Abstract
The conducting materials of carbon black, iron powder and carbon nanotube were doped into poly(vinylidene fluoride) (PVDF) and piezoelectric lead zirconate titanate (PZT) ceramics composite powder to prepare piezoelectric composite. The result showed that an appropriate doping phase could improve the polarization and piezoelectric properties of composite materials. Independently from the chemical nature of the doping phase, when its amount was equal to 0.6%, the piezoelectric voltage constant of piezoelectric composite reached the maximum value. When the added quantities, the power storage capacities of piezoelectric composites reached the peak value when the amount of added carbon black or iron powder was 0.6% and that of carbon nanotube was 0.9%.
Similar content being viewed by others
References
Q. M. Zhang, V. Bharti, and X. Zhao, Science 280, 2101 (1998).
H. T. Li and X. H. Sun, Mod. Technol. Ceram. 14 (2), 28 (2009).
L. M. Zhang and D. You, Compos. Mater. Acad. J. 21 (3), 142 (2004).
D. H. Kuo, C. C. Chang, T. Y. Su, and B. Y. Lin, Mater. Chem. Phys. 85, 201 (2004).
N. Hu and X. N. Liu, Compos. Mater. Acad. J. 22 (5), 78 (2005).
K. Arlt and K. Wegener, IEEE Trans. Dielectr. Electr. Insul. 17 (4), 1178 (2010).
M. Raffaele, R. Janne, and H. Glenn, Science 299, 1872 (2003).
R. Li, C. X. Xiong, D. L. Kuang, L. J. Dong, and Y. A. Lei, Macromol. Rapid Commun. 29, 1449 (2008).
H. Cheng and Q. M. Zhang, Appl. Phys. Lett. 82, 3502 (2003).
I. S. Bayer, A. Biswas, and C. M. Megaridis, Appl. Phys. Lett. 93, 173902 (2008).
J. T. Xu, W. Jin, G. D. Liang, and Z. Q. Fan, Polymer 46, 1709 (2005).
R. Li, C. C. Wang, P. Z. Wang, and J. Z. Pei, Fuel 181, 935 (2016).
S. A. Wise, Sens. Actuators, A 69 (1), 33 (1998).
Z. M. Dang, Y. H. Zhang, and S. C. Tjong, Synth. Met. 146, 79 (2004).
S. C. Tjong, S. P. Bao, and G. D. Liang, J. Polym. Sci., Part B: Polym. Phys. 43, 3112 (2005).
Y. M. Tian and Y. Q. Xue, Electron. Technol. 19 (3), 9 (1998).
S. Hu and Y. Shen, New Chem. Mater. 35(12), 14 (2007).
H. Y. Quan and X. L. Xie, Nanchang Aeronaut. Univ. J. 26, 66 (2012).
Sh. Hu and Sh.Y. Sh, J. Funct. Mater. 38, 748 (2007).
C. W. Nan, Prog. Mater. Sci. 37(1), 1 (1993).
W. Lehmann, Nature 410, 447 (2001).
C. Huang, Q. M. Zhang, J. Yu. Li, and M. Rabeony, Appl. Phys. Lett. 87, 182901 (2005).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Li, R., Shi, Z., Zhao, Z. et al. Impact of doping phase on the electrical properties of lead zirconate titanate−poly(vinylidene fluoride) composites. Polym. Sci. Ser. A 59, 228–232 (2017). https://doi.org/10.1134/S0965545X17020055
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0965545X17020055