Enhanced electrical conductivities of N-doped carbon nanotubes by controlled heat treatment

Abstract

The thermal stability of nitrogen (N) functionalities on the sidewalls of N-doped multi-walled carbon nanotubes was investigated at temperatures ranging between 1000 °C and 2000 °C. The structural stability of the doped tubes was then correlated with the electrical conductivity both at the bulk and at the individual tube levels. When as-grown tubes were thermally treated at 1000 °C, we observed a very significant decrease in the electrical resistance of the individual nanotubes, from 54 kΩ to 0.5 kΩ, which is attributed to a low N doping level (e.g. 0.78 at% N). We noted that pyridine-type N was first decomposed whereas the substitutional N was stable up to 1500 °C. For nanotubes heat treated to 1800 °C and 2000 °C, the tubes exhibited an improved degree of crystallinity which was confirmed by both the low R value (ID/IG) in the Raman spectra and the presence of straight graphitic planes observed in TEM images. However, N atoms were not detected in these tubes and caused an increase in their electrical resistivity and resistance. These partially annealed doped tubes with enhanced electrical conductivities could be used in the fabrication of robust and electrically conducting composites, and these results could be extrapolated to N-doped graphene and other nanocarbons.

Graphical abstract: Enhanced electrical conductivities of N-doped carbon nanotubes by controlled heat treatment

Supplementary files

Article information

Article type
Paper
Submitted
04 Jul 2011
Accepted
15 Aug 2011
First published
12 Sep 2011

Nanoscale, 2011,3, 4359-4364

Enhanced electrical conductivities of N-doped carbon nanotubes by controlled heat treatment

K. Fujisawa, T. Tojo, H. Muramatsu, A. L. Elías, S. M. Vega-Díaz, F. Tristán-López, J. H. Kim, T. Hayashi, Y. A. Kim, M. Endo and M. Terrones, Nanoscale, 2011, 3, 4359 DOI: 10.1039/C1NR10717H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements