Ultramicrohardness of aluminum and aluminum alloy thin films

doi:10.1016/0040-6090(89)90117-X

Thin Solid Films

Volume 172, Issue 1, 1 May 1989, Pages 51-60

https://doi.org/10.1016/0040-6090(89)90117-X Get rights and content

Abstract

The ultramicrohardness (UMH) of vapor-deposited aluminum and aluminum alloy thin films was determined at room temperature by indentation experiments at small indenter forces. For pure aluminum films both the dependence of the measured hardness upon film thickness and the hardness-microstructure relationship are described. The increase in UMH of aluminum by alloying was studied for alloy films prepared by simultaneous vapor deposition of aluminum with the metals silver, copper, titanium or vanadium.

The hardness of the pure aluminum films hardly changes upon annealing. The as-deposited aluminum alloy films are single-phase alloys, which are highly supersaturated. Consequently, their hardness values are rather high. Alloy softening was observed after an anneal treatment at relatively high temperature. The importance of the various hardening mechanisms will be discussed.

References (13)

J.J. van den Broek et al.
Thin Solid Films
(1985)
P.E. Wierenga et al.
Thin Solid Films
(1984)
A. Wagendristel et al.
Thin Solid Films
(1987)
H. Bangert et al.
Thin Solid Films
(1986)
Y. Tsukamoto et al.
Thin Solid Films
(1987)
T.B. Massalski et al.
Binary Alloy Phase Diagrams
(1986)

There are more references available in the full text version of this article.

Cited by (0)

View full text