2017 Volume 41 Issue 3 Pages 66-69
The magnetic-field-induced blend films, poly(L-lactide)(PLLA10) (Mn = 1.0 × 105) and poly(DL-lactide) (Mw = 1.0 × 104 (PDLLA1) and 1.0 × 105 (PDLLA10)) were prepared in isothermal process under the magnetic-field 10 T. The effects of amorphous region, i.e., molecular weight of PDLLA effect on crystallization and orientation of PLLA in the films were investigated using wide-angle X-ray diffraction and polarizing microscopy. The crystallinity of each films showed 60% at crystallization growth time tc = 30 hrs irrespective of PDLLA molecular weight. The degree of orientation of PLLA10/PDLLA10 film increased with increasing tc. We concluded that the blending with amorphous high-molecular-weigh PDLLA and crystallization in an applied high magnetic field is effective to achieve the PLLA film that has higher crystallinity and orientation.