Abstract
The edge termination of SiC by the implantation of an inert ion species is used widely to increase the breakdown voltage of high power devices. We report results of the edge termination of Schottky barrier diodes using 30keV Ar+ ions with particular emphasis on the role of postimplant, relatively low temperature, annealing. The device leakage current measured at 100V is increased from 2.5nA to 7μA by the implantation of 30keV Ar+ ions at a dose of 1×1015 cm−2. This is reduced by two orders of magnitude following annealing at 600°C for 60 seconds, while a breakdown voltage in excess of 750V is maintained. The thermal evolution of the defects introduced by the implantation was monitored using positron annihilation spectroscopy (PAS) and deep-level-transient spectroscopy (DLTS). While a concentration of open-volume defects in excess of 1×1019cm−3 is measured using PAS in all samples, electrically active trapping sites are observed at concentrations ~1×1015cm−3 using DLTS. The trap level is well-defined at Ec−Et = 0.9eV.
Similar content being viewed by others
References
D Alok, B J Baliga, P K McLarty, IEEE Electron Device Letters, 15, 394 (1994).
S J Pearton, International Journal of Modem Physics B., 7, 4687 (1993).
P Asoka-Kumar, K G Lynn, and D O Welch, J. Appl. Phys., 76, 4935 (1994).
G Brauer, W Anwand, P G Coleman, A P Knights, F Plazaola, Y Pacaud, W Skorupa, J. Stormer and P Willutski, Phys Rev B 54 3084 (1996)
G Brauer, W Anwand, P G Coleman, J Stoermer, F Plazaola, J. M. Campillo, Y Pacaud and W Skorupa, J. Phys. Condens. Matter 10 1147 (1998)
D. Alok, B J Baliga, M Kothandaramam, and P K McLarty, Proceedings of Silicon Carbide and related materials, Kyoto, Japan, (1995) pp. 565–568.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Knights, A.P., Morrison, D.J., Wright, N.G. et al. The Effect of Annealing on Argon Implanted Edge Terminations for 4H-SiC Schottky Diodes. MRS Online Proceedings Library 572, 129 (1999). https://doi.org/10.1557/PROC-572-129
Published:
DOI: https://doi.org/10.1557/PROC-572-129