Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Individually addressable epitaxial ferroelectric nanocapacitor arrays with near Tb inch−2 density

Abstract

Ferroelectric materials have emerged in recent years as an alternative to magnetic and dielectric materials for nonvolatile data-storage applications1,2,3,4,5. Lithography is widely used to reduce the size of data-storage elements in ultrahigh-density memory devices6,7,8,9. However, ferroelectric materials tend to be oxides with complex structures that are easily damaged by existing lithographic techniques, so an alternative approach is needed to fabricate ultrahigh-density ferroelectric memories. Here we report a high-temperature deposition process that can fabricate arrays of individually addressable metal/ferroelectric/metal nanocapacitors with a density of 176 Gb inch−2. The use of an ultrathin anodic alumina membrane as a lift-off mask makes it possible to deposit the memory elements at temperatures as high as 650 °C, which results in excellent ferroelectric properties.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Fabrication of the nanocapacitors.
Figure 2: MFM nanocapacitor.
Figure 3: Ferroelectric properties.
Figure 4: High-resolution X-ray diffraction patterns of epitaxial PZT nanoislands grown on Pt/MgO(100).

Similar content being viewed by others

References

  1. Auciello, O., Scott, J. F. & Ramesh, R. The physics of ferroelectric memories. Phys. Today 51, 22–27 (July 1998).

    Article  CAS  Google Scholar 

  2. Cheong, S.-W. & Mostovoy, M. Multiferroics: a magnetic twist for ferroelectricity. Nature Mater. 6, 13–20 (2007).

    Article  CAS  Google Scholar 

  3. Cho, Y. Nanoscale ferroelectric information storage based on scanning nonlinear dielectric microscopy. J. Nanosci. Nanotechnol. 7, 105–116 (2007).

    CAS  Google Scholar 

  4. Cross, L. E. Ferroelectric Ceramics (ed. Setter, N. ) 1–85 (Birkhäuser, Basel, 1993).

    Book  Google Scholar 

  5. Evans, P. R. et al. Toward self-assembled ferroelectric random access memories: Hard-wired switching capacitor arrays with almost Tb/in.2 densities. Nano Lett. 7, 1134–1137 (2007).

    Article  CAS  Google Scholar 

  6. Alexe, M., Harnagea, C., Hesse, D. & Gösele, U. Polarization imprint and size effects in mesoscopic ferroelectric structures. Appl. Phys. Lett. 70, 242–244 (2001).

    Article  Google Scholar 

  7. Bühlmann, S., Dwir, B., Baborowski, J. & Muralt, P. Size effect in mesoscopic epitaxial ferroelectric structures: Increase of piezoelectric response with decreasing feature size. Appl. Phys. Lett. 80, 3195–3197 (2002).

    Article  Google Scholar 

  8. Ganpule, C. S. et al. Scaling of ferroelectric and piezoelectric properties in Pt/SrBi2Ta2O9/Pt thin films. Appl. Phys. Lett. 75, 3874–3876 (1999).

    Article  CAS  Google Scholar 

  9. Stanishevsky, A. et al. Radiation damage and its recovery in focused ion beam fabricated ferroelectric capacitors. J. Appl. Phys. 92, 3275–3278 (2002).

    Article  CAS  Google Scholar 

  10. Ahn, C. H. et al. Local, nonvolatile electronic writing of epitaxial Pb(Zr0.52Ti0.48)O3/SrRuO3 heterostructures. Science 276, 1100–1103 (1997).

    Article  CAS  Google Scholar 

  11. Gruverman, A., Auciello, O. & Tokumoto, H. Imaging and control of domain structures in ferroelectric thin films via scanning force microscopy. Annu. Rev. Mater. Sci. 28, 101–123 (1998).

    Article  CAS  Google Scholar 

  12. Cho, Y., Hashimoto, S., Odagawa, N., Tanaka, K. & Hiranaga, Y. Nanodomain manipulation for ultrahigh density ferroelectric data storage. Nanotechnology 17, S137–S141 (2006).

    Article  CAS  Google Scholar 

  13. Kalinin, S. V. et al. Intrinsic single-domain switching in ferroelectric materials on a nearly ideal surface. Proc. Natl Acad. Sci. USA 104, 20204–20209 (2007).

    Article  CAS  Google Scholar 

  14. Odagawa, N. & Cho, Y. Wall behavior of nanodomains as a function of their initial state. Appl. Phys. Lett. 89, 192906 (2006).

    Article  Google Scholar 

  15. Torii, K. et al. Fabrication and properties of one-mask-patterned ferroelectric integrated capacitors. Electr. Eng. Jpn. 121, 43–50 (1997).

    Article  Google Scholar 

  16. Lee, S.-K. et al. Well-ordered large-area arrays of epitaxial ferroelectric (Bi,La)4Ti3O12 nanostructures fabricated by gold nanotube-membrane lithography. Appl. Phys. Lett. 86, 152906 (2005).

    Article  Google Scholar 

  17. Lee, W., Alexe, M., Nielsch, K. & Gösele, U. Metal membranes with hierarchically organized nanotube arrays. Chem. Mater. 17, 3325–3327 (2005).

    Article  CAS  Google Scholar 

  18. Chu, M.-W., Szafraniak, I., Hesse, D., Alexe, M. & Gösele, U. Elastic coupling between 90 ° twin walls and interfacial dislocations in epitaxial ferroelectric perovskites: A quantitative high-resolution transmission electron microscopy study. Phys. Rev. B 72, 174112 (2005).

    Article  Google Scholar 

  19. Lee, K., Yi, H., Park, W.-H., Kim, Y. K. & Baik, S. Lateral size effects on domain structure in epitaxial PbTiO3 thin films. J. Appl. Phys. 100, 051615 (2006).

    Article  Google Scholar 

  20. Jesse, S. et al. Direct imaging of the spatial and energy distribution of nucleation centers in ferroelectric materials. Nature Mater. 7, 209–215 (2008).

    Article  CAS  Google Scholar 

  21. Lee, K., Kim, K., Kwon, S.-J. & Baik, S. Two-dimensional planar size effects in epitaxial PbTiO3 thin films. Appl. Phys. Lett. 85, 4711–4713 (2004).

    Article  CAS  Google Scholar 

  22. Nagarajan, V. et al. Dynamics of ferroelastic domains in ferroelectric thin films. Nature Mater. 2, 43–47 (2002).

    Article  Google Scholar 

  23. Speck, J. S. & Pompe, W. Domain configurations due to multiple misfit relaxation mechanisms in epitaxial ferroelectric thin films. I. Theory. J. Appl. Phys. 76, 466–476 (1994).

    Article  CAS  Google Scholar 

  24. Masuda, H. & Fukuda, K. Ordered metal nanohole arrays made by a two-step replication of honeycomb structures of anodic alumina. Science 268, 1466–1468 (1995).

    Article  CAS  Google Scholar 

  25. Li, A. P., Müller, F., Birner, A., Nielsch, K. & Gösele, U. Hexagonal pore arrays with a 50–420 nm interpore distance formed by self-organization in anodic alumina. J. Appl. Phys. 84, 6023–6026 (1998).

    Article  CAS  Google Scholar 

  26. Lee, W., Ji, R., Ross, C. A., Gösele, U. & Nielsch, K. Wafer-scale Ni imprint stamps for porous alumina membranes based on interference lithography. Small 2, 978–982 (2006).

    Article  CAS  Google Scholar 

  27. Choi, J., Nielsch, K., Reiche, R., Wehrspohn, R. B. & Gösele, U. Fabrication of monodomain alumina pore arrays with an interpore distance smaller than the lattice constant of the imprint stamp. J. Vac. Sci. Technol. B 21, 763–766 (2003).

    Article  CAS  Google Scholar 

  28. Sun, Z. & Kim, H. K. Growth of ordered, single-domain, alumina nanopore arrays with holographically patterned aluminum films. Appl. Phys. Lett. 81, 3458–3460 (2002).

    Article  CAS  Google Scholar 

  29. Masuda, H., Yamada, H., Satoh, M. & Asoh, H. Highly ordered nanochannel-array architecture in anodic alumina. Appl. Phys. Lett. 71, 2770–2772 (1997).

    Article  CAS  Google Scholar 

  30. Lee, W., Ji, R., Gösele, U. & Nielsch, K. Fast fabrication of long-range ordered porous alumina membranes by hard anodization. Nature Mater. 5, 741–747 (2006).

    Article  CAS  Google Scholar 

  31. Harnagea, C., Pignolet, A., Alexe, M. & Hesse, D. Piezoresponse scanning force microscopy: What quantitative information can we really get out of piezoresponse measurements on ferroelectric thin films. Intergr. Ferroelectr. 44, 113–124 (2002).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

H. Han is grateful for the award of a fellowship of the German Academic Exchange Service (DAAD) and for support by DFG and KRF. Financial support from the Volkswagen Foundation (Project I/80897) and partly from the Brain Korea 21 Program is also acknowledged. We are thankful to S. Swatek and N. Schammelt for TEM sample preparation. We also thank R. Hillebrand for discussions on statistical analyses for the size distribution and 2D ordering of ferroelectric nanocapacitors.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Woo Lee.

Supplementary information

Rights and permissions

Reprints and permissions

About this article

Cite this article

Lee, W., Han, H., Lotnyk, A. et al. Individually addressable epitaxial ferroelectric nanocapacitor arrays with near Tb inch−2 density. Nature Nanotech 3, 402–407 (2008). https://doi.org/10.1038/nnano.2008.161

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nnano.2008.161

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing