Functionalized Graphene Derivatives: Antibacterial Properties and Cytotoxicity

Valentini, Federica; Calcaterra, Andrea; Ruggiero, Vincenzo; Pichichero, Elena; Martino, Assunta; Iosi, Francesca; Bertuccini, Lucia; Antonaroli, Simonetta; Mardente, Stefania; Zicari, Alessandra; Mari, Emanuela; Iovenitti, Giulia; Leone, Gemma; Botta, Maurizio; Talamo, Maurizio

doi:https://doi.org/10.1155/2019/2752539

Journal of Nanomaterials

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2019 | Article ID 2752539 | https://doi.org/10.1155/2019/2752539

Functionalized Graphene Derivatives: Antibacterial Properties and Cytotoxicity

Federica Valentini,^1,2Andrea Calcaterra,²Vincenzo Ruggiero,^3,4Elena Pichichero,⁴Assunta Martino,⁴Francesca Iosi,⁵Lucia Bertuccini,⁵Simonetta Antonaroli,¹Stefania Mardente,⁶Alessandra Zicari,⁶Emanuela Mari,⁶and Giulia Iovenitti³ et al.

Academic Editor: Jianbo Yin

Received23 Aug 2018

Revised28 Nov 2018

Accepted03 Dec 2018

Published14 Feb 2019

Abstract

In this work, the authors prepared and characterized two different graphene oxides: one chemically synthesized (GO sample) and the other one electrochemically synthesized (GO_(LiCl)). Both samples were fully characterized with atomic force microscopy (AFM), Raman and Fourier transform infrared (FTIR) spectroscopies, X-ray photo electron spectroscopy (XPS), thermal analysis (TG/DTA), and -potential. The antibacterial properties of both graphene oxides were studied using Gram-negative Escherichia coli ATCC 25922 and Gram-positive Staphylococcus aureus ATCC 25923 by spectrophotometer and viable cell count as indirect and direct methods, respectively. Results demonstrated that the GO_(LiCl) exhibited a significant antibacterial activity compared to GO that showed a bacteriostatic effect on both pathogens. Electron microscopy analysis confirmed the antibacterial effects of both graphene oxides toward the pathogens, especially working at 80 μg/mL, for 24 h. Additional studies were also performed and both GO samples were not cytotoxic at 2 μg/mL toward neuroblastoma cells. Moreover, 2 μg of GO was suitable to carry the minimum effective dose (5.74 ng/mL) of kinase inhibitor S29 (1-(2-chloro-2-(4-chlorophenyl)ethyl)-N-(4-fluorobenzyl)-1H-pyrazolo[3,4-d] pyrimidin-4-amine), providing negligible side effects related to the S29 treatment (this latter being specifically active on the neuroblastoma cell lines (SK-N-BE(2))).

1. Introduction

One of the most important research field applications for medicine focuses on new therapeutic agents’ delivery tools, with the first aim to improve therapy efficiency. Recent advances in the nanomaterial field provide useful biocompatible nanostructured materials and nanocomposites, suitable for drug delivery systems. Among all the innovative materials, graphene derivatives [1] have attracted a great deal of scientific interest in biomedicine and pharmacology sciences. Graphene, a single layer of sp²-hybridized carbon atoms arranged in a honeycomb two-dimensional (2-D) crystal lattice, exhibits excellent chemical-physical, biochemical [2], mechanical, and engineering properties, extremely useful for several applications in sensors [3] and optoelectronic devices [4], environmental monitoring tools [5], food quality control [6], and medical devices [7]. With particular regard to the fields of application that include food quality control and medicine field applications, the antibacterial features [8] and the biocompatibility properties toward the real matrixes (as food or normal human cell lines, organic tissue, and blood) represent a key point that nanomaterials must possess. There are several cases of study, described in literature by interesting review articles concerning the improved antibacterial activity [9] and the increased biocompatibility [10] properties, exhibited by the graphene derivatives. These last properties mainly depend on the synthesis routes applied for graphene production [11]. According to this, Valentini et al. [12] recently report about a metal-free green graphene oxide (GO_(LiCl)), synthesized by the electrochemical exfoliation of micrometric graphite electrodes (2015 patent no. 102015000023739). GO_(LiCl) was fully characterized, resulting in antibacterial material, and finally applied for in vitro cellular experiments, to establish its biocompatibility [12]. The novelty of this work consists of a new green chemistry synthetic route (under patent) for the fabrication of GO samples. The latter showed a bacteriostatic activity (if compared with the bactericidal action, exhibited by GO_(LiCl)), in the presence of both pathogens, as the Gram-negative E. coli ATCC 25922 and the Gram-positive S. aureus ATCC 25923. A cytotoxicity assay was performed, in order to identify in GO a new promising nanocarrier for compound S29: 1-(2-chloro-2-(4-chlorophenyl)ethyl)-N-(4-fluorobenzyl)-1H-pyrazolo[3,4-d]pyrimidin-4-amine, therapeutic agent. The scientific interest on S29 as a therapeutic agent consists of its ability to reduce tumor mass in neuroblastoma xenograft mice models. For this purpose, in this study the SK-N-BE(2) neuroblastoma cell lines were used for the cytotoxicity investigation, concerning the S29 therapeutic anticancer agent. S29 shows an unfavorable pharmacokinetic profile, causing a limited use in the treatment of cancer. Until now, in literature, liposomes [13] and human serum albumin (HSA) [14] have been applied to improve S29 delivery, biodistribution, and bioavailability but the concentration of liposomes and HAS nanoparticles had to be very high and this leads to significant high cytotoxicity in vitro and in vivo [13, 14] experiments. Instead, in this work, it has been shown that graphene derivatives were not cytotoxic and they could be used at extremely low levels of concentration, if compared with those applied in the presence of liposomes and HAS nanoparticles. In particular, according to the results exhibited by the GO samples, this latter seems to be more eligible for S29 delivery.

2. Materials and Methods

2.1. Chemicals

The electrochemically grown graphene oxide sample (labelled as GO_(LiCl)) was obtained by a patented synthetic approach, as widely reported in a 2015 patent (no. 102015000023739) and also in reference [12]. For the chemical synthesis of the graphene oxide (labelled as GO), a new wet mechanic-chemical exfoliation synthesis was developed by the same authors of this work, and now it is under patent. The other chemicals used in the analysis were purchased from Sigma-Aldrich (USA). All reagents were of analytical grade and used as received without further purification.

The procedure of preparing GO and GO_(LiCl) nanosheet dispersions was similar for the cytotoxicity and antibacterial tests, except that GO suspension was carried out by using phosphate-buffered saline (PBS) for the cytotoxicity analysis and by using a saline solution 0.9% (10 mL) in the case of the antibacterial tests. The finial graphene oxide dispersions were transparent, and they were very well dispersed by sonication with a polytronic probe, at room temperature.

2.2. Material Characterization

The AFM measurements were performed in air using a Veeco Multiprobe IIIa instrument (Veeco, Santa Barbara, CA, USA). The GO was deposited using an aqueous solution on the mica substrates. The experiments were carried out at room temperature (20°C) in tapping mode using Si tips with a spring constant of about 40 N/m and a typical curvature radius on the tip of 7 nm. The XPS measurements were carried out using an Omicron DAR 400 Al/Mg Kα nonmonochromatic X-ray source and a VG-CLAM2 electron spectrometer. GO (1 mg/mL) was very well dispersed in ethanol using an ultrasonic probe and then deposited on the silicon wafer. ζ-potential was determined by Dynamic Light Scattering (DLS) (Zetasizer Nano ZS90, Malvern Instruments Ltd., Malvern, UK). Graphene oxide samples were diluted in water, providing an optical density (OD) of 0.1 at 420 nm, and then measured at 24° C with a scattering angle of 90°. ζ-potential measurements were carried out using folded capillary cells (Malvern). Thermogravimetric analysis was carried out by a Q600 thermogravimetric analyzer (TA Instruments-Waters, USA). Samples (~20 mg) were put in a platinum crucible and heated from 30°C to 700°C, with a rate of 10°C/min, under nitrogen purge gas.

2.3. Cytotoxicity Tests: Cell Culture

The long-term neuroblastoma cell lines, SH-SY5Y and SK-N-BE(2) (ACC no. 209 and ACC no. 632, respectively), obtained from DSMZ, Braunschweig, Germany, in October 2012, were maintained in RPMI 1640 (Gibco, Grand Island, NY, USA) with or without phenol red, supplemented with heat-inactivated 10% FCS containing 2 mM L-glutamine. Preliminary time and concentration course experiments with GO 0.57, 5.74, and 57.4 μg/mL were performed in our laboratory in order to establish the conditions at which GO did not cause cell necrosis. Cell vitality was monitored before each experiment by a trypan blue (Sigma-Aldrich) [15] exclusion assay, in which dead cells are stained and those with intact membranes are not. Briefly, cell viability was determined using the trypan blue exclusion test. SK-N-BE(2) cells (5 × 10⁴/mL) were suspended in a 10 μL suspension containing trypan blue (0.4% w/v; Sigma-Aldrich) in phosphate-buffered saline (PBS) and incubated at room temperature for 5 min, followed by examination under a light microscope to determine the percentage of cells with clear (viable cells) and blue (nonviable cells) cytoplasm.

2.4. Antibacterial Activity

GO or GO_(LiCl) (2 mg) were dispersed in saline solution 0.9% (10 mL) by sonication with a polytronic probe. The suspensions were sterilized by autoclaving, at 121°C for 15 min, before being inoculated with bacteria to reach a final concentration ranging from 20 to 80 μg/mL. Staphylococcus aureus subspecies aureus derived from ATCC 25923 and Escherichia coli derived from ATCC 25922 were purchased from Microbiologics (USA). Tryptic Soy Broth (TSB) was purchased from VWR Prolabo Chemicals (Italy) and prepared as reported in data sheet. Nutrient Agar with NaCl was purchased from BioLife (Italy) and prepared as reported in product information. Saline solution 0.9% (NaCl: VWR Prolabo Chemicals, Italy) was prepared dissolving 9 g of NaCl in 1000 mL of distilled water, sterilized by autoclaving at 121°C for 15 min. E. coli (ATCC 25922) and S. aureus (ATCC 25923) were used to perform viability tests. Bacteria were grown in TSB medium at 37°C overnight, and cells were collected via centrifugation (4000 rpm for 20 min). The cells were washed three times with sterile saline solution to remove residual macromolecules and other growth medium constituents. The pellets were then suspended in saline solution at 0.9% [16, 17]. Bacterial cell suspensions were diluted in NaCl 0.9% to obtain cell samples having an optical density at 600 nm (OD₆₀₀) at corresponding to 10⁷-10⁸ CFU/mL (OD₆₀₀ = 0.4 for S. aureus and OD₆₀₀ = 0.3 for E. coli). Cells were incubated with different concentrations (20, 40, and 80 μg/mL) of GO or GO_(LiCl) at 37°C for 4 hours () and 24 hours (). The untreated samples with E. coli or S. aureus were used as the control. Growth of treated and untreated samples were followed by measuring OD at 600 nm with spectrophotometer NANOCOLOR UV/VIS II (MACHEREY-NAGEL, Germany), at 1-hour intervals for 6 hours and then after 24 hours of treatment. The viability was evaluated by the colony-counting method. Briefly, bacterial amount at the starting time (), after 4 hours of treatment (), and after 24 hours () was determined by performing a series of 10-fold cell dilutions (100 μL each) that were spread onto Nutrient Agar plates and allowed to grow overnight at 37°C. Colonies were counted and compared with those on control plates to calculate the change in cell growth inhibition. The antibacterial activity was expressed as a function of cell viability loss; the loss of cell viability (%) was determined by using the number of colonies found in the experimental mixture incubated with GO and the number of colonies found in the “inoculum only,” incubated without GO. All the experiments were done in duplicate, and the average values were reported. For SEM (FE-SEM Quanta Inspect F, FEI, Thermo Fisher Scientific) analysis, a steady state culture of E. coli (ATCC 29522) and S. aureus (ATCC 29523), grown in LB at 37°C o.n., was washed in physiological saline solution and incubated with GO or GO_(LiCl) 80 μg/mL, for 8 and 24 hours at 37°C. Successively, samples were fixed with 2.5% glutaraldehyde in 0.1 M sodium cacodylate buffer and were left to adhere on poly-lysine-treated glass coverslips for 4 hours at room temperature (RT) and o.n. at 4°C. Then, adhered bacteria were washed and postfixed with 1% OsO₄ in 0.1 M sodium cacodylate buffer for 1 h at RT and dehydrated through a graded series of ethanol solutions (from 30% to 100%), according to reference [18]. For TEM (EM 208S transmission electron microscope, FEI, Thermo Fisher, equipped with the acquisition system Olympus MegaView SIS camera, at 100 kV) analysis, the same bacterial cultures were fixed in 2.5% glutaraldehyde, 2% paraformaldehyde, and 2 mM CaCl₂ in 0.1 M sodium cacodylate buffer, pH 7.4, overnight at 4°C, and were processed according to Perry and Gilbert [19]. Samples were washed in cacodylate buffer and postfixed with 1% OsO4 in 0.1 M sodium cacodylate buffer for 1 hour at RT, treated with 1% tannic acid for 30 min and rinsed in 1% sodium sulphate, for 10 min. Postfixed specimens were washed, dehydrated through a graded series of ethanol solutions (30–100% ethanol), and embedded in Agar 100 (Agar Scientific Ltd., UK).

3. Results and Discussion

3.1. Characterization of GO Samples

These two graphene oxide samples were synthesized by a chemical and electrochemical synthesis pathway, respectively, and fully characterized by using AFM, EDAX, and XPS techniques. The main characterization results have been highlighted in Tables 1, 2, and 3. In Table 1, it is possible to recognize that the two kinds of graphene oxide samples were very similar in thickness and number of layers; on the other hand, chemically synthesized graphene (GO) had a lower surface area value, if compared with that exhibited by the electrochemically synthesized graphene sample (GO_(LiCl)). Instead, as regards the content of metals, the microanalysis (EDAX) unequivocally showed that the metal content resulted below the detection limit of the microanalysis technique, indicating that both these GO samples were metal-free graphene-based nanomaterials.

XPS analysis was carried out to study the chemical shift of GO samples. The C1s XPS core level spectrum analysis of GOs with the corresponding quantitative parameters is shown in Table 2 (for GO) and Table 3 (for GO_(LiCl)). From Table 2, it is possible to observe that the chemically synthesized graphene oxide sample results are more oxidized, with a greater presence of carbonyl and/or carboxylic functional groups, if compared with those exhibited by the graphene synthesized by the electrochemical route strategy (see also Table 3). The electrochemically synthesized graphene sample results in a more reduced C1s chemical shift (i.e., less oxidized if compared to the chemical shift of graphene obtained by chemical synthesis approach).

The functionalization degree and the chemical shift of graphene oxide samples certainly represent very useful parameters, strictly related to the antibacterial activity and biocompatibility properties. According to the literature [20], the oxygenated functional groups are firstly responsible for the antibacterial behavior of GO nanosheets. The mechanism underlying this feature involved the generation of reactive oxygen species (ROS), able to provoke the oxidative stress through an electronic transfer mechanism. Functionalities strictly influence the electronic and/or electron-transfer processes, especially since graphene oxide shows a more insulating profile, when compared with pristine (metallic behavior) and reduced graphene sheets (semiconductor-semimetal transitions with reduction). The electronic/electron-transfer interaction mechanisms mainly occur between the positively charged Gram-negative E. coli and the negatively charged GO and GO_(LiCl), preferentially. In the case of the Gram-positive S. aureus (having negatively charged bacterial walls), the semiconductive properties of GO_(LiCl) could provoke a greater electrostatic repulsion (when compared to the insulating GO), because it delivers a greater electron density, toward the negatively charged S. aureus pathogen walls (and the electron-transfer mechanism is discussed in detail in Results and Discussion, Section 3 of this paper).

Several authors affirmed that the antibacterial features of nanomaterials are also the result of a complex interaction between two main additional factors: size and shape. Liu et al. [21] demonstrated that the antibacterial activity of GO sheets toward E. coli cells is lateral size dependent. Larger GO sheets show stronger antibacterial activity than smaller ones, and they have different time- and concentration-dependent antibacterial features. The same authors [21] described that the lateral size-dependent antibacterial properties of GO sheets are caused by neither their aggregation states nor oxidation ability. Large GO sheets more easily cover cells, and cells cannot proliferate once fully covered, resulting in the cell viability loss, experimentally observed in the following colony-countingtest. In contrast, small GO sheets adhere to the bacterial surfaces, which cannot effectively isolate cells from the environment.

As far as the form is concerned, it is stated in the literature that the geometries/shapes of both nanomaterials and bacteria are fundamental to guarantee the mutual interaction of the two systems. In particular, Akhavan et al. [22] affirmed that the graphene nanoribbons showed much higher cytotoxicity than the graphene sheets. The ROS (Radical Oxygenated Species) generation and direct contact interaction of the extremely sharp edges of graphene with the membrane of the cells were found as the main mechanisms involved in the cytotoxicity of both shapes of graphene: nanoribbons and nanosheets [22].

Moreover, the shape of the bacteria is also relevant. Hui et al. [23] report about diverse Graphene Quantum Dots (GQDs) with basal planes similar to those of graphene oxide sheets lacking an antibacterial property, which is prepared by rupturing the C60 cage which effectively kills Staphylococcus aureus, including its antibiotic-tolerant persisters, but not Bacillus subtilis, Escherichia coli, or Pseudomonas aeruginosa. The observed activity may correlate with a GQD’s ability to disrupt the bacterial cell envelope and is the initial step for cell envelope disruption, suggesting the importance of GQDs’ chemical composition and shapes.

The same parameters (i.e., mainly the functionalization degree, size, and shape/geometries) also influence the biocompatibility of graphene and GO derivatives. In particular, the functionalization seems to be the required/necessary condition to achieve the highest biocompatibility for nanomaterials [24] because they provide oxygenated bridges, very useful in establishing covalent and/or electrostatic interactions with biopolymers and biomolecules. This strategy focuses on the fabrication of several different biocompatible coatings; surrounding the nanostructured material surfaces, edges, and sides; and increasing their biocompatibility towards cells and tissues.

There is also a first level of functionalization degree, which is absent in biopolymers and present only in as-deposited GO and GO derivatives (this latter as post-synthesis treated carbon-based graphene materials). In this case, the only presence of the oxygenated functional groups on the GO surface mainly provides a better dispersibility in the working medium [25]. A stable nanodispersion, in liquid phase, offers two important advantages during the experiments: (1)Graphene nanosheets are more easily distributed in the cellular compartments, avoiding aggregation and their subsequent expulsion by gravimetric settling(2)Graphene nanodispersion phases improve safety biodistribution processes [26] into the cells, minimizing the ROS generation mechanisms very well. This is especially due to the establishment of the couple electrostatic interactions between the oxygenated functional groups (mainly C(=O)OH, C(=O)R, C(=O)H, OH, etc.) and the aqueous working medium. The couple interactions strongly compete with the side reactions, involved in the formation of ROS radicals, since the electrostatic interactions, established with solvent-working medium, thermodynamically stabilize the resulting nanodispersion systems [27, 28]

According to the main importance of the functionalization degree on the GO properties and performances, FTIR spectra profiles (see Figure 1), TG/DTA, and Raman results (these latter reported in Table 4) were also inserted/included in the manuscript, in order to confirm the XPS data analysis. Moreover, the acidic site evaluation (nmol/mg), reported in Table 4, mainly quantifies the C(=O)OH functional groups. These latter were also detected by using the -potential measurement technique that revealed negative values of -28.7 mV for GO and -32.1 mV for GO_(LiCl) (typically achieved when in the presence of the negatively charged carboxylate anions C(=O)O^-).

Furthermore, TEM analysis (Figure 2) confirmed the presence of more defective structures in the case of the most oxidized sample, as GO. This latter appeared as a multilayer of graphene oxide (A), while GO_(LiCl) showed a more regular shape/geometry of the resulting nanosheets, similar to that exhibited by the pristine single layer of graphene.

(a)

(b)

3.2. Cytotoxicity: Evaluation of Cellular Proliferation

Cell growth curves in Figure 3 show that there is a decrease in growth rate during exposure to 2 μg/mL GO for 24 and 48 hours compared to controls. Cell mortality rate, detected by trypan blue dye, was between 4% and 6%. We had previously established that higher doses of GO (10 and 20 μg) were cytotoxic for SK-N-BE(2) cells but 2 μg/mL GO did not induce cell damage, so this concentration of GO provided the right concentration for carrying the minimum toxic concentration of S29. Treatment of cells with 10 μM S29 and 2 μg/mL GO started to inhibit cell growth after 24 h of exposure and became significantly different from GO alone or S29 alone at 48 h and 72 h. 10 nM and 100 nM S29 with, respectively, 5.74 ng/mL and 57.4 ng/mL GO failed to induce significant cell growth inhibition after 24 h from addition to cultures, meaning that S29 has a very low cytotoxicity in SK-N-BE(2) cells. In particular, these optimized concentration values for both the nanocarrier and S29 therapeutic agent were the lowest results compared to those declared in literature [31]. Moreover, the same authors [31] do not load drugs but only evaluate the cytotoxicity of the GO-Ag nanocarrier, at the highest concentration values in cells. Cell counts with trypan blue exclusion test demonstrated a low rate of cell necrosis even after 72 h of culture with 10 μM S29 and 2 μg GO, meaning that the inhibition of cell growth may be probably due to longer cell cycles or induction of apoptosis (the trypan blue data were also confirmed by the LDH assay, carried out as previously reported in reference [12]). Observation of cell cultures (40x inverted microscopy) showed that cells did not change their morphology nor detach from plastic after treatments (Figure 4).

(a)

(b)

(c)

3.3. Antibacterial Activity

Figures 5 and 6 showed the growth curves of GO-treated and GO_(LiCl)-treated E. coli and S. aureus bacterial cells, respectively. Both treated bacteria grew following the trend exhibited by the corresponding control samples. When the bacteria cells were incubated with different graphene oxide concentrations, a significant reduction of the OD values was recorded (if compared to the controls, reported in Figures 5(b) and 5(d) and Figures 6(b) and 6(d)). Results indicated that the bacteria cells exhibited a reduction of their growth, proportionally to the GO concentrations. This agreed with the literature [32] where the lower sizes of GO sheets adhered on the bacteria surfaces, without isolating them from the nutrient environment. Increasing the GO concentrations, bacteria cell results were more covered, effectively isolated from the environment and condemned to die. The bacteria cells, treated with GO_(LiCl), exhibited a significant reduction to their growth, already at the lowest concentrations and independent of the GO_(LiCl) concentrations. This could be explained considering the largest area of GO_(LiCl) (Table 1), which was suitable to cover the external surface of the bacteria cells, provoking the indirect toxicity by biologically isolating them from the growth medium. Consequently, the bacterial cells could neither proliferate nor consume the nutrients and died. The death rate of the bacteria was determined by the colony-counting method. Figure 7 showed that both GO and GO_(LiCl) reduced the growth of the S. aureus and E. coli (over 90%), when bacteria were exposed to different concentrations of graphene oxides, at . The E. coli control samples at were 1.9 × 10⁸ UFC/mL, and after 4 h, the control increased up to 1.25 × 10⁹ CFU/mL. After 4 h, the E.coli cells grew up to 1.64 × 10⁸ (at 20 μg/mL of GO), 1.13 × 10⁸ (at 80 μg/mL of GO), 1.22 × 10⁸ (at 20 μg/mL of GO_(LiCl)), and 1.01 × 10⁸ CFU/mL (at 80 μg/mL of GO_(LiCl)). At , the control sample for S. aureus was 3.8 × 10⁷ CFU/mL, and after 4 h, the control increased up to 1.53 × 10⁸ UFC/mL. S. aureus-treated cells, at , grew up to 7.27 × 10⁶ (at 80 μg/mL of GO), 1.85 × 10⁷ (at 20 μg/mL of GO), 2.32 × 10⁶ (at 80 μg/mL of GO_(LiCl)), and 9.64 × 10⁶ CFU/mL (at 20 μg/mL of GO_(LiCl)). After 24 hours (), the experimental results showed that E. coli control increased up to 1.35 × 10⁸. The cells grew up to 9.52 × 10⁷ (at 80 μg/mL of GO), reaching the value of 1.03 × 10⁸ (at 20 μg/mL of GO). Incubating E. coli with GO_(LiCl), cells grew up to 7.14 × 10⁷ (at 80 μg/mL GO_(LiCl)) and reached the values of 9.30 × 10⁷ CFU/mL (at 20 μg/mL GO_(LiCl)). In the case of S. aureus, the control increased up to 1.41 × 10⁵. The treated S. aureus cells grew up to 5.38 × 10⁴ (at 80 μg/mL of GO), 5.72 × 10⁴ (at 20 μg/mL of GO), 3.91 × 10⁴ (at 80 μg/mL of GO_(LiCl)), and 5.64 × 10⁴ CFU/mL (at 20 μg/mL of GO_(LiCl)). The antibacterial effects on E. coli were highly evident at 4 hours, with a growth reduction of 90%, for both GO samples. At 24 hours, the antibacterial activity for E. coli in the presence of GO_(LiCl) (Figure 8(a)) was superior to GO and also higher if compared with S. aureus. A reasonable explanation could be the presence of a much thinner peptidoglycan wall, in the E. coli structure [31]. For S. aureus, the antibacterial effects were observed at , with a bacterial growth reduction of 95%. At 24 hours, the bacterial cell growth reduction was about 60%, working with GO, and slightly higher (75%) in the presence of GO_(LiCl) (Figure 8(b)). After 24 h of GO incubation, S. aureus showed a typical bacteriostatic activity, if compared with E. coli. The experimental results could be explained as a combination of different parameters [33], such as the bacteria morphology/structure [34, 35] and the conductivity behavior of the GO [36] (more insulating nanomaterial) and GO_(LiCl) [37] (a semiconductive material), these latter being responsible for the electron-transfer interaction between the graphene derivatives and the bacteria cells.

(a)

(b)

(c)

(d)

(a)

(b)

(c)

(d)

(a)

(b)

(c)

(d)

(a)

(b)

To examine whether direct interaction of bacteria and graphene oxide nanosheets could exhibit a key role in the antibacterial activity of graphene oxide (80 μg/mL), the morphological changes of both bacterial cells, S. aureus and E. coli, were studied using SEM and TEM analysis, respectively. E. coli control exhibited normal rod-like morphology with regular and intact membranes (Figure 9(a)). E. coli incubated with GO exhibited severe membrane deformations, and cell shape was seriously distorted with evident shrinkage effects (Figure 9(b)). These effects could be probably due to a collapse of the internal structure. In some cases, the outer membranes merged with those belonging to the other bacteria cells (Figure 9(c)). E. coli, when incubated with GO_(LiCl), also exhibited similar behavior (Figures 9(d) and 9(e)). The experimental results could be explained considering a typical electron-transfer process from the positively charged Gram-negative E. coli and the negatively charged GO and GO_(LiCl) nanomaterials. The results could be interpreted considering a synergy of effects such as an electron transfer [38] (from graphene oxide toward the bacterial membranes), the oxidative stress [39], and the mechanical tearing (cutting effect depending on the shape and size of the graphene nanosheets).

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

(i)

(j)

In the case of S. aureus cells, SEM micrographs showed a regular sphere shape (Figure 9(f), inset) and a typical grape-like aggregation in the entire control sample (Figure 9(f), the main image). When S. aureus cells were incubated with 80 μg/mL of GO (24 h), they showed a lightly irregular and shrunken shape (Figure 9(g)). The graphene oxide-bacteria interactions developed strong forces of attraction among cells that induced the formation of numerous spherical bacterial aggregates around graphene oxide nanosheets (Figure 9(h)), which are completely absent in the case of E. coli, when incubated with the same GO. This result could be explained when considering a strong electrostatic interaction between the Gram-positive S. aureus (with an isoelectric point [40] ~3, versus -5 in the case of E. coli [41]) and the more insulating GO nanomaterial. When inoculated with GO_(LiCl), the aggregation effects were also recorded (Figures 9(i) and 9(j)) in S. aureus cells but much less evident than those shown in Figure 9(h), for GO. The explanation could be related to the semiconductive properties of GO_(LiCl) that could provoke a greater electrostatic repulsion, because it delivers more electrons toward the negatively charged bacterial walls, as in the case of the S. aureus pathogen (with the result of decreasing the value of the electrostatic potential membrane ). TEM analysis confirmed that the direct contact of the graphene oxide nanosheets with bacterial cells induced the loss of the structural integrity, in both bacterial species and the presence of both GO samples. TEM micrographs of E. coli exposed to GO for 24 h showed that the bacterial shrinkage, observed by SEM, was consistent with plasma membrane damage and retraction, leading to the leakage of intracellular material in the periplasmic space (Figures 10(b) and 10(c) versus Figure 10(a) that is the control). Therefore, it is reasonable to think that an electron-transfer process can be triggered, following the breaking of the membrane and consequent leakage of periplasmic materials. The effective and irreversible damages of the bacterial cells could happen after the electronic transfer processes, in combination with the oxidative stress or additional mechanical tearing processes [42]. In Figure 10(c), the “insertion/cutting mode” interaction between GO and E. coli clearly highlighted a nanosheet while it entered into the phospholipid bilayer, cutting the membrane (Figure 10(c)), as reported in literature [43]. Similar profiles were detected incubating E. coli with GO_(LiCl) nanosheets (Figures 10(d) and 10(e)). S. aureus, incubated with 80 μg/mL of GO for 24 h, showed numerous contacts with GO, with a great number of cells characterized by several types of plasma membrane damage, having significant condensation of the intracellular material [44] (Figure 10(g) versus the unaltered control in Figure 10(f)). The initial plasma membrane damage evolved in the leakage of intracellular material and the loss of cell wall integrity (Figure 10(h)), provoking the cell death. A similar trend was observed when S. aureus was incubated with GO_(LiCl), where the cell damage seemed to be related to the electron diffusion mechanisms, from the graphene nanosheets toward the bacterial plasma membranes, which is especially more significant for the semimetallic graphene (GO_(LiCl)) samples (Figures 10(i) and 10(j)). Concerning the antibacterial activity, it is necessary to underline that both types of graphene intrinsically exhibited this property [31] without the synergy with a traditional antibacterial agent, such as the silver element.

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

(i)

(j)

4. Conclusions

In this study, two different metal-free graphene oxide products were synthesized, by using chemical and electrochemical procedures. The resulting graphene oxides showed different functionalization degrees (mainly as C(=O)OH groups), which determined different electronic features: a semiconductive behavior in the presence of GO_(LiCl) and a more insulating profile in the case of chemically synthesized GO. These features could explain the slightly different reactivity, observed working with GO and GO_(LiCl) in bacteria and in neuroblastoma cells, respectively. In particular, both graphene oxides (2 μg/mL) showed a negligible effect of cytotoxicity, being eligible as a carrier of the S29 compound. Furthermore, both graphene oxides possess an interesting antimicrobial activity, especially GO_(LiCl) which resulted in a bactericidal agent, and GO was a bacteriostatic ecofriendly nanomaterial. In particular, this last feature represents an important biocompatibility property that elects the GO as the new nanovector of anticancer drugs, especially in neuroblastoma cell lines.

Data Availability

The data used to support the findings of this study are included within the article.

Conflicts of Interest

The authors declare no competing financial interest.

Acknowledgments

The work was financially supported by the Smart Campus Project (CUP E82I15000980002). The authors also wish to thank Professor Silvia Schenone from the Department of Pharmacy, Università degli Studi di Genova, Viale Benedetto XV, 3, 16132, Genova (IT), for technical support.

References

A. Jafarizad, A. Taghizadehgh-Alehjougi, M. Eskandani et al., “PEGylated graphene oxide/Fe₃O₄ nanocomposite: synthesis, characterization, and evaluation of its performance as de novo drug delivery nanosystem,” Bio-medical Materials and Engineering, vol. 29, no. 2, pp. 177–190, 2018.
View at: Publisher Site | Google Scholar
Kenry, W. C. Lee, K. P. Loh, and C. T. Lim, “When stem cells meet graphene: opportunities and challenges in regenerative medicine,” Biomaterials, vol. 155, pp. 236–250, 2018.
View at: Publisher Site | Google Scholar
Y. Wu, B. Yao, C. Yu, and Y. Rao, “Optical graphene gas sensors based on microfibers: a review,” Sensors, vol. 18, no. 4, pp. 941–957, 2018.
View at: Publisher Site | Google Scholar
F.-X. Liang, Y. Gao, C. Xie, X.-W. Tong, Z.-J. Li, and L.-B. Luo, “Recent advances in the fabrication of graphene–ZnO heterojunctions for optoelectronic device applications,” Journal of Materials Chemistry C, vol. 6, no. 15, pp. 3815–3833, 2018.
View at: Publisher Site | Google Scholar
M. A. Kang, S. Ji, S. Kim et al., “Highly sensitive and wearable gas sensors consisting of chemically functionalized graphene oxide assembled on cotton yarn,” RSC Advances, vol. 8, no. 22, pp. 11991–11996, 2018.
View at: Publisher Site | Google Scholar
Y. Chyan, R. Ye, Y. Li, S. P. Singh, C. J. Arnusch, and J. M. Tour, “Laser-induced graphene by multiple lasing: toward electronics on cloth, paper, and food,” ACS Nano, vol. 12, no. 3, pp. 2176–2183, 2018.
View at: Publisher Site | Google Scholar
S. Afsahi, M. B. Lerner, J. M. Goldstein et al., “Novel graphene-based biosensor for early detection of Zika virus infection,” Biosensors and Bioelectronics, vol. 100, pp. 85–88, 2018.
View at: Publisher Site | Google Scholar
P. Choudhary, T. Parandhaman, B. Ramalingam, N. Duraipandy, M. S. Kiran, and S. K. Das, “Fabrication of nontoxic reduced graphene oxide protein nanoframework as sustained antimicrobial coating for biomedical application,” ACS Applied Materials & Interfaces, vol. 9, no. 44, pp. 38255–38269, 2017.
View at: Publisher Site | Google Scholar
S. P. Singh, Y. Li, A. Be’er, Y. Oren, J. M. Tour, and C. J. Arnusch, “Laser-induced graphene layers and electrodes prevents microbial fouling and exerts antimicrobial action,” ACS Applied Materials & Interfaces, vol. 9, no. 21, pp. 18238–18247, 2017.
View at: Publisher Site | Google Scholar
X. Zhao, Z. Wei, Z. Zhao et al., “Design and development of graphene oxide nanoparticle/chitosan hybrids showing pH-sensitive surface charge-reversible ability for efficient intracellular doxorubicin delivery,” ACS Applied Materials & Interfaces, vol. 10, no. 7, pp. 6608–6617, 2018.
View at: Publisher Site | Google Scholar
J. Sturala, J. Luxa, M. Pumera, and Z. Sofer, “Chemistry of graphene derivatives: synthesis, applications, and perspectives,” Chemistry - A European Journal, vol. 24, no. 23, pp. 5992–6006, 2018.
View at: Publisher Site | Google Scholar
F. Valentini, E. Mari, A. Zicari et al., “Metal free graphene oxide (GO) nanosheets and pristine-single wall carbon nanotubes (p-SWCNTs) biocompatibility investigation: a comparative study in different human cell lines,” International Journal of Molecular Sciences, vol. 19, no. 5, p. 1316, 2018.
View at: Publisher Site | Google Scholar
M. Celano, S. Schenone, D. Cosco et al., “Cytotoxic effects of a novel pyrazolopyrimidine derivative entrapped in liposomes in anaplastic thyroid cancer cells in vitro and in xenograft tumors in vivo,” Endocrine-Related Cancer, vol. 15, no. 2, pp. 499–510, 2008.
View at: Publisher Site | Google Scholar
A. L. Fallacara, A. Mancini, C. Zamperini et al., “Pyrazolo[3,4-d]pyrimidines-loaded human serum albumin (HSA) nanoparticles: preparation, characterization and cytotoxicity evaluation against neuroblastoma cell line,” Bioorganic & Medicinal Chemistry Letters, vol. 27, no. 14, pp. 3196–3200, 2017.
View at: Publisher Site | Google Scholar
E. Mari, A. Zicari, F. Fico, I. Massimi, L. Martina, and S. Mardente, “Action of HMGB1 on miR-221/222 cluster in neuroblastoma cell lines,” Oncology Letters, vol. 12, no. 3, pp. 2133–2138, 2016.
View at: Publisher Site | Google Scholar
S. A. Wells Jr and M. Santoro, “Update: the status of clinical trials with kinase inhibitors in thyroid cancer,” The Journal of Clinical Endocrinology & Metabolism, vol. 99, no. 5, pp. 1543–1555, 2014.
View at: Publisher Site | Google Scholar
S. Martina Ferrari, C. La Motta, S. Sartini et al., “Pyrazolopyrimidine derivatives as antineoplastic agents: with a special focus on thyroid cancer,” Mini-Reviews in Medicinal Chemistry, vol. 16, no. 2, pp. 86–93, 2015.
View at: Publisher Site | Google Scholar
L. Bertuccini, R. Russo, F. Iosi, and F. Superti, “Effects of Lactobacillus rhamnosus and Lactobacillus acidophilus on bacterial vaginal pathogens,” International Journal of Immunopathology and Pharmacology, vol. 30, no. 2, pp. 163–167, 2017.
View at: Publisher Site | Google Scholar
M. M. Perry and A. B. Gilbert, “Yolk transport in the ovarian follicle of the hen (Gallus domesticus): lipoprotein-like particles at the periphery of the oocyte in the rapid growth phase,” Journal of Cell Science, vol. 39, pp. 257–272, 1979.
View at: Google Scholar
S. Bykkam, K. V. Rao, C. H. S. Chakra, and T. Thunugunta, “Synthesis and characterization of graphene oxide and its antimicrobial activity against Klebseilla and Staphylococus,” International Journal of Advanced Biotechnology and Research, vol. 4, pp. 1005–1009, 2013.
View at: Google Scholar
S. Liu, M. Hu, T. H. Zeng et al., “Lateral dimension-dependent antibacterial activity of graphene oxide sheets,” Langmuir, vol. 28, no. 33, pp. 12364–12372, 2012.
View at: Publisher Site | Google Scholar
O. Akhavan, E. Ghaderi, H. Emamy, and F. Akhavan, “Genotoxicity of graphene nanoribbons in human mesenchymal stem cells,” Carbon, vol. 54, pp. 419–431, 2013.
View at: Publisher Site | Google Scholar
L. Hui, J. Huang, G. Chen, Y. Zhu, and L. Yang, “Antibacterial property of graphene quantum dots (both source material and bacterial shape matter),” ACS Applied Materials & Interfaces, vol. 8, no. 1, pp. 20–25, 2016.
View at: Publisher Site | Google Scholar
K. Yang, Y. Li, X. Tan, R. Peng, and Z. Liu, “Behavior and toxicity of graphene and its functionalized derivatives in biological systems,” Small, vol. 9, no. 9-10, pp. 1492–1503, 2013.
View at: Publisher Site | Google Scholar
D. Konatham and A. Striolo, “Molecular design of stable graphene nanosheets dispersions,” Nano Letters, vol. 8, no. 12, pp. 4630–4641, 2008.
View at: Publisher Site | Google Scholar
X. Zhang, J. Yin, C. Peng et al., “Distribution and biocompatibility studies of graphene oxide in mice after intravenous administration,” Carbon, vol. 49, no. 3, pp. 986–995, 2011.
View at: Publisher Site | Google Scholar
S. Vesaratchanon, A. Nikolov, and D. T. Wasan, “Sedimentation in nano-colloidal dispersions: effects of collective interactions and particle charge,” Advances in Colloid and Interface Science, vol. 134-135, pp. 268–278, 2007.
View at: Publisher Site | Google Scholar
T. Kuila, S. Bose, A. K. Mishra, P. Khanra, N. H. Kim, and J. H. Lee, “Chemical functionalization of graphene and its applications,” Progress in Materials Science, vol. 57, no. 7, pp. 1061–1105, 2012.
View at: Publisher Site | Google Scholar
Y. S. Kim and C. R. Park, “One-pot titration methodology for the characterization of surface acidic groups on functionalized carbon nanotubes,” Carbon, vol. 96, pp. 729–741, 2016.
View at: Publisher Site | Google Scholar
S. Visentin, N. Barbero, S. Musso et al., “Sensitive and practical fluorimetric test for CNT acidic site determination,” Chemical Communications, vol. 46, pp. 1443–1445, 2010.
View at: Google Scholar
W. Shao, X. Liu, H. Min, G. Dong, Q. Feng, and S. Zuo, “Preparation, characterization, and antibacterial activity of silver nanoparticle-decorated graphene oxide nanocomposite,” ACS Applied Materials & Interfaces, vol. 7, no. 12, pp. 6966–6973, 2015.
View at: Publisher Site | Google Scholar
S. Jaworski, M. Wierzbicki, E. Sawosz et al., “Graphene oxide-based nanocomposites decorated with silver nanoparticles as an antibacterial agent,” Nanoscale Research Letters, vol. 13, no. 1, p. 116, 2018.
View at: Publisher Site | Google Scholar
S. R.-V. Castrillón, F. Perreault, A. F. de Faria, and M. Elimelech, “Interaction of graphene oxide with bacterial cell membranes: insights from force spectroscopy,” Environmental Science & Technology Letters, vol. 2, no. 4, pp. 112–117, 2015.
View at: Publisher Site | Google Scholar
J. Li, G. Wang, H. Zhu et al., “Antibacterial activity of large-area monolayer graphene film manipulated by charge transfer,” Scientific Reports, vol. 4, no. 1, 2015.
View at: Publisher Site | Google Scholar
J. Chen, H. Peng, X. Wang, F. Shao, Z. Yuan, and H. Han, “Graphene oxide exhibits broad-spectrum antimicrobial activity against bacterial phytopathogens and fungal conidia by intertwining and membrane perturbation,” Nanoscale, vol. 6, no. 3, pp. 1879–1889, 2014.
View at: Publisher Site | Google Scholar
S. Saxena, T. A. Tyson, S. Shukla, E. Negusse, H. Chen, and J. Bai, “Investigation of structural and electronic properties of graphene oxide,” Applied Physics Letters, vol. 99, no. 1, pp. 13104–13107, 2011.
View at: Publisher Site | Google Scholar
C. Gómez-Navarro, R. T. Weitz, A. M. Bittner et al., “Electronic transport properties of individual chemically reduced graphene oxide sheets,” Nano Letters, vol. 7, no. 11, pp. 3499–3503, 2007.
View at: Publisher Site | Google Scholar
O. Akhavan and E. Ghaderi, “Escherichia coli bacteria reduce graphene oxide to bactericidal graphene in a self-limiting manner,” Carbon, vol. 50, no. 5, pp. 1853–1860, 2012.
View at: Publisher Site | Google Scholar
S. Gurunathan, J. Woong Han, A. Abdal Daye, V. Eppakayala, and J.-h. Kim, “Oxidative stress-mediated antibacterial activity of graphene oxide and reduced graphene oxide in Pseudomonas aeruginosa,” International Journal of Nanomedicine, vol. 7, pp. 5901–5914, 2012.
View at: Publisher Site | Google Scholar
M. Moldovan, D. Prodan, C. Sarosi et al., “Synthesis, morpho-structural properties and antibacterial effect of silicate based composites containing graphene oxide/hydroxyapatite,” Materials Chemistry and Physics, vol. 217, pp. 48–53, 2018.
View at: Publisher Site | Google Scholar
K. Prasad, G. S. Lekshmi, K. Ostrikov et al., “Synergic bactericidal effects of reduced graphene oxide and silver nanoparticles against Gram-positive and Gram-negative bacteria,” Scientific Reports, vol. 7, no. 1, pp. 1591–1602, 2017.
View at: Publisher Site | Google Scholar
A. Al-Jumaili, S. Alancherry, K. Bazaka, and M. Jacob, “Review on the antimicrobial properties of carbon nanostructures,” Materials, vol. 10, no. 9, 2017.
View at: Publisher Site | Google Scholar
V. T. H. Pham, V. K. Truong, M. D. J. Quinn et al., “Graphene induces formation of pores that kill spherical and rod-shaped bacteria,” ACS Nano, vol. 9, no. 8, pp. 8458–8467, 2015.
View at: Publisher Site | Google Scholar
X. Zou, L. Zhang, Z. Wang, and Y. Luo, “Mechanisms of the antimicrobial activities of graphene materials,” Journal of the American Chemical Society, vol. 138, no. 7, pp. 2064–2077, 2016.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2019 Federica Valentini et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3107

Downloads

1997

Citations