Solvent capacity of different substances on gutta-percha and Resilon

Mário Tanomaru-Filho^I; Tais d' Azeredo Orlando^I; Eduardo Antunes Bortoluzzi^II; Guilherme Ferreira da Silva^I; Juliane Maria Guerreiro Tanomaru^I

^IDepartment of Restorative Dentistry, Araraquara Dental School, São Paulo State University, Araraquara, SP, Brazil

^IIDepartment of Dentistry, Florianópolis Dental School, Federal University of Santa Catarina, Florianópolis, SC, Brazil

^{Correspondence} Correspondence: Prof. Dr. Mário Tanomaru Filho Rua Humaitá, 1680, Cx. Postal 331, Centro 14801-903 Araraquara, SP, Brasil Tel: +55-16-3301-6390. Fax: +55-16-3301-6392 E-mail: tanomaru@uol.com.br

ABSTRACT

The aim of this study was to evaluate the effectiveness of 3 solvents (eucalyptol, orange oil, and xylol) on 2 types of gutta-percha (conventional and thermoplastic) and Resilon. Specimens (10 mm diameter x 1 mm thick; n=7 per condition) were prepared and maintained at 37ºC for 48 h. Each specimen was weighed on a precision scale every 24 h until its mass was stable, at which time the initial mass was determined. Specimens (n=7) were then immersed in the solvent solutions and, after 48 h at 37ºC, they were reweighed at 24- h intervals, until stabilization (final mass). The difference between the final and the initial mass determined the solvent capacity of each solvent. Data were subjected to analysis of variance and Tukey's test at 5% significance level. The results demonstrated that xylol was the most effective, especially on conventional gutta-percha and Resilon (p<0.05). Eucalyptol and orange oil were more effective on thermoplastic gutta-percha than the other materials (p<0.05). It was concluded that all evaluated substances presented solvent action, but xylol was the most effective on both gutta-percha or Resilon.

Key words: Gutta-percha, retreatment, solvent, Resilon.

RESUMO

O objetivo deste estudo foi avaliar a efetividade de 3 solventes em 2 tipos de guta-percha e no Resilon. Os materiais avaliados foram: guta convencional (Endo points), guta termoplastificada (Endo points TP) e cones de Resilon (RE). Amostras circulares medindo 10 mm de diâmetro e 1 mm de espessura foram preparadas, sendo mantidas a 37°C por 48 h. Cada amostra, com o anel metálico, foi pesada em uma balança de precisão a cada 24 h até estabilização da massa, quando a massa inicial era determinada. As amostras (n=7) foram imersas, então, nas soluções solventes avaliadas (eucaliptol, óleo de laranja, e xilol). Após 48 h a 37ºC, as amostras foram pesadas outra vez a cada 24 h, até a estabilização (massa final). A diferença entre a massa final e inicial determinou a capacidade solvente de cada material. Os dados foram submetidos à análise de variância em nível de significância de 5% e teste de Tukey. Os resultados demonstraram que o xylol foi mais eficaz solvente, especialmente na guta convencional e no Resilon (p<0,05). O eucaliptol e o óleo de laranja foram mais eficazes sobre a guta thermoplastificada em relação aos outros materiais obturadores (p<0,05). Conclui-se que todas as substâncias testadas apresentam ação solvente, contudo, o xilol foi o mais efetivo sobre a guta-percha ou Resilon.

INTRODUCTION

The primary goal of the endodontic therapy is to completely fill and seal the root canal system. If these parameters are not achieved during endodontic therapy, failure might result (1,2). When endodontic retreatment is indicated, removal of the filling material is an important step in determining its success (3,4). Xylol and eucalyptol (5) are the most commonly used solvents.

An alternative solvent for gutta-percha and endodontic cements is orange oil (5-8). It is a readily available solvent, and may be a good alternative for use in endodontic retreatment, due to its lower toxicity compared to other substances (5,6). Oyama et al. (6) evaluated the solvent action of xylol, eucalyptol, halotane, chloroform, and orange oil on gutta-percha in root canals filled with gutta-percha and N-Rickert cement. Dissolution of gutta-percha was assessed by inserting a spacer 5 mm into the obturating cone. Results demonstrated that xylol and orange oil were more effective than the other solvents.

Resilon (Resilon Research LLC, Madison, CT, USA) is a thermoplastic synthetic polymer-based root canal filling material with similar properties to gutta-percha (9). It is also presented as cones and is used in association with Ephiphany (Pentron Clinical Technologies, Wallingford, CT, USA), a dual-cured resin-based cement. Somma et al. (10), evaluating the removal of 3 different filling materials (gutta-percha, Resilon, and EndoRez) during retreatment, observed that all techniques left remnants of filling material on the root canal walls.

Magalhães (11) evaluated the solubility of gutta-percha in 4 solvents: xylol, orange oil, eucalyptol, and chloroform. Xylol presented the best solvent capacity. Chloroform, orange oil, and eucalyptol performed similarly.

Martos et al. (7) evaluated the solubility of 3 types of root canal sealers in 3 organic solvents (eucalyptol, xylol, orange oil), and concluded that xylol and orange oil presented similar solvent effects with a significant solubility of the tested cements. The guidelines for choosing the ideal solvent for endodontic retreatment point to a balance between toxicity, clinical safety, and chemical solvent capacity. These characteristics should aid the clinician in solvent selection among the substances available (6).

Complete removal of existing root canal filling material is desirable during endodontic retreatment (12). Due to the introduction of alternatives to gutta-percha, such as Resilon, the purpose if this study was to evaluate the solvent action of different substances on gutta-percha and Resilon.

MATERIAL AND METHODS

Two different types of gutta-percha - conventional gutta-percha (Endopoints, Paraíba do Sul, RJ, Brazil), and thermoplastic gutta-percha (Endopoints TP; Endopoints) - and Resilon (RE; Pentron Clinical Technologies) were used.

Seven specimens (10 mm diameter x 1 mm thickness) from each material were fabricated for each evaluated solvent. The materials were immersed in water for 60 s in a water bath apparatus used to soften impression materials (Plastificador de Godiva Righetto e Cia., Campinas, SP, Brazil) at 70ºC, monitored by a digital thermometer.

Following that, the heated materials were placed in standard metallic ring molds with the previously described dimensions, and pressed between two glass slabs under constant controlled pressure of 0.5 N for 1 min. Next, the specimens were maintained at 37ºC for 24 h.

The evaluated solvents were: xylol (Biodinâmica, Ibiporã, PR, Brazil), orange oil (Biodinâmica), and eucalyptol (Biodinâmica).

Each specimen, along with its metallic ring, was weighed at 24-h intervals until stabilization of the mass for determination of the initial mass in grams. After weighing on a precision scale (model BL 210S; Sartorius, Gottingen, Germany, accurate to 0.0001), the specimens were immersed in one of the solvents at 24 ± 1ºC for 5 min, followed by immersion in distilled water for 20 min in order to neutralize the solvent action. After that, the specimens were removed from the water, stored at 37ºC for 48 h, and then reweighed at 24-h intervals, until stabilization of the mass in order to determine the final mass. The difference between the initial and final mass was calculated to determine the solvent action.

Data were subjected to analysis of variance and Tukey's test at 5% significance level.

RESULTS

Table 1 depicts the solvent action of eucalyptol, xilol and orange oil solvents on the studied root canal filling materials. The mean mass loss of gutta-percha and Resilon is presented.

DISCUSSION

Mechanical, thermal, or chemical techniques may be individually applied or combined for removal of filling materials during endodontic retreatment. However, it is often impossible to achieve complete removal of existing obturating materials from the canals (13,14).

The present results demonstrated that xylol was the solvent with the strongest action on Resilon. Orange oil presented no effect on Resilon, while eucalyptol had the lowest effect. A previous study (12) demonstrated that the Resilon/Epiphany system can be removed from the root canal with rotary files and chloroform.

In the present study, xylol was the most effective among the tested solvents in dissolving both conventional and thermoplastic gutta-percha. This finding is in agreement with those of Oyama et al. (6), but disagrees with the results of Martos et al. (7), who reported that orange oil and xylol presented similar solvent effect on gutta-percha.

Xylol is an aromatic organic solvent, usually available in the form of di-methyl-benzene. It presents as a universal solvent of organic substances, mainly hydrocarbons (which comprise the gutta-percha cones in the form of alkadienes) and the polyurethanes (which comprise the Resilon cones), probably due to destabilization of the covalent bonds between the carbon atoms (15).

De Oliveira et al. (12) compared filling material remnants and the working time necessary to remove gutta-percha/AH 26 and Resilon/Epiphany in root canals of extracted teeth. Retreatment was performed using chloroform and 2 rotary techniques (K3 and Liberator files). Resilon/Epiphany was effectively removed by both techniques. Hassanloo (13) studied the retreatment of root canals filled with Epiphany. Sixty roots had their canals obturated with the Epiphany/Resilon system (experimental) or gutta-percha/AH Plus (control). After 8 weeks, canals were retreated with or without chloroform. Filling material residues were found in all 3 levels of the root canals. It has been demonstrated that the substances with best solvent action on gutta-percha are also the most toxic (11). Xylol, which presented overall better results as a solvent for gutta-percha in the present study, is also known for its potentially irritant effect on periapical tissues.

In the present study, orange oil and eucalyptol had similar effects on conventional gutta-percha (p>0.05), but none was as effective as xylol. Magalhães (11), in 2007 evaluated the solubility of gutta-percha in 4 organic solvents used in Endodontics: xylol, orange oil, eucalyptol, chloroform, and observed stronger dissolution in xylol. Conversely, another study evaluating the efficacy of 5 solvents (xylol, eucalyptol, halotane, chloroform, and orange oil) on gutta-percha observed similar results for xylol and orange oil (6). Eucalyptol demonstrated greater solvent effect on thermoplastic gutta-percha, while conventional gutta-percha was the material least affected by eucalyptol.

The effect of solvents on endodontic sealers was evaluated by our research group in a previous study (16) demonstrating action of eucalyptol and xylol on zinc oxide and eugenol-based cement (Intrafill) and no effect of these solvents on resin-based cements (AH Plus, Epiphany, and Endo Rez) or silicone (Roeko Seal). Similar results were reported by Martos et al. (7). Erdemir et al. (17) tested the solvent action of chloroform and halotane and observed good results on Sultan U/P, Diaket, and Roeko Seal cements, but no action on the resin-based cements AH 26 and AH Plus.

Eucalyptol presented mild solvent action on conventional gutta-percha. Different authors (11,18) recommend the use of essential oils in Endodontics due to their biocompatibility. These authors highlight eucalyptol and orange oil as effective alternatives for dissolving gutta-percha.

The present study demonstrated that all evaluated solvents (xylol, orange oil, and eucalyptol) presented stronger solvent effect on thermoplastic gutta-percha than on conventional gutta-percha. In fact, orange oil was only active on thermoplastic gutta-percha. This is probably related to the fact that thermoplastic cones contain a higher percentage of gutta-percha, in order to improve their thermoplastic properties (19). Gurgel-Filho et al. (19) evaluated chemically and radiographically 5 commercial brands of gutta-percha and observed different percentages of gutta-percha by weight. These varied from 14.5 ± 0.70% for Dentsply gutta-percha cones to 20.4 ± 0.40% for Analitic cones. Gurgel-Filho et al. (20) evaluated the ability of 5 different commercially available gutta-percha points to fill simulated lateral canals, showing that the brand of gutta-percha cone had an influence on the length of filling within lateral canals. This may be a reflection of the chemical formulation of the gutta-percha points. Regarding clinical implications of the findings of the present study, eucalyptol presented solvent effect on gutta-percha, while orange oil was particularly active on thermoplastic gutta-percha.

In conclusion, although all analyzed substances presented different solvent action, xylol was the most effective on both gutta-percha and Resilon.