1.IntroductionPhoton upconversion based on triplet–triplet annihilation (TTA-UC) has attracted much attention for its potential applications in renewable energy production technologies.1–10 In the typical TTA-UC process, (1) a triplet excited state of the donor is formed by intersystem crossing (ISC) from a photoexcited singlet state, (2) acceptor triplet excited states are populated by triplet energy transfer (TET) from the donor triplets, and (3) annihilation between two acceptor triplets (TTA) generates an acceptor singlet excited state, from which upconverted delayed fluorescence is emitted [Fig. 1(a)]. One of the advantages of TTA-UC is its occurrence at lower excitation intensity compared with the other UC mechanisms due to the large absorption coefficient of the donor chromophores and the long triplet lifetime of acceptor molecules. To achieve efficient TTA-UC under weak incident light sources, diffusion of triplet species should be high enough to enable annihilation within their lifetimes. Consequently, the majority of TTA-UC systems have been studied in solution8,11–15 or soft polymer matrices,16–20 in which the TET and TTA processes are mediated by molecular diffusion and collision. Meanwhile, it is desirable for device applications that TTA-UC processes occur in the solid state without molecular diffusion. In this perspective, it is natural to develop triplet energy migration-based photon upconversion (TEM-UC),10 in which triplet excitons effectively diffuse in densely organized molecular assemblies without molecular diffusion.21–32 Among various assembly systems, molecular crystals with ordered chromophore arrangements should be promising for achieving fast TEM. However, the crystalline systems have suffered from the aggregation of donor molecules and their segregation in acceptor crystals, which caused poor TET efficiency.4 Despite efforts to solve this problem,28,29,32–34 the development of a simple and rational strategy to molecularly accommodate donor molecules in acceptor crystals is still anticipated. Here, we describe a kinetically controlled crystal growth approach that improves the dispersibility of donors in acceptor crystals and, consequently, increased the efficiency of TEM-UC. We employed the donor–acceptor pair of Pt(II) octaethylporphyrin (PtOEP) and 9,10-diphenylanthracene (DPA), which has been widely used as a benchmark. Due to their inherent structural mismatch, PtOEP and DPA do not mix homogeneously in crystals and tend to phase segregate.4 Meanwhile, miscibility of molecules coexisting in multicomponent assemblies has been kinetically controlled for organic molecular crystals35 and peptide assemblies.36,37 We apply this kinetic control concept to improve the miscibility of donor PtOEP and acceptor DPA in nanocrystals. For this, we adopted a colloid chemistry approach; tetrahydrofuran (THF) solutions of DPA–PtOEP were injected into aqueous cetyltrimethylammonium bromide (CTAB).38–40 Upon the diffusion of injected THF into the aqueous phase, the nucleation of water-insoluble aromatic crystals occurs. Adsorption of CTAB molecules on the growing crystal surfaces would reduce their interfacial energy, thus enhancing the dispersion stability of these crystals.38–40 Significantly, it was found that the increase in the concentration of DPA–PtOEP caused faster crystallization of DPA, which allowed PtOEP molecules to be kinetically trapped with improved dispersibility in DPA crystals [Fig. 1(b)]. 2.Experimental Details2.1.Materials and MethodsAll the solvents were used as received without further purification. DPA was purchased from Aldrich and purified by sublimation in order to minimize the amount of impurities, which may act as quencher in the solid system. PtOEP and CTAB were purchased from Aldrich and Wako chemical and used as received. UV–visible absorption spectra were recorded on a JASCO V-670 spectrophotometer. Fluorescence spectra were measured by using a PerkinElmer LS 55 fluorescence spectrometer. Powder x-ray diffraction (PXRD) analyses were conducted on a BRUKER D2 PHASER with a Cu source (). Scanning electron microscope (SEM) images were obtained by using a Hitachi S-5000. For SEM measurements, samples were collected by suction filtration using membrane filters with pore size of . These filters were directly used for SEM measurements after platinum sputtering with the thickness of ca. 2 nm. Time-resolved photoluminescence lifetime measurements were carried out by using a time-correlated single photon counting lifetime spectroscopy system, Hamamatsu Quantaurus-Tau C11567-01. Dynamic light scattering measurements were carried out by using Malvern Nano-ZS ZEN3600. For TTA-UC measurements, the samples were sealed between quartz plates by using hot-melt adhesive in an Ar-filled glove box (). For TTA-UC emission spectra, a diode laser (532 nm, 200 mW, RGB Photonics) was used as an excitation source. The laser power was controlled by combining a software (Ltune) and a variable neutral density filter and measured using a PD300-UV photodiode sensor (OPHIR Photonics). The laser beam was focused on a sample using a lens. The diameter of the laser beam () was measured at the sample position using a CCD beam profiler SP620 (OPHIR Photonics). The typical area of laser irradiation spot estimated from the diameter was . The emitted light was collimated by an achromatic lens, the excitation light was removed using a notch filter (532 nm), and the emitted light was again focused by an achromatic lens to an optical fiber connected to a multichannel detector MCPD-9800, which was supplied and calibrated by Otsuka Electronics and equipped with a CCD sensor for the detection of whole visible range with high sensitivity. TTA-UC and donor phosphorescence quantum yields were measured by using an absolute quantum yield measurement system. The sample was held in an integration sphere and excited by the laser excitation source (532 nm, 200 mW, RGB Photonics). The scattered excitation light was removed using a 532 nm notch filter, and emitted light was monitored with a multichannel detector C10027-01 (Hamamatsu Photonics). The spectrometer was calibrated including the integration sphere and notch filter by Hamamatsu Photonics.22 2.2.Sample PreparationsDPA and PtOEP were dissolved in THF at three different concentrations. As a moderately diluted condition, DPA (2 mM)–PtOEP() in THF was employed (condition 1). Separately, saturated solutions of DPA (140 mM) with two different PtOEP concentrations (140 and ) were prepared for the rapid crystallization (conditions 2A and 2B). All the experiments of crystal growth and collection were carried out at room temperature (around 20°C). No preformed crystals in the 140 mM DPA solution were detected from dynamic light scattering measurements. 0.5 mL of DPA–PtOEP mixed THF solutions were rapidly injected into the aqueous CTAB (0.5 mM, 5 mL) at room temperature under 1000 rpm stirring. These mixtures were kept stirring for 3 min and then left to stand for 2 h. After the incubation for 2 h, the crystals were collected by centrifugation at 10,000 rpm for 5 min, washed with water for three times, and dried under vacuum at room temperature. 3.Results and Discussions3.1.Characterization of the CrystalsWhen the THF solution of DPA (2 mM)–PtOEP () was injected into the aqueous CTAB (condition 1) under stirring, the immediately formed suspension turned into a uniform dispersion within 3 min of stirring. This specimen was then incubated for 2 h, during which crystalline particles were gradually formed. On the other hand, precipitates were immediately formed upon injection of the saturated DPA solutions into aqueous CTAB (, and , conditions 2A and 2B), which showed almost no changes during the standing for 2 h. The composition of the obtained crystals was determined by dissolving the crystals in THF and measuring their absorption spectra. The DPA–PtOEP molar ratios were , , and for those obtained under the conditions 1, 2A, and 2B, respectively. The content of PtOEP in the obtained crystals was lower than the initial mixing ratio in THF for condition 1 (), whereas it was higher than those for conditions 2A () and 2B (). The enhanced accumulation of PtOEP in DPA crystals under conditions 2A and 2B suggests that the rapid growth of DPA microcrystals facilitate kinetic entrapment of PtOEP molecules in the interior. The crystallinity of obtained samples was confirmed by using PXRD measurements (Fig. 2). The diffraction patterns of the crystals formed under these conditions showed good agreements with the PXRD pattern of bulk DPA. On the other hand, the diffraction peaks of bulk PtOEP, for example, the peak at , were hardly observed from those of the composite crystals, which would be due to the high dispersibility of the donor molecules or the too small amount of PtOEP for detection. It is confirmed that the basic arrangement of DPA molecules is almost independent of the crystallization conditions. To get insights into the crystal growth processes, the crystals were collected by suction filtration before and after the 2 h of incubation, and their morphology was observed by scanning electron microscopy. In the case of the condition 1 sample, partly aggregated irregular nanorods were observed before incubation. After standing for 2 h, a few -sized rods and a few tens of -sized sheets appeared [Fig. 3(a)]. The observed morphological changes suggest that the ordered crystals gradually grew in the course of incubation. On the other hand, samples obtained under the conditions 2A and 2B gave larger spherical microstructures with similar size before and after the incubation process [Figs. 3(b) and 3(c)]. It is to be noted that the morphology of crystals differs considerably depending on the preparative conditions, i.e., kinetic parameters determine both of the nucleation and growth processes. When the same preparation procedure was carried out for PtOEP without DPA, only a few tens of nm-sized nanocrystals were observed, and thus the above-mentioned -sized objects cannot be the crystals consisting of pure PtOEP. 3.2.Photophysical Properties of the CrystalsTo investigate the dispersed state of PtOEP molecules in acceptor DPA crystals, UV–vis absorption spectra of PtOEP were measured (Fig. 4). A THF solution of PtOEP ) showed a band at 534 nm, whereas this band is red-shifted to 552 nm in the cast solid sample due to aggregation.41 Interestingly, absorption spectra obtained for PtOEP in DPA–PtOEP composite crystals showed blue shifts compared to that of the neat cast solid. Notably, the peaks of the condition 2A (537 nm) and 2B (536 nm) samples are more blue shifted compared to that of the crystals obtained under condition 1 (541 nm). It is to note that the main peak of the condition 2B sample is close to that observed for the diluted THF solution, with a suppressed shoulder component at around 547 nm. This shoulder component reflects the presence of interchromophore interactions among PtOEP molecules. Apparently, the sample prepared under the condition 2B showed the spectrum revealing the most isolated PtOEP chromophores, showing the highest dispersibility of PtOEP is achieved under the rapid crystal growth condition with the high DPA:PtOEP molar ratio. We confirmed that the DPA–PtOEP crystals prepared in the absence of CTAB showed a pronounced aggregate-shoulder peak, indicating that CTAB significantly influenced the crystallization kinetics in the aqueous mixtures. The fluorescence quantum yields with direct excitation of DPA (, ) were 42%, 28%, and 54% for powdery samples obtained under conditions 1, 2A, and 2B, respectively. Since the higher values were observed for crystals with lower PtOEP contents, it is possible that the DPA-to-PtOEP singlet–singlet energy transfer and/or the reabsorption of the DPA fluorescence by the donor molecules takes place. The TTA-UC characteristics of each composite crystals were then evaluated. Under excitation with a 532-nm laser, upconverted emission was clearly observed for each sample with the maximum intensity at around 440 nm (Fig. 5). It is to be noted that these TTA-UC behaviors observed for the present DPA–PtOEP crystals prepared by the CTAB-assisted colloid technique is significantly improved as compared to that previously reported for the DPA single crystal doped with PtOEP.4 The donor phosphorescence at 650 nm was much weaker than the UC emission, and the phosphorescence quantum yields of all the three samples were less than 0.1%. These results suggest that the triplet energy of the donor molecules is efficiently transferred to the surrounding acceptor molecules or thermally dissipated in the donor aggregates.41 TTA-UC quantum yields for samples obtained under each condition were determined by the absolute method using the integrating sphere and the laser excitation source, to avoid inaccuracy that could arise from the strong light scattering of the crystals. In general, the quantum yield is defined as the ratio of absorbed photons to emitted photons, and thus the maximum yield () of the bimolecular TTA-UC process is 50%. However, many reports multiply this value by 2 to set the maximum quantum yield at 100%. To avoid the confusion between these different definitions, the UC quantum yield is written as () when the maximum efficiency is normalized to 100%. The value detemined for the condition 1 sample was as low as (Fig. 6). On the other hand, much higher values were observed for crystals prepared under the conditions 2A () and 2B (). To understand the observed difference, factors affecting to the value need to be considered. is represented by the following equation: where , , , and represent the quantum efficiencies of donor ISC, donor-to-acceptor TET, TTA, and acceptor emission.4,8 The parameter is the statistical probability for obtaining a singlet excited state after the annihilation of two triplet states. Considering that of the condition 2A sample was smaller (28%) than that of the condition 1 sample (42%), the higher value of the condition 2A sample as compared to the condition 1 sample should be originated from the other parameters. The value and can be assumed to be the same for the identical donor–acceptor pair with the similar crystal structure as confirmed by PXRD. It is then suggested that the better dispersibility of donor molecules in condition 2A sample, as evidenced by the absorption spectra (Fig. 4), improved the net value and consequently afforded the better . As described above, the condition 2B sample showed the highest donor dispersibility among all the samples prepared in this study (Fig. 4). It is reasonable that the condition 2B sample showed higher than the condition 2A sample, which was also benefitted from the smaller content of the donor that allowed to maintain higher (54%). The UC quantum yields remain low () at the solar irradiance ( at , air mass 1.5), requiring future efforts to decrease the needed excitation intensity.We would like to call attention to the complexity of the condensed systems when the donor distribution is not homogeneous in acceptor crystals. Generally, TTA-UC emission intensity shows a quadratic dependence with the incident light intensity at low excitation intensity, where the thermal deactivation of the triplet states is governed by the main deactivation pathway. The quadratic-to-linear transition occurs by increasing the excitation intensity, and the transition point gives a threshold excitation intensity ().42–44 Above , the TTA becomes the main deactivation channel for the acceptor triplets. The quadratic-to-linear transitions were observed for all the three conditions (Fig. 7). Despite the considerable difference in the UC quantum yield (Fig. 6), these three samples showed rather similar values in the range of 326 to . This discrepancy might be explained by the following hypothesis. In the condition 1 sample, not all donor molecules form aggregates and some donor molecules well dispersed in acceptor crystals contribute to the excitation intensity dependence with value similar to the condition 2B sample. However, as we described above, most of the donor molecules are present as aggregates in the condition 1 sample, which hinder the donor-to-acceptor TET and resulted in the observed low UC quantum yield. It is therefore essential to characterize the UC characteristics in a comprehensive manner, and the determination of UC quantum yields is prerequisite for the evaluation of solid upconverters. 4.Conclusions and Future RemarksWe show the promising potential of kinetically controlled crystal growth to improve the dispersibility of donor molecules in acceptor crystals and to achieve efficient TEM-UC in the solid state. By simply increasing the concentration of the donor and acceptor in the surfactant-assisted reprecipitation process, the kinetic entrapment of the donor in acceptor crystals is facilitated with the enhanced dispersibility. Consequently, the UC quantum yield was dramatically enhanced. The concept of kinetically controlled crystal growth is successfully demonstrated for the benchmark TTA-UC pair, DPA and PtOEP, which has been known to undergo severe phase segregation. The present kinetically controlled crystallization concept for improving donor dispersibility in acceptor crystals would be widely applicable to a variety of chromophore combinations, including the recently developed precious metal-free systems25,45,46 and NIR-to-visible UC systems.12–15,47,48 For further improvement of the current method, we consider that the key is to suppress the formation of defect sites that deactivate the triplet excitons.28 The development of approaches to circumvent this issue is under way in our laboratory. AcknowledgmentsThis work was partly supported by the JSPS KAKENHI Grant Nos. JP25220805, JP17H04799, JP16H06513 (Coordination Asymmetry), JP16H00844 (Soft Molecular Systems), PRESTO program on “Molecular Technology and Creation of New Functions” from JST (JPMJPR14KE), and the Asahi Glass Foundation. ReferencesS. Baluschev et al.,
“Up-conversion fluorescence: noncoherent excitation by sunlight,”
Phys. Rev. Lett., 97 143903
(2006). http://dx.doi.org/10.1103/PhysRevLett.97.143903 PRLTAO 0031-9007 Google Scholar
T. N. Singh-Rachford and F. N. Castellano,
“Photon upconversion based on sensitized triplet–triplet annihilation,”
Coord. Chem. Rev., 254 2560
–2573
(2010). http://dx.doi.org/10.1016/j.ccr.2010.01.003 CCHRAM 0010-8545 Google Scholar
J. Z. Zhao, S. M. Ji and H. M. Guo,
“Triplet–triplet annihilation based upconversion: from triplet sensitizers and triplet acceptors to upconversion quantum yields,”
RSC Adv., 1 937
–950
(2011). http://dx.doi.org/10.1039/c1ra00469g Google Scholar
A. Monguzzi et al.,
“Low power, non-coherent sensitized photon up-conversion: modelling and perspectives,”
Phys. Chem. Chem. Phys., 14 4322
–4332
(2012). http://dx.doi.org/10.1039/c2cp23900k PPCPFQ 1463-9076 Google Scholar
Y. C. Simon and C. Weder,
“Low-power photon upconversion through triplet–triplet annihilation in polymers,”
J. Mater. Chem., 22 20817
–20830
(2012). http://dx.doi.org/10.1039/c2jm33654e JMACEP 0959-9428 Google Scholar
J. H. KimJ. H. Kim,
“Encapsulated triplet–triplet annihilation-based upconversion in the aqueous phase for sub-band-gap semiconductor photocatalysis,”
J. Am. Chem. Soc., 134 17478
–17481
(2012). http://dx.doi.org/10.1021/ja308789u JACSAT 0002-7863 Google Scholar
V. Gray et al.,
“Triplet–triplet annihilation photon-upconversion: towards solar energy applications,”
Phys. Chem. Chem. Phys., 16 10345
–10352
(2014). http://dx.doi.org/10.1039/C4CP00744A PPCPFQ 1463-9076 Google Scholar
T. W. Schmidt and F. N. Castellano,
“Photochemical upconversion: the primacy of kinetics,”
J. Phys. Chem. Lett., 5 4062
–4072
(2014). http://dx.doi.org/10.1021/jz501799m JPCLCD 1948-7185 Google Scholar
J. Zhou et al.,
“Upconversion luminescent materials: advances and applications,”
Chem. Rev., 115 395
–465
(2015). http://dx.doi.org/10.1021/cr400478f CHREAY 0009-2665 Google Scholar
N. Yanai and N. Kimizuka,
“Recent emergence of photon upconversion based on triplet energy migration in molecular assemblies,”
Chem. Commun., 53 655
–655
(2017). http://dx.doi.org/10.1039/C6CC90564A Google Scholar
M. A. Filatov et al.,
“Reversible oxygen addition on a triplet sensitizer molecule: protection from excited state depopulation,”
Phys. Chem. Chem. Phys., 17 6501
–6510
(2015). http://dx.doi.org/10.1039/C4CP05025H PPCPFQ 1463-9076 Google Scholar
Z. Y. Huang et al.,
“Hybrid molecule-nanocrystal photon upconversion across the visible and near-infrared,”
Nano Lett., 15 5552
–5557
(2015). http://dx.doi.org/10.1021/acs.nanolett.5b02130 NALEFD 1530-6984 Google Scholar
K. Okumura et al.,
“Employing core-shell quantum dots as triplet sensitizers for photon upconversion,”
Chem. Eur. J., 22 7721
–7726
(2016). http://dx.doi.org/10.1002/chem.201600998 CEUJED 0947-6539 Google Scholar
C. Mongin et al.,
“Direct observation of triplet energy transfer from semiconductor nanocrystals,”
Science, 351 369
–372
(2016). http://dx.doi.org/10.1126/science.aad6378 SCIEAS 0036-8075 Google Scholar
Y. Sasaki et al.,
“Near infrared-to-blue photon upconversion by exploiting direct S-T absorption of a molecular sensitizer,”
J. Mater. Chem. C, 5 5063
–5067
(2017). http://dx.doi.org/10.1039/C7TC00827A Google Scholar
R. R. Islangulov et al.,
“Noncoherent low-power upconversion in solid polymer films,”
J. Am. Chem. Soc., 129 12652
–12653
(2007). http://dx.doi.org/10.1021/ja075014k JACSAT 0002-7863 Google Scholar
J. H. Kim et al.,
“High efficiency low-power upconverting soft materials,”
Chem. Mater., 24 2250
–2252
(2012). http://dx.doi.org/10.1021/cm3012414 CMATEX 0897-4756 Google Scholar
F. Marsico et al.,
“Hyperbranched unsaturated polyphosphates as a protective matrix for long-term photon upconversion in air,”
J. Am. Chem. Soc., 136 11057
–11064
(2014). http://dx.doi.org/10.1021/ja5049412 JACSAT 0002-7863 Google Scholar
S. H. Lee et al.,
“Glassy poly(methacrylate)terpolymers with covalently attached emitters and sensitizers for low-power light upconversion,”
J. Polym. Sci. A Polym. Chem., 53 1629
–1639
(2015). http://dx.doi.org/10.1002/pola.v53.14 Google Scholar
A. Monguzzi et al.,
“Solid-state sensitized upconversion in polyacrylate elastomers,”
J. Phys. Chem. C, 120 2609
–2614
(2016). http://dx.doi.org/10.1021/acs.jpcc.6b00223 JPCCCK 1932-7447 Google Scholar
R. Vadrucci, C. Weder and Y. C. Simon,
“Low-power photon upconversion in organic glasses,”
J. Mater. Chem. C, 2 2837
–2841
(2014). http://dx.doi.org/10.1039/C3TC32473G Google Scholar
P. F. Duan et al.,
“Photon upconversion in supramolecular gel matrixes: spontaneous accumulation of light-harvesting donor–acceptor arrays in nanofibers and acquired air stability,”
J. Am. Chem. Soc., 137 1887
–1894
(2015). http://dx.doi.org/10.1021/ja511061h JACSAT 0002-7863 Google Scholar
T. Ogawa et al.,
“Highly efficient photon upconversion in self-assembled light-harvesting molecular systems,”
Sci. Rep., 5 10882
(2015). http://dx.doi.org/10.1038/srep10882 SRCEC3 2045-2322 Google Scholar
P. F. Duan et al.,
“Aggregation-induced photon upconversion through control of the triplet energy landscapes of the solution and solid states,”
Angew. Chem. Int. Ed., 54 7544
–7549
(2015). http://dx.doi.org/10.1002/anie.201501449 Google Scholar
T. C. Wu, D. N. Congreve and M. A. Baldo,
“Solid state photon upconversion utilizing thermally activated delayed fluorescence molecules as triplet sensitizer,”
Appl. Phys. Lett., 107 031103
(2015). http://dx.doi.org/10.1063/1.4926914 APPLAB 0003-6951 Google Scholar
S. Hisamitsu, N. Yanai and N. Kimizuka,
“Photon-upconverting ionic liquids: effective triplet energy migration in contiguous ionic chromophore arrays,”
Angew. Chem. Int. Ed., 54 11550
–11554
(2015). http://dx.doi.org/10.1002/anie.201505168 Google Scholar
J. S. Lissau et al.,
“Photon upconversion from chemically bound triplet sensitizers and emitters on mesoporous : implications for solar energy conversion,”
J. Phys. Chem. C, 119 25792
–25806
(2015). http://dx.doi.org/10.1021/acs.jpcc.5b08907 JPCCCK 1932-7447 Google Scholar
M. Hosoyamada et al.,
“Molecularly dispersed donors in acceptor molecular crystals for photon upconversion under low excitation intensity,”
Chem. Eur. J., 22 2060
–2067
(2016). http://dx.doi.org/10.1002/chem.201503318 Google Scholar
M. Oldenburg et al.,
“Photon upconversion at crystalline organic–organic heterojunctions,”
Adv. Mater., 28 8477
–8482
(2016). http://dx.doi.org/10.1002/adma.v28.38 ADVMEW 0935-9648 Google Scholar
A. Monguzzi et al.,
“Unraveling triplet excitons photophysics in hyper-cross-linked polymeric nanoparticles: toward the next generation of solid-state upconverting materials,”
J. Phys. Chem. Lett., 7 2779
–2785
(2016). http://dx.doi.org/10.1021/acs.jpclett.6b01115 JPCLCD 1948-7185 Google Scholar
N. Kimizuka, N. Yanai and M. Morikawa,
“Photon upconversion and molecular solar energy storage by maximizing the potential of molecular self-assembly,”
Langmuir, 32 12304
–12322
(2016). http://dx.doi.org/10.1021/acs.langmuir.6b03363 LANGD5 0743-7463 Google Scholar
K. Kamada et al.,
“Efficient triplet–triplet annihilation upconversion in binary crystalline solids fabricated via solution casting and operated in air,”
Mater. Horiz., 4 83
–87
(2017). http://dx.doi.org/10.1039/C6MH00413J Google Scholar
S. Baluschev et al.,
“Two pathways for photon upconversion in model organic compound systems,”
J. Appl. Phys., 101 023101
(2007). http://dx.doi.org/10.1063/1.2409618 JAPIAU 0021-8979 Google Scholar
H. Goudarzi and P. E. Keivanidis,
“Triplet–triplet annihilation-induced up-converted delayed luminescence in solid-state organic composites: monitoring low energy photon up-conversion at low temperatures,”
J. Phys. Chem. C, 118 14256
–14265
(2014). http://dx.doi.org/10.1021/jp5052936 JPCCCK 1932-7447 Google Scholar
Q. H. Cui, Y. S. Zhao and J. N. Yao,
“Controlled synthesis of organic nanophotonic materials with specific structures and compositions,”
Adv. Mater., 26 6852
–6870
(2014). http://dx.doi.org/10.1002/adma.v26.40 ADVMEW 0935-9648 Google Scholar
B. Li et al.,
“Nonequilibrium self-assembly of π-conjugated oligopeptides in solution,”
ACS Appl. Mater. Interfaces, 9 3977
–3984
(2017). http://dx.doi.org/10.1021/acsami.6b15068 AAMICK 1944-8244 Google Scholar
H. A. M. Ardona et al.,
“Kinetically controlled coassembly of multichromophoric peptide hydrogelators and the impacts on energy transport,”
J. Am. Chem. Soc., 139 8685
–8692
(2017). http://dx.doi.org/10.1021/jacs.7b04006 JACSAT 0002-7863 Google Scholar
X. J. Zhang et al.,
“Single-crystal 9,10-diphenylanthracene nanoribbons and nanorods,”
Chem. Mater., 20 6945
–6950
(2008). http://dx.doi.org/10.1021/cm801896r CMATEX 0897-4756 Google Scholar
B. Yang et al.,
“Shape-controlled micro/nanostructures of 9,10-diphenylanthracene (DPA) and their application in light-emitting devices,”
J. Phys. Chem. C, 115 7924
–7927
(2011). http://dx.doi.org/10.1021/jp112195k JPCCCK 1932-7447 Google Scholar
C. Zhang et al.,
“Self-modulated white light outcoupling in doped organic nanowire waveguides via the fluctuations of singlet and triplet excitons during propagation,”
Adv. Mater., 23 1380
–1384
(2011). http://dx.doi.org/10.1002/adma.v23.11 ADVMEW 0935-9648 Google Scholar
M. Campione et al.,
“Control of interactions in epitaxial films of platinum(II) octaethyl porphyrin,”
Chem. Mater., 23 832
–840
(2011). http://dx.doi.org/10.1021/cm102139h CMATEX 0897-4756 Google Scholar
A. Monguzzi et al.,
“Upconversion-induced fluorescence in multicomponent systems: steady-state excitation power threshold,”
Phys. Rev. B, 78 195112
(2008). http://dx.doi.org/10.1103/PhysRevB.78.195112 Google Scholar
Y. Y. Cheng et al.,
“On the efficiency limit of triplet–triplet annihilation for photochemical upconversion,”
Phys. Chem. Chem. Phys., 12 66
–71
(2010). http://dx.doi.org/10.1039/B913243K PPCPFQ 1463-9076 Google Scholar
A. Haefele et al.,
“Getting to the (square) root of the problem: how to make noncoherent pumped upconversion linear,”
J. Phys. Chem. Lett., 3 299
–303
(2012). http://dx.doi.org/10.1021/jz300012u JPCLCD 1948-7185 Google Scholar
N. Yanai et al.,
“Increased vis-to-UV upconversion performance by energy level matching between a TADF donor and high triplet energy acceptors,”
J. Mater. Chem. C, 4 6447
–6451
(2016). http://dx.doi.org/10.1039/c6tc01816e Google Scholar
V. Gray et al.,
“Loss channels in triplet–triplet annihilation photon upconversion: importance of annihilator singlet and triplet surface shapes,”
Phys. Chem. Chem. Phys., 19 10931
–10939
(2017). http://dx.doi.org/10.1039/C7CP01368J PPCPFQ 1463-9076 Google Scholar
S. Amemori et al.,
“Near-infrared-to-visible photon upconversion sensitized by a metal complex with spin-forbidden yet strong absorption,”
J. Am. Chem. Soc., 138 8702
–8705
(2016). http://dx.doi.org/10.1021/jacs.6b04692 JACSAT 0002-7863 Google Scholar
M. F. Wu et al.,
“Solid-state infrared-to-visible upconversion sensitized by colloidal nanocrystals,”
Nat. Photonics, 10 31
–34
(2016). http://dx.doi.org/10.1038/nphoton.2015.226 NPAHBY 1749-4885 Google Scholar
BiographyTaku Ogawa received his MS degree in engineering from Kyushu University in 2015. He is currently a PhD candidate under the supervision of Prof. N. Kimizuka and Dr. N. Yanai in the Department of Chemistry and Biochemistry. His current research focuses on triplet energy dynamics in self-assembled materials. Nobuhiro Yanai received his PhD from Kyoto University in 2011 with Prof. Susumu Kitagawa and Dr. Takashi Uemura on polymer properties in MOFs. He was a postdoctoral researcher with Prof. Steve Granick at the University of Illinois at Urbana–Champaign, working on self-assembly of MOF colloids. In 2012, he became an assistant professor at Kyushu University, where he has been an associate professor since 2015. His current research interests are in materials chemistry for photon upconversion. Hironori Kouno received his MS degree in engineering from Kyushu University in 2017. He is currently a PhD candidate under the supervision of Prof. N. Kimizuka and Dr. N. Yanai in the Department of Chemistry and Biochemistry. His current research focuses on establishment of aqueous photon upconversion molecular system. His research interests also include development of functional materials for energy-related and biological applications. Nobuo Kimizuka received his PhD from Kyushu University in 1990 with Prof. Toyoki Kunitake on the excitonic chromophore interactions in molecular membranes. After working as a postdoctoral researcher with Prof. Helmut Ringsdorf at Mainz University, he was promoted to an associate professor in 1992 and a full professor in 2000. His work encompasses the synthesis and functions of molecular self-assemblies and nanomaterials with recent focus on photon energy conversion in organized molecular systems. |