, pore diameter, and pore volume relate to the deterioration of the textural properties of SBA-15 upon the incorporation of the organic moieties (pore diameter and volume) due to partial pore blocking of such organic moieties and surface area due to the partial covering of the surface with the anchored organic moieties.
Thermogravimetry studies confirmed the presence of loaded organic compounds on the SBA-15 surface as shown in Figure 6. In two TGA curves, the weight loss (up to 150 °C) was due to physisorbed water from the mesoporous material. The obtained results pointed out that SBA-Pr-Is-TAP is hydrophilic because of the existence of more nitrogen atoms. The weight loss at 200 and 650 °C was related to the breakdown and removal of organic compounds while that at 700 °C corresponds to the dehydroxylation of silanol groups. TGA curves indicated, respectively, weight losses of ∼6% (0.76 mmol), ∼16% (0.845 mmol), and 24% (0.809 mmol) of organic compounds for SBA-Pr-Cl, SBA-Pr-Is, and SBA-Pr-Is-TAP as expected for materials with increasing loadings of organic content.

3. Fluorescence Response of SBA-Pr-Is-TAP to Fe3+

Fluorescence studies of SBA-Pr-Is-TAP after adding different cations M(NO3)x (M = Na+, Al3+, Cu2+, Mg2+, K+, Cd2+, Ca2+, Mn2+, Co2+, Li+, Zn2+, Ni2+, Ba2+, Hg2+, Sr2+, Cs+, Pb2+, Fe2+, Cr3+, Ag+, and Fe3+) were conducted at 420 nm as shown in Figure 7. Luminescence intensities were influenced by adding Fe3+ ions as compared to other metal ions, pointing to SBA-Pr-Is-TAP with potential recognition and sensing of Fe3+ ions. The interaction between SBA-Pr-Is-TAP and Fe3+ was displayed in Scheme 2, believed to be related to the interaction of Fe3+ species with nitrogen groups present in the organic moieties of SBA-Pr-Is-TAP.
This high selectivity can be interpreted due to the different charge densities of metal ions and their interaction between guest and host. The charge density (ρ) of a metal ion is defined as the amount of electric charge/unit volume [36,37]. It is one of the most important parameters of the relative electrophilicity of a metal ion for interaction between ligand and ion. The charge densities of metal ions were calculated according to Equation (1):
ρ = q/(4/3 πr3)
where q is the formal charge and r denotes the Shannon ionic radius [38]. The calculated charge density of the cations increase in the following order: Al3+ (4.67) < Cr3+ (3.08) < Fe3+ (6.45).
The results indicate that the charge density of Fe3+ ion is the largest among all of competition ions. Therefore, the electrophilic ability (capability of forming a coordination complex with an electron-rich ligand) of an Fe3+ ion is the strongest among cations. On the other hand, metal ions (as guest) can diffuse into the functionalized nanochannels of SBA-15 (as a host) [38]. The host-guest interaction depends on the concentration of ion and chelating capability into the channels, with Fe3+ ions having an enhanced interaction with the strong electrophilicity of amine groups (TAP).
Selectivity studies of SBA-Pr-Is-TAP towards Fe3+ ions were subsequently conducted in the presence of other cations (Figure 8). Spectra were recorded at λex = 220 nm and λem = 420 nm after the addition of SBA-Pr-Is-TAP suspension (0.02 g L−1, 3 mL H2O) to the 100 µL of Fe3+ mixture (1 × 10−4 M) with 100 µL (1 × 10−4 M) of the mentioned metal cations. Remarkably, results indicated that SBA-Pr-Is-TAP has good selectivity for Fe3+ among a range of different tested cations.
A fluorescence titration experiment was also carried out with the addition of various amounts of Fe3+ ions (1 × 10−4 to 100 × 10−4 M) into the aqueous suspension of SBA-Pr-Is-TAP. The relation between fluorescence intensity and different concentrations of Fe3+ is shown in Figure 9. Fluorescence intensity was enhanced by increasing Fe3+ concentrations. A linear relation between fluorescence intensity and concentration of Fe3+ was observed, with R2 of 0.9991 as shown in Figure 10. The detection limit was calculated according to the following equation: DL = KSd/m. DL was calculated to be 2.43 × 10−6, where Sd is the standard deviation of the blank solution measured five times, m is the slope of fluorescence intensity of SBA-Pr-Is-TAP versus [Fe3+], and K is 3 as a confidence level. It showed good detection of limit in comparison with the other fluorescent compounds in Table 2.
Fluorescence studies of SBA-Pr-Is-TAP after adding different anions An−, including = I−, CN−, Cl−, F−, Br−, CO32−, SO42−, HCO3−, H2PO4−, NO2−, NO3−, CH3COO−, SCN−, S2O32−, OH−, and Cr2O72−, was obtained at λex = 220 nm, λem = 420 nm as shown in Figure 11 and Scheme 3. Luminescence intensities were influenced by adding Cr2O72− ions as compared to other anions. Therefore, SBA-Pr-Is-TAP also showed a potential recognition and sensing for Cr2O72− ions.
The selectivity of SBA-Pr-Is-TAP towards Cr2O72− ions was subsequently investigated in the presence of other anions (Figure 12). In this regard, spectra were recorded at λex = 255 nm and λem = 420 nm after the addition of SBA-Pr-Is-TAP suspension (0.02 g L−1, 3 mL H2O) to the mixture of Cr2O72− (100 µL, 1 × 10−4 M) and the mentioned anions (100 µL, 1 × 10−4 M). The obtained results showed that the SBA-Pr-Is-TAP has good selectivity for Cr2O72−.
A fluorescence titration experiment was next carried out with the addition of various amounts of Cr2O72− ions (1 × 10−5 to 100 × 10−5 M) into the aqueous suspension of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1). The relation between fluorescence intensity and different concentrations of Cr2O72− is shown in Figure 13. Fluorescence intensity decreased while the concentration of Cr2O72− ions gradually increased. A linear relation between fluorescence intensity and concentration of Cr2O72− was found, with R2 of 0.9941 as shown in Figure 14. The detection limit was calculated (similarly to that for Fe3+) to be 3.96 × 10−7 M and compared with the other chemosensor compounds in Table 3.
The quenching mechanism of SBA-Pr-Is-TAP with Cr2O72− was subsequently investigated using the Stern-Volmer equation. Figure 14 shows a linear plot of I0/I against the concentration of Cr2O72− ions which indicates a static quench. UV-Vis spectrum of Cr2O72− ions exhibits two maximum absorption wavelengths at 257 and 350 nm in UV range and another at 440 nm in the visible domain which has good spectral overlap with the fluorescence emission peak of SBA-Pr-Is-TAP [47]. Therefore, the strong inner filter effect (IFE) possibly occurs after the addition of Cr2O72− in the dispersed SBA-Pr-Is-TAP [48,49]. In several reports, IFE has been proposed as a fluorescence quenching mechanism in optical dichromate sensors [18,50]. This quenching mechanism was proposed based on the formation of hydrogen bonding between the oxygen group of Cr2O72− and hydrogen atoms belong to the amine or carboxyl group of functionalized TAP into the nanochannel of SBA-15 [51]. This hydrogen bonding may change the electronic distribution of TAP; thereby, the fluorescence emissions can be quenched and intensity changed. Therefore, besides IFE, hydrogen bonding is suggested as fluorescence quenching mechanism of SBA-Pr-Is-TAP with Cr2O72−.

4. Conclusions

SBA-Pr-Is-TAP as organic-inorganic nanohybrid via SBA-15 modification with isatin and 2,4,6-triaminopyrimidine was synthesized and characterized. Textural and physicochemical properties confirmed the successful incorporation of organic groups on SBA-15. Fluorescence studies demonstrated the hybrid or an organic material can be a selective sensor for Fe3+ and Cr2O72− recognition in H2O, with detection limits of 2.43 × 10−6 and 3.96 × 10−7 M, respectively.

5. Experimental Section

5.1. Synthesis of SBA-15, SBA-Pr-Cl, and SBA-Pr-Is

Materials were prepared based on our previous reported contributions [27,31,33].

5.2. Synthesis of SBA-Pr-Is-TAP

SBA-15-Pr-Is (1 g) was dispersed in dry EtOH. 2,4,6-triaminopyrimidine (0.62 g, 5 mmol) was added to the mixture of reactions. It was refluxed for 24 h, and then filtered to obtain the dark brown powder, which was soxhlated with dried EtOH to obtain pure SBA-15-Pr-Is.
Low-angle X-ray scattering measurements were performed using an X’Pert Pro MPD diffractometer using Cu Kα radiation (λ = 1.5418 Ǻ).
N2 adsorption-desorption isotherms were obtained using a BELSORP-miniII instrument at liquid nitrogen temperature (−196 °C). Degassing process for all samples was performed at 100 °C before the measurements. The Brunauer-Emmett-Teller (BET) and Barrett-Joyner-Halenda (BJH) equations were applied on sorption data using BELSORP analysis software to calculate the physical properties of materials such as the specific surface area, pore diameter, pore-volume, and pore size distribution.
Thermogravimetric analyses (TGA) were carried out by a TGA Q50 V6.3 Build 189 instrument from ambient temperature to 1000 °C with a ramp rate of 10 ℃ min−1 in the air. SEM analysis was performed on a Hitachi S-4160 operated at 30 kV.
FT-IR spectra were obtained in KBr disks on a RAYLEIGH WQF-510A FT-IR spectrometer in the 600–4000 cm−1 region. Fluorescence measurements were collected on a Cary Eclipse Fluorescent Spectrophotometer.
Additional information can be found in the Supplementary Materials submitted with this article.

6. Calculation of Detection Limit (DL)

DLs can be calculated based on the standard deviation of the response (Sd) of the curve and the slope of the calibration curve (m) at levels approximating the DL according to the formula: DL = 3 (Sd/m). The standard deviation of the response can be determined based on the standard deviation of y-intercepts of regression lines. The slope and Sd can be obtained with one order of magnitude of the calibration curve.

Supplementary Materials

Supplementary materials are available online at https://www.mdpi.com/article/10.3390/nano11102533/s1.

Author Contributions

Conceptualization, design, supervision, G.M.Z.; writing—original draft preparation, M.A.; writing—review and editing, F.M.; Scientific counselling, A.B. and R.L. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by MINECO under project PID2019-109953GB-I00, co-financed with FEDER funds.

Data Availability Statement

Not applicable.

Acknowledgments

We gratefully acknowledge the support of the research council of Alzahra University.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Kresge, C.T.; Leonowicz, M.E.; Roth, W.J.; Vartuli, J.C.; Beck, J.S. Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism. Nature 1992, 359, 710–712. [Google Scholar] [CrossRef]
  2. Han, Y.; Zhang, D. Ordered mesoporous silica materials with complicated structures. Curr. Opin. Chem. Eng. 2012, 1, 129–137. [Google Scholar] [CrossRef]
  3. Ying, J.Y.; Mehnert, C.P.; Wong, M.S. Synthesis and applications of supramolecular-templated mesoporous materials. Angew. Chem. Int. Ed. 1999, 38, 56–77. [Google Scholar] [CrossRef]
  4. Schüth, F. Non-siliceous mesostructured and mesoporous materials. Chem. Mater. 2001, 13, 3184–3195. [Google Scholar] [CrossRef]
  5. Wan, Y.; Zhao, D. On the controllable soft-templating approach to mesoporous silicates. Chem. Rev. 2007, 107, 2821–2860. [Google Scholar] [CrossRef]
  6. Zhao, D.; Sun, J.; Li, Q.; Stucky, G.D. Morphological control of highly ordered mesoporous silica SBA-15. Chem. Mater. 2000, 12, 275–279. [Google Scholar] [CrossRef]
  7. Klimova, T.; Esquivel, A.; Reyes, J.; Rubio, M.; Bokhimi, X.; Aracil, J. Factorial design for the evaluation of the influence of synthesis parameters upon the textural and structural properties of SBA-15 ordered materials. Microporous Mesoporous Mater. 2006, 93, 331–343. [Google Scholar] [CrossRef]
  8. Boahene, P.E.; Soni, K.K.; Dalai, A.K.; Adjaye, J. Application of different pore diameter SBA-15 supports for heavy gas oil hydrotreatment using FeW catalyst. Appl. Catal. A General. 2011, 402, 31–40. [Google Scholar] [CrossRef]
  9. Lei, Z.; Gao, L.; Shui, H.; Chen, W.; Wang, Z.; Ren, S. Hydrotreatment of heavy oil from a direct coal liquefaction process on sulfided Ni–W/SBA-15 catalysts. Fuel Process. Technol. 2011, 92, 2055–2060. [Google Scholar] [CrossRef]
  10. Mouli, K.C.; Soni, K.; Dalai, A.; Adjaye, J. Effect of pore diameter of Ni–Mo/Al-SBA-15 catalysts on the hydrotreating of heavy gas oil. Appl. Catal. A General. 2011, 404, 21–29. [Google Scholar] [CrossRef]
  11. Mohajer, F.; Mohammadi Ziarani, G.; Badiei, A. The synthesis of SBA-Pr-3AP@ Pd and its application as a highly dynamic, eco-friendly heterogeneous catalyst for Suzuki–Miyaura cross-coupling reaction. Res. Chem. Intermed. 2020, 46, 4909–4922. [Google Scholar] [CrossRef]
  12. Moradi, R.; Mohammadi Ziarani, G.; Badiei, A.; Mohajer, F. Synthesis and characterization of mesoporous organosilica supported palladium (SBA-Pr-NCQ-Pd) as an efficient nanocatalyst in the Mizoroki–Heck coupling reaction. Appl. Organomet. Chem. 2020, 34, e5916. [Google Scholar] [CrossRef]
  13. Mohajer, F.; Mohammadi Ziarani, G.; Anafch, M.; Badiei, A. Experimental and Computational Study of Acridine-1,8-Dione Derivative in Etoh as a Fluorescent Sensor for Fe(III). In Proceedings of the International Conference on Sustainable Energy and Energy Calculations, Online Live Conference, 4–5 September 2020; Available online: http://www.greenconferences.org/program.html (accessed on 14 September 2021).
  14. Stevens, W.J.; Lebeau, K.; Mertens, M.; Van Tendeloo, G.; Cool, P.; Vansant, E.F. Investigation of the morphology of the mesoporous SBA-16 and SBA-15 materials. J. Phys. Chem. B 2006, 110, 9183–9187. [Google Scholar] [CrossRef] [PubMed]
  15. Zhang, F.; Yan, Y.; Yang, H.; Meng, Y.; Yu, C.; Tu, B.; Zhao, D. Understanding effect of wall structure on the hydrothermal stability of mesostructured silica SBA-15. J. Phys. Chem. B 2005, 109, 8723–8732. [Google Scholar] [CrossRef] [PubMed]
  16. Rahmat, N.; Abdullah, A.Z.; Mohamed, A.R. Recent progress on innovative and potential technologies for glycerol transformation into fuel additives: A critical review. Renew. Sustain. Energy Rev. 2010, 14, 987–1000. [Google Scholar] [CrossRef]
  17. Zhao, L.; Sui, D.; Wang, Y. Fluorescence chemosensors based on functionalized SBA-15 for detection of Pb2+ in aqueous media. RSC Adv. 2015, 5, 16611–16617. [Google Scholar] [CrossRef]
  18. Hosseini, M.; Gupta, V.K.; Ganjali, M.R.; Rafiei-Sarmazdeh, Z.; Faridbod, F.; Goldooz, H.; Badiei, A.R.; Norouzi, P. A novel dichromate-sensitive fluorescent nano-chemosensor using new functionalized SBA-15. Anal. Chim. Acta. 2012, 715, 80–85. [Google Scholar] [CrossRef] [PubMed]
  19. Lashgari, N.; Mohammadi Ziarani, G. Synthesis of heterocyclic compounds based on isatin through 1,3-dipolar cycloaddition reactions. Ark. Online J. Org. Chem. 2012. [Google Scholar] [CrossRef]
  20. Mohammadi Ziarani, G.; Moradi, R.; Lashgari, N. Asymmetric synthesis of chiral 3,3-disubstituted oxindoles using isatin as starting material. Tetrahedron Asymmetry 2015, 26, 517–541. [Google Scholar] [CrossRef]
  21. Mohammadi Ziarani, G.; Moradi, R.; Lashgari, N. Synthesis of spiro-fused heterocyclic scaffolds through multicomponent reactions involving isatin. Ark. Online J. Org. Chem. 2016. [Google Scholar] [CrossRef] [Green Version]
  22. Andrews, N.C. Disorders of iron metabolism. N. Engl. J. Med. 1999, 341, 1986–1995. [Google Scholar] [CrossRef]
  23. Hyman, L.M.; Franz, K.J. Probing oxidative stress: Small molecule fluorescent sensors of metal ions, reactive oxygen species, and thiols. Coord. Chem. Rev. 2012, 256, 2333–2356. [Google Scholar] [CrossRef] [Green Version]
  24. Zhao, Q.; Li, F.; Huang, C. Phosphorescent chemosensors based on heavy-metal complexes. Chem. Soc. Rev. 2010, 39, 3007–3030. [Google Scholar] [CrossRef]
  25. O’Connor, T.P. Mussel Watch results from 1986 to 1996. Mar. Pollut. Bull. 1998, 37, 14–19. [Google Scholar] [CrossRef]
  26. Mohammadi Ziarani, G.; Akhgar, M.; Mohajer, F.; Badiei, A. SBA-Pr-IS-MN synthesis and its application as Ag+ optical sensor in aqueous media. Res. Chem. Intermed. 2021, 47, 2845–2855. [Google Scholar] [CrossRef]
  27. Mohammadi Ziarani, G.; Ebrahimi, Z.; Mohajer, F.; Badiei, A. A Fluorescent Chemosensor Based on Functionalized Nanoporous Silica (SBA-15 SBA-IC-MN) for Detection of Hg2+ in Aqueous Media. Arab. J. Sci. Eng. 2021, 1–10. [Google Scholar] [CrossRef]
  28. Mohajer, F.; Mohammadi Ziarani, G.; Badiei, A.; Ghasemi, J.B. SBA-Pr-Imine-Furan as an environmental adsorbent of Pd (II) in aqueous solutions. Environ. Chall. 2021, 3, 100032. [Google Scholar] [CrossRef]
  29. Lashgari, N.; Badiei, A.; Mohammadi Ziarani, G. A novel functionalized nanoporous SBA-15 as a selective fluorescent sensor for the detection of multianalytes (Fe3+ and Cr2O72−) in water. J. Phys. Chem Solids 2017, 103, 238–248. [Google Scholar] [CrossRef]
  30. Karimi, M.; Badieia, A.; Mohammadi Ziarani, G. Fluorescence-enhanced optical sensor for detection of Al3+ in water based on functionalised nanoporous silica type SBA-15. Chem. Pap. 2016, 70, 1431–1438. [Google Scholar] [CrossRef]
  31. Shiravand, G.; Badiei, A.; Mohammadi Ziarani, G. Carboxyl-rich g-C3N4 nanoparticles: Synthesis, characterization and their application for selective fluorescence sensing of Hg2+ and Fe3+ in aqueous media. Sens. Act. B Chem. 2017, 242, 244–252. [Google Scholar] [CrossRef]
  32. Afshani, J.; Badiei, A.; Lashgari, N.; Mohammadi Ziarani, G. A simple nanoporous silica-based dual mode optical sensor for detection of multiple analytes (Fe3+, Al3+ and CN−) in water mimicking XOR logic gate. RSC Adv. 2016, 6, 5957–5964. [Google Scholar] [CrossRef]
  33. Yadavi, M.; Badiei, A.; Mohammadi Ziarani, G. A novel Fe3+ ions chemosensor by covalent coupling fluorene onto the mono, di-and tri-ammonium functionalized nanoporous silica type SBA-15. Appl. Surf. Sci. 2013, 279, 121–128. [Google Scholar] [CrossRef]
  34. Zhao, D.; Feng, J.; Huo, Q.; Melosh, N.; Fredrickson, G.H.; Chmelka, B.F.; Stucky, G.D. Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores. Science 1998, 279, 548–552. [Google Scholar] [CrossRef] [Green Version]
  35. Karimi, M.; Badiei, A.; Mohammadi Ziarani, G. A click-derived dual organic-inorganic hybrid optical sensor based on SBA-15 for selective recognition of Zn2+ and CN− in water. Inorg. Chim. Acta 2016, 450, 346–352. [Google Scholar] [CrossRef]
  36. Shannon, R.D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallogr. Sect. A 1976, 5, 751–767. [Google Scholar] [CrossRef]
  37. Badiei, A.; Yadavi, M.; Karimi, M. A novel diethyl 2-(9-fluorenyl) malonate functionlized SBA-15 for selective optical sensing of Iron. J. Nanostruct. 2019, 1, 146–153. [Google Scholar] [CrossRef]
  38. Minoru, S.; Saito, K.; Ogawa, M. Host–guest chemistry of mesoporous silicas: Precise design of location, density and orientation of molecular guests in mesopores. Sci. Technol. Adv. Mater. 2015. [Google Scholar] [CrossRef] [Green Version]
  39. Zhang, Y.; Xiao, Y.; Zhang, Y.; Wang, Y. Carbon quantum dots as fluorescence turn-off-on probe for detecting Fe3+ and ascorbic acid. J. Nanosci. Nanotechnol. 2020, 1, 3340–3347. [Google Scholar] [CrossRef] [PubMed]
  40. Salahshoor, Z.; Ghasemi, J.B.; Shahbazi, A.; Badiei, A. Highly selective silica-based fluorescent nanosensor for ferric ion (Fe3+) detection in aqueous media. Spectrochim. Acta A Mol. 2019, 5, 293–298. [Google Scholar] [CrossRef] [PubMed]
  41. Kordi, Z.K.; Mohammadi Ziarani, G.; Badiei, A.; Lashgari, N. Synthesis of 1, 4-Dihydropyridine as a Fluorescent and Colorimetric Chemosensor for Detection of Fe3+ Ion. Sensor Lett. 2019, 17, 747–754. [Google Scholar] [CrossRef]
  42. Guo, Y.; Wang, L.; Zhuo, J.; Xu, B.; Li, X.; Zhang, J.; Zhang, Z.; Chi, H.; Dong, Y.; Lu, G. A pyrene-based dual chemosensor for colorimetric detection of Cu2+ and fluorescent detection of Fe3+. Tet. Lett. 2017, 58, 3951–3956. [Google Scholar] [CrossRef]
  43. Ravichandiran, P.; Prabakaran, D.S.; Maroli, N.; Kim, A.R.; Park, B.H.; Han, M.K.; Ramesh, T.; Ponpandian, S.; Yoo, D.J. Mitochondria-targeted acridine-based dual-channel fluorescence chemosensor for detection of Sn4+ and Cr2O72− ions in water and its application in discriminative detection of cancer cells. J. Hazard. Mater. 2021, 16, 126409. [Google Scholar] [CrossRef]
  44. Zhu, H.; Li, Y.H.; Xiao, Q.Q.; Cui, G.H. Three luminescent Cd (II) coordination polymers containing aromatic dicarboxylate and flexible bis (benzimidazole) ligands as highly sensitive and selective sensors for detection of Cr2O72– oxoanions in water. Polyhedron 2020, 187, 114648. [Google Scholar] [CrossRef]
  45. Yao, Z.Q.; Li, G.Y.; Xu, J.; Hu, T.L.; Bu, X.H. A Water-Stable Luminescent ZnII Metal-Organic Framework as Chemosensor for High-Efficiency Detection of Cr VI-Anions (Cr2O72− and CrO42−) in Aqueous Solution. Chem. Eur. J. 2018, 24, 3192–3198. [Google Scholar] [CrossRef] [PubMed]
  46. Bai, H.; Tu, Z.; Liu, Y.; Tai, Q.; Guo, Z.; Liu, S. Dual-emission carbon dots-stabilized copper nanoclusters for ratiometric and visual detection of Cr2O72− ions and Cd2+ ions. J. Hazardous Mater. 2020, 386, 121654. [Google Scholar] [CrossRef] [PubMed]
  47. Shiravand, G.; Badiei, A.; Goldooz, H.; Karimi, M.; Mohammadi Ziarani, G.; Faridbod, F.; Ganjali, M.R. A Fluorescent g-C3N4 nanosensor for detection of dichromate ions. Curr. Anal. Chem. 2020, 16, 593–601. [Google Scholar] [CrossRef]
  48. Rong, M.; Lin, L.; Song, X.; Wang, Y.; Zhong, Y.; Yan, J.; Feng, Y.; Zeng, X.; Chen, X. Fluorescence Sensing of Chromium (VI) and Ascorbic Acid Using Graphitic Carbon Nitride Nanosheets as a Fluorescent “Switch”. Biosens. Bioelectron. 2015, 68, 210–217. [Google Scholar] [CrossRef] [PubMed]
  49. Zheng, M.; Xie, Z.; Qu, D.; Li, D.; Du, P.; Jing, X.; Sun, Z. On-Off-On Fluorescent Carbon Dot Nanosensor for Recognition of Chromium(VI) and Ascorbic Acid Based on the Inner Filter Effect. ACS Appl. Mater. Interfaces. 2013, 5, 13242–13247. [Google Scholar] [CrossRef] [PubMed]
  50. Karimi, M.; Badiei, A.; Mohammadi Ziarani, G. SBA-15 functionalized with naphthalene derivative for selective optical sensing of Cr2O72− in water. Anal. Sci. 2016, 32, 511–516. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  51. Chen, W.; Cao, F.; Zheng, W.; Tian, Y.; Xianyu, Y.; Xu, P.; Zhang, W.; Wang, Z.; Deng, K.; Jiang, X. Detection of the nanomolar level of total Cr[(iii) and (vi)] by functionalized gold nanoparticles and a smartphone with the assistance of theoretical calculation models. Nanoscale 2015, 7, 2042–2049. [Google Scholar] [CrossRef]
Nanomaterials 11 02533 sch001 550
Scheme 1. Schematic preparation of SBA-Pr-Is-TAP.
Scheme 1. Schematic preparation of SBA-Pr-Is-TAP.
Nanomaterials 11 02533 sch001
Nanomaterials 11 02533 g001 550
Figure 1. FT-IR spectra of (a) SBA-15, (b) SBA-Pr-Cl, (c) SBA-Pr-Is, and (d) SBA-Pr-Is-TAP.
Figure 1. FT-IR spectra of (a) SBA-15, (b) SBA-Pr-Cl, (c) SBA-Pr-Is, and (d) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g001
Nanomaterials 11 02533 g002 550
Figure 2. Low-angle XRD profiles of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Figure 2. Low-angle XRD profiles of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g002
Nanomaterials 11 02533 g003 550
Figure 3. SEM images of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Figure 3. SEM images of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g003
Nanomaterials 11 02533 g004 550
Figure 4. TEM images of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Figure 4. TEM images of (a) SBA-15 and (b) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g004
Nanomaterials 11 02533 g005 550
Figure 5. Nitrogen adsorption-desorption isotherms of (a) SBA-15, (b) SBA-Pr-Is, and (c) SBA-Pr-Is-TAP.
Figure 5. Nitrogen adsorption-desorption isotherms of (a) SBA-15, (b) SBA-Pr-Is, and (c) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g005
Nanomaterials 11 02533 g006 550
Figure 6. TGA curves of (a) SBA-Pr-Cl, (b) SBA-Pr-Is, and (c) SBA-Pr-Is-TAP.
Figure 6. TGA curves of (a) SBA-Pr-Cl, (b) SBA-Pr-Is, and (c) SBA-Pr-Is-TAP.
Nanomaterials 11 02533 g006
Nanomaterials 11 02533 g007 550
Figure 7. Fluorescence emission of SBA-Is-TAP (3 mL H2O suspension, 0.2 g L−1) by different cations including Na+, Mg2+, Al3+, K+, Ca2+, Mn2+, Cd2+, Co2+, Cu2+, Li+, Zn2+, Ni2+, Ba2+, Hg2+, Sr2+, Cs+, Pb2+, Fe2+, Cr3+, Ag+, and Fe3+ (100 µL, 1 × 10−4 M, λex = 220 nm and λem = 420 nm).
Figure 7. Fluorescence emission of SBA-Is-TAP (3 mL H2O suspension, 0.2 g L−1) by different cations including Na+, Mg2+, Al3+, K+, Ca2+, Mn2+, Cd2+, Co2+, Cu2+, Li+, Zn2+, Ni2+, Ba2+, Hg2+, Sr2+, Cs+, Pb2+, Fe2+, Cr3+, Ag+, and Fe3+ (100 µL, 1 × 10−4 M, λex = 220 nm and λem = 420 nm).
Nanomaterials 11 02533 g007
Nanomaterials 11 02533 sch002 550
Scheme 2. Suggested bonding mode of SBA-Pr-Is-TAP with Fe3+.
Scheme 2. Suggested bonding mode of SBA-Pr-Is-TAP with Fe3+.
Nanomaterials 11 02533 sch002
Nanomaterials 11 02533 g008 550
Figure 8. Selectivity of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) for Fe3+ (100 µL, 1 × 10−4 M) using equal amounts of cations (λex = 220 nm and λem = 420 nm).
Figure 8. Selectivity of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) for Fe3+ (100 µL, 1 × 10−4 M) using equal amounts of cations (λex = 220 nm and λem = 420 nm).
Nanomaterials 11 02533 g008
Nanomaterials 11 02533 g009 550
Figure 9. Fluorescence response of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) by adding different concentrations of Fe3+.
Figure 9. Fluorescence response of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) by adding different concentrations of Fe3+.
Nanomaterials 11 02533 g009
Nanomaterials 11 02533 g010 550
Figure 10. Stern-Volmer plot for titration of SBA-Pr-Is-TAP with different concentrations of Fe3+.
Figure 10. Stern-Volmer plot for titration of SBA-Pr-Is-TAP with different concentrations of Fe3+.
Nanomaterials 11 02533 g010
Nanomaterials 11 02533 g011 550
Figure 11. Fluorescence spectra of the aqueous suspended SBA-Pr-Is-TAP (0.2 g L−1) in the presence of different anions (100 µL of Mn− (1×10−4 M)), including I−, CN−, Cl−, F−, Br−, CO32−, SO42−, NO2−, NO3−, HCO3−, H2PO4−, CH3COO−, SCN−, S2O32−, OH−, and Cr2O72− (λex = 220 nm, λem = 420 nm).
Figure 11. Fluorescence spectra of the aqueous suspended SBA-Pr-Is-TAP (0.2 g L−1) in the presence of different anions (100 µL of Mn− (1×10−4 M)), including I−, CN−, Cl−, F−, Br−, CO32−, SO42−, NO2−, NO3−, HCO3−, H2PO4−, CH3COO−, SCN−, S2O32−, OH−, and Cr2O72− (λex = 220 nm, λem = 420 nm).
Nanomaterials 11 02533 g011
Nanomaterials 11 02533 sch003 550
Scheme 3. The suggested bonding mode of SBA-Pr-Is-TAP with Cr2O72−.
Scheme 3. The suggested bonding mode of SBA-Pr-Is-TAP with Cr2O72−.
Nanomaterials 11 02533 sch003
Nanomaterials 11 02533 g012 550
Figure 12. Selectivity of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) for Cr2O72− (100 µL, 1 × 10−4 M) in the presence of equal amounts of anions (λex = 255 nm and λem = 420 nm).
Figure 12. Selectivity of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) for Cr2O72− (100 µL, 1 × 10−4 M) in the presence of equal amounts of anions (λex = 255 nm and λem = 420 nm).
Nanomaterials 11 02533 g012
Nanomaterials 11 02533 g013 550
Figure 13. Fluorescence response of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) upon the addition of various concentrations of Cr2O72−.
Figure 13. Fluorescence response of SBA-Pr-Is-TAP (3 mL H2O suspension, 0.2 g L−1) upon the addition of various concentrations of Cr2O72−.
Nanomaterials 11 02533 g013
Nanomaterials 11 02533 g014 550
Figure 14. Stern-Volmer plot for titration of SBA-Pr-Is-TAP with different concentrations of Cr2O72−.
Figure 14. Stern-Volmer plot for titration of SBA-Pr-Is-TAP with different concentrations of Cr2O72−.
Nanomaterials 11 02533 g014
Table
Table 1. Structural parameters of SBA-15, SBA-Pr-Is, and SBA-Pr-Is-TAP.
Table 1. Structural parameters of SBA-15, SBA-Pr-Is, and SBA-Pr-Is-TAP.
SampleSBET (m2·g−1)V (cm3·g−1)DBJH (nm)
SBA-156720.694.6
SBA-Pr-Is5500.644.1
SBA-Pr-Is-TAP2500.370.8
Table
Table 2. Comparison of Detection Limits of different fluorescent compounds.
Table 2. Comparison of Detection Limits of different fluorescent compounds.
CompoundIonDL
Carbon quantum dot [39]Fe3+2.78 × 10−6 M
SBA-15-DNPH [40]Fe3+29 × 10−6 M
1,4-Dihydropyridine Colorimetric [41]Fe3+8.3 × 10−6 M
A pyrene-based dual chemosensor [42]Fe3+2.0 × 10−6 M
Table
Table 3. Comparison of Detection Limits of different fluorescent compounds.
Table 3. Comparison of Detection Limits of different fluorescent compounds.
CompoundIonDL
Mitochondria-targeted acridine-based [43]Cr2O72−1.6 × 10−7 M
{[Cd(TCPA)(L)]·H2O}n [44]Cr2O72−4 × 10−7 M
ZnII-MOF [45]Cr2O72−3 × 10−7 M
GSH@CDs-Cu NCs [46]Cr2O72−9 × 10−7 M
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Ziarani, G.M.; Akhgar, M.; Mohajer, F.; Badiei, A.; Luque, R. SBA-Pr-Is-TAP Functionalized Nanostructured Silica as a Highly Selective Fluorescent Chemosensor for Fe3+ and Cr2O72− Ions in Aqueous Media. Nanomaterials 2021, 11, 2533. https://doi.org/10.3390/nano11102533

AMA Style

Ziarani GM, Akhgar M, Mohajer F, Badiei A, Luque R. SBA-Pr-Is-TAP Functionalized Nanostructured Silica as a Highly Selective Fluorescent Chemosensor for Fe3+ and Cr2O72− Ions in Aqueous Media. Nanomaterials. 2021; 11(10):2533. https://doi.org/10.3390/nano11102533

Chicago/Turabian Style

Ziarani, Ghodsi Mohammadi, Maryam Akhgar, Fatemeh Mohajer, Alireza Badiei, and Rafael Luque. 2021. "SBA-Pr-Is-TAP Functionalized Nanostructured Silica as a Highly Selective Fluorescent Chemosensor for Fe3+ and Cr2O72− Ions in Aqueous Media" Nanomaterials 11, no. 10: 2533. https://doi.org/10.3390/nano11102533

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.