Abstract
Correlated electrons in transition metal oxides exhibit a variety of emergent phases. When transition metal oxides are confined to a single-atomic-layer thickness, experiments so far have shown that they usually lose diverse properties and become insulators. In an attempt to extend the range of electronic phases of the single-atomic-layer oxide, we search for a metallic phase in a monolayer-thick epitaxial SrRuO3 film. Combining atomic-scale epitaxy and angle-resolved photoemission measurements, we show that the monolayer SrRuO3 is a strongly correlated metal. Systematic investigation reveals that the interplay between dimensionality and electronic correlation makes the monolayer SrRuO3 an incoherent metal with orbital-selective correlation. Furthermore, the unique electronic phase of the monolayer SrRuO3 is found to be highly tunable, as charge modulation demonstrates an incoherent-to-coherent crossover of the two-dimensional metal. Our work emphasizes the potentially rich phases of single-atomic-layer oxides and provides a guide to the manipulation of their two-dimensional correlated electron systems.
Similar content being viewed by others
Introduction
With the size of electronic devices getting ever smaller, continued efforts to use different schemes, such as single-molecule transistors, are being made to overcome the quantum limit. The discovery of graphene in 2004 and later van der Waals material groups suggests a direction of atomically thin two-dimensional (2D) electronics1,2,3. From the fundamental scientific point of view, an ideal 2D system can provide physics distinct from that of three-dimensional (3D) systems. Accordingly, the 2D van der Waals material groups, associated devices4, heterostructures5, and Moiré superlattices6,7 have been the most intensively studied subjects in condensed matter physics in the past 15 years. However, it is still quite difficult to obtain high-quality and large-size flakes of van der Waals materials for practical applications.
On the other hand, the strongly correlated electron system of transition metal oxides possesses numerous exotic electronic phases with physical properties, e.g., high-temperature superconductivity, Mott transition, and ferromagnetism8,9,10. Most of these phases appear in three-dimensionally connected oxide crystals such as perovskite oxides. These exotic properties in principle can be utilized for device applications. In light of the direction in the 2D van der Waals materials research, transition metal oxides with single-atomic-layer thickness can offer functionalities in the nanometer scale by bridging correlated electron systems and the field of 2D materials. However, only a few oxides are known to have van der Waals bonding and can be exfoliated into atomically thin flakes11,12.
Epitaxial thin film growth can provide an alternative approach to constructing artificial 2D oxides and their devices on a range of lattice-matched oxide substrates13 or Si wafer14. Despite extensive efforts to realize the 2D electronic oxides, most of the ultrathin oxide films exhibit a metal-to-insulator transition in approaching the single-atomic-layer limit15,16, which is usually attributed to correlation-driven Mott insulating phases or localization effects. Such monotonous behavior detains the functional spectrum of 2D oxides and limits the integration of the intrinsic physical properties into real devices. Therefore, the demonstration of a metallic single-atomic-layer oxide is highly desired to extend the boundary of functionalities and application possibilities for oxide films.
Here, we report the metallic electronic structure of a single-atomic-layer oxide, a monolayer SrRuO3 (SRO) film with a single RuO2 atomic plane. The challenge in the investigation of a single-atomic-layer oxide arises from the film’s vulnerability to extrinsic disorders. We employed angle-resolved photoemission spectroscopy (ARPES) measurement to obtain the intrinsic electronic structure of a single unit-cell (uc) SRO. The electronic structure of a monolayer SRO is found to be strongly correlated. We unveil the origin of the correlated phase and demonstrate the tunable electronic phase by charge modulation. This work adds electronic states to the library of single-atomic-layer oxides which has been limited to insulators until now.
Results
Fabrication of charging-free ultrathin heterostructures
In the study of ultrathin oxide films, transport measurements are routinely performed to study the physical properties. However, transport properties can be sensitive to extrinsic effects such as disorder17. Such extrinsic effects tend to be more pronounced for films with reduced thicknesses due to the increased scattering from interfaces and surfaces18. More importantly, transport measurements require a conducting path in the film over a macroscopic scale, which is not generally guaranteed. Particularly, the conducting channel can be broken near the step-edges of substrates19. In that regard, ARPES, which detects electrons with periodic motion and does not require macroscopic connectivity, can be an effective tool to study the intrinsic electronic property of ultrathin oxide films.
There have been several ARPES studies on ultrathin epitaxial transition metal oxide films20,21,22,23,24. For the case of SrIrO3 and LaNiO3, the studies have even reached the monolayer limit, for which insulating electronic structures have been observed. Here, we note the similarity between monolayer oxide films and their quasi-two-dimensional counterparts; both Sr2IrO425 and NdSrNiO426 are antiferromagnetic insulators. Based on this analogy, we chose a single-atomic-layer-thick SRO film (Fig. 1a) whose electronic ground state is currently under debate27,28. The monolayer SRO can be also regarded as a two-dimensional analog of a metallic single layer perovskite Sr2RuO4 which has been intensively studied for its unconventional superconductivity29 and recently for magnetism30.
We grew high-quality and charging-free ultrathin SRO heterostructures with various thicknesses. Figure 1b shows a schematic of the SRO heterostructure which consists of 4 uc SRO layer, 10 uc SrTiO3 (STO) buffer layer, and n uc ultrathin SRO layer (n uc SRO), sequentially grown on an STO (001) substrate. In ARPES measurements on ultrathin films, escaping photoelectrons can cause a charging effect that distorts the measured spectra. By introducing a current path of 4 uc-thick SRO layer (conducting layer), we successfully removed the charging effect in the measurements of ultrathin SRO (Fig. 1c) [See “Supplementary Fig. 4” for comparison of the ARPES data with and without the conducting layer]. The 10 uc STO buffer layer (4 nm thickness) decouples the electronic structure of the topmost ultrathin SRO from that of the conducting layer [See “Supplementary Fig. 7” for details].
Scanning transmission electron microscopy (STEM) provides atomic-scale visualization of our charging-free ultrathin SRO heterostructures. Figure 1d displays a cross-sectional high-angle annular dark-field STEM (HAADF-STEM) image with STO [100] zone axis. To image the monolayer SRO, we deposited an additional 10 uc STO capping layer to protect the monolayer SRO. The conducting layer, buffer layer, monolayer SRO, and capping layer are well organized in the preferred order. In the plot of HAADF-STEM intensity across the monolayer SRO and adjacent interfaces shown in Fig. 1e, an abrupt Ru peak out of the surrounding Ti peaks is evident. The abrupt SRO/STO interfaces are further corroborated by energy-dispersive X-ray spectroscopy (EDS) analysis in Fig. 1f. Taken together, we confirmed that our ultrathin SRO layers possess lateral uniformity and atomically sharp interfaces, which will allow for a systematic ARPES study.
Electronic structures of atomically thin SRO
Using the charging-free heterostructures in Fig. 1b, we examine the electronic ground state of the ultrathin SRO film. We performed in-situ ARPES on heterostructures with n = 0, 1, 2, 3, and 4 uc. Figure 1c shows angle-integrated photoemission spectra of the heterostructures near Γ. Definite Fermi edges survive down to the monolayer, showing the persistent density of states (DOS) at the Fermi level. A pronounced spectral weight is observed near the Fermi level for 4 and 3 uc samples, consistent with previously reported thick film ARPES results31. As the thickness is reduced, the spectral weight shifts toward the high-binding energy side, resulting in weak but definite spectral weight at the Fermi level for the 1 uc film. While the underlying mechanism for the spectral weight transfer needs further investigations, we can clearly observe a metallic electronic ground state for the monolayer SRO.
In order to better understand the metallic behavior of the monolayer SRO film in view of the electronic structure, we investigate the thickness-dependent evolution of the Fermi surfaces (FSs). FSs plotted in Fig. 2a are consistent with the angle-integrated photoemission results in Fig. 1c, showing metallic FSs down to the monolayer limit. Here, following the convention used for Sr2RuO432, we label the three FSs of the t2g bands as α, β, and γ as shown in Fig. 2b. The FS maps of 4 and 3 uc films in Fig. 2a show that α and β bands are sharp while the γ is broad. For the thinner 2 and 1 uc films, α and β bands are also slightly broadened. Otherwise, FSs do not show a qualitative change as the thickness varies.
Density functional theory (DFT) calculation of a monolayer SRO in Fig. 2b reproduces the characteristic band structure of experimentally observed FSs [See “Methods” for DFT calculation of a monolayer SRO]. The van Hove singularity (VHS) of the γ band is located at the X point. The broad spectral weight at the X point on the kx = 0 line (See Fig. 2a) indicates that the VHS lies close to the Fermi level. We would like to note that the spectral weight near the X point on the ky = 0 line is weak due to the matrix element effect; our ARPES data were measured with He-Iα light mostly polarized in the vertical direction33.
To look at a more detailed thickness-dependent evolution of the α and β bands which are composed of dyz and dzx orbitals, we plot in Fig. 2c Γ-M high-symmetry cut (‘Cut’ 1 in Fig. 2a) data and momentum distribution curves (MDCs) at the Fermi energy. We observe only two bands for the 2 and 1 uc films despite the three t2g orbitals. The two dispersive bands are attributed to α and β bands located near k∥ = 0.6 and 0.8Å−1, respectively, while the γ band can be counted out as we will discuss later. The α band, marked with an inverted triangle in the MDC plot in the upper panel, is resolved at the Fermi level regardless of the thickness [See “Supplementary Fig. 5” for the analysis on the β band]. Putting it all together, the α and β bands are dispersive at all thicknesses but their spectral functions gradually become less coherent as the thickness is reduced.
We now turn our attention to the γ band to understand the origin of the thickness-dependent spectral weight transfer to high-binding energy in ultrathin SROs. The VHS of the γ band at the X point lies close to the Fermi level which leads to the high DOS (Fig. 3a). Since the high DOS from a VHS can significantly affect the physical properties, it is worth examining the electronic band structures near the VHS. Figure 3b shows the E-k dispersions along the kx = 0 line, indicated as ‘Cut 2’ in Fig. 2a. In addition to the β band, a coherent heavy γ band is clearly observed in the 4 and 3 uc data, whereas the 2 and 1 uc data show only an incoherent γ band. As a side note, we attribute the weak β band to the matrix element effect as α and β bands remain consistently coherent at the Fermi level in the Γ-M (‘Cut 1’ in Fig. 2c) and the Γ-X data along the ky = 0 line [See “Supplementary Fig. 5” for details]33.
The thickness-dependent evolution of the γ band can be better seen in energy distribution curves (EDCs) near the X point, (kx, ky) = (0, 0.75), shown in Fig. 3c. The coherent peak marked by the inverted triangle appears as a kink in the EDCs in the 4 and 3 uc SRO data. On the other hand, the coherent peak disappears in the 2 and 1 uc SRO data, in which the spectral weight is believed to be transferred to the incoherent band. Such behavior is reminiscent of the strongly correlated metallic states in the vicinity of a Mott state as observed in, for example, under-doped cuprates above its superconducting dome34. Considering what we learned from the EDCs, it can be deduced that the thickness-dependent electronic transition is closely related to the strong correlation in the γ band. Therefore, we may refer to the electronic state of monolayer SRO as an orbital-selectively correlated and incoherent metal. The orbital selective correlated metallic behavior should be closely related to the orbital-selective Mott phase found in Ca2−xSrxRuO435.
Finally, we discuss the magnetism in these films. While bulk SRO is ferromagnet36, its quasi-2D analog, Sr2RuO4, does not show ferromagnetism29. It implies a possible magnetic transition in the ultrathin SRO films. We investigated the spin polarization of ultrathin SRO films by performing spin-resolved ARPES (SARPES). Figure 3d shows spin-resolved EDCs measured at 10 K near Γ. In the high-binding energy region, we observe a sizable difference in the intensity between majority and minority spins for 4 and 3 uc SRO films, indicating ferromagnetism24. However, the ferromagnetism is not observed for the 2 and 1 uc SRO films for which no difference is seen in the SARPES data.
Dimensionality-driven electronic transition
Note that the different behaviors between in- and out-of-plane orbital bands ascertain the quantum confinement (QC) effect of ultrathin SRO films37; the reduced dimensionality affects only the out-of-plane orbital dyz and dzx bands (Fig. 4a). We also notice that there is a remarkable coincidence between the band coherence and ferromagnetism in ultrathin SRO films. Both coherent-to-incoherent and ferromagnetic-to-nonmagnetic transitions start to occur at the 2 uc thickness, which suggests a strong interplay between electronic correlation and magnetism.
In 3D cubic SRO, three t2g orbitals (dxy, dyz, and dzx) are degenerate and each one of them has a VHS. The octahedral rotation, as well as the epitaxial strain, slightly breaks the degeneracy, resulting in a lower energy level for the dxy VHS, as schematically shown in Fig. 4c38,39. The QC effect selectively reconstructs the electronic structure of dyz and dzx orbitals. In the 2D monolayer limit, the dyz and dzx bands have strong 1D singularities at the band edges and reduced DOS at the Fermi level (‘2D’ in Fig. 4c). This reduction in the Fermi-level DOS induces the thickness-driven ferromagnetic-to-nonmagnetic transition between 3 and 2 uc SRO films37.
The high DOS from the dxy VHS (Fig. 4c) can enhance the effective electron correlation, e.g., Coulomb interaction and Hund’s coupling40. The instability from the high DOS at the Fermi level can be avoided by splitting the dxy band into spin majority and minority bands, as shown for 4 and 3 uc SRO (left panel, Fig. 4d). However, without the ferromagnetic spin splitting, the dxy band in 1 and 2 uc films retains the VHS, and thus the high DOS near the Fermi level. Then, the strong correlation drives the monolayer SRO system to an incoherent-metallic phase (right panel, Fig. 4d). The bilayer SRO case is presumably at the boundary between the coherent ferromagnetic metal and incoherent correlated metal.
Control of the 2D correlated electronic phase
With the underlying mechanism for the thickness-driven electronic transition understood, we attempt to exploit the mechanism to control the electronic phase of the monolayer SRO. As the key to the incoherent-metallic phases is the VHS, tuning the chemical potential is likely to break the correlated phase (right panel, Fig. 4d). We used in-situ K dosing to dope electrons into the incoherent-metallic phase of monolayer SRO. Figure 5a shows FS maps of monolayer SRO before and after K dosing. The Fermi wavevector, kF, of the β band changes from 0.52 to 0.60 Å−1 along the kx = 0 line, indicating that electrons are doped into the system [see “Supplementary Fig. 8” for E-k dispersions and MDCs]. Overall, the K-dosed FS feature is much better resolved in comparison with the result of the pristine case.
The most distinct change occurs in the γ band. Figure 5b shows E-k band dispersions along the kx = − 0.2 Å−1 line before and after K dosing. The strongly correlated γ band has never been sharply resolved in the pristine state but it appears coherent with a clear dispersive feature after K dosing. The γ FS became a hole pocket, which indicates the VHS is now located below the Fermi level (Fig. 2b). This is consistent with our scenario proposed above; the electron doping moves the VHS away from the Fermi level, and consequently, the spectral weight is transferred from the incoherent to coherent peaks. EDCs in Fig. 5c show spectral-weight transfer as well as the emergence of the coherent quasi-particle peak.
We also noticed that the high-binding hump-like peak at E = −1.5 eV, which is only observed in monolayer SRO (Fig. 1c), disappears after K dosing as shown in Fig. 5d. A similar hump-like peak at high-binding energy has been reported in photoemission spectroscopy results of CaRuO3 and (Ca, Sr)VO341,42 and was attributed to a strong electronic correlation effect. When the Coulomb interaction between electrons increases, a coherent peak near the Fermi level is expected to be suppressed because its spectral weight is transferred to the incoherent lower Hubbard band42,43,44. Thus, we believe that the appearance of the high-binding energy hump with decreasing thickness is also a sign of enhanced electronic correlation in thinner films. The disappearance of the hump-like peak upon K dosing reveals that electron correlations become weaker as the VHS moves away from the Fermi level.
It is worth mentioning a couple of findings from the electron-doping experiments of single-atomic-layer SRO. First of all, we can exclude extrinsic disorders as the origin of the incoherent metallicity in the monolayer SRO. If the incoherent metallicity were due to defects or disorders, it would have been persistent even after K dosing. The reappearance of the coherent peak and disappearance of the high-binding energy hump peak with K dosing support the view for the intrinsic nature of the observed incoherent metallicity of monolayer SRO. The other is that K-dosing results highlight the rich spectrum of electronic phases in monolayer SRO and their giant tunability via charge modulation. The considerable spectral weight at the Fermi energy and clear dispersive bands indicate a good metallicity in the electron-doped monolayer SRO. The incoherent-to-coherent crossover might be exploited to realize atomically thin oxide field-effect-transistors, which have not been realized so far.
2D materials and their applications are a rapidly growing field in contemporary condensed matter physics and materials science. This trend is becoming predominant not only for van der Waals materials but also for oxides. In very recent years, free-standing oxide membranes have been prepared out of the epitaxial oxide heterostructures45, and the size has reached a wafer scale46. Moreover, the high-quality membranes of dielectric oxides are shown to maintain their crystallinity even down to the monolayer limit47. By demonstrating a metallic single-atomic-layer oxide, our work expands the scope of 2D oxides that has been limited to insulators so far. The strong electronic correlation gives rise to highly tunable correlated electronic phases, which will be a distinct and advantageous feature of 2D oxides for future research on-device applications. We expect that other emergent phases in oxides, such as unconventional superconductivity48, could appear in a single-atomic-layer and thus that our findings pave the way to the two-dimensional correlated electronics49,50.
Methods
Fabrication of heterostructures
Epitaxial SrRuO3 and SrTiO3 thin films were grown on (001)-oriented SrTiO3 single crystal substrates by the pulsed laser deposition technique. Prior to the growth, the SrTiO3 substrate was dipped in deionized water and sonicated for 30 minutes. The substrate was subsequently in-situ annealed in the growth chamber, and the annealing temperature, background oxygen partial pressure, and annealing time were 1,050 ∘C, 5.0 × 10−6 Torr, and 30 min, respectively. Polycrystalline SrRuO3 and SrTiO3 targets were ablated using a KrF excimer laser. For the growth of SrRuO3 films, the substrate temperature, background oxygen partial pressure, and laser energy density were kept at 670 ∘C, 100 mTorr, and 1.9 J/cm2, respectively. For the growth of SrTiO3 films, the substrate temperature, background oxygen partial pressure, and laser energy density were kept at 670 ∘C, 10 mTorr, and 1.2 J/cm2, respectively. After the growth, all samples have been cooled down to the room temperature with a rate of 50 ∘C/min in an oxygen partial pressure of 100 mTorr.
In-situ angle-resolved photoemission spectroscopy
In-situ ARPES measurements were performed at 10 K using the home lab system equipped with a Scienta DA30 analyzer and a discharge lamp from the Fermi instrument. He-Iα (hv = 21.2 eV) light partially polarized with linear vertical was used. Low-energy electron diffraction patterns are taken after ARPES measurements. Spin polarization was measured with a spin-resolved ARPES system in our laboratory. The system was equipped with a SPECS PHOIBOS 225 analyzer and a very low energy electron diffraction (VLEED) spin detector. For the spin detector, an oxidized iron film deposited on W(100) was used as the scattering target. He-Iα (hv = 21.2 eV) light was used as the light source. To clean the surface of SRO thin films, we post-annealed them at 550 ∘C for 10 mins [See “Supplementary Fig. 9” for details].
First-principles calculation
We performed the first-principles calculation using the DFT method without spin-orbit coupling. The PBEsol form of the exchange-correlation functional was used as implemented in VASP51,52. To simulate our experimental situation, we prepared a slab geometry with 20 Å vacuum in which 4 uc of SrTiO3 is sandwiched by 1 uc of SrRuO3 which preserves the mirror symmetry with respect to the middle SrO layer. We used a 600 eV plane wave cut-off energy and 12 × 12 × 1 k-points for all calculations and the projector augmented wave method. During the geometry optimizations, the in-plane lattice constant was fixed at the experimental value of SrTiO3, 3.905 Å, and the tolerance on atomic forces was set to 4 meV Å−1. The electronic density of states was calculated using a fine mesh 12 × 12 × 1 k-points. For the Fermi surface calculations, we used the PyProcar package53 to unfold the band structure. The chemical potential in the calculated dispersion was shifted by 70 meV so that kF of the β band coincides with the experimental value.
Scanning transmission electron microscopy measurement
Cross-sectional scanning transmission electron microscopy (STEM) specimen was prepared utilizing focused ion beam milling with FEI Helios 650 FIB and further thinned by focused Ar-ion milling with Fischione NanoMill 1040. STEM images and energy-dispersive X-ray spectroscopy (EDS) were acquired using Thermo Fisher Scientific Themis Z equipped with a corrector of spherical aberrations, a high-brightness Schottky-field emission gun operated at a 300 kV electron acceleration voltage, and Super-X EDX system. The semi-convergence angle of the electron probe was 25.1 mrad.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5, 722–726 (2010).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Cao, Y. et al. Correlated insulator behaviour at half-filling in magic-angle graphene superlattices. Nature 556, 80–84 (2018).
Cao, Y. et al. Unconventional superconductivity in magic-angle graphene superlattices. Nature 556, 43–50 (2018).
Imada, M., Fujimori, A. & Tokura, Y. Metal-insulator transitions. Rev. Mod. Phys. 70, 1039 (1998).
Dagotto, E. Correlated electrons in high-temperature superconductors. Rev. Mod. Phys. 66, 763 (1994).
Tokura, Y. & Tomioka, Y. Colossal magnetoresistive manganites. J. Magn. Magn. Mater. 200, 1–23 (1999).
Yu, Y. et al. High-temperature superconductivity in monolayer Bi2Sr2CaCu2O8+δ. Nature 575, 156–163 (2019).
Hu, G. et al. Topological polaritons and photonic magic angles in twisted α-MoO3 bilayers. Nature 582, 209–213 (2020).
Schlom, D. G. et al. Elastic strain engineering of ferroic oxides. MRS Bulletin 39, 118–130 (2014).
McKee, R. A., Walker, F. J. & Chisholm, M. F. Crystalline oxides on silicon: the first five monolayers. Phys. Rev. Lett. 81, 3014 (1998).
Scherwitzl, R. et al. Metal-insulator transition in ultrathin LaNiO3 films. Phys. Rev. Lett. 106, 246403 (2011).
Huijben, M. et al. Critical thickness and orbital ordering in ultrathin La0.7Sr0.3MnO3 films. Phys. Rev. B 78, 094413 (2008).
Anderson, P. W. Absence of diffusion in certain random lattices. Phys. Rev. 109, 1492 (1958).
Ge, J.-F. et al. Superconductivity above 100 K in single-layer FeSe films on doped SrTiO3. Nat. Mater. 14, 285–289 (2015).
Lagally, M. G. & Zhang, Z. Thin-film cliffhanger. Nature 417, 907–909 (2002).
Schütz, P. et al. Dimensionality-driven metal-insulator transition in spin-orbit-coupled SrIrO3. Phys. Rev. Lett. 119, 256404 (2017).
Yoshimatsu, K. et al. Metallic quantum well states in artificial structures of strongly correlated oxide. Science 333, 319–322 (2011).
King, P. et al. Atomic-scale control of competing electronic phases in ultrathin LaNiO3. Nat. Nanotechnol. 9, 443–447 (2014).
Yoo, H. K. et al. Thickness-dependent electronic structure in ultrathin LaNiO3 films under tensile strain. Phys. Rev. B 93, 035141 (2016).
Sohn, B. et al. Sign-tunable anomalous hall effect induced by symmetry-protected nodal structures in ferromagnetic perovskite oxide thin films. Nat Mater. https://doi.org/10.1038/s41563-021-01101-4 (2021).
Kim, B. et al. Novel Jeff = 1/2 Mott state induced by relativistic spin-orbit coupling in Sr2IrO4. Phys. Rev. Lett. 101, 076402 (2008).
Uchida, M. et al. Pseudogap of metallic layered nickelate R2−xSrxNiO4 (R = Nd, Eu) crystals measured using angle-resolved photoemission spectroscopy. Phys. Rev. Lett. 106, 027001 (2011).
Jeong, S. G. et al. Phase instability amid dimensional crossover in artificial oxide crystal. Phys. Rev. Lett. 124, 026401 (2020).
Boschker, H. et al. Ferromagnetism and conductivity in atomically thin SrRuO3. Phys. Rev. X 9, 011027 (2019).
Mackenzie, A. P. & Maeno, Y. The superconductivity of Sr2RuO4 and the physics of spin-triplet pairing. Rev. Mod. Phys. 75, 657 (2003).
Grinenko, V. et al. Split superconducting and time-reversal symmetry-breaking transitions in Sr2RuO4 under stress. Nat. Phys. 17, 748–754 (2021).
Shai, D. et al. Quasiparticle mass enhancement and temperature dependence of the electronic structure of ferromagnetic SrRuO3 thin films. Phys. Rev. Lett. 110, 087004 (2013).
Puchkov, A., Shen, Z.-X., Kimura, T. & Tokura, Y. ARPES results on Sr2RuO4: Fermi surface revisited. Phys. Rev. B 58, R13322 (1998).
Iwasawa, H. et al. Interplay among coulomb interaction, spin-orbit interaction, and multiple electron-boson interactions in Sr2RuO4. Phys. Rev. Lett. 105, 226406 (2010).
Chen, S.-D. et al. Incoherent strange metal sharply bounded by a critical doping in Bi2212. Science 366, 1099–1102 (2019).
Kim, M. et al. Observation of kondo hybridization with an orbital-selective mott phase in 4d Ca2−xSrxRuO4. arXiv https://doi.org/10.21203/rs.3.rs-48339/v1 (2021).
Koster, G. et al. Structure, physical properties, and applications of SrRuO3 thin films. Rev. Mod. Phys. 84, 253 (2012).
Chang, Y. J. et al. Fundamental thickness limit of itinerant ferromagnetic SrRuO3 thin films. Phys. Rev. Lett. 103, 057201 (2009).
Kim, B., Khmelevskyi, S., Franchini, C., Mazin, I. & Kim, K. SrRuO3-SrTiO3 heterostructure as a possible platform for studying unconventional superconductivity in Sr2RuO4. Phys. Rev. B 101, 220502 (2020).
Ko, E., Kim, B., Kim, C. & Choi, H. J. Strong orbital-dependent d-band hybridization and Fermi-surface reconstruction in metallic Ca2−xSrxRuO4. Phys. Rev. Lett. 98, 226401 (2007).
Lee, H. J., Kim, C. H. & Go, A. Interplay between spin-orbit coupling and Van Hove singularity in the Hund’s metallicity of Sr2RuO4. Phys. Rev. B 102, 195115 (2020).
Maiti, K. et al. Electronic structure of Ca1−xSrxVO3: a tale of two energy scales. Europhys. Lett. 55, 246 (2001).
Yang, H. F. et al. Comparative angle-resolved photoemission spectroscopy study of CaRuO3 and SrRuO3 thin films: pronounced spectral weight transfer and possible precursor of lower hubbard band. Phys. Rev. B 94, 115151 (2016).
Mo, S.-K. et al. Prominent quasiparticle peak in the photoemission spectrum of the metallic phase of V2O3. Phys. Rev. Lett. 90, 186403 (2003).
Neupane, M. et al. Observation of a novel orbital selective mott transition in Ca1.8Sr0.2RuO4. Phys. Rev. Lett. 103, 097001 (2009).
Lu, D. et al. Synthesis of freestanding single-crystal perovskite films and heterostructures by etching of sacrificial water-soluble layers. Nat. Mater. 15, 1255–1260 (2016).
Kum, H. S. et al. Heterogeneous integration of single-crystalline complex-oxide membranes. Nature 578, 75–81 (2020).
Ji, D. et al. Freestanding crystalline oxide perovskites down to the monolayer limit. Nature 570, 87–90 (2019).
Kim, Y. K. et al. Fermi arcs in a doped pseudospin-1/2 Heisenberg antiferromagnet. Science 345, 187–190 (2014).
Takagi, H. & Hwang, H. Y. An emergent change of phase for electronics. Science 327, 1601–1602 (2010).
Ahn, C., Triscone, J.-M. & Mannhart, J. Electric field effect in correlated oxide systems. Nature 424, 1015–1018 (2003).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).
Herath, U. et al. Pyprocar: a python library for electronic structure pre/post-processing. Comput. Phys. Commun. 251, 107080 (2020).
Acknowledgements
We gratefully acknowledge useful discussions with Woo Seok Choi, Kookrin Char, Kee Hoon Kim, Hongki Min, Bohm Jung Yang, Sang Mo Yang, and Seo Hyoung Chang. This work is supported by the Institute for Basic science in Korea (Grant No. IBS-R009-D1, IBS-R009-G2). We acknowledge the support from the Korean government through National Research Foundation (2017R1A2B3011629). Cs-corrected STEM works were supported by the Research Institute of Advanced Materials (RIAM) in Seoul National University.
Author information
Authors and Affiliations
Contributions
B.S., J.R.K., T.W.N. and C.K. conceived the project. B.S. synthesized and characterized the SrRuO3 films. J.R.K. conceived and fabricated the charging-free ultrathin heterostructures. B.S., J.R.K., Youns.K., D.K. and Young.K. conducted ARPES measurements. B.S., Sung.H. and Soon.H. conducted spin-resolved ARPES measurements. C.H.K. carried out first-principle calculations. S.L. performed TEM analysis under the supervision of M.K., B.S. and J.R.K. analyzed ARPES data supported by W.K. and M.K., B.S., J.R.K., T.W.N. and C.K. wrote the paper with contributions from other authors. All authors participated in the discussions and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Dawei Shen and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sohn, B., Kim, J.R., Kim, C.H. et al. Observation of metallic electronic structure in a single-atomic-layer oxide. Nat Commun 12, 6171 (2021). https://doi.org/10.1038/s41467-021-26444-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-26444-z
This article is cited by
-
Tuning orbital-selective phase transitions in a two-dimensional Hund’s correlated system
Nature Communications (2023)
-
From Stoner to local moment magnetism in atomically thin Cr2Te3
Nature Communications (2023)
-
Quantization condition of strongly correlated electrons in oxide nanostructures
Communications Materials (2023)
-
Emergent ferromagnetism and insulator-metal transition in δ-doped ultrathin ruthenates
npj Quantum Materials (2022)
-
Evolution of electronic band reconstruction in thickness-controlled perovskite SrRuO\(_3\) thin films
Journal of the Korean Physical Society (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.