Abstract
The oxygen storage capacity of Ce0.2Zr0.8O2 solid solutions, prepared by different synthesis routes and aged at 1000°C, is investigated by means of temperature-programmed reduction, total- and dynamic-OSC measurements. The use of CO and H2 as reducing agent is compared under dynamic conditions. It is observed that the dynamic OSC is critically dependent on sample pre-treatment and the nature of the reducing agent in the texturally unstable sample. In contrast, on a thermally stable Ce0.2Zr0.8O2 only minor effects of the pre-treatment upon dynamic OSC are noticed.
Similar content being viewed by others
References
J. Kašpar, P. Fornasiero and M. Graziani, Catal. Today 50 (1999) 285.
J.P. Cuif, G. Blanchard, O. Touret, A. Seigneurin, M. Marczi and E. Quémeré, SAE 970463 (1997).
G. Balducci, P. Fornasiero, R. Di Monte, J. Kašpar, S. Meriani and M. Graziani, Catal. Lett. 33 (1995) 193.
P. Fornasiero, G. Balducci, R. Di Monte, J. Kašpar, V. Sergo, G. Gubitosa, A. Ferrero and M. Graziani, J. Catal. 164 (1996) 173.
N. Izu, T. Omata and S. Otsuka-Yao-Matsuo, J. Alloys Compd. 270 (1998) 107.
S. Otsuka-Yao-Matsuo, T. Omata, N. Izu and H. Kishimoto, J. Solid State Chem. 138 (1998) 47.
R.T. Baker, S. Bernal, G. Blanco, A.M. Cordon, J.M. Pintado, J.M. Rodriguez-Izquierdo, F. Fally and V. Perrichon, J. Chem. Soc. Chem. Commun. (1999) 149.
P. Fornasiero, J. Kašpar and M. Graziani, Appl. Catal. B 22 (1999) L11.
P. Fornasiero, R. Di Monte, G. Ranga Rao, J. Kašpar, S. Meriani, A. Trovarelli and M. Graziani, J. Catal. 151 (1995) 168.
G. Vlaic, P. Fornasiero, S. Geremia, J. Kašpar and M. Graziani, J. Catal. 168 (1997) 386.
G. Vlaic, R. Di Monte, P. Fornasiero, E. Fonda, J. Kašpar and M. Graziani, J. Catal. 182 (1999) 378.
C.E. Hori, H. Permana, K.Y.S. Ng, A. Brenner, K. More, K.M. Rahmoeller and D.N. Belton, Appl. Catal. B 16 (1998) 105.
T. Egami, W. Dmowski and R. Brezny, SAE 970461 (1997).
P. Vidmar, P. Fornasiero, J. Kašpar, G. Gubitosa and M. Graziani, J. Catal. 171 (1997) 160.
P. Courty, H. Ajot, C. Marcilly and B. Delmon, Powder Technol. 7 (1973) 21.
C. Marcilly, P. Courty and B. Delmon, J. Am. Ceram. Soc. 53 (1970) 56.
M. Yashima, H. Arashi, M. Kakihana and M. Yoshimura, J. Am. Ceram. Soc. 77 (1994) 1067.
G. Colon, F. Valdivieso, M. Pijolat, R.T. Baker, J.J. Calvino and S. Bernal, Catal. Today 50 (1999) 271.
D. Kim, H. Jung and I. Yang, J. Am. Ceram. Soc. 76 (1993) 2106.
M. Maczka, E.T.G. Lutz, H.J. Verbeek, K. Oskam, A. Meijerink, J. Hanuza and M. Stuivinga, J. Phys. Chem. Solids 60 (1999) 1909.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kašpar, J., Di Monte, R., Fornasiero, P. et al. Dependency of the Oxygen Storage Capacity in Zirconia–Ceria Solid Solutions upon Textural Properties. Topics in Catalysis 16, 83–87 (2001). https://doi.org/10.1023/A:1016682831177
Issue Date:
DOI: https://doi.org/10.1023/A:1016682831177