2017 Volume 125 Issue 1 Pages 55-56
Waste soda lime glass powder was hydrothermally treated twice at 150°C, and the resulting powder was mixed with CaCO3 powder in the weight ratio of 1:3 and heat-treated at 1450°C. The resulting powder was identified as Ca3SiO5 as the main phase with small amounts of Ca3Al2O6, which are both common Portland cement sources. The elemental composition of the resulting cements was evaluated and all minor components (Cl, Na, SO3, etc.) were found to be less than the JIS standard value for eco-cement.