Abstract
The microstructure of Al/α-Al2O3 composites made by infiltrating molten Al into dense mullite preforms has been characterized using transmission electron microscopy. The growth of the Al/Al2O3 composites was found to proceed through three stages. Initially, Al infiltrates into a dense mullite preform through grain boundary diffusion, and reacts with mullite at grain boundaries to form a partial reaction zone. Then, a complete reaction takes place in the reaction region between the partial reaction zone and the full reaction zone to convert the dense mullite preform to a composite of α-Al2O3 (matrix) and an Al-Si phase (thin channels). Finally, the reduced Si from the reaction diffuses out of the Al/Al2O3 composite through the metal channels, whereas Al from the molten Al pool is continuously drawn to the reaction region until the mullite preform is consumed or the sample is removed from the molten Al pool. Based on the observed microstructure, infiltration mechanisms have been discussed, and a growth model of the composites is proposed in which the process involves repeated nucleation of Al2O3 grains and grain growth.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
M. J. Koczak and M. K. Premkumar, J. Metals January, 44 (1993).
V. V. Krstic, P. S. Nicholson, and R. G. Hoagland, J. Am. Ceram. Soc. 64, 499 (1981).
M. S. Newkirk, H. D. Lesher, D. R. White, C. R. Kennedy, A. W. Urqhart, and T. D. Claar, Ceram. Eng. Sci. Proc. 8, 879 (1987).
F. F. Lange, B. V. Velamakanni, and A. G. Evans, J. Am. Ceram. Soc. 73, 388 (1990).
T. D. Claar, W. B. Johnson, C. A. Abdersson, and G. H. Schiroky, Ceram. Eng. Sci. Proc. 10, 599 (1989).
R. E. Loehman, K. Ewsuk, and A. P. Tomsia, J. Am. Ceram. Soc. (1995, in press).
M. S. Newkirk, A. W. Urquhart, H. R. Zwicker, and E. Breval, J. Mater. Res. 1, 81 (1986).
A. S. Fareed, B. Sonuparlak, C. T. Lee, A. J. Fortini, and G. H. Schiroky, Ceram. Eng. Sci. Proc. 11, 782 (1990).
M. K. Aghajanian, N. H. Macmillan, C. R. Kennedy, S. J. Luszcz, and R. Roy, J. Mater. Sci. 24, 658 (1989).
E. Breval, M. K. Aghajanian, and S. J. Luszcz, J. Am. Ceram. Soc. 73, 2610 (1990).
S. Antolin, A. S. Nagelberg, and D. K. Creber, J. Am. Ceram. Soc. 75, 447 (1992).
A. E. Standage and M. S. Gani, J. Am. Ceram. Soc. 50, 101 (1967).
K. Prabriputaloong and M. R. Piggott, J. Am. Ceram. Soc. 55, 184 (1972).
Binary Alloy Phase Diagrams, 2nd ed. (ASM INTERNATIONAL, Materials Park, OH, 1990).
JCPD files, Newtown Square, PA, Card No. 10-425.
J. Jia, M. S. Thesis, New Mexico Institute of Mining and Technology (1994).
J. A. Cornie, Y. M. Chiang, D. R. Uhlmann, A. Mortensen, and J. M. Collins, Am. Ceram. Soc. Bull. 65, 293 (1986).
K. C. Russell, J. A. Cornie, and S. Y. Oh, in Interfaces in Metal-Matrix Composites, edited by A. K. Dhingra and S. G. Fishman (AIME, Metals Park, OH, 1986), p. 61.
S. Y. Oh, J. A. Cornie, and K. C. Russell, Ceram. Eng. Sci. Proc. 8, 912 (1987).
D. A. Weirauch, Jr., J. Mater. Res. 3, 729 (1988).
R. E. Loehman and K. Ewsuk, unpublished results.
F. Lihl, E. Nachtigall, and A. Schwaiger, Z. Metallk. 59, 213 (1968).
S. Das, T. K. Dan, S. V. Prasad, and P. K. Rohatgi, J. Mater. Sci. Lett. 5, 562 (1986).
G. J. van Gurp, J. Appl. Phys. 44, 2040 (1973).
A. S. Nagelberg, S. Antolin, and A.W. Urquhart, J. Am. Ceram. Soc. 75, 455 (1992).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gao, Y., Jia, J., Loehman, R.E. et al. Transmission electron microscopy study of Al/Al2O3 composites fabricated by reactive metal infiltration. Journal of Materials Research 10, 1216–1225 (1995). https://doi.org/10.1557/JMR.1995.1216
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1995.1216