Solidification/Stabilization of Arsenic-Containing Tailings by Steel Slag-Based Binders with High Efficiency and Low Carbon Footprint

1
School of Energy and Environmental Engineering, University of Science and Technology Beijing, Beijing 100083, China
2
Key Laboratory of High-Efficient Mining and Safety of Metal Mines, Ministry of Education, Beijing 100083, China
3
Key Laboratory of Resource-Oriented Treatment of Industrial Pollutants, Beijing 100083, China
4
School of Civil and Resource Engineering, University of Science and Technology Beijing, Beijing 100083, China
5
Technology Center of HBIS Group Hansteel Company, Handan 056015, China
*
Authors to whom correspondence should be addressed.
Materials 2021, 14(19), 5864; https://doi.org/10.3390/ma14195864
Submission received: 4 September 2021 / Revised: 25 September 2021 / Accepted: 29 September 2021 / Published: 7 October 2021

Abstract

:
The disposal of nonferrous metal tailings poses a global economic and environmental problem. After employing a clinker-free steel slag-based binder (SSB) for the solidification/stabilization (S/S) of arsenic-containing tailings (AT), the effectiveness, leaching risk, and leaching mechanism of the SSB S/S treated AT (SST) were investigated via the Chinese leaching tests HJ/T299-2007 and HJ557-2010 and the leaching tests series of the multi-process Leaching Environmental Assessment Framework (LEAF). The test results were compared with those of ordinary Portland cement S/S treated AT (PST) and showed that the arsenic (As) curing rates for SST and PST samples were in the range of 96.80–98.89% and 99.52–99.2%, respectively, whereby the leached-As concentration was strongly dependent on the pH of the leachate. The LEAF test results showed that the liquid–solid partitioning limit of As leaching from AT, SST, and PST was controlled by solubility, and the highest concentrations of leached As were 7.56, 0.34, and 0.33 mg/L, respectively. The As leaching mechanism of monolithic SST was controlled by diffusion, and the mean observed diffusion coefficient of 9.35 × 1015 cm2/s was higher than that of PST (1.55 × 10−16 cm2/s). The findings of this study could facilitate the utilization of SSB in S/S processes, replacing cement to reduce CO2 emissions.

1. Introduction

Nonferrous metals are an important basic material for the development of the Chinese economy [1]. However, the mining, processing, and smelting industry of non-ferrous metals is the most significant source of heavy metal and metalloid emissions in China (e.g., Hg, 53.6%; Cd, 88.9%; Pb, 81%; As, 61.8%) [2]. Mine wastewater, smelting slag, dust, and tailings are mainly piled up in tailings ponds, which poses high potential environmental risks [3]. It is imperative to develop effective and economically viable technologies to reduce pollution from the non-ferrous metal industry.
Backfilling is an ecological solidification/stabilization (S/S) method for the safe disposal of non-ferrous metal tailings, which could support underground goaf to prevent surface collapse, improve the recovery rate of resources, and prevent the release of contaminants from the tailings [4]. Ordinary Portland cement (OPC) is a traditionally used binder in backfilling S/S processes, but in the production of clinker, the raw materials need to be calcined in a rotary kiln at temperatures up to 1500 °C, leading to abundant emissions of CO2 in the process of decomposing the calcium carbonate into calcium oxide (CaO) and CO2. Cement accounts for 8% of total anthropogenic CO2 emissions [5]. The atmospheric CO2 concentration of about 420 ppm has already reached the halfway mark to 560 ppm which is double the preindustrial levels of 280 ppm [6]. Thus, any efforts to reduce carbon emissions are urgently needed. Research into developing low-carbon clinker-free binders or cement admixtures for S/S include ground granulated blast furnace slag (GGBFS) [7] as admixture, magnesium oxysulfate cement [8], red mud-enhanced magnesium phosphate cement [9], zero-valent iron or magnetic biochar [10], alkali-activated clay binder [11], fly ash-based Si-modified magnesia-style cement [12], fly ashes, and geopolymer binders surface-tailored with metakaolin composites [13]. However, few reports have been published on the application of steel slag [14,15,16,17,18]. Steel slag is a by-product of the steel-making process, known as overburnt clinker due to its mineral phase composition similar to cement clinker, of which 149.45 million tons were produced in China in 2019 with a comprehensive utilization rate of less than 30% [19]. The large accumulation of steel slag led to great pressure on the environment [20]. GGBFS is a by-product of the steel-making industry and is used as supplementary cementitious material. In the present study, steel slag-based binders (steel slag mass fraction ≥ 60 wt.%) (SSBs) composed of varying amounts of steel slag powder (SSP), GGBFS, and flue gas desulphurization gypsum (FGDG) were investigated as S/S binders. In the hydration process of SSBs, the relatively high alkalinity of SSP facilitates the breakage of Si–O and Al–O bonds in the GGBFS vitreous structure to form the anions S i O 4 4 and A l O 4 5 [21,22], which react with dissolved Ca2+ to form calcium silicoaluminate hydrate (C–A–S–H) gels [11,23]. The A l O 4 5 anions dissolved in solution transform from four-coordinated aluminum ions to six-coordinated aluminum ions [Al(OH)6]3− in alkaline environments, which react with Ca2+ and S O 4 2 ions dissolved from FGDG to form ettringite [24].
Since the leaching characteristics of S/S materials under different environmental conditions are of high concern, numerous leaching test methods have been proposed. The system proposed by Lewin et al. [25] classifies leaching tests based on whether the leachant is renewed or not as either extraction tests such as TCLP, SPLP, HJ/T 299-2007 [26], and HJ 557-2010 [27] or dynamic tests such as ASTM C1308-08 [28]. While a single leaching test could not evaluate S/S efficiency scientifically, the leaching test series of the Leaching Environmental Assessment Framework (LEAF) developed by the United States Environmental Protection Agency (EPA, Washington, D.C., WA, USA) [29] were used to obtain more accurate estimates of the release of targeted contaminants from SSB S/S treated materials. Considering the low-permeability monolithic property of SSB S/S treated materials, the most appropriate methods are Method 1313, Method 1315, and Method 1316, which provide data to approximate local chemical equilibria as a function of the pH of the extract or the liquid–solid ratio, for evaluating the maximal leaching concentration, and the rate of release under conditions where mass transport dominates the rate of constituent release, respectively.
In the present study, tailings with high As concentrations were collected as the study objects, where the leaching risk of other hazardous elements was low after S/S treatment. The leaching tests performed on SSB S/S treated tailings (SST) include the Chinese extraction tests HJ/T299-2007 [26] and HJ557-2010 [27] and the LEAF series tests (Method1313, Method 1315, and Method 1316) [29] to investigate the effectiveness, leaching risk, and leaching mechanism of the SST. And the potential to reduce carbon emissions of utilization of SSB compared to cement was also discussed. The findings of this study could facilitate the utilization of steel slag in backfilling S/S processes, replacing cement to reduce CO2 emission.

2. Materials and Methods

2.1. Raw Materials

The SSBs were composed of SSP, GGBFS, and FGDG, pulverized and grounded to a specific surface area of 440, 435, and 350 m2/kg, respectively. The chemical components of the raw materials are listed in Table 1, and the XRD patterns are shown in Figure 1. The main phase of SSP included dicalcium silicate (C2S), tricalcium aluminate (C3A), dicalcium ferrite (C2F), akermanite, (MgO)0.239(FeO)0.761 (RO Phase), CaO, and quartz, which belonged to low-alkaline steel slag (alkalinity, M, of 2.05, Equation (1) [30]). The GGBFS consisted of abundant glassy phases and a small amount of akermanite and C2S, which was the superior product due to the activity coefficient K = 1.82 > 1.6 (Equation (2)) according to the Chinese standard GB/T203-2008 (Granulated Blast Furnace Slag Used for Cement Production). The main phase of FGDG was CaSO4·2H2O. A polycarboxylic acid water reducer (WR) was used to achieve an acceptable flowability of the mortar.
M = W C a O / W S i O 2 + W P 2 O 5
K = W C a O + W M g O + W A l 2 O 3 / W S i O 2 + W M n O + W T i O 2
Arsenic-containing tailings (AT) were collected from a closed lead and zinc tailings pond in Hechi Nandan, Guangxi (China). The main components of the tailings were quartz, calcite, and fluorite, of which the D50 and D90 particle sizes were 42 and188 μm, respectively. According to the XANES analysis results of tailings in the same tailings pond in the literature [31], the main forms of arsenic (As) in tailings are arsenopyrite (66 wt.%), arsenate (17 wt.%) and arsenite (17 wt.%). The total As concentration of the tailings was 2098 mg/kg as determined with an Agilent 7500a ICP-MS system (Agilent Technologies, Santa Clara, CA, USA) after aqua regia digestion (concentrated HNO3 and HCl in a ratio of 1:3 (v/v)) according to the Chinese standard method HJ 803-2016.

2.2. Preparation of SST

In the preparation of SSTs, the different constituents of SSBs were mixed with tailings at specific ratios as outlined in Table 2; although sufficient FGDG must be present for GGBFS hydration, excessive FGDG may lead to matrix expansion in the later stage of the hydration reaction; therefore, the proportion of FGDG was fixed at 10% [32]. These SSBs were mixed with the tailings and water according to the following procedure whilst maintaining the binders-to-tailings (B/T), water-to-solid (W/S), and WR-to-solid (WR/S) mass ratios of 0.25, 0.19, and 0.01, respectively, which also applied to the OPC S/S treated AT (PST) sample set as control group. SSB and tailings were mixed for 1 min using a standard cement mortar mixer; then, distilled water containing the dissolved WR was added, and the blended mortar was mixed for another 5 min before being cast into steel molds (40 mm × 40 mm × 160 mm). All samples were cured in a moist cabinet at (40 ± 2) °C and (90 ± 1)% relative humidity (similar to the underground filling environment in Guangxi [33]) for 3 d and then de-molded and placed under the same curing conditions until the appropriate degree of ageing was achieved.
The fluidity of the prepared SST samples and the PST sample was 300 mm, meeting the needs of artesian backfill, which was determined according to the Chinese standard GB/T 2419-2005 (Method for Determination of Fluidity of Cement Mortar). The unconfined compressive strength (UCS) of the samples was obtained according to GB/T 17671-1999 (Test Method for Strength of Cement Mortar (ISO method)). With the increase of the SSP content in the SSBs, the 3-d, 7-d, and 28-d UCS of the SST samples decreased while the 90-d UCS of the SST samples displayed a fluctuating behavior (Table 2). Based on the intention to use steel slag in large quantities and meeting the UCS requirement of underground backfilling (1-5 MPa for 28 d [4]), T-3 was chosen to investigate the characteristic As-leaching behavior based on the leaching tests.

2.3. Leaching Tests

2.3.1. Extraction Tests

The single-batch extraction tests included a horizontal vibration method (HV) (HJ 557-2010, China). After being crushed and sieved to a particle size of less than 3 mm, the SST and PST samples were placed in deionized water with a liquid/solid ratio of 10 L/kg and were horizontally vibrated for 8 h at room temperature with an oscillation frequency of approximately 110 ± 10 per min before standing for a further 16 h. Furthermore, the sulfuric acid and nitric acid method (SN) (HJ/T299-2007, China) was employed. After being crushed and sieved to a particle size smaller than 9.5 mm, the SST and PST samples were placed in an extraction fluid with a liquid/solid ratio of 10 L/kg, prepared by adding a 2:1 (by mass) mixture of H2SO4 (18.4 N) and HNO3 (15.6 N) to deionized water until a target pH of 3.20 ± 0.05 was obtained; the sample mixtures were tumbled at (30 ± 2) rpm for 18 ± 2 h. These methods were employed on the SST and PST samples at a 3-d, 7-d, 28-d, and 90-d curing period. The As curing rate was calculated according to Equation (3):
Curing   Rate   =   1     C S / S / C T   ×   100 %
where Cs/s is the concentration of As leached from SST and PST, μg/L; CT is the concentration of As leached from untreated tailings, μg/L.

2.3.2. Leaching Environmental Assessment Framework Tests

Leaching Tests as per Method 1313

The leaching test was conducted as per Method 1313 of the EPA (“Liquid–Solid Partitioning (LSP) as a Function of Extract pH for Constituents in Solid Materials Using a Parallel Batch Extraction Procedure (LSP-pH)”) to investigate the influence of equilibrium pH of the leachate on characteristic leaching behavior. T-3 and PST samples were crushed and sieved to a particle size of less than 0.3 mm. Dilute nitric acid (2.0 N) and aqueous potassium hydroxide (1.0 N) solutions were used to adjust the pH, and samples were tumbled at (30 ± 2) rpm for (24 ± 2) h to achieve liquid–solid equilibrium. A liquid-to-solid ratio of 10 mL/g-dry was used for all batch tests. The final pH targets of the extracts were 2 ± 0.5, 4 ± 0.5, 5.5 ± 0.5, 7 ± 0.5, 8 ± 0.5, 9 ± 0.5, 10.5 ± 0.5, 12 ± 0.5, and 13 ± 0.5. Since the pH-dependent leaching of many elements may be sensitive to minor fluctuations in leachate pH, it is necessary to interpolate the test results of Method 1313 to the specified pH-target values to provide reproducible and comparative results. Interpolated leachate concentrations are obtained by standard linear interpolation of log-transformed data from two neighboring Method 1313 leachates (Equation (4)):
log C = log C a + p H p H a   ×   log C b log C a / p H b p H a
where log C is the log-transform of the leachate concentration interpolated to the target-pH value of 2, 4, 5.5, 7, 8, 9, 10.5, 12, or 13, log(mg/L); pHa and pHb are the measured pH value of leachate a and leachate b close to the target pH value; log Ca and log Cb are the log-transforms of the measured leachate concentration at pHa and pHb, respectively, log(mg/L).

Leaching Tests as per Method 1316

The leaching test was conducted as per Method 1316 of the EPA (“Liquid–Solid Partitioning (LSP) as a Function of Liquid–Solid Ratio for Constituents in Solid Materials Using a Parallel Batch Extraction Procedure (LSP-L/S)”) to investigate the influence of the liquid–solid ratio (L/S) on characteristic leaching behavior. T-3 samples were crushed and sieved to a particle size of less than 0.3 mm for 85 wt.% of the sample. The L/S was 10, 5, 2, 1, and 0.5 mL/g-dry with deionized water as leachant, and samples were tumbled at (30 ± 2) rpm for (24 ± 2) h.

Leaching Tests as per Method 1315

The leaching test was conducted as per Method 1315 of the EPA (“Mass Transfer Rates of Constituents in Monolithic or Compacted Granular Materials Using a Semi-dynamic Tank Leaching Procedure”) to investigate characteristic mass-transfer-based leaching behavior from a monolithic sample under completely saturated conditions whereby the leachant was renewed at the prescribed intervals. The T-3 and PST amples cured for 90 d (50 × 50 × 50 mm3) were completely immersed in deionized water in sealed vessels. The ratio of liquid to exposed surface area was maintained at 10 mL/cm2 for all samples. Leachates were collected at intervals of 0.8, 1, 2, 7, 14, 28, 42, 49, 63, and 112 d.
The flux (F) across the exposed surface and the observed effective diffusion coefficient (Dobs) of the T-3 sample cured for 90 d (T-3-90d) and the PST sample cured for the same time (PST-90d) can be calculated by Equations (5) and (6); if diffusion is the dominant mechanism, de Groot and van der Sloot [34] suggested the relationship described by Equation (7).
F i = M i / t i t i 1
D o b s = a n A n / Δ t n 2 × V / S 2 × T n
log B t   =   1 2 log t + log U m a x d D o b s / π
where Fi is the flux in interval i, mg/m2·s; Mi is the mass released during the current leaching interval i, mg/m2; ti is the cumulative time at the end of the current leaching interval i, s; ti-1 is the cumulative time at the end of the previous leaching interval i-1, s; Dobs is the observed effective diffusion coefficient in chemically reactive systems, m2/s; an is the mass released during leaching interval n, mg; An is the initial concentration, mg; Δtn is the leaching interval, days; V is the volume of the solidified monolithic samples, m3; S is the surface area of the solidified monolithic samples, m2; Tn is the generalized mean of leaching time, s; Bt is the cumulative maximum release of the compound, mg/m2; Umax is the maximum leachable quantity, mg/kg; d is the bulk density of the S/S product, kg/m3.
After conducting leaching test Method 1315, the UCS of the monolithic samples was tested to investigate their physical stability. All leachates were filtered through 0.45-μm polypropylene membrane filters, preserved with HNO3, and stored at 4 °C. As concentrations were determined by a PerkinElmer Optima 8300 ICP-OES (Perkin Elmer, Cumberland, NJ, USA) or an Agilent 7500a ICP-MS (Agilent Technologies, Santa Clara, CA, USA) system. Method blanks (deionized water), analytical blanks, and replicates were prepared and analyzed for quality control purposes.

3. Results

3.1. Extraction Tests Results

Figure 2 shows the results of the single-batch extraction tests. All leached-As concentrations of SST samples were below the type IV water threshold of the Chinese standard as published in the Standard for Groundwater Quality (GB/T 14848-2017) (50 μg/L, transverse solid line) with the exception of T-4-7d (52 μg/L), while the leached-As concentrations of the PST samples were below the type III water threshold (10 μg/L, transverse dotted line). The difference of the leached-As concentrations of samples cured for 3, 7, 28, and 90 d indicated that the hydration reaction affected the As S/S. The leachate pH values for SST and PST samples were in the range of 11.43–12.12 and 12.39–12.62, respectively. With the increase in SSP content in SSB, the leachate pH increased due to the intrinsically high pH of SSP. The As curing rate (Equation (3)) for SST and PST samples were in the range of 96.80–98.89% and 99.52–99.92%, respectively.

3.2. Results of pH-Dependent LSP

Figure 3 presents the acid/basic neutralization capacity (ANC/BNC) and LSP As, Ca, Si, Al, and Fe concentrations as a function of the leachate pH value. The natural pH of T-3 (3 d, 11.79; 28 d, 11.83; 90 d, 12.16) and P (28 d, 12.55; 90 d, 12.56) increased sharply compared to the untreated AT (8.36), and the ANC (leachate pH = 7) of T-3 (~2 meq/g-dry) and P (~4 meq/g-dry) significantly improved in comparison to the untreated AT (~0 meq/g-dry). Accounting for the complete exposure of the tailings into acid rain and acid mine wastewater caused by pyrite oxidation, the applicable pH domain of 4–9 for AT was chosen rather than the default 5.5–9 used for the natural pH of soil, while the pH domain for T-3-90d and PST-90d was chosen as 7–13 to capture the natural pH and anticipated environmental processes (e.g., carbonation) that may occur over time (Figure 3a,b).
Figure 3b illustrates the pH-dependent As equilibrium concentration of AT, T3-90d, and PST-90d. The As concentration of AT increased continuously from 1.044 mg/L (natural pH 8.36) with added KOH and reached 4.476 mg/L at pH 13 due to the dissolution of arsenopyrite (Equation (8)) and the deprotonation in alkaline solution because of the amphoteric property of As [35]. With decreasing pH, the As concentration of AT decreased to the lowest value at pH 5.5 (0.626 mg/L) and then increased to the highest value at pH 2 (25.491 mg/L), which was attributed to the adsorption of iron and aluminum oxides/hydroxides on As in different valence states and the dissolution of the oxides/hydroxides as the pH went down [36]. The As equilibrium concentration of T-3 and PST was between one and two orders of magnitude lower than that of AT over a pH range of 2–13 due to the reaction of hydration products of SSB and OPC with As in AT; the As concentration of T-3-90d was 0.0276 mg/L at natural pH 12.16, while that of PST-90d was 0.004 mg/L at natural pH 12.56. The HV and SN leaching test results are also presented, which data sets were close to the equilibrium curves, indicating that the extraction test results depended significantly on the pH of the leachate.
2 FeAsS + 10 O H + 7 O 2 = F e 2 O 3 + 2 A s O 4 3 + 2 S O 4 2 + 5 H 2 O
Figure 3c–f present the equilibrium concentrations of the main elements of T3-90d and PST-90d as a function of leachate pH by interpolation to the target pH for clarity (Equation (4)), which were closely related to the release of As. The Ca concentrations of natural T3-90d and PST-90d were 199 and 803 mg/L, respectively, which increased with decreasing pH and decreased when base was added. The line in Figure 3c represents the solubility equilibrium curve of Ca(OH)2 at 25 °C (Equation (9)), indicating that the solubility of Ca(OH)2 controlled the Ca release over pH 12–13 for PST-90d and at pH 13 for T3-90d, leading to the decline in Ca concentration to 38 mg/L and 35 mg/L, respectively, at pH 13. The natural pH for PST-90d was close to the pH of 12.60 for saturated Ca(OH)2 solution at 25 °C because the hydration products of OPC contain Ca(OH)2 (~25 wt.% [37]); since the hydration reaction of SSB only contributes to a very small amount of Ca(OH)2 [11], the leachate was unsaturated in Ca for T3-90d with added KOH over the pH range of 12–13. Figure 3d shows that the Si concentration increased with the addition of acid, except for the observed plateaus for T-3-90d and PST-90d over the pH ranges of 5.5–11 and 8–11, respectively.
K s p = C C a 2 + × C o H 2 = C C a 2 + × 10 p H 14 2     M C a 2 + = 1.88 × 10 27 2 p H   25   ° C
Figure 3e shows the rapid increase in Al concentration of T3-90d and PST-90d below pH 4 in accordance with the aluminum hydroxide solubility equilibrium, which adsorbed As effectively at pH 4–7.7 [38,39], while Al concentrations did not increase sharply at pH > 9, where the C-A-S-H and ettringite influenced the release of Al [40]. The Fe concentration in solution as a function of pH is often a useful indicator of the redox state of a system. At pH values between 4.8 and 10, the Fe3+ concentration would remain below 10 μg/L due to the Fe(OH)3 solubility equilibrium while Fe(OH ) 4 appeared at pH > 10, increasing the Fe concentration. Thus, the Fe concentration presented in Figure 3f indicated the presence of moderately and weekly reducing conditions for T3-90d and PST-90d, respectively; according to the results of geochemical speciation modeling [41], these conditions were caused by the different states of Fe in SSP (Fe, FeO, Fe3O4, Fe2O3, 2CaO·Fe2O3, and MgO·2FeO [42]) and OPC (4CaO·Al2O3·Fe2O3).

3.3. Results of L/S-Dependent LSP

Figure 4 presents the As LSP behavior as a function of L/S, where the leachate pH of T-3 and PST remained at ~12 and ~12.6 respectively, over the L/S range of 0.5–10. The As concentration of T3-90d and PST-90d decreased and then remained unchanged at L/S ≥ 2 as the L/S increased. The As concentration of T3-28d and PST-28d first decreased in a similar way compared to the samples cured for 90 d but exhibited an upward trend at L/S ≥ 5 with significantly higher values at an L/S of 10, which is consistent with the characteristic As leaching behavior in the pH range of 12–13 (Figure 3b).

3.4. Results of Mass Transfer Rates

Figure 5a shows the UCS of T3 and PST at curing times of 3, 7, 28, and 90 d and after 112 d of semi-dynamic leaching tests. The UCS of P reached its highest value after 28 d of curing, while the UCS of T3 still greatly improved from 28 d to 90 d. After the semi-dynamic leaching tests, the UCS of T3-90d and PST-90d decreased by 12.14% and 8.78%, respectively. Figure 5b,c show the leachate pH and As concentrations of every interval, where the pH of PST-90d fluctuated at 11.5 and that of T3-90d ranged from ~10 to ~11 except at the first 2-h leaching interval (pH 7.81), and the As concentrations of T3-90d and PST-90d ranged from 2–20 and 0–5 μg/L, respectively, which were far lower than the pH-dependent LSP results (Figure 3b), indicating that the “dilute” boundary condition was met for As mass transfer. The growth rate of cumulative As release of T3-90d and PST-90d decreased gradually with extended leaching time (Figure 5d), and the cumulative As release of T3-90d reached 9.674 mg/m2 at 112 d, which was 8.28 times higher than that of PST-90d (1.168 mg/m2, Table 3). Log-transformed As flux (Equation (5)) during the intervals and log-transformed cumulative As release are presented in Figure 5e,f, respectively, as a function of the log-transformed leaching time. The log-log plot of cumulative As release and leaching time of T3-90d and PST-90d can be fitted by a straight line throughout the entire leaching duration with slopes of 0.48 (R2 = 0.96) and 0.47 (R2 = 0.85), respectively, indicating that the As leaching mechanisms were similarly controlled by diffusion.

4. Discussion

This study demonstrates that the usage of SSP as the main component of binders for AT S/S treatment is feasible based on the results of UCS, the extraction tests, and the LEAF series tests. Only single-point leaching data could be provided by the extraction leaching tests, and the results are greatly controlled by the pH of the leachate. Notably, LEAF leaching tests could provide more scientific information. Combining Method 1313 and Method 1316 test results, full LSP screening assessment demonstrated that the LSP limits of AT, T3-90d, and PST-90d were controlled by solubility according to Equation (10) [43], and the highest concentrations over the pH and L/S range were 7.56 (at pH 4), 0.34 (at pH 13), and 0.33 (at pH 9) mg/L, respectively. When considering the effect of a relatively small volume of leachate interacting with a larger groundwater body and associated transport toward a down-gradient exposure point through the use of dilution and attenuation factors (DAF), a DAF value of 10 was assumed for oxyanions when risk assessment values were not available [44]. The DAF-related leaching assessment ratio (ARDAF) of AT, T3-90d, and PST-90d were 75.6, 3.4, and 3.3, respectively (Table 4), indicating that AT poses a high environmental pollution risk and SSB with 80 wt.% SSP is highly effective on S/S of AT and equally effective compared to OPC. However, the above results were based on the LSP-pH and LSP-L/S equilibrium analysis, revealing the maximum degree of leaching. The monolithic property of S/S waste controlling the leaching rate was not considered. Method 1315 leaching test results showed that As leaching from monolithic T3-90d and PST-90d was controlled by diffusion with very low values of Dobs (T3-90d, 9.35 × 10−15 cm2/s; PST-90d, 1.55 × 10−16 cm2/s), which could be applied for “controlled utilization” [45].
I f   C max p H 2 ,   9 ,   13 × 1 0.28 C max p H   d o m a i n × 1 + 0.28 > 1 ,   L S P   l i m i t   w a s   c o n t r o l l e d   b y   s o l u b i l i t y
The results of the Method 1313 leaching tests also included Ca, Si, Al, and Fe leaching data related to the As release at final leachate pH ranges of 2–13 for T3-90d and PST-90d (Table 5), which provided an approach to investigate the S/S mechanism. As reported in literature, Ca–As co-precipitation considerably influenced the release of As at alkaline pH in S/S matrices (Equations (11)–(13)) [33], and As was dissolved in large quantities at Ca concentrations below 100 mg/L [46]. Thus, the characteristic As leaching properties of T-3-90d and PST-90d over pH 12–13 (Figure 3b) was controlled by the equilibrium between Ca–As co-precipitation and dissolution and influenced by the Ca equilibrium concentrations of Ca(OH)2. The hydration products of SSB and OPC, ettringite and C–A–S–H, were dissolved in the pH range of 7–12 (Table 5) [47], while As leaching did not increase with the leaching of Ca, Si, and Al at pH 7–10.5, possibly because the products related to the hydration of As first dissolved and were then fixed by Fe(OH)3 gels. The moderately reducing property of SSP would reduce As(V) to As(III), but the As concentrations of T-3-90d in the pH range of 2–10.5 did not increase compared with PST-90d (Figure 2b), indicating that Fe(III) would stabilize As(V) and As(III) at pH > 4. Other techniques, such as microanalysis, are needed to verify the controlling S/S mechanism at every final leachate pH interval to identify a method to promote S/S efficiency.
5 Ca 2 + + 3 AsO 4 3 + OH = Ca 5 AsO 4 3 OH ,   k s p = 10 40.12   ( 25   ° C )
4 Ca 2 + + 2 AsO 4 3 + 2 OH = Ca 4 OH 2 AsO 4 2 · 4 H 2 O , k s p   = 10 27.49   25   ° C
Ca 2 +   +   HAsO 3 2   =   CaHAsO 3 ,   k s p   = 10 6.52   ( 25   ° C )
The main greenhouse gas component of cement industry is CO2. According to different emission sources, it includes the process emissions generated by carbonate decomposition and the small amount of organic carbon combustion in the raw material, fuel combustion emissions, and indirect emissions generated by power consumption in the production process [48]. The cement carbon emission factor (CO2 emission per unit of cement produced) ranges from 0.65 to 0.92 t CO2/t-cement [49,50,51]. The carbon emission of SSB mainly comes from the indirect emissions generated by power consumption in the grinding process. The CO2 emission factor of electricity consumption is about 1 kg CO2/KWh. According to the different grinding processes, the power consumption per unit of steel slag powder converted to 450 m2/kg is about 31-59 kWh/t [52]. Blast furnace slag and flue gas desulphurization gypsum is easier to grind than steel slag. Even if the CO2 emissions of SSB is calculated according to the grinding energy consumption of steel slag, it is about 0.031–0.059 t CO2/t-SSB, which is much lower than cement. Thus, the utilization of SSB in S/S process has great potential in carbon reduction.

5. Conclusions

In the present study, a series of leaching tests were performed on SST to evaluate the feasibility of SSB as binder for AT S/S. Compared with the single-batch extraction leaching tests, the multi-process LEAF tests could present more detailed and scientific information on the waste leaching risk and for the evaluation of the S/S effectiveness of the binders. Conducting leaching tests over a range of pH values provided an approach to investigate the S/S mechanism. Based on the results obtained from this study, the following conclusions can be drawn:
  • The extraction test results showed that the As curing rate for SST and PST samples were in the range of 96.80–98.89% and 99.52–99.2%, respectively.
  • The LSP limits of AT, T3-90d, and PST-90d were controlled by solubility, and the highest concentrations over the investigated pH and L/S range were 7.56 (at pH 4), 0.34 (at pH 13), and 0.33 (at pH 9) mg/L, respectively.
  • The As leaching mechanism of monolithic SST (T3-90d) was controlled by diffusion, and the mean Dobs of T3-90d of 9.35 × 10−15 cm2/s was higher than that of PST-90d (1.55 × 10−16 cm2/s).
  • As leaching of SST (T3-90d) and PST (PST-90d) was controlled by the equilibrium between Ca–As co-precipitation and dissolution and influenced by the Ca equilibrium concentrations of Ca(OH)2 when the leachate pH was in the range of 12–13. Furthermore, As leaching was strongly correlated to Fe-ion leaching when the leachate pH was less than 10.5.
  • The utilization of SSB in S/S process has great potential in carbon reduction.

Author Contributions

Formal analysis, W.G.; funding acquisition, X.L.; investigation, W.G. and Y.Z.; visualization, G.T.; methodology, W.G.; project administration, S.Z.; resources, S.Z.; supervision, S.Z.; validation, W.G., Z.L., S.Z. and W.N.; writing—original draft, W.G.; writing—review and editing, Z.L., S.Z. and W.N. All authors have read and agreed to the published version of the manuscript.

Funding

This work was funded by the Key Research and Development Program of Hebei Province (No. 19273805D).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Liu, G.; Jia, F.; Yue, Q.; Ma, D.; Pan, H.; Wu, M. Decoupling of nonferrous metal consumption from economic growth in China. Environ. Dev. Sustain. 2016, 18, 221–235. [Google Scholar] [CrossRef]
  2. Ministry of Ecology and Environment of the People’s Republic of China. Annual Report on Environmental Statistics. 2017. Available online: http://www.mee.gov.cn/hjzl/sthjzk/sthjtjnb/ (accessed on 8 August 2021).
  3. Cheng, X.; Qi, W.; Huang, Q.; Zhao, X.; Fang, R.; Xu, J. Typical Geo-Hazards and Countermeasures of Mines in Yunnan Province, Southwest China. IOP Conf. Series Earth Environ. Sci. 2016, 44, 022008. [Google Scholar] [CrossRef] [Green Version]
  4. Li, J.; Zhang, S.; Wang, Q.; Ni, W.; Li, K.; Fu, P.; Hu, W.; Li, Z. Feasibility of using fly ash–slag-based binder for mine backfilling and its associated leaching risks. J. Hazard. Mater. 2020, 400, 123191. [Google Scholar] [CrossRef] [PubMed]
  5. Habert, G.; Miller, S.A.; John, V.M.; Provis, J.L.; Favier, A.; Horvath, A.; Scrivener, K.L. Environmental impacts and decarbonization strategies in the cement and concrete industries. Nat. Rev. Earth Environ. 2020, 1, 559–573. [Google Scholar] [CrossRef]
  6. Voosen, P. Earth’s climate destiny finally seen more clearly. Science 2020, 369, 354–355. [Google Scholar] [CrossRef]
  7. Wang, L.; Yu, K.; Li, J.-S.; Tsang, D.C.; Poon, C.S.; Yoo, J.-C.; Baek, K.; Ding, S.; Hou, D.; Dai, J.-G. Low-carbon and low-alkalinity stabilization/solidification of high-Pb contaminated soil. Chem. Eng. J. 2018, 351, 418–427. [Google Scholar] [CrossRef]
  8. Guo, B.; Tan, Y.; Wang, L.; Chen, L.; Wu, Z.; Sasaki, K.; Mechtcherine, V.; Tsang, D.C. High-efficiency and low-carbon remediation of zinc contaminated sludge by magnesium oxysulfate cement. J. Hazard. Mater. 2020, 408, 124486. [Google Scholar] [CrossRef]
  9. Wang, L.; Chen, L.; Guo, B.; Tsang, D.C.; Huang, L.; Ok, Y.S.; Mechtcherine, V. Red mud-enhanced magnesium phosphate cement for remediation of Pb and As contaminated soil. J. Hazard. Mater. 2020, 400, 123317. [Google Scholar] [CrossRef]
  10. Li, J.; Zhang, Y.; Wang, F.; Wang, L.; Liu, J.; Hashimoto, Y.; Hosomi, M. Arsenic immobilization and removal in contaminated soil using zero-valent iron or magnetic biochar amendment followed by dry magnetic separation. Sci. Total. Environ. 2021, 768, 144521. [Google Scholar] [CrossRef]
  11. Wang, L.; Cho, D.-W.; Tsang, D.C.; Cao, X.; Hou, D.; Shen, Z.; Alessi, D.; Ok, Y.S.; Poon, C.S. Green remediation of As and Pb contaminated soil using cement-free clay-based stabilization/solidification. Environ. Int. 2019, 126, 336–345. [Google Scholar] [CrossRef]
  12. Wang, L.; Chen, L.; Cho, D.-W.; Tsang, D.C.; Yang, J.; Hou, D.; Baek, K.; Kua, H.W.; Poon, C.S. Novel synergy of Si-rich minerals and reactive MgO for stabilisation/solidification of contaminated sediment. J. Hazard. Mater. 2018, 365, 695–706. [Google Scholar] [CrossRef]
  13. Rasaki, S.A.; Bingxue, Z.; Guarecuco, R.; Thomas, T.; Minghui, Y. Geopolymer for use in heavy metals adsorption, and advanced oxidative processes: A critical review. J. Clean. Prod. 2018, 213, 42–58. [Google Scholar] [CrossRef]
  14. Xiao, B.; Wen, Z.; Miao, S.; Gao, Q. Utilization of steel slag for cemented tailings backfill: Hydration, strength, pore structure, and cost analysis. Case Stud. Constr. Mater. 2021, 15, e00621. [Google Scholar] [CrossRef]
  15. Feng, Y.-S.; Zhou, S.-J.; Xia, W.-Y.; Du, Y.-J. Solidify/stabilise a heavy metal-contaminated soil using a novel steel slag-based binder. Environ. Geotech. 2020, 1–16. [Google Scholar] [CrossRef]
  16. Nejad, Z.D.; Rezania, S.; Jung, M.C.; Al-Ghamdi, A.A.; Mustafa, A.E.-Z.M.; Elshikh, M.S. Effects of fine fractions of soil organic, semi-organic, and inorganic amendments on the mitigation of heavy metal(loid)s leaching and bioavailability in a post-mining area. Chemosphere 2021, 271, 129538. [Google Scholar] [CrossRef] [PubMed]
  17. Singh, S.; Jyoti; Vashistha, P. Development of newer composite cement through mechano-chemical activation of steel slag. Constr. Build. Mater. 2020, 268, 121147. [Google Scholar] [CrossRef]
  18. Gao, W.; Ni, W.; Zhang, Y.; Li, Y.; Shi, T.; Li, Z. Investigation into the semi-dynamic leaching characteristics of arsenic and antimony from solidified/stabilized tailings using metallurgical slag-based binders. J. Hazard. Mater. 2019, 381, 120992. [Google Scholar] [CrossRef] [PubMed]
  19. Zhao, L.; Zhang, F. Comprehensive Utilization and Development Prospect of Steel Slag Resources. Mater. Rep. 2020, 34, 1319–1322+1333. Available online: https://kns.cnki.net/kcms/detail/detail.aspx?FileName=CLDB2020S2065&DbName=CJFQ2020 (accessed on 8 August 2021).
  20. Jiang, Y.; Ling, T.-C.; Shi, C.; Pan, S.-Y. Characteristics of steel slags and their use in cement and concrete—A review. Resour. Conserv. Recycl. 2018, 136, 187–197. [Google Scholar] [CrossRef]
  21. Liao, Y.; Jiang, G.; Wang, K.; Al Qunaynah, S.; Yuan, W. Effect of steel slag on the hydration and strength development of calcium sulfoaluminate cement. Constr. Build. Mater. 2020, 265, 120301. [Google Scholar] [CrossRef]
  22. Li, Y.; Ni, W.; Gao, W.; Zhang, Y.; Yan, Q.; Zhang, S. Corrosion evaluation of steel slag based on a leaching solution test. Energy Sources Part A Recover. Util. Environ. Eff. 2018, 41, 790–801. [Google Scholar] [CrossRef]
  23. Wang, L.; Geddes, D.; Walkley, B.; Provis, J.L.; Mechtcherine, V.; Tsang, D.C. The role of zinc in metakaolin-based geopolymers. Cem. Concr. Res. 2020, 136, 106194. [Google Scholar] [CrossRef]
  24. Li, Y.; Wu, B.; Ni, W.; Mu, X. Synergies in early hydration reaction of slag-steel slag-gypsum system. J. Northeast. Univ. 2020, 41, 6. [Google Scholar] [CrossRef]
  25. Lewin, K.; Bradshaw, K.; Blackley, N.C.; Turrell, J.; Hennings, S.M.; Flaving, R.J. Leaching Tests for Assessment of Contaminated Land: Interim NRA Guidance; National Rivers Authority R&D Note 301; National Rivers Authority: Bristol, UK, 1994. [Google Scholar]
  26. SEPA. Solid Waste-Extraction Procedure for Leaching Toxicity-Sulphuric Acid & Nitric Acid Method; SEPA: Beijing, China, 2007. [Google Scholar]
  27. SEPA. Solid Waste-Extraction procedure for leaching toxicity-Horizontal Vibration Method; SEPA: Beijing, China, 2010. [Google Scholar]
  28. ASTM. Standard Test Method for Accelerated Leach Test for Diffusive Releases from Solidified Waste and a Computer Program to Model Diffusive, Fractional Leaching from Cylindrical Waste Forms; ASTM International: West Conshohocken, PA, USA, 2008. [Google Scholar]
  29. Agency U.S.E.P. Leaching Environmental Assessment Framework (LEAF) Methods and Guidance. 2017. Available online: https://www.epa.gov/hw-sw846/leaching-environmental-assessment-framework-leaf-methods-and-guidance (accessed on 8 August 2021).
  30. Zhao, H.; Yu, Q.; Wei, J.; Li, J.; Gong, C. Influence on composition and morphology of mineral of steel slag and cementitious property. J. Wuhan Univ. Technol. 2010, 32, 22–26+38. [Google Scholar] [CrossRef]
  31. Jian, L.; Huang, Z.; Liu, Y.; Yang, Z.; Hu, T. Comparative analysis of arsenic speciation in sediments of the Diaojiang River using X-ray absorption near edge structure spectra and sequential chemical extraction. Res. Environ. Sci. 2012, 25, 7–820. [Google Scholar] [CrossRef]
  32. Gao, W.; Li, Z.; Zhang, S.; Zhang, Y.; Fu, P.; Yang, H.; Ni, W. Enhancing Arsenic Solidification/Stabilisation Efficiency of Metallurgical Slag-Based Green Mining Fill and Its Structure Analysis. Metals 2021, 11, 1389. [Google Scholar] [CrossRef]
  33. Zhang, Y.; Zhang, S.; Ni, W.; Yan, Q.; Gao, W.; Li, Y. Immobilisation of high-arsenic-containing tailings by using metallurgical slag-cementing materials. Chemosphere 2019, 223, 117–123. [Google Scholar] [CrossRef]
  34. de Groot, G.J.; van der Sloot, H.A. Determination of leaching characteristics of waste materials leading to environmental product certification. In Stabilization and Solidification of Hazardous, Radioactive, and Mixed Wastes; Gilliam, T., Wiles, C., Eds.; ASTM International: West Conshohocken, PA, USA, 1992; Volume 2, Available online: https://doi.org/10.1520/STP19548S (accessed on 8 August 2021). [CrossRef]
  35. Carlito, B.T.; Toshifumi, I.; Mylah, V.T.; Ilhwan, P.; Einstine, M.O.; Mayumi, I.; Naoki, H. Arsenic, selenium, boron, lead, cadmium, copper, and zinc in naturally contaminated rocks: A review of their sources, modes of enrichment, mechanisms of release, and mitigation strategies. Sci. Total. Environ. 2018, 645, 1522–1553. [Google Scholar] [CrossRef]
  36. Almeida, C.C.; Fontes, M.P.F.; Dias, A.C.; Pereira, T.T.C.; Ker, J.C. Adsorption and desorption of arsenic and its immobilization in soils. Sci. Agricol. 2021, 78, 11. [Google Scholar] [CrossRef]
  37. Chen, Q.Y.; Tyrer, M.; Hills, C.D.; Yang, X.M.; Carey, P. Immobilisation of heavy metal in cement-based solidification/stabilisation: A review. Waste Manag. 2009, 29, 390–403. [Google Scholar] [CrossRef] [PubMed]
  38. Huang, X.; Zhu, C.; Wang, Q.; Yang, G. Mechanisms for As(OH)3 and H3AsO4 adsorption at anhydrous and hydrated surfaces of gibbsite and possibility for anionic As(III) and As(V) formation. Appl. Surf. Sci. 2020, 525, 11. [Google Scholar] [CrossRef]
  39. Tiberg, C.; Sjstedt, C.; Eriksson, A.K.; Klysubun, W.; Gustafsson, J.P. Phosphate competition with arsenate on poorly crystalline iron and aluminum (hydr)oxide mixtures. Chemosphere 2020, 255, 8. [Google Scholar] [CrossRef]
  40. Deng, G.; He, Y.; Lu, L.; Hu, S. Evolution of aluminate hydrate phases in fly ash-cement system under the sulfate conditions. Constr. Build. Mater. 2020, 252, 11. [Google Scholar] [CrossRef]
  41. US EPA. Leaching Test Relationships, Laboratory-to-Field Comparisons and Recommendations for Leaching Evaluation using the Leaching Environmental Assessment Framework (LEAF); US EPA: Washington, DC, USA, 2014.
  42. Piatak, N.M.; Parsons, M.B.; Seal, R.R. Characteristics and environmental aspects of slag: A review. Appl. Geochem. 2015, 57, 236–266. [Google Scholar] [CrossRef]
  43. US EPA. Leaching Environmental Assesment Framwork (LEAF) How-To Guide; US EPA: Washington, DC, USA, 2017; p. 92.
  44. US EPA. Human and Ecological Risk Assessment of Coal Combustion Residuals; US EPA: Washington, DC, USA, 2014.
  45. Zhang, Y.; Gao, W.; Ni, W.; Zhang, S.; Li, Y.; Wang, K.; Huang, X.; Fu, P.; Hu, W. Influence of calcium hydroxide addition on arsenic leaching and solidification/stabilisation behaviour of metallurgical-slag-based green mining fill. J. Hazard. Mater. 2020, 390, 122161. [Google Scholar] [CrossRef] [PubMed]
  46. Cornelis, G.; Johnson, A.; Gerven, T.V.; Vandecasteele, C. Leaching mechanisms of oxyanionic metalloid and metal species in alkaline solid wastes: A review. Appl. Geochem. 2008, 23, 955–976. [Google Scholar] [CrossRef]
  47. Xie, Y.; Wu, X.; Fan, Y. Volatilization characteristic and model study of harmful constituents in process of treatment of MSWI fly ash by PC kiln. Cement 2010, 2, 1–5. [Google Scholar] [CrossRef]
  48. Liu, J.; Wang, L. Instance analysis on application of alternative materials to reduce CO2 emissions from cement industry. New Build. Mater. 2017, 44, 97–99+118. [Google Scholar]
  49. Shen, W.; Cao, L.; Li, Q.; Zhang, W.; Wang, G.; Li, C. Quantifying CO2 emissions from China’s cement industry. Renew. Sustain. Energy Rev. 2015, 50, 1004–1012. [Google Scholar] [CrossRef]
  50. Benhelal, E.; Zahedi, G.; Shamsaei, E.; Bahadori, A. Global strategies and potentials to curb CO2 emissions in cement industry. J. Clean. Prod. 2013, 51, 142–161. [Google Scholar] [CrossRef]
  51. Wei, J.; Geng, Y.; Shen, L.; Cen, K. Analysis of Chinese Cement Production and CO2 Emission. Environ. Sci. Technol. 2015, 38, 80–86. [Google Scholar] [CrossRef]
  52. Shen, J.; Qin, Z.; Shao, J.; Li, X. Application research of steel slag grinding process. Cement 2021, 1, 20–24. [Google Scholar] [CrossRef]
Figure 1. XRD patterns of the raw materials: (a) GGBFS; (b) SSP; (c) FGDG; (d) AT.
Figure 1. XRD patterns of the raw materials: (a) GGBFS; (b) SSP; (c) FGDG; (d) AT.
Materials 14 05864 g001
Figure 2. Concentration of leached As, leachate pH, and As curing rate of (a) the horizontal vibration method tests; (b) the sulfuric acid and nitric acid method tests.
Figure 2. Concentration of leached As, leachate pH, and As curing rate of (a) the horizontal vibration method tests; (b) the sulfuric acid and nitric acid method tests.
Materials 14 05864 g002
Figure 3. Method 1313 results for (a) acid/base neutralization capacity; (b) As concentrations; (c) Ca concentrations; (d) Fe concentrations; (e) Al concentrations; (f) Si concentrations as a function of leachate pH for T-3-90d and PST-90d.
Figure 3. Method 1313 results for (a) acid/base neutralization capacity; (b) As concentrations; (c) Ca concentrations; (d) Fe concentrations; (e) Al concentrations; (f) Si concentrations as a function of leachate pH for T-3-90d and PST-90d.
Materials 14 05864 g003
Figure 4. Method 1316 results for (a) pH; (b) As concentration; (c) As release from T3 and PST at curing for 28 d and 90 d.
Figure 4. Method 1316 results for (a) pH; (b) As concentration; (c) As release from T3 and PST at curing for 28 d and 90 d.
Materials 14 05864 g004
Figure 5. Method 1315 results: (a) comparison of UCS values of samples with different curing times to the results after 112 d of semi-dynamic leaching; (b) pH; (c) As concentration; (d) cumulative As release; (e) flux in the different intervals; (f) log-log plot of cumulative As release over time for T3-90d and PST-90d.
Figure 5. Method 1315 results: (a) comparison of UCS values of samples with different curing times to the results after 112 d of semi-dynamic leaching; (b) pH; (c) As concentration; (d) cumulative As release; (e) flux in the different intervals; (f) log-log plot of cumulative As release over time for T3-90d and PST-90d.
Materials 14 05864 g005
Table 1. Chemical components (wt.%) and pH value of the raw materials.
Table 1. Chemical components (wt.%) and pH value of the raw materials.
NotationSiO2TiO2Al2O3Fe2O3MnOP2O5MgOCaONa2OK2OSO3As2O3FLOIpH
AT53.230.125.071.650.70.11.1725.49-1.381.120.186.0510.617.64
SSP17.050.915.7322.333.631.729.0138.420.160.09---1.4211.96
GGBFS33.320.8515.431.010.520.0510.7836.890.490.38---0.1211.78
FGDG2.030.040.780.480.030.061.0430.010.060.1544.97--22.077.68
Table 2. Formulations for SSB, SST, and PST.
Table 2. Formulations for SSB, SST, and PST.
NotationSteel Slag-Based Binder
(Mass Fraction/ wt.%)
B/T
(w/w)
W/S
(w/w)
WR/S
(w/w)
Fluidity
(mm)
UCS (MPa)
SSPGGBFSFGDG3 d7 d28 d90 d
T-16030100.250.190.013009.112.214.315.1
T-27020103006.38.110.113.2
T-38010103003.54.87.214.5
T-4900103001.11.92.59.8
PST 110030012.518.224.126.2
1 OPC as binder for control group.
Table 3. Cumulative As release, mean Dobs, and log-transformed fitting curve equation.
Table 3. Cumulative As release, mean Dobs, and log-transformed fitting curve equation.
SampleCumulative Release /(mg/m2)Fitting Curve EquationR2SlopeMechanismMean Dobs
/(cm2/s)
28 d63 d112 d
T3-90d5.0917.9439.674logy = 0.48logx + 3.040.960.48diffusion9.35 × 10−15
PST-90d0.6030.9641.168logy = 0.47logx + 1.980.850.47diffusion1.55 × 10−16
Table 4. Full As LSP screening assessment, leaching assessment ratios (ARs), and leaching ARs considering dilution and attenuation (ARDAF) for AT, T3-90d, and PST-90d.
Table 4. Full As LSP screening assessment, leaching assessment ratios (ARs), and leaching ARs considering dilution and attenuation (ARDAF) for AT, T3-90d, and PST-90d.
AsThreshold Value 1 /(mg/L)Total Content /(mg/kg-dry)Method 1313Method 1316AR 2ARDAF 3
Available Content /(mg/L)pH for Available Content Max Conc. Over pH Domain /(mg/L)pH at Max Conc.Limitation by Available Content or SolubilityMax. Conc. over L/S RangeL/S at
Max. Conc.
AT0.012098 25.4927.564Solubility--75675.6
T3-90d0.01137610.9620.3413Solubility0.0250.5343.4
PST-90d0.0113767.7820.339Solubility0.0041333.3
1 The type III water threshold of the Chinese standard published in the Standard for Groundwater Quality (GB/T 14848-2017); 2 AR = Cmax/Threshold value; 3 ARDAF = AR/DAF.
Table 5. Mean concentrations of leached As, Ca, Si, Al, and Fe and growth trend at continuous pH intervals for T3-90d and PST-90d after Method 1313 leaching tests.
Table 5. Mean concentrations of leached As, Ca, Si, Al, and Fe and growth trend at continuous pH intervals for T3-90d and PST-90d after Method 1313 leaching tests.
pH13–1212–10.510.5–99–77–5.55.5–44–2
ElementMLC 1TrendMLC 1TrendMLC 1TrendMLC 1TrendMLC 1TrendMLC 1TrendMLC 1Trend
T3-90dAs0.2030.1140.1690.1870.2240.3735.761
Ca11770916952679521182509799
Si0.632.484.2589.25953.12257.81155
Al3.2612.5751.5732.58894.56386.71420
Fe0.7950.6420.7011.106162.5411.7684.1
PST-90dAs0.066↘↗0.0590.2280.2740.2240.3883.800
Ca723.5305257947435920113,15216,120
Si0.555.6613.5622.2130.5596.28392.7
Al0.7091.6101.9891.5723.098353.1791.3
Fe0.9950.9290.6650.3560.28670.65275.5
1 MLC is the mean leaching concentration, mg/L.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Gao, W.; Li, Z.; Zhang, S.; Zhang, Y.; Teng, G.; Li, X.; Ni, W. Solidification/Stabilization of Arsenic-Containing Tailings by Steel Slag-Based Binders with High Efficiency and Low Carbon Footprint. Materials 2021, 14, 5864. https://doi.org/10.3390/ma14195864

AMA Style

Gao W, Li Z, Zhang S, Zhang Y, Teng G, Li X, Ni W. Solidification/Stabilization of Arsenic-Containing Tailings by Steel Slag-Based Binders with High Efficiency and Low Carbon Footprint. Materials. 2021; 14(19):5864. https://doi.org/10.3390/ma14195864

Chicago/Turabian Style

Gao, Wei, Zifu Li, Siqi Zhang, Yuying Zhang, Guoxiang Teng, Xiaoqi Li, and Wen Ni. 2021. "Solidification/Stabilization of Arsenic-Containing Tailings by Steel Slag-Based Binders with High Efficiency and Low Carbon Footprint" Materials 14, no. 19: 5864. https://doi.org/10.3390/ma14195864

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop